CN104031445B - 一种含有双丙酮丙烯酰胺的水性涂料 - Google Patents

一种含有双丙酮丙烯酰胺的水性涂料 Download PDF

Info

Publication number
CN104031445B
CN104031445B CN201410208272.0A CN201410208272A CN104031445B CN 104031445 B CN104031445 B CN 104031445B CN 201410208272 A CN201410208272 A CN 201410208272A CN 104031445 B CN104031445 B CN 104031445B
Authority
CN
China
Prior art keywords
daam
water
raw material
water paint
stir
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410208272.0A
Other languages
English (en)
Other versions
CN104031445A (zh
Inventor
糜锡骏
糜昊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Liang Xi Environmental Friendly Material Co Ltd
Original Assignee
Anhui Liang Xi Environmental Friendly Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Liang Xi Environmental Friendly Material Co Ltd filed Critical Anhui Liang Xi Environmental Friendly Material Co Ltd
Priority to CN201410208272.0A priority Critical patent/CN104031445B/zh
Publication of CN104031445A publication Critical patent/CN104031445A/zh
Application granted granted Critical
Publication of CN104031445B publication Critical patent/CN104031445B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有双丙酮丙烯酰胺的水性涂料，其特征在于：其是由下述重量份的原料制得：六偏磷酸钠2-5、水100-120、水溶性环氧树脂30-40，双丙酮丙烯酰胺1-2、丙烯酸甲酯5-7，乙酸乙酯0.1-0.2、苯丙乳液10-15，硅溶胶2-4、石英砂4-6，成膜助剂3-5、氧化锌1-2，碳酸钙1-2，磷酸三丁酯0.1-0.2，羧甲基纤维素3-8，分散剂NNO？0.05-0.15，乙二胺8-10；本发明提供的水性涂料易于涂抹，分散性好无气泡，同时提高了涂层的光泽和寿命。

Description

一种含有双丙酮丙烯酰胺的水性涂料
技术领域
本发明涉及双丙酮丙烯酰胺领域，确切地说是一种双丙酮丙烯酰胺的水性涂料。
背景技术
双丙酮丙烯酰胺具有两种反应性基团：N-取代的酰胺和甲酮，极易与其他乙烯及单体共聚，从而向聚合物中引入酮羰基，利用酮羰基的化学性质，可以使聚合物发生交联接枝等反应，用于制备各种粘合剂、增稠剂、纸张补强剂、交联剂等。目前已广泛应用于涂料、粘合剂、日用化工、环氧树脂固化剂、感光树脂助剂、纺织助剂、医疗卫生等领域中。
发明内容
本发明的目的在于提供一种含有双丙酮丙烯酰胺的水性涂料。
上述目的通过以下方案实现：
一种含有双丙酮丙烯酰胺的水性涂料，其特征在于：其是由下述重量份的原料制得：六偏磷酸钠2-5、水100-120、水溶性环氧树脂30-40，双丙酮丙烯酰胺1-2、丙烯酸甲酯5-7，乙酸乙酯0.1-0.2、苯丙乳液10-15，硅溶胶2-4、石英砂4-6，成膜助剂3-5、氧化锌1-2，碳酸钙1-2，磷酸三丁酯0.1-0.2，羧甲基纤维素3-8，分散剂NNO0.05-0.15，乙二胺8-10；
所述的成膜助剂由下述重量份的原料制得：甲基丙烯酸甲酯2-4、苯甲酸钠1-2、高岭土4-5、马来酸二丁酯1-2、过硫酸钾0.2-0.4、氧化聚乙烯蜡1-2、硼酸锌1-2、抗氧剂22460.2-0.4、硅烷偶联剂kh5801-2、丙酮17-20；
所述的成膜助剂的制备方法为：将称取的各原料先于500-700转/分下搅拌混合5-10分钟，后于200-300转/分下35-45℃下搅拌混合10-20分钟，停止搅拌，即得。
所述的一种含有双丙酮丙烯酰胺的水性涂料，其特征在于：
包括以下步骤：
(1)反应釜中依次加入水、六偏磷酸钠、水溶性环氧树脂、双丙酮丙烯酰胺、丙烯酸甲酯、乙酸乙酯、硅溶胶、羧甲基纤维素，400-600r/min下搅拌15-20min；
(2)再加入其余原料，于800-1000r/min下搅拌25-40min；
(3)研磨到细度≤50μm，即得。
本发明的有益效果为：本发明提供的水性涂料易于涂抹，分散性好无气泡，同时提高了涂层的光泽和寿命。
具体实施方式
一种含有双丙酮丙烯酰胺的水性涂料，其是由下述重量kg的原料制得：六偏磷酸钠5、水120、水溶性环氧树脂40，双丙酮丙烯酰胺2、丙烯酸甲酯7，乙酸乙酯0.2、苯丙乳液15，硅溶胶4、石英砂6，成膜助剂5、氧化锌2，碳酸钙2，磷酸三丁酯0.2，羧甲基纤维素6，分散剂NNO0.15，乙二胺10；
所述的成膜助剂由下述重量kg的原料制得：甲基丙烯酸甲酯4、苯甲酸钠1、高岭土5、马来酸二丁酯2、过硫酸钾0.4、氧化聚乙烯蜡2、硼酸锌2、抗氧剂22460.4、硅烷偶联剂kh5801、丙酮18；
所述的成膜助剂的制备方法为：将称取的各原料先于600转/分下搅拌混合10分钟，后于300转/分下45℃下搅拌混合20分钟，停止搅拌，即得。
所述的一种含有双丙酮丙烯酰胺的水性涂料，
包括以下步骤：
(1)反应釜中依次加入水、六偏磷酸钠、水溶性环氧树脂、双丙酮丙烯酰胺、丙烯酸甲酯、乙酸乙酯、硅溶胶、羧甲基纤维素，50r/min下搅拌20min；
(2)再加入其余原料，于1000r/min下搅拌40min；
(3)研磨到细度≤50μm，即得。
将本实施例所得涂料涂覆于墙面上，平均膜厚为70-100微米；
性能指标如下：
按照GB/T1732测试，抗冲击性≥45kg·cm；
按照GB/T6739测试，铅笔硬度≥H级；
480hQUV-B加速光老化试验测试得，保光率达86％。
所得涂层表面平整，无气泡，颗粒、缩孔、针孔。

Claims (2)

1.一种含有双丙酮丙烯酰胺的水性涂料，其特征在于：其是由下述重量份的原料制得：六偏磷酸钠2-5、水100-120、水溶性环氧树脂30-40，双丙酮丙烯酰胺1-2、丙烯酸甲酯5-7，乙酸乙酯0.1-0.2、苯丙乳液10-15，硅溶胶2-4、石英砂4-6，成膜助剂3-5、氧化锌1-2，碳酸钙1-2，磷酸三丁酯0.1-0.2，羧甲基纤维素3-8，分散剂NNO0.05-0.15，乙二胺8-10；
所述的成膜助剂由下述重量份的原料制得：甲基丙烯酸甲酯2-4、苯甲酸钠1-2、高岭土4-5、马来酸二丁酯1-2、过硫酸钾0.2-0.4、氧化聚乙烯蜡1-2、硼酸锌1-2、抗氧剂22460.2-0.4、硅烷偶联剂KH5801-2、丙酮17-20；
所述的成膜助剂的制备方法为：将称取的各原料先于500-700转/分下搅拌混合5-10分钟，后于200-300转/分下35-45℃下搅拌混合10-20分钟，停止搅拌，即得。
2.根据权利要求1所述的一种含有双丙酮丙烯酰胺的水性涂料，其特征在于：
包括以下步骤：
（1）反应釜中依次加入水、六偏磷酸钠、水溶性环氧树脂、双丙酮丙烯酰胺、丙烯酸甲酯、乙酸乙酯、硅溶胶、羧甲基纤维素，400-600r/min下搅拌15-20min；
（2）再加入其余原料，于800-1000r/min下搅拌25-40min；
（3）研磨到细度≤50μm，即得。
CN201410208272.0A 2014-05-16 2014-05-16 一种含有双丙酮丙烯酰胺的水性涂料 Active CN104031445B (zh)