CN104058718A - High-strength jade bluish white porcelain - Google Patents

High-strength jade bluish white porcelain Download PDF

Info

Publication number
CN104058718A
CN104058718A CN201410297579.2A CN201410297579A CN104058718A CN 104058718 A CN104058718 A CN 104058718A CN 201410297579 A CN201410297579 A CN 201410297579A CN 104058718 A CN104058718 A CN 104058718A
Authority
CN
China
Prior art keywords
parts
porcelain
strength
bluish white
white
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410297579.2A
Other languages
Chinese (zh)
Inventor
王爱国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Guohang Xiangyu Technology Service Co Ltd
Original Assignee
Qingdao Guohang Xiangyu Technology Service Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Guohang Xiangyu Technology Service Co Ltd filed Critical Qingdao Guohang Xiangyu Technology Service Co Ltd
Priority to CN201410297579.2A priority Critical patent/CN104058718A/en
Publication of CN104058718A publication Critical patent/CN104058718A/en
Pending legal-status Critical Current

Abstract

The invention discloses high-strength jade bluish white porcelain which is characterized by comprising the following substances in parts by weight: 15-30 parts of kaolin from the Ma Cang mountain, 20-30 parts of white feldspar, 5-10 parts of aluminum nitride, 10-15 parts of kaolin, 3-12 parts of sodium oxide, 11-32 parts of niobium pentoxide, 7-14 parts of cobalt oxide, 25-34 parts of white feldspar, 6-19 parts of quartz, 10-19 parts of magnesite, 10-18 parts of smaltum, 20-29 parts of nepheline, 3-8 parts of illite, 3-5 parts of aluminum oxide, 10-19 parts of talcum powder, 9-18 parts of iron ores and 15-27 parts of agate. The high-strength jade bluish white porcelain has the beneficial effects that all raw material components in the technical scheme are firmly combined; the preparation method can be used for improving the strength of Ru porcelain and avoiding generating cracks; the prepared Ru porcelain is uniform in texture and attractive in body color; external gracked glaze is adopted to replace internal gracked glaze, so that the high-strength jade bluish white porcelain is convenient to use and free of influence to attractive appearance.

Description

The beautiful bluish white tire porcelain of a kind of high strength
Technical field
The present invention relates to the beautiful bluish white tire porcelain of a kind of high strength.
Background technology
One of Ru Cishi China five your name's porcelain, its manufacturing process is once once lost, by technician's lucubrate, now resumes production.It is modelled after an antique as main that but your current porcelain making still be take, and its manufacture craft also exists certain deficiency.In the manufacture craft of your porcelain, your porcelain tea set of little device shape is two-way hacking, and due to the long-time use of tea set, easily in tea set inside, hacks the residual tea stain of cracks, affects the use of tea set, has affected the sight of your porcelain and the value of artwork.
Summary of the invention
Technical problem to be solved by this invention is to provide the beautiful bluish white tire porcelain of a kind of high strength.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
The beautiful bluish white tire porcelain of high strength, is characterized in that, comprises the material of following parts by weight: numb storehouse soil 15-30 part, white feldspar 20-30 part, aluminium nitride 5-10 part, kaolin 10-15 part, sodium oxide 3-12 part, Niobium Pentxoxide 11-32 part, cobalt oxide 7-14 part, white feldspar 25-34 part, quartzy 6-19 part, magnesite 10-19 part, Soviet Union fiber crops are from blue or green 10-18 part, nepheline 20-29 part, illite 3-8 part, aluminum oxide 3-5 part, talcum powder 10-19 part, iron ore 9-18 part, Agate 15-27 part.
The invention has the beneficial effects as follows:
In the technical program, each material composition is in conjunction with firmly, and preparation method can improve the intensity of your porcelain, prevents that crackle from producing, and your porcelain made is homogeneous, tire look attractive in appearance, hacks outward, inside do not hack easy to use not affecting the appearance.
Embodiment
Embodiment 1
The beautiful bluish white tire porcelain of high strength, comprises the material of following parts by weight: 15 parts, numb storehouse soil, 20 parts of white feldspars, 10 parts of aluminium nitride, 10 parts of kaolin, 3 parts of sodium oxides, 15 parts of Niobium Pentxoxides, 7 parts of cobalt oxides, 34 parts of white feldspars, quartzy 6 parts, magnesite 10-19 part, Soviet Union fiber crops are from blue or green 18 parts, 20 parts of nephelines, 8 parts of illites, 5 parts, aluminum oxide, 19 parts of talcum powder, 18 parts of iron ores, 27 parts of Agates.

Claims (1)

1. the beautiful bluish white tire porcelain of high strength, is characterized in that, comprises the material of following parts by weight: numb storehouse soil 15-30 part, white feldspar 20-30 part, aluminium nitride 5-10 part, kaolin 10-15 part, sodium oxide 3-12 part, Niobium Pentxoxide 11-32 part, cobalt oxide 7-14 part, white feldspar 25-34 part, quartzy 6-19 part, magnesite 10-19 part, Soviet Union fiber crops are from blue or green 10-18 part, nepheline 20-29 part, illite 3-8 part, aluminum oxide 3-5 part, talcum powder 10-19 part, iron ore 9-18 part, Agate 15-27 part.
CN201410297579.2A 2014-06-29 2014-06-29 High-strength jade bluish white porcelain Pending CN104058718A (en)