CN104016637A - Interface treating agent for ceramic brick - Google Patents
Interface treating agent for ceramic brick Download PDFInfo
- Publication number
- CN104016637A CN104016637A CN201410243081.8A CN201410243081A CN104016637A CN 104016637 A CN104016637 A CN 104016637A CN 201410243081 A CN201410243081 A CN 201410243081A CN 104016637 A CN104016637 A CN 104016637A
- Authority
- CN
- China
- Prior art keywords
- parts
- treating agent
- ceramic brick
- mortar
- adhesive force
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an interface treating agent for a ceramic brick and belongs to building materials, and aims to provide a building material capable of improving the adhesive force on the surface of the ceramic brick. The interface treating agent is prepared by mixing the following raw materials in parts by weight: 400 parts of PO52.5 cement, 400 parts of 80-100-mesh quartz sands, 50 parts of super-fine silicon powder, 127 parts of first-level coal ash, 30 parts of 200-thousand-viscosity cellulose ether, 20 parts of redispersible powder, 2 parts of water repellent and 8 parts of polycarboxylate water reducer. The treating agent disclosed by the invention can be directly scratched to the smooth surface of the ceramic brick, and the coating solidified has high strength and good flexibility. Mortar is free from phenomena such as cracks, hollowness and falling. Therefore, the treating agent provided by the invention can effectively avoid troubles that ceramics need to be knocked down when the old wall is renovated and the like. The treating agent is a building material which improves the adhesive force on the surface of the ceramic brick.
Description
Technical field
The present invention relates to a kind of material of construction, relate in particular to a kind of ceramic tile interface treatment agent.
Background technology
As everyone knows, ceramic tile surface smoother, cannot be coated with Puttying or coating on its surface.If will carry out renewal and reform to being pasted with the old body of wall of ceramic tile, the current common practice is that ceramic tile is knocked out, and then is coated with the surfacings such as Puttying or coating; Not only time-consuming, and construction bothers, cost is high.
Summary of the invention
In order to overcome the defect existing in prior art, the present invention aims to provide a kind of ceramic tile interface treatment agent that improves ceramic tile surface sticking power.
To achieve these goals, technical scheme of the present invention is evenly mixed by the raw material of following weight part: 400 parts of PO52.5 cement, 400 parts of 80~100 object quartz sands, 50 parts of super-fine silicon micro-powders, 127 parts of first level flour coal ash, 3 parts, 200,000 viscosity cellulose ether, 20 parts of redispersable latex powders, 2 parts of hydrophober, 8 parts of polycarboxylate water-reducers.
In technique scheme, cement mainly plays bonding and performance later strength.Quartz sand plays fine aggregate effect, and it is combined with cement and can significantly improves mortar strength.Silicon powder is mainly used to fill space, can significantly improve mortar workability, improve mortar strength.Flyash can improve concrete weather resistance and intensity, minimizing water consumption.Ether of cellulose is the macromolecular compound with ether structure of being made by Mierocrystalline cellulose.In cellulose macromolecule, each glucose basic ring contains three hydroxyls, the primary hydroxyl on the 6th carbon atom, the secondary hydroxyl on second and third carbon atom, and the hydrogen in hydroxyl is replaced by alkyl and generates ether of cellulose analog derivative; It is the resultant that the hydrogen of hydroxyl in Mierocrystalline cellulose polymer is replaced by alkyl.Mierocrystalline cellulose can be water-soluble after etherificate, dilute alkaline soln and organic solvent, and have thermoplasticity.Ether of cellulose is widely used as thickening material, tackiness agent and protective colloid etc., has good thickening and water retention property, can obviously improve performance, the raising sag resistance of mortar, thereby prevent that mortar from gliding in mortar.Redispersable latex powder is the multipolymer by the binary such as a kind of vinyl acetate and tertiary ethylene carbonate-VeoVa or ethene or acrylate or ternary, through the dry modified emulsion powder obtaining of spraying; There is good redispersible, while contacting with water, be again dispersed into emulsion, and its chemical property is identical with initial latex.Redispersable latex powder disperses rear film forming and brings into play enhancement as the second tackiness agent; Protective colloid is absorbed (after film forming, can not fallen by water destruct, or " twice dispersing ") by mortar; The fluoropolymer resin of film forming is distributed in whole mortar as strongthener, thereby has increased the force of cohesion of mortar.Redispersable latex powder can improve workability in wet mortar, improve liquidity can, increase thixotroping with the anti-property of hanging down, improve force of cohesion, extend the open hour, strengthen water-retentivity etc.; In addition, redispersable latex powder also can improve tensile strength, increases bend resistance intensity, reduces Young's modulus, improves deformability, increases material degree of compactness, increases abrasive wear resistance, improves cohesive strength, reduces carbonation depth, reduce material water-absorbent after mortar solidifies, and makes material have splendid hydrophobicity (adding hydrophobicity rubber powder).In a word, redispersable latex powder can increase mortar snappiness, prevents mortar cracking, hollowing, comes off.Hydrophober can play waterproof action in mortar.Polycarboxylate water-reducer can reduce water cement ratio, improves the later strength of mortar.
Compared with the prior art, the present invention is owing to having adopted technique scheme, and treatment agent of the present invention can be affine with ceramic tile surface at normal temperatures after scraping construction through being coated with, and crosslinking curing and form the polymer reticulated structure coating that strong adhesion, intensity are high, temper toughness with gentleness; And after this coating curing, be rich in pore, can form fabulous avidity with putty or coating.Treatment agent of the present invention can directly be criticized the ceramic tile surface of scraping in smooth, and coating solidifies that rear intensity is high, snappiness good, the phenomenon such as mortar there will not be cracking, hollowing, come off; While therefore using treatment agent of the present invention that old body of wall renewal and reform can effectively be avoided, need knock out many troubles such as ceramic tile.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, and concrete steps are as follows:
Calculate by weight, by 400 parts of PO52.5 cement, 400 parts of 80~100 object quartz sands, 50 parts of super-fine silicon micro-powders, 127 parts of first level flour coal ash, 3 parts, 200,000 viscosity cellulose ether, 20 parts of redispersable latex powders, 2 parts of hydrophober, 8 parts of polycarboxylate water-reducers, put into concentrated the stirring of high-speed stirring and get final product (about 5 minutes).During use, the water cement ratio by 0.25 mixes to criticize and scrapes in ceramic tile surface.
Claims (1)
1. a ceramic tile interface treatment agent, is characterized in that evenly being mixed by the raw material of following weight part: 400 parts of PO52.5 cement, 400 parts of 80~100 object quartz sands, 50 parts of super-fine silicon micro-powders, 127 parts of first level flour coal ash, 3 parts, 200,000 viscosity cellulose ether, 20 parts of redispersable latex powders, 2 parts of hydrophober, 8 parts of polycarboxylate water-reducers.