A kind of multifunctional transparent water-soluble metalworking liquid
Technical field
The invention belongs to cutting fluid technical field, specifically a kind of multifunctional transparent water-soluble metalworking liquid.
Background technology
In recent ten years, due to improving constantly of cutting technology, the continuing to bring out of advanced cutting machine, the development of cutter and workpiece material, has promoted the development of cutting fluid technology.Along with the deep development of advanced manufacturing technology and the reinforcement of people's environmental protection consciousness, cutting fluid technology has been proposed to new requirement, it will promote cutting fluid technology and develop to higher field.
Cutting fluid is divided into oil soluble liquid and the large class of water-soluble liquid two by oil product chemical constitution, and general oil soluble cutting fluid lubrication performance is good, but poor cooling performance, and contain large amount of organic, contaminate environment.Although some water-soluble metalworking liquid cooling performances are good, there is again the poor problem of oilness and rust-proof effect.
Summary of the invention
The object of the present invention is to provide a kind of multifunctional transparent water-soluble metalworking liquid.
Object of the present invention can be achieved through the following technical solutions:
A kind of multifunctional transparent water-soluble metalworking liquid, it is characterized in that, by weight, its formula consists of: ethylene glycol 50-60 part, glycol ether 15-20 part, Starso 1.2-1.6 part, sodium phosphate 0.8-2.2 part, Sodium Benzoate 0.5-1.5 part, Sodium Nitrite 0.1-2 part, glycerine 1-5 part, petroleum sodium sulfonate 2-5 part, soybean oil 1-3 part, methyl methacrylate 0.2-3 part, boric acid 0.3-1.5 part, trolamine 2-6 part, rust-preventive agent 0.03-0.07 part, water 50-60 part.
By weight, its formula consists of in the present invention: 55 parts of ethylene glycol, 17.5 parts of glycol ethers, 1.4 parts of Starsos, 1.5 parts of sodium phosphates, 1 part of Sodium Benzoate, 1 part of Sodium Nitrite, 3 parts of glycerine, 3.5 parts of petroleum sodium sulfonates, 2 parts of soybean oil, 1.5 parts of methyl methacrylates, 0.9 part of boric acid, 4 parts of trolamines, 0.05 part of rust-preventive agent, 55 parts, water.
The present invention is prepared by following methods: ethylene glycol, glycol ether, Starso, sodium phosphate, Sodium Benzoate, Sodium Nitrite, glycerine, soybean oil, petroleum sodium sulfonate, methyl methacrylate, boric acid, trolamine, rust-preventive agent, water are added to stirrer successively, stir, described mixing speed is 1300 turn/min, whipping temp is 72 ℃, churning time 25min, obtains multifunctional transparent water-soluble metalworking liquid of the present invention.
Beneficial effect of the present invention: cutting fluid of the present invention has excellent cooling, cleaning performance, and lubricant effect and wear resistance are good; The present invention has good stability.In storage with while using, not stratified and separate out throw out, be difficult for corrupt; The present invention adds rust-preventive agent, has good chemistry, heat-resistant quality and rust-preventing characteristic.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
55 parts of 55 parts of ethylene glycol, 17.5 parts of glycol ethers, 1.4 parts of Starsos, 1.5 parts of sodium phosphates, 1 part of Sodium Benzoate, 1 part of Sodium Nitrite, 3 parts of glycerine, 2 parts of soybean oil, 3.5 parts of petroleum sodium sulfonates, 1.5 parts of methyl methacrylates, 0.9 part of boric acid, 4 parts of trolamines, 0.05 part of rust-preventive agent, water are added to stirrer successively, stir, described mixing speed is 1300 turn/min, whipping temp is 72 ℃, churning time 25min, obtains multifunctional transparent water-soluble metalworking liquid of the present invention.
Embodiment 2
50 parts of 50 parts of ethylene glycol, 15 parts of glycol ethers, 1.2 parts of Starsos, 1 part of sodium phosphate, 0.6 part of Sodium Benzoate, 0.2 part of Sodium Nitrite, 1 part of glycerine, 1 part of soybean oil, 2 parts of petroleum sodium sulfonates, 0.3 part of methyl methacrylate, 0.5 part of boric acid, 2 parts of trolamines, 0.03 part of rust-preventive agent, water add stirrer successively, stir, described mixing speed is 1300 turn/min, whipping temp is 72 ℃, churning time 25min, obtains multifunctional transparent water-soluble metalworking liquid of the present invention.
Embodiment 3
60 parts of 60 parts of ethylene glycol, 20 parts of glycol ethers, 1.6 parts of Starsos, 2 parts of sodium phosphates, 1.5 parts of Sodium Benzoates, 2 parts of Sodium Nitrites, 5 parts of glycerine, 3 parts of soybean oil, 5 parts of petroleum sodium sulfonates, 3 parts of methyl methacrylates, 1.5 parts of boric acid, 6 parts of trolamines, 0.07 part of rust-preventive agent, water add stirrer successively, stir, described mixing speed is 1300 turn/min, whipping temp is 72 ℃, churning time 25min, obtains multifunctional transparent water-soluble metalworking liquid of the present invention.
Embodiment 1-3 cutting fluid is carried out to performance test, and result is as shown in the table.