CN104028245A - 一种具有较好吸附效果的改性纳米二氧化钛及其制备方法 - Google Patents

一种具有较好吸附效果的改性纳米二氧化钛及其制备方法 Download PDF

Info

Publication number
CN104028245A
CN104028245A CN201410197175.6A CN201410197175A CN104028245A CN 104028245 A CN104028245 A CN 104028245A CN 201410197175 A CN201410197175 A CN 201410197175A CN 104028245 A CN104028245 A CN 104028245A
Authority
CN
China
Prior art keywords
powder
nano
parts
titanium dioxide
stir
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410197175.6A
Other languages
English (en)
Other versions
CN104028245B (zh
Inventor
谷屿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maanshan Longteng Electromechanical Technology Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410197175.6A priority Critical patent/CN104028245B/zh
Publication of CN104028245A publication Critical patent/CN104028245A/zh
Application granted granted Critical
Publication of CN104028245B publication Critical patent/CN104028245B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种具有较好吸附效果的改性纳米二氧化钛，其特征在于，由下列重量份的原料制备制成：纳米二氧化钛85-90、粉碎玻化微珠2-3、膨胀石墨粉2-3、苯胺甲基三乙氧基硅烷1-1.5、粗孔硅胶粉2-3、三聚磷酸钠2.5-3.5、钛酸丁酯4-6、纳米硅藻土粉5-6、聚异丁烯1-2、改性二氧化硅2-3；本发明配方合理，通过添加玻化微珠、膨胀石墨粉、粗孔硅胶等疏松多孔的原料，增加了粉体的吸附性能，通过配合高分子聚合物，使得本发明经久耐用，本发明对室内微量有害气体甲醛的吸附和降解十分有效，可以作为甲醛的扑集剂和甲醛分析的吸收载体材料，还可用作油漆、涂料、塑料等填料。

Description

一种具有较好吸附效果的改性纳米二氧化钛及其制备方法
技术领域
本发明涉及工业填料领域，特别是一种具有较好吸附效果的改性纳米二氧化钛及其制备方法。
背景技术
由于纳米二氧化钛具有良好的抗紫外线性能、良好的耐候性、耐化学腐蚀性、耐热性、光催化性、热稳定性、对人体无害等特征，被广泛应用于颜料如涂料、橡胶、塑料、造纸等行业，同时还作为光催化剂、光电电池、紫外线屏蔽剂等被广泛应用；随着现代工业的飞速发展，室外大气的环境污染已成为世界各国亟待解决的问题。另外，由于人们的物质水平的不断提高，入住新居装修的高档化而带来的室内有害气体的严重污染，也越来越引起重视。本发明的目的在于克服现有技术的诸多不足之处，提供一种工艺简单、成本低廉，对室内微量有害气体甲醛的吸附和降解十分有效的纳米二氧化钛的制备方法。
发明内容
本发明的目的是提供一种具有较好吸附效果的改性纳米二氧化钛及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种具有较好吸附效果的改性纳米二氧化钛，由下列重量份的原料制备制成：纳米二氧化钛85-90、粉碎玻化微珠2-3、膨胀石墨粉2-3、苯胺甲基三乙氧基硅烷1-1.5、粗孔硅胶粉2-3、三聚磷酸钠2.5-3.5、钛酸丁酯4-6、纳米硅藻土粉5-6、聚异丁烯1-2、改性二氧化硅2-3；
所述改性二氧化硅由以下重量份的原料制成：二氧化硅55-60、纳米麦饭石粉2-4、纳米级硅微粉4-6、二缩三丙二醇二丙烯酸酯5-7、1-羟乙基-2-油基咪唑啉1-2、环烷酸钴3-4、丙烯酸缩水甘油酯3-5、EDTA二钠2-4、水50-60；制备方法是首先加入纳米二氧化硅、纳米麦饭石粉、纳米级硅微粉、1-羟乙基-2-油基咪唑啉、水搅拌均匀，形成悬浮液，在55-60℃下烘干至含水量2-3%，然后立即加入二缩三丙二醇二丙烯酸酯、环烷酸钴、丙烯酸缩水甘油酯，加热至130-150℃，混合搅拌25-35分钟，冷却至室温，然后加入其余剩余成分，1200-1500转/分条件下搅拌1-2小时，在60-70℃下烘干，研磨即得。
本发明所述一种具有较好吸附效果的改性纳米二氧化钛，由以下具体步骤制成：
（1）将纳米二氧化钛、粉碎玻化微珠、膨胀石墨粉、苯胺甲基三乙氧基硅烷、粗孔硅胶粉、三聚磷酸钠混合均匀加入研磨机内，以1500-2000转/分钟 的速度研磨 15-20 分钟，得混合粉末待用；
（2）将钛酸丁酯放入混料筒中，加入纳米硅藻土粉、聚异丁烯，升温至130-160℃，搅拌15-20分钟后倒出，得胶粉；
（3）将混合粉末与胶粉混合均匀，加入适量水，搅拌均匀，在80℃下超声振荡1-2小时，然后继续研磨20-30分钟，形成混悬液待用；
（4）将混悬液与改性二氧化硅混合，800-1000转/分下搅拌10-15分钟，烘干、放入纳米粉碎机中粉碎即得。
本发明的有益效果是：本发明配方合理，通过添加玻化微珠、膨胀石墨粉、粗孔硅胶等疏松多孔的原料，增加了粉体的吸附性能，通过配合高分子聚合物，使得本发明经久耐用，本发明对室内微量有害气体甲醛的吸附和降解十分有效，可以作为甲醛的扑集剂和甲醛分析的吸收载体材料，还可用作油漆、涂料、塑料等填料。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种具有较好吸附效果的改性纳米二氧化钛，其特征在于，由下列重量份（公斤）的原料制备制成：纳米二氧化钛85、粉碎玻化微珠2、膨胀石墨粉2、苯胺甲基三乙氧基硅烷1、粗孔硅胶粉2、三聚磷酸钠2.5、钛酸丁酯4、纳米硅藻土粉5、聚异丁烯1、改性二氧化硅2；
所述改性二氧化硅由以下重量份（公斤）的原料制成：二氧化硅55、纳米麦饭石粉2、纳米级硅微粉4、二缩三丙二醇二丙烯酸酯5、1-羟乙基-2-油基咪唑啉1、环烷酸钴3、丙烯酸缩水甘油酯3、EDTA二钠2、水50；制备方法是首先加入纳米二氧化硅、纳米麦饭石粉、纳米级硅微粉、1-羟乙基-2-油基咪唑啉、水搅拌均匀，形成悬浮液，在55-60℃下烘干至含水量2-3%，然后立即加入二缩三丙二醇二丙烯酸酯、环烷酸钴、丙烯酸缩水甘油酯，加热至130-150℃，混合搅拌25-35分钟，冷却至室温，然后加入其余剩余成分，1200-1500转/分条件下搅拌1-2小时，在60-70℃下烘干，研磨即得。
本发明所述一种具有较好吸附效果的改性纳米二氧化钛，由以下具体步骤制成：
（1）将纳米二氧化钛、粉碎玻化微珠、膨胀石墨粉、苯胺甲基三乙氧基硅烷、粗孔硅胶粉、三聚磷酸钠混合均匀加入研磨机内，以1500-2000转/分钟 的速度研磨 15-20 分钟，得混合粉末待用；
（2）将钛酸丁酯放入混料筒中，加入纳米硅藻土粉、聚异丁烯，升温至130-160℃，搅拌15-20分钟后倒出，得胶粉；
（3）将混合粉末与胶粉混合均匀，加入适量水，搅拌均匀，在80℃下超声振荡1-2小时，然后继续研磨20-30分钟，形成混悬液待用；
（4）将混悬液与改性二氧化硅混合，800-1000转/分下搅拌10-15分钟，烘干、放入纳米粉碎机中粉碎即得。
本实施例得到的改性纳米二氧化钛的比表面积明显增加
样品 原纳米二氧化钛 改性纳米二氧化钛
比表面积/ m2/g 90-200 150-250

Claims (2)

1.一种具有较好吸附效果的改性纳米二氧化钛，其特征在于，由下列重量份的原料制备制成：纳米二氧化钛85-90、粉碎玻化微珠2-3、膨胀石墨粉2-3、苯胺甲基三乙氧基硅烷1-1.5、粗孔硅胶粉2-3、三聚磷酸钠2.5-3.5、钛酸丁酯4-6、纳米硅藻土粉5-6、聚异丁烯1-2、改性二氧化硅2-3；
所述改性二氧化硅由以下重量份的原料制成：二氧化硅55-60、纳米麦饭石粉2-4、纳米级硅微粉4-6、二缩三丙二醇二丙烯酸酯5-7、1-羟乙基-2-油基咪唑啉1-2、环烷酸钴3-4、丙烯酸缩水甘油酯3-5、EDTA二钠2-4、水50-60；制备方法是首先加入纳米二氧化硅、纳米麦饭石粉、纳米级硅微粉、1-羟乙基-2-油基咪唑啉、水搅拌均匀，形成悬浮液，在55-60℃下烘干至含水量2-3%，然后立即加入二缩三丙二醇二丙烯酸酯、环烷酸钴、丙烯酸缩水甘油酯，加热至130-150℃，混合搅拌25-35分钟，冷却至室温，然后加入其余剩余成分，1200-1500转/分条件下搅拌1-2小时，在60-70℃下烘干，研磨即得。
2.根据权利要求1所述一种具有较好吸附效果的改性纳米二氧化钛，其特征在于，由以下具体步骤制成：
（1）将纳米二氧化钛、粉碎玻化微珠、膨胀石墨粉、苯胺甲基三乙氧基硅烷、粗孔硅胶粉、三聚磷酸钠混合均匀加入研磨机内，以1500-2000转/分钟 的速度研磨 15-20 分钟，得混合粉末待用；
（2）将钛酸丁酯放入混料筒中，加入纳米硅藻土粉、聚异丁烯，升温至130-160℃，搅拌15-20分钟后倒出，得胶粉；
（3）将混合粉末与胶粉混合均匀，加入适量水，搅拌均匀，在80℃下超声振荡1-2小时，然后继续研磨20-30分钟，形成混悬液待用；
（4）将混悬液与改性二氧化硅混合，800-1000转/分下搅拌10-15分钟，烘干、放入纳米粉碎机中粉碎即得。
CN201410197175.6A 2014-05-12 2014-05-12 一种具有较好吸附效果的改性纳米二氧化钛及其制备方法 Expired - Fee Related CN104028245B (zh)