CN104031499A - Water-based air purification paint and preparation method thereof - Google Patents
Water-based air purification paint and preparation method thereof Download PDFInfo
- Publication number
- CN104031499A CN104031499A CN201410251188.7A CN201410251188A CN104031499A CN 104031499 A CN104031499 A CN 104031499A CN 201410251188 A CN201410251188 A CN 201410251188A CN 104031499 A CN104031499 A CN 104031499A
- Authority
- CN
- China
- Prior art keywords
- water
- purifying air
- auxiliary agent
- percent
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based air purification paint which comprises the following components in percentage by mass: 25-30 percent of water, 0.5-1 percent of a dispersing agent, 10 percent of nano negative ion powder, 25-30 percent of color packing, 1-5 percent of air purification aid, 30-35 percent of acrylic emulsion and 1-3 percent of aids. The acrylic emulsion prepared by the invention can absorb and decompose formaldehyde and harmful substances in indoor air for a long time, so that an effect of purifying air is achieved, acetaldehyde, acetic acid and ammonia gas with severe cigarette taste and rot smell in air and other odors can be absorbed and decomposed through the photocatalyst action, and the anti-mildew and antibacterial effects can be achieved. Meanwhile, the water-based air purification paint does not contain a harmful organic solvent, is non-toxic, tasteless, environmental friendly, high in water resistance, weather resistance, aging resistance and hot and cold cycle resistance, high in adhesive force, flat and soft in film, good in decorative effect, safe to store and transport and convenient to use and can be widely applied to outer walls and inner walls of house buildings.
Description
Technical field
The present invention relates to chemical field, more specifically refer to a kind of water-based purifying air paint and preparation method thereof.
Background technology
Air quality is generally not high at present, atmospheric haze is serious, and industrial, the major part that people use is now the oil-base paint of not environmental protection still, in the paint of oiliness, contain strong solvent, as toluene, dimethylbenzene, N-BUTYL ACETATE, pimelinketone, butyl ester etc., these not environmental protection of material, severe contamination air, more and more can not meet the environmental requirement of current increasingly stringent.
Summary of the invention
Main purpose of the present invention is to provide a kind of water-based purifying air paint that can effectively purify air, and preparation method thereof.
To achieve these goals, the present invention has adopted following technical scheme:
A water-based purifying air paint, comprises the component of following mass percent: water 25% ~ 30%; Dispersion agent 0.5% ~ 1%; Nanometer anion powder 10%; Color filler: 25% ~ 30%; Purifying air auxiliary agent 1% ~ 5%; ACRYLIC EMULSION: 30% ~ 35%; Auxiliary agent: 1% ~ 3%.
As a kind of preferred technical scheme, a kind of water-based purifying air paint, comprises the component of following mass percent: water 25%; Dispersion agent 0.6%; Nanometer anion powder 10%; Color filler: 26%; Purifying air auxiliary agent 2%; ACRYLIC EMULSION: 35%; Auxiliary agent: 1.4%.
Further, described dispersion agent is sodium polyacrylate dipersant.Such dispersion agent has low foaming and improves the excellent properties of the mobility of coating, stable slurry viscosity.Excellent dispersion, highly versatile, a small amount of interpolation is capable of regulating low-viscosity dope, slurry, coating stability is relatively good, coating, the viscosity of slurry does not change, and dispersed color well, thus the paint of producing without loose colour, color spot.
Further, described nanometer anion powder, i.e. tourmalinite, a kind of silicate mineral of natural ring texture, its particle diameter is 4000 orders, Main Function is: the carcinogenic substances such as formaldehyde that absorb and degrade in empty gas.
Further, described color filler comprises titanium dioxide or wollastonite powder.
Further, described air purifying preparation is for being gac or bamboo charcoal powder, and Main Function is: the carcinogenic substances such as formaldehyde that absorb and degrade in empty gas.
Further, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 1 ~ 2:0.1:0.2 ~ 0.3:0.5, wherein, film coalescence aid is alcohol ester 12 film coalescence aid, it can assist paint film film formation, and defoamer is a kind of mineral oil, and it can eliminate the bubble producing in production process, make paint film fine and close, can opening is effective.Antisepticize and mildew preventive is BIT compound, and it can make paint never degenerate, the effect of moistureproof and mildewproof bacterium.Thickening material is association type acrylic compound, and making to paint denseness increases.
The preparation method of water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and color filler, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, purifying air auxiliary agent, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.
The water-based purifying air paint that the present invention makes can absorb and decompose the objectionable impuritiess such as formaldehyde in indoor air for a long time, thereby play the effect purifying air, by photocatalyst effect, can also absorb and decompose airborne cigarette taste, the acetaldehyde that decomposed odour is heavy, the peculiar smell such as acetic acid and ammonia, all right antimildew and antibacterial, the paint of this purifying air is not simultaneously containing harmful organic solvent, nontoxic, tasteless, environmental protection, water-fast, weather-proof, ageing-resistant, cold-hot good cycle, strong adhesion, paint film is smooth soft, good decorating effect, storing and transporting security, easy to use, can be widely used on the exterior wall and interior wall of building construction.
Embodiment
Now describe in conjunction with specific embodiments the present invention in detail, wherein the defoamer in following embodiment is all outer purchased from Dongguan City De Feng defoamer company limited, and production code member is mineral oil antifoam agent DF-877; Film coalescence aid is alcohol ester 12 film coalescence aid; Antisepticize and mildew preventive is BIT compound, and dispersion agent is sodium polyacrylate dipersant, and nanometer anion powder is that particle diameter is 4000 object tourmalinite.
Embodiment mono-
A water-based purifying air paint, comprises the component of following mass percent: water 25%; Dispersion agent 0.6%; Nanometer anion powder 10%; Titanium dioxide: 26%; Gac 2%; ACRYLIC EMULSION: 35%; Auxiliary agent: 1.4%.Wherein, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 1.5:0.1:0.25:0.5.
The preparation method of above-mentioned water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and titanium dioxide, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, gac, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.
Embodiment bis-
A water-based purifying air paint, comprises the component of following mass percent: water 25%; Dispersion agent 0.5%; Nanometer anion powder 10%; Wollastonite powder: 27%; Bamboo charcoal powder 3%; ACRYLIC EMULSION: 33%; Auxiliary agent: 1.5%.Wherein, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 2:0.1:0.3:0.5.
The preparation method of water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and wollastonite powder, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, bamboo charcoal powder, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.
Embodiment tri-
A water-based purifying air paint, comprises the component of following mass percent: water 26%; Dispersion agent 1%; Nanometer anion powder 10%; Titanium dioxide: 29%; Gac 1%; ACRYLIC EMULSION: 30%; Auxiliary agent: 1%.Wherein, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 1.3:0.1:0.24:0.5.
The preparation method of water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and titanium dioxide, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, gac, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.
Embodiment tetra-
A water-based purifying air paint, comprises the component of following mass percent: water 30%; Dispersion agent 0.7%; Nanometer anion powder 10%; Wollastonite powder: 26%; Bamboo charcoal powder 2%; ACRYLIC EMULSION: 30%; Auxiliary agent: 1.3%.Wherein, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 1.8:0.1:0.26:0.5.
The preparation method of water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and wollastonite powder, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, bamboo charcoal powder, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.
Embodiment five
A water-based purifying air paint, comprises the component of following mass percent: water 26%; Dispersion agent 1%; Nanometer anion powder 10%; Titanium dioxide: 25%; Gac 5%; ACRYLIC EMULSION: 30%; Auxiliary agent: 3%.Wherein, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 1.3:0.1:0.25:0.5.
The preparation method of water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and titanium dioxide, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, gac, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.
Embodiment six
A water-based purifying air paint, comprises the component of following mass percent: water 27%; Dispersion agent 0.7%; Nanometer anion powder 10%; Wollastonite powder: 28%; Bamboo charcoal powder 1%; ACRYLIC EMULSION: 32%; Auxiliary agent: 1.3%.Wherein, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 2:0.1:0.2:0.5.
The preparation method of water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and color filler, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, purifying air auxiliary agent, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.
The aqueous foam paint that above-mentioned several embodiment makes and meet the environment protection industry standard HJ/T 2357-2014 of the People's Republic of China (PRC), its performance index measurement result is as following table:
| Sample | Outward appearance | Water tolerance | Weathering resistance | Antifog property | Degradation Formaldehyde rate | Sticking power |
| Embodiment mono- | Outward appearance, without caking, is uniform state | 110h | 60h | 0 grade | 89.12% | 1 grade |
| Embodiment bis- | Outward appearance, without caking, is uniform state | 98h | 54h | 0 grade | 87% | 1 grade |
| Embodiment tri- | Outward appearance, without caking, is uniform state | 96h | 50h | 0 grade | 88.2% | 1 grade |
| Embodiment tetra- | Outward appearance, without caking, is uniform state | 100h | 48h | 0 grade | 87.13% | 1 grade |
| Embodiment five | Outward appearance, without caking, is uniform state | 105h | 54h | 0 grade | 87.35% | 1 grade |
| Embodiment six | Outward appearance, without caking, is uniform state | 105h | 56h | 0 grade | 88.9% | 1 grade |
The technical scheme above embodiment of the present invention being provided is described in detail, applied specific case herein the principle of the embodiment of the present invention and embodiment are set forth, the explanation of above embodiment is only applicable to help to understand the principle of the embodiment of the present invention; , for one of ordinary skill in the art, according to the embodiment of the present invention, in embodiment and range of application, all will change, in sum, this description should not be construed as limitation of the present invention meanwhile.
Claims (8)
1. a water-based purifying air paint, is characterized in that, comprises the component of following mass percent: water 25% ~ 30%; Dispersion agent 0.5% ~ 1%; Nanometer anion powder 10%; Color filler: 25% ~ 30%; Purifying air auxiliary agent 1% ~ 5%; ACRYLIC EMULSION: 30% ~ 35%; Auxiliary agent: 1% ~ 3%.
2. a kind of water-based purifying air paint according to claim 1, is characterized in that, a kind of water-based purifying air paint comprises the component of following mass percent: water 25%; Dispersion agent 0.6%; Nanometer anion powder 10%; Color filler: 26%; Purifying air auxiliary agent 2%; ACRYLIC EMULSION: 35%; Auxiliary agent: 1.4%.
3. a kind of water-based purifying air paint according to claim 1 and 2, is characterized in that, described dispersion agent is sodium polyacrylate dipersant.
4. a kind of water-based purifying air paint according to claim 1 and 2, is characterized in that, described nanometer anion powder is that particle diameter is 4000 object tourmalinite.
5. a kind of water-based purifying air paint according to claim 1 and 2, is characterized in that, described color filler comprises titanium dioxide or wollastonite powder.
6. a kind of water-based purifying air paint according to claim 1 and 2, is characterized in that, described air purifying preparation is for being gac or bamboo charcoal powder.
7. a kind of water-based purifying air paint according to claim 1 and 2, is characterized in that, described auxiliary agent is that mass ratio is the mixture of film coalescence aid, defoamer, Antisepticize and mildew preventive and the thickening material composition of 1 ~ 2:0.1:0.2 ~ 0.3:0.5.
8. a kind of water-based purifying air paint described in claim 1 ~ 7 any one, it is characterized in that, the preparation method of water-based purifying air paint, comprise the steps: under normal temperature, in container, add water and color filler, use dispersion machine to disperse 30 minutes being greater than under the rotating speed of 500r/min, and then add dispersion agent, nanometer anion powder, purifying air auxiliary agent, ACRYLIC EMULSION and auxiliary agent, continue to be dispersed to and mix, with sand mill, being ground to fineness is below 20 microns, can make water-based purifying air paint.