CN104047003A - 一种除铜表面氧化皮的方法 - Google Patents

一种除铜表面氧化皮的方法 Download PDF

Info

Publication number
CN104047003A
CN104047003A CN201410283251.5A CN201410283251A CN104047003A CN 104047003 A CN104047003 A CN 104047003A CN 201410283251 A CN201410283251 A CN 201410283251A CN 104047003 A CN104047003 A CN 104047003A
Authority
CN
China
Prior art keywords
copper
surface scale
removal surface
copper removal
oxide scale
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410283251.5A
Other languages
English (en)
Inventor
冯玉权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuzhou Hengsheng Electronic Technology Co Ltd
Original Assignee
Wuzhou Hengsheng Electronic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuzhou Hengsheng Electronic Technology Co Ltd filed Critical Wuzhou Hengsheng Electronic Technology Co Ltd
Priority to CN201410283251.5A priority Critical patent/CN104047003A/zh
Publication of CN104047003A publication Critical patent/CN104047003A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种除铜表面氧化皮的方法，旨在提供一种简单易行，可高效去除铜表面氧化皮的方法；该方法依次包括下述步骤：1)将1重量份除铜表面氧化皮的试剂和1-5重量份水混合均匀，得到除铜表面氧化皮的混合液；2)将需要除氧化皮的铜抖动浸泡在步骤1)所述的除铜表面氧化皮的混合液中10-30秒；3)将浸泡后的铜取出水洗干净即可；属于金属清洁技术领域。

Description

一种除铜表面氧化皮的方法
技术领域
本发明涉及一种除铜表面氧化皮的方法，具体地说，是涉及一种去除黄铜、紫铜表面氧化皮的方法，属于金属清洁技术领域。
背景技术
氧化皮是钢铁在高温下发生氧化作用而形成的腐蚀产物，由氧化亚铁、四氧化三铁、三氧化二铁组成。从内向外为：氧化亚铁、四氧化三铁、三氧化二铁。其中氧化亚铁结构疏松，保护作用较弱，而四氧化三铁、三氧化二铁结构致密，有较好的保护性。
氧化皮质脆，没有延伸性，在机械作用下和热加工作用下，很容易产生龟裂而脱离。氧化铁和氧化亚铁在水作用下生成氢氧化铁，使得氧化皮膨胀而龟裂，甚至脱落。
在原有的氧化皮上，总是存在着深达基体的裂纹，当电解质涌进裂纹后，铁和氧化皮构成原电池。氧化皮是阴极，铁作为阳极而加速腐蚀，因此氧化皮的面积越大，钢铁基体的腐蚀速度越快，腐蚀越严重。因此，在电镀前要将金属表面的氧化皮去除。
发明内容
针对上述问题，本发明的目的在于提供一种简单易行，可高效去除铜表面氧化皮的方法。
为此，本发明提供的技术方案是这样的：该除铜表面氧化皮的方法，依次包括下述步骤：
1)将1重量份除铜表面氧化皮的试剂和1-5重量份水混合均匀，得到除铜表面氧化皮的混合液；
2)将需要除氧化皮的铜抖动浸泡在步骤1)所述的除铜表面氧化皮的混合液中10-30秒；
3)将浸泡后的铜取出水洗干净即可。
其中：
步骤1)所述的每升试剂由下述组分构成：过硫酸铵50-150g，硫酸50-150g，草酸50-80g，脂肪醇聚氧乙烯醚12-16g，烷基酚聚氧乙烯醚3-5g，硫脲2-4g，乙二胺四乙酸二钠5-8g，乌洛托品5-8g，余量为水。
进一步的，上述的除铜表面氧化皮的方法，每升试剂含下述组分：过硫酸铵80-120g，硫酸70-120g，草酸60-70g，脂肪醇聚氧乙烯醚13-15g，烷基酚聚氧乙烯醚4g，硫脲3g，乙二胺四乙酸二钠6-7g，乌洛托品6-7g，余量为水。
与现有技术相比，本发明提供的技术方案具有如下优点：
本发明提供的技术方案可以快速去除铜表面的氧化皮，操作简单，去除氧化皮效果好，生产成本低。
具体实施方式
下面结合具体实施，对本发明的权利要求做进一步的详细说明，任何人在本发明权利要求范围内所做的有限次的修改，仍在本发明的权利要求保护范围之内。
实施例1
本发明提供的一种除铜表面氧化皮的方法，该方法依次包括下述步骤：
1)将1重量份除铜表面氧化皮的试剂和1重量份水混合均匀，得到除铜表面氧化皮的混合液；
2)将需要除氧化皮的铜抖动浸泡在步骤1)所述的除铜表面氧化皮的混合液中10秒；
3)将浸泡后的铜取出水洗干净即可。
本发明所用的除铜表面氧化皮的试剂每升含下述组分：过硫酸铵120g，硫酸120g，草酸50g，脂肪醇聚氧乙烯醚13g，烷基酚聚氧乙烯醚4g，硫脲3g，乙二胺四乙酸二钠6g，乌洛托品7g。
实施例2
本发明提供的另一种除铜表面氧化皮的方法，该方法依次包括下述步骤：
1)将1重量份除铜表面氧化皮的试剂和5重量份水混合均匀，得到除铜表面氧化皮的混合液；
2)将需要除氧化皮的铜抖动浸泡在步骤1)所述的除铜表面氧化皮的混合液中30秒；
3)将浸泡后的铜取出水洗干净即可。
本发明所用的除铜表面氧化皮的试剂每升含下述组分：过硫酸铵100g，硫酸100g，草酸70g，脂肪醇聚氧乙烯醚15g，烷基酚聚氧乙烯醚5g，硫脲2g，乙二胺四乙酸二钠7g，乌洛托品7g。
实施例3
本发明提供的另一种除铜表面氧化皮的方法，该方法依次包括下述步骤：
1)将1重量份除铜表面氧化皮的试剂和3重量份水混合均匀，得到除铜表面氧化皮的混合液；
2)将需要除氧化皮的铜抖动浸泡在步骤1)所述的除铜表面氧化皮的混合液中20秒；
3)将浸泡后的铜取出水洗干净即可。
本发明所用的除铜表面氧化皮的试剂每升含下述组分：过硫酸铵50g，硫酸150g，草酸50g，脂肪醇聚氧乙烯醚16g，烷基酚聚氧乙烯醚3g，硫脲4g，乙二胺四乙酸二钠5g，乌洛托品8g。
实施例4
本发明提供的另一种除铜表面氧化皮的方法，该方法依次包括下述步骤：
1)将1重量份除铜表面氧化皮的试剂和2重量份水混合均匀，得到除铜表面氧化皮的混合液；
2)将需要除氧化皮的铜抖动浸泡在步骤1)所述的除铜表面氧化皮的混合液中20秒；
3)将浸泡后的铜取出水洗干净即可。
本发明所用的除铜表面氧化皮的试剂每升含下述组分：过硫酸铵150g，硫酸50g，草酸80g，脂肪醇聚氧乙烯醚12g，烷基酚聚氧乙烯醚5g，硫脲2g，乙二胺四乙酸二钠8g，乌洛托品5g。
实施例1至4中任意一种除铜表面氧化皮的试剂的制备方法如下：
1)按上述质量数称取各个组分；
2)将步骤1)称取的组分放入烧瓶，加水至1L，然后在常温下搅拌8分钟混匀，即得除铜表面氧化皮的试剂。

Claims (2)

1.一种除铜表面氧化皮的方法，其特征在于，该方法依次包括下述步骤：
1)将1重量份除铜表面氧化皮的试剂和1-5重量份水混合均匀，得到除铜表面氧化皮的混合液；
2)将需要除氧化皮的铜抖动浸泡在步骤1)所述的除铜表面氧化皮的混合液中10-30秒；
3)将浸泡后的铜取出水洗干净即可。
其中：
步骤1)所述的每升试剂含下述组分：过硫酸铵50-150g，硫酸50-150g，草酸50-80g，脂肪醇聚氧乙烯醚12-16g，烷基酚聚氧乙烯醚3-5g，硫脲2-4g，乙二胺四乙酸二钠5-8g，乌洛托品5-8g，余量为水。
2.根据权利要求1所述的除铜表面氧化皮的方法，其特征在于，每升试剂含下述组分：过硫酸铵80-120g，硫酸70-120g，草酸60-70g，脂肪醇聚氧乙烯醚13-15g，烷基酚聚氧乙烯醚4g，硫脲3g，乙二胺四乙酸二钠6-7g，乌洛托品6-7，余量为水。
CN201410283251.5A 2014-06-23 2014-06-23 一种除铜表面氧化皮的方法 Pending CN104047003A (zh)