CN104032509B - A kind of pregnant woman is with velvet ribbon dyeing processing technique - Google Patents
A kind of pregnant woman is with velvet ribbon dyeing processing technique Download PDFInfo
- Publication number
- CN104032509B CN104032509B CN201410202204.3A CN201410202204A CN104032509B CN 104032509 B CN104032509 B CN 104032509B CN 201410202204 A CN201410202204 A CN 201410202204A CN 104032509 B CN104032509 B CN 104032509B
- Authority
- CN
- China
- Prior art keywords
- yarn
- temperature
- time
- pregnant woman
- processing technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of pregnant woman with velvet ribbon dyeing processing technique, comprise the steps: ceeling → yarn steaming → bag yarn → pressure yarn → boil yarn → dyeing → post processing → mistake supple-settlement.The present invention adds easy fuse, when ribbon high-temperature dyeing, easy fuse melting at ribbon edge, warp and the parallel of edge is bonded together, so that ribbon is difficult to tear.
Description
Technical field
Present invention relates particularly to a kind of pregnant woman with velvet ribbon dyeing processing technique.
Background technology
Ribbon is to make narrow web fabric or tubing with various yarns and elastic core wire for raw material, it is widely used in each industrial fields such as dress ornament, footwear material, case and bag, industry, agricultural, military supplies and communications and transportation, the most extensive in garment industry application, development along with society, the raw material of ribbon are by original cotton thread, yarn progressively develops into polyamide fibre, polyvinyl, terylene, polypropylene fibre, spandex, viscose glue etc., and weaving method and purposes also develop into diversification.
Ribbon is mainly used on brassiere and underpants at garment industry, although the function of existing ribbon has got more and more, and applicable crowd also gets more and more, but special population this for pregnant woman, ribbon is required by it can be much higher compared to general population, especially in soft feeling, require the velvet of the ribbon face superelevation to be had of skin-proximal especially, but ribbon velvet to be realized, it is necessary to ribbon density reduces, and which results in ribbon edge and easily tears.
The interior shrinkage through weft yarn of fabric is one of important parameter of fabric construction, and it is related to analysis and the design of many physical and mechanical properties, outward appearance, weaving process and the fabric of fabric.The different dyeing and finishing process of yarn have different impacts to the shrinkage of yarn.
The big veriety of terylene has chopped fiber, drawn yarn, textured filament, decoration long filament, industrial long filament and various fibre in differentiation.Polyster fibre and filament yarn fabric have the strongest hydrophobicity, common dyestuff and colouring method nearly all cannot catch look, can only use disperse dyeing.But the overall process of such dyeing the most just can complete.
Summary of the invention
Goal of the invention: the present invention provides a kind of pregnant woman with velvet ribbon dyeing processing technique.
Technical scheme: a kind of pregnant woman, with velvet ribbon dyeing processing technique, comprises the steps:
(1) ceeling；
(2) yarn steaming: the temperature of yarn steaming is 75-95 DEG C, the time of yarn steaming is 18-23min；
(3) bag yarn: add easy fuse at ribbon edge；
(4) pressure yarn；
(5) boiling yarn: the temperature boiling yarn is 110-145 DEG C, the time boiling yarn is 7-13min；
(6) dyeing: add flocking adhesive, and after adding auxiliary agent and dyestuff in dye liquor, spun polyester thread is soaked at water temperature is 30 DEG C 5min, then carry out after temperature reaches 80 DEG C with the speed of 2.5 DEG C/min washing 5min, with the speed of 1.0 DEG C/min, temperature is risen to 115 DEG C the most again, after washing 5min, after temperature rises to 130 DEG C with the speed of 0.8 DEG C/min, wash 30min；Finally, water temperature drop to 80 DEG C；
(7) post processing: after the yarn normal temperature washing after dyeing, carrying out reduction treatment, temperature is 75-83 DEG C, and the time is 16-23min；
(8) supple-settlement is crossed: carrying out supple-settlement at normal temperatures, the time is 7-14min.
As optimization, the temperature of described yarn steaming is 80 DEG C, and the time of yarn steaming is 20min.
As optimization, described in boil the temperature of yarn be 120 DEG C, the time boiling yarn is 10min.
As optimization, the temperature of described reduction treatment is 80 DEG C, and the time is 20min.
As optimization, the described time crossing supple-settlement is 10min
Beneficial effect: the present invention adds easy fuse, when ribbon high-temperature dyeing, easy fuse melting at ribbon edge, warp and the parallel of edge is bonded together, so that ribbon is difficult to tear.Disclosure satisfy that high fracture strength, super soft feeling, requirement comfortable and easy to wear, every technical parameter touches the mark: ribbon ultimate strength >=600N；Ribbon dyefastness >=4 grade；Ribbon content of formaldehyde: do not detect；Ribbon drapability < 50；Fine hair abrasion resistance > 800；Finished size rate of change: warp-wise-3.0%, broadwise-3.0%.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be described in detail.
Specific embodiment 1:
A kind of pregnant woman, with velvet ribbon dyeing processing technique, comprises the steps:
(1) ceeling；
(2) yarn steaming: the temperature of yarn steaming is 75 DEG C, the time of yarn steaming is 18min；
(3) bag yarn: add easy fuse at ribbon edge；
(4) pressure yarn；
(5) boiling yarn: the temperature boiling yarn is 110 DEG C, the time boiling yarn is 7min；
(6) dyeing: add flocking adhesive, and after adding auxiliary agent and dyestuff in dye liquor, spun polyester thread is soaked at water temperature is 30 DEG C 5min, then carry out after temperature reaches 80 DEG C with the speed of 2.5 DEG C/min washing 5min, with the speed of 1.0 DEG C/min, temperature is risen to 115 DEG C the most again, after washing 5min, after temperature rises to 130 DEG C with the speed of 0.8 DEG C/min, wash 30min；Finally, water temperature drop to 80 DEG C；
(7) post processing: after the yarn normal temperature washing after dyeing, carrying out reduction treatment, temperature is 75 DEG C, and the time is 16min；
(8) supple-settlement is crossed: carrying out supple-settlement at normal temperatures, the time is 7min.
Specific embodiment 2:
A kind of pregnant woman, with velvet ribbon dyeing processing technique, comprises the steps:
(1) ceeling；
(2) yarn steaming: the temperature of yarn steaming is 95 DEG C, the time of yarn steaming is 23min；
(3) bag yarn: add easy fuse at ribbon edge；
(4) pressure yarn；
(5) boiling yarn: the temperature boiling yarn is 145 DEG C, the time boiling yarn is 13min；
(6) dyeing: add flocking adhesive, and after adding auxiliary agent and dyestuff in dye liquor, spun polyester thread is soaked at water temperature is 30 DEG C 5min, then carry out after temperature reaches 80 DEG C with the speed of 2.5 DEG C/min washing 5min, with the speed of 1.0 DEG C/min, temperature is risen to 115 DEG C the most again, after washing 5min, after temperature rises to 130 DEG C with the speed of 0.8 DEG C/min, wash 30min；Finally, water temperature drop to 80 DEG C；
(7) post processing: after the yarn normal temperature washing after dyeing, carrying out reduction treatment, temperature is 83 DEG C, and the time is 23min；
(8) supple-settlement is crossed: carrying out supple-settlement at normal temperatures, the time is 14min.
Specific embodiment 3:
A kind of pregnant woman, with velvet ribbon dyeing processing technique, comprises the steps:
(1) ceeling；
(2) yarn steaming: the temperature of yarn steaming is 80 DEG C, the time of yarn steaming is 20min；
(3) bag yarn: add easy fuse at ribbon edge；
(4) pressure yarn；
(5) boiling yarn: the temperature boiling yarn is 120 DEG C, the time boiling yarn is 10min；
(6) dyeing: add flocking adhesive, and after adding auxiliary agent and dyestuff in dye liquor, spun polyester thread is soaked at water temperature is 30 DEG C 5min, then carry out after temperature reaches 80 DEG C with the speed of 2.5 DEG C/min washing 5min, with the speed of 1.0 DEG C/min, temperature is risen to 115 DEG C the most again, after washing 5min, after temperature rises to 130 DEG C with the speed of 0.8 DEG C/min, wash 30min；Finally, water temperature drop to 80 DEG C；
(7) post processing: after the yarn normal temperature washing after dyeing, carrying out reduction treatment, temperature is 80 DEG C, and the time is 20min；
(8) supple-settlement is crossed: carrying out supple-settlement at normal temperatures, the time is 10min.
Claims (5)
1. a pregnant woman is with velvet ribbon dyeing processing technique, it is characterised in that: comprise the steps:
(1) ceeling；
(2) yarn steaming: the temperature of yarn steaming is 75-95 DEG C, the time of yarn steaming is 18-23min；
(3) bag yarn: add easy fuse at ribbon edge；
(4) pressure yarn；
(5) boiling yarn: the temperature boiling yarn is 110-145 DEG C, the time boiling yarn is 7-13min；
(6) dyeing: add flocking adhesive, and after adding auxiliary agent and dyestuff in dye liquor,
Spun polyester thread soaks at water temperature is 30 DEG C 5min, and then temperature is with 2.5 DEG C/min's
Speed carries out washing 5min after reaching 80 DEG C, the most again with the speed of 1.0 DEG C/min by temperature
Degree rises to 115 DEG C, and after washing 5min, temperature rises to the speed of 0.8 DEG C/min
After 130 DEG C, wash 30min；Finally, water temperature drop to 80 DEG C；
(7) post processing: after the yarn normal temperature washing after dyeing, carrying out reduction treatment, temperature is
75-83 DEG C, the time is 16-23min；
(8) supple-settlement is crossed: carrying out supple-settlement at normal temperatures, the time is 7-14min.
Pregnant woman the most according to claim 1 exists by velvet ribbon dyeing processing technique, its feature
In: the temperature of described yarn steaming is 80 DEG C, and the time of yarn steaming is 20min.
Pregnant woman the most according to claim 1 exists by velvet ribbon dyeing processing technique, its feature
In: described in boil the temperature of yarn be 120 DEG C, the time boiling yarn is 10min.
Pregnant woman the most according to claim 1 exists by velvet ribbon dyeing processing technique, its feature
In: the temperature of described reduction treatment is 80 DEG C, and the time is 20min.
Pregnant woman the most according to claim 1 exists by velvet ribbon dyeing processing technique, its feature
In: the described time crossing supple-settlement is 10min.