CN107601985A - A kind of ceramic tile interface agent - Google Patents
A kind of ceramic tile interface agent Download PDFInfo
- Publication number
- CN107601985A CN107601985A CN201710917382.8A CN201710917382A CN107601985A CN 107601985 A CN107601985 A CN 107601985A CN 201710917382 A CN201710917382 A CN 201710917382A CN 107601985 A CN107601985 A CN 107601985A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- acrylic emulsion
- water
- aggregate
- aqua
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ceramic tile interface agent, the ceramic tile interface agent includes powder material and aqua material, the powder material is mixed by aggregate, filler, adjuvant and adhesive material, the aggregate is made up of coarse aggregate and fine aggregate, the filler is activity filler, the adjuvant is made up of mica powder, water-loss reducer and water reducer, and the adhesive material is cement；The aqua material is mixed by the one or more in silicone acrylic emulsion, pure-acrylic emulsion and styrene-acrylic emulsion and water, and the styrene-acrylic emulsion is viscous force adjuvant；The powder material is with aqua material according to weight than 2.3:1~2.8:1 ratio is mixed.The present invention provides the ceramic tile interface agent that a kind of adhesive force is strong, weatherability is strong, realizes that direct paving ceramic tile is so as to simplify working procedure in ceramic tile smooth surface, dust caused by ceramic tile and building waste are destroyed in reduction, improve operating efficiency, reduce engineering cost.
Description
Technical field
The present invention relates to a kind of ceramic tile interface agent of building material field, and especially one kind can be directly on old tile decorative surface
The ceramic tile interface agent of the new ceramic tile of paving and grout filling hollowing.
Background technology
With living standards of the people and the increasingly raising of living conditions, high-compactness and low water absorption tapestry brick big rule
Mould is applied to the decorative engineering on wall ground, and tapestry brick typically use ceramic tile adhesive or cement mortar paving, but easily appearance by
It is incorrect in paving mode and the situation of hollowing occur.And the species such as color, material, decoration with tapestry brick is more and more,
The ceramic tile retreading frequency in the places such as hotel, shop, office and house also more and more higher.Traditional ceramic tile retreading is repaiied
Multiple hollowing needs first to destroy the ceramic tile of ground or metope, then with ceramic tile adhesive or the new ceramic tile of cement mortar paving, it is traditional
Renovation restorative procedure process is more, and time-consuming, and dust pollution is big and sticking strength is low, and cost is high.
The development step in epoch is followed, occurs some super-strength ceramic tile interface agents, such as Application No. successively on the market
201610391756.2, data of publication of application is on May 17th, 2017, and a kind of entitled super-strength ceramic tile interface agent, it is wrapped
Include powder and liquid material, the powder includes cement, quartz sand, latex powder and cellulose ether, and the liquid material includes styrene-acrylic emulsion, pure
Acrylic emulsion, synergist, dispersant, it is anti-be divided into agent and water, the powder is with liquid material according to 2:1 ratio is mixed, during use
Interfacial agents need to be painted on to the back side of ceramic tile, after the placement super-strength ceramic tile interface agent such as 1~2 hour is dry, by ceramic tile and cement
Slurry carries out paving, though this invention can solve to cause viscous with all kinds of cement matrixs due to high-compactness and the low water absorption of ceramic tile
The problem of relay difference is so as to produce hollowing and peel off, but paving process is added, and ceramic tile hollowing gap reality can not be directly injected into
Reparation at existing ceramic tile hollowing, if directly there are interfacial agents if the new ceramic tile of ceramic tile surface paving and can not solidify to lose viscous force, therefore
Still need to break into pieces old ceramic tile that destroy just can be with the new ceramic tile of paving at the new ceramic tile of paving and hollowing before repairing, it is impossible to solve traditional turn over
The problem of new restorative procedure process is more, and time-consuming, and dust pollution is big, and cost is high.
Therefore, it is necessary to design a kind of high compactedness material adhesive ability by force and have certain mobility and enough dense
Denseness can be directly in the new ceramic tile of ceramic tile surface paving, and can be directly injected into the ceramic tile interface at ceramic tile hollowing gap reparation hollowing
Agent, realizes easy to use, simplifies operational procedure, reduces renovation, the cost of re-posted ceramic tile, effectively avoids the effect of dust pollution,
To solve the above problems.
The content of the invention
The purpose of the invention is to provide a kind of high compactedness material adhesive ability by force and has certain mobility
And density can be directly in the new ceramic tile of ceramic tile surface paving enough, and the porcelain at ceramic tile hollowing gap reparation hollowing can be directly injected into
Brick interfacial agents.
To reach above-mentioned purpose, the present invention adopts the following technical scheme that：A kind of ceramic tile interface agent, the ceramic tile interface agent bag
Include powder material and aqua material, the ceramic tile interface agent includes powder material and aqua material, the powder material by aggregate,
Filler, adjuvant and adhesive material are mixed, and the aggregate is made up of coarse aggregate and fine aggregate, and the filler is active filler
Material, the adjuvant are made up of mica powder, water-loss reducer and water reducer, and the adhesive material is cement；The aqua material is by silicon
One or more and water in acrylic emulsion, pure-acrylic emulsion and styrene-acrylic emulsion are mixed, and the styrene-acrylic emulsion is viscous force adjuvant；
The powder material is with aqua material according to weight than 2.3:1~2.8:1 ratio is mixed.In powder material of the present invention
Aggregate forms fine and close support framework structure as the resistance to compression support frame after interfacial agents solidification, coarse aggregate and fine aggregate, improves boundary
Hardness after the agent solidification of face.Filler mixes the compactness after improving aggregate solidification with aggregate, and mica powder can strengthen in adjuvant
Ceramic tile interface agent solidification after pliability, improve weatherability, avoid because expanded with heat and contract with cold caused by climate change cause solidification after
There are crack conditions in interfacial agents.Adhesive material provides viscous force, ensures that ceramic tile can be adhered tightly on old ceramic tile；It is pure in aqua material
Acrylic emulsion is improves the main material of interfacial agents cohesive force and weatherability, and silicone acrylic emulsion and styrene-acrylic emulsion are as auxiliary material, benzene
Acrylic emulsion can improve the bonding force and weatherability of interfacial agents, and water is mixed to form the interfacial agents with viscous force with adhesive material, and water adds
Entering amount and crossing at most causes cohesive force to decline, and adding water and crossing easily causes cement solidification in interfacial agents powder material not thorough at least,
So as to reduce intensity.Powder material and aqua material mix according to certain formula rate, when powder material and aqua material
Mixed proportion is less than 2.3:1, cause that moisture can not be excessively completely dried or drying time is long, influence to use, and pulvis
The small viscosity for then reducing interfacial agents of material proportion；When the mixed proportion of powder material and aqua material is more than 2.8:1, moisture
It is too low to make interfacial agents poor fluidity, cause interfacial agents to be difficult to sprawl on ceramic tile.Powder material and aqua material are according to certain
Formed after formula rate mixing with the strong interfacial agents of certain fluidity, cohesive force, directly can tile boundary on the facing of ceramic tile
The new ceramic tile of paving or directly it is poured in the hollowing of ceramic tile after the agent of face, releases position, ceramic tile can be by after the interfacial agents solidification
Cement, it is easy to operate simple, it is not necessary to which that ability paving is new after breaking the ceramic tile that original old ceramic tile or hollowing release into pieces removing
Ceramic tile, reduce renovation, the cost of re-posted ceramic tile.
Yet further, each composition is as follows according to the formula accounting of percentage by weight in the powder material：
Aggregate is 30% ~ 45%, and wherein coarse aggregate is 5%~15%, and fine aggregate is 25%~40%；Coarse aggregate accounting is less than 5% interface
The skeleton hardness formed after agent solidification is low, can not bear larger pressure, and coarse aggregate accounting causes slurry easily to sink higher than 15%
Bottom, it can not uniformly smear and paste ceramic tile；Fine aggregate accounting is less than 25% gap that can not be filled up completely with coarse aggregate, makes interfacial agents
The consistency of solidification back skeleton is low, and bearing capacity is weak, and the reduction of coarse aggregate accounting is caused if fine aggregate accounting is higher than 40%, can not
Form the big pressure-bearing skeleton of hardness and reduce crack resistance.
Activity filler is 10%~15%；The activity filler accounting is on the weak side less than 10% interfacial agents mobility, makes boundary
Face agent can not in the smooth surface of ceramic tile drawout；Activity filler accounting makes interfacial agents mobility too strong higher than 15%, in ceramic tile
Smooth surface on can not aggegation together.
The adjuvant is 2.35%~3.55%, and wherein mica powder is 2%~3%, and water-loss reducer is 0.25%~0.35%, diminishing
Agent is 0.1%~0.2%；The pliability of mica powder increase interfacial agents, reduce because climate change interfacial agents are expanded with heat and contract with cold appearance
Fracture, mica powder content can not effectively strengthen the pliability after ceramic tile interface agent solidification less than 2%, can if content is higher than 3%
Reduce the adherence force after ceramic tile interface agent solidification；Water-loss reducer realizes water conservation denseness, improves interfacial agents mobile performance, makes interfacial agents can
Smooth scrape is put in ceramic tile smooth surface or the ceramic tile back side, when water conservation agent content is less than 0.25% effect that can not realize water-keeping thickening,
Cause interfacial agents mobility is excessive to reduce its cohesive force if content is higher than 0.35%；Water reducer can reduce mixing water amount, can have
Diminishing is imitated up to 10%, viscosity is improved, shortens the time of interfacial agents dry solidification, be unable to reach if reduced water content is less than 0.1%
Water-reducing effect, cause interfacial agents water content high, dry solidification time length, cause interfacial agents stream if reduced water content is higher than 0.2%
Dynamic property is too strong.
The adhesive material cement is 40%~55%, and cement mainly plays adhesive action, when cement content is less than 40% boundary
The stickiness of face agent reduces, and shortens ceramic tile service life, fragility after higher than 55% interfacial agents solidification of cement content compared with
Greatly, product is influenceed；
Each composition is as follows according to the formula accounting of percentage by weight in the aqua material：
Silicone acrylic emulsion is 0%~80%；
Pure-acrylic emulsion is 30%~80%；
Styrene-acrylic emulsion is 0%~50%；
Water is 20%~25%.
Pure-acrylic emulsion is improves the main material of interfacial agents cohesive force and weatherability in the aqua material, silicone acrylic emulsion and
Styrene-acrylic emulsion is as auxiliary material.Silicone acrylic emulsion and styrene-acrylic emulsion are added without in aqua material will not cause under interfacial agents adherence force
Drop, and the adherence force and weatherability of interfacial agents can then be improved by adding silicone acrylic emulsion and styrene-acrylic emulsion, make the using effect of interfacial agents
More preferably.Water content easily causes because hypohydration cement easily ftractures less than 20%, influences to use ceramic tile service life, water contains
The cohesive force of higher than 25% reduction interfacial agents of amount.
Yet further, each composition is as follows according to the formula accounting of percentage by weight in the powder material：
Aggregate is 45%, and wherein coarse aggregate is 5%, fine aggregate 40%；
Activity filler is 12.6%；
Adjuvant is 2.4%, and wherein mica powder is 2%, water-loss reducer 0.25%, water reducer 0.15%；
Adhesive material cement is 40%；
Each composition is as follows according to the formula accounting of percentage by weight in the aqua material：
Silicone acrylic emulsion is 0%；
Pure-acrylic emulsion is 80%；
Styrene-acrylic emulsion is 0%；
Water is 20%；
The powder material is with aqua material according to weight than 2.3:1 ratio is mixed.Such composition proportion, it can make
Cohesive force and mobility of the interfacial agents in ceramic tile smooth surface reach optimal, it is possible to achieve new ceramic tile is directly on old ceramic tile smooth surface upper berth
Patch, and can directly being repaired by irrigating interfacial agents at ceramic tile hollowing and the gap released, simplifies working procedure, reduce renovation with
Repair the cost of ceramic tile.
Yet further, each composition is as follows according to the formula accounting of percentage by weight in the powder material：
Aggregate is 37.1%, and wherein coarse aggregate is 5%, fine aggregate 32.1%；
Activity filler is 10%；
The adjuvant is 2.9%, and wherein mica powder is 2.5%, water-loss reducer 0.3%, water reducer 0.1%；
The adhesive material cement is 50%；
Each composition is as follows according to the formula accounting of percentage by weight in the aqua material：
Silicone acrylic emulsion is 20%；
Pure-acrylic emulsion is 50%；
Styrene-acrylic emulsion is 10%；
Water is 20%；
The powder material is with aqua material according to weight than 2.5:1 ratio is mixed.Such composition proportion, it can make
Cohesive force and mobility of the interfacial agents in ceramic tile smooth surface reach optimal, it is possible to achieve new ceramic tile is directly on old ceramic tile smooth surface upper berth
Patch, and can directly being repaired by irrigating interfacial agents at ceramic tile hollowing and the gap released, simplifies working procedure, reduce renovation with
Repair the cost of ceramic tile.
Yet further, each composition is as follows according to the formula accounting of percentage by weight in the powder material：
Aggregate is 30%, and wherein coarse aggregate is 5%, fine aggregate 25%；
Activity filler is 11.45%；
Adjuvant is 3.55%, and wherein mica powder is 3%, water-loss reducer 0.35%, water reducer 0.2%；
Adhesive material cement is 55%；
Each composition is as follows according to the formula accounting of percentage by weight in aqua material：
Silicone acrylic emulsion is 20%；
Pure-acrylic emulsion is 30%；
Styrene-acrylic emulsion is 25%；
Water is 25%；
The powder material is with aqua material according to weight than 2.8:1 ratio is mixed.Such composition proportion, it can make
Cohesive force and mobility of the interfacial agents in ceramic tile smooth surface reach optimal, it is possible to achieve new ceramic tile is directly on old ceramic tile smooth surface upper berth
Patch, and can directly being repaired by irrigating interfacial agents at ceramic tile hollowing and the gap released, simplifies working procedure, reduce renovation with
Repair the cost of ceramic tile.
Yet further, the mica powder includes the mica powder of the mesh of 800 mesh~1200.Less than 800 mesh mica powder due to
Granularity is excessive to lose the enhancing flexible effect of ceramic tile interface agent, and the mica powder more than 1200 mesh then causes ceramic tile interface agent flexible
Property it is excessive and influence its hardness, reduce ceramic tile anti-pressure ability.
Yet further, the activity filler is flyash, and the flyash quality rank is I grade of national standard or national standard II
Level.Flyash improves the compactness after interfacial agents solidification, can also improve powder material and the mixed mobility of aqua material, just
In even spread, and flyash is the fine ash that catching is got off in flue gas after coal combustion, is readily available.
Yet further, the water-loss reducer is starch ether, and water reducer is lignosulfonates, naphthalene sulphonate formaldehyde polymer
Or high-efficiency water-reducing agent of poly-carboxylic acid.When adding aqua material in powder material, water-loss reducer increases the water-retaining property of mortar, increases denseness,
Mobile performance is improved, interfacial agents is smoothly scraped and is put in ceramic tile smooth surface or the ceramic tile back side.Water reducer can reduce mixing water amount,
Effectively diminishing up to 10%, viscosity can be improved, shortens the time of interfacial agents dry solidification.
Yet further, the coarse aggregate is thick river sand or rubble sand, and the fine aggregate is thin river sand or fine quartz sand,
The thick river sand is the thick river sand of purpose of 25 mesh~40, and rubble sand is the rubble sand of the mesh of 25 mesh~40, and the thin river sand is 80
The thin river sand of purpose of mesh~150, fine quartz sand are the river sand ash of the fine quartz sand of the mesh of 80 mesh~150, the thick river sand and thin river sand
Native content is below 0.3%.Thick river sand or rubble sand primarily form the skeleton after interfacial agents solidification.The thin river sand or microlith
Sand mainly cooperates with thick river sand or rubble sand, interfacial agents is formed the pressure-bearing support frame of densification after solidifying.River sand
Dirt content can also influence the hardness after interfacial agents solidification higher than 0.3%, and cause interfacial agents viscous force to decline, so as to influence to use
Life-span.
Yet further, the strength of cement grade is 32.5 or 42.5.The cement of this strength grade can reach daily
The requirement of compression strength, cost are cheap.
Composition is mixed evenly by conventional method respectively for the preparation of powder material and the aqua material.
In use, powder material:Aqua material presses 2.3:1~2.8:1 ratio is mechanical or manual well mixed rear direct
The new ceramic tile of paving or reparation ceramic tile hollowing release place, can normally trample use after standing preliminary solidification in 24 hours, reach within 7~28 days
To complete solidification.
Compared with prior art, the advantageous effects of the invention：
Firstth, adhesive force is strong, and weatherability is strong.Traditional ceramic tile uses tile paste agent or cement mortar paving, but high fine and close
Adhesion is weak on degree material, hollowing easily occurs and releases.The silicone acrylic emulsion viscosity that is included in present component, pure-acrylic emulsion glue
Degree and styrene-acrylic emulsion have the function that to improve interfacial agents viscosity, adhesive force of the raising interfacial agents on high compactedness material；Pass through
Coarse aggregate and fine aggregate add interfacial agents according to a certain percentage, and hardness is high after making interfacial agents solidification, and mica powder improves interfacial agents
Pliability, avoid because expanded with heat and contract with cold caused by climate change cause solidification after interfacial agents there are crack conditions, weatherability is strong,
Improve the service life of ceramic tile.
Secondth, construction is simple is convenient, improves operating efficiency.Traditional ceramic tile retreading and hollowing, release reparation and be required to original
There is ceramic tile to destroy again again with tile paste agent or the new ceramic tile of cement mortar paving, and super-strength ceramic tile circle on the market at present
Face agent can not realize that directly hollowing and the new ceramic tile of paving directly in ceramic tile smooth surface are repaired in perfusion, make ceramic tile reparation and renovation process
More, time-consuming.The activity filler that the present invention adds makes interfacial agents have certain mobility, can be sprawled in ceramic tile smooth surface
Open, the hollowing that can also be directly poured in ceramic tile releases place；Carried additionally by addition silicone acrylic emulsion, pure-acrylic emulsion and styrene-acrylic emulsion
The cohesive force of high interfacial agents, and water reducer reduces the addition of water so as to accelerate the rate of drying of interfacial agents, makes interfacial agents straight
It is connected on to solidify in the ceramic tile smooth surface of high-compactness and bonds new ceramic tile, can be in the new porcelain of ceramic tile surface paving without destroying original ceramic tile
Brick, easy to use, working procedure simplifies, and improves operating efficiency.
3rd, engineering cost is reduced, reduces the pollution of dust and building waste.Traditional ceramic tile retreading and hollowing, release and repair
Be required to destroy original ceramic tile again again with tile paste agent or the new ceramic tile of cement mortar paving again, cause engineering cost compared with
Height, and work progress produces substantial amounts of dust and building waste, and certain pollution is caused to environment.The present invention can be in original ceramic tile
Smooth surface on direct paving new ceramic tile, without destroying original ceramic tile, and interfacial agents need to be only fed at the crack of ceramic tile hollowing
Hollowing can be repaired and release place, without original ceramic tile is destroyed, save the expense destroyed ceramic tile and clear up fragment dregs, significantly
Engineering cost is reduced, while reduces the pollution of dust and building waste.
Embodiment
For ease of more fully understanding the purpose of the present invention, structure, feature and effect etc., in conjunction with embodiment pair
The present invention is described further.
Embodiment 1
The ceramic tile interface agent of the present invention includes powder material and aqua material, the powder material including aggregate, activity filler,
Adjuvant and adhesive material, the content of the aggregate are 45%, and its mild-crude river sand is the thick river sand of purpose of 25 mesh~40,25 mesh
The content of the thick river sand of~40 purposes is 5%, and the thin river sand is the thin river sand of purpose of 80 mesh~150, and 80 mesh~150 purposes are thin
The content of river sand is 40%, and the activity filler is flyash, and the content of the flyash is 12.6%, and credit rating is national standard
I grade, the content of the adjuvant is 2.4%, and wherein mica powder is 800 mesh mica powders, and the content of the 800 mesh mica powder is 2%,
The water-loss reducer is starch ether, and the content of the starch ether is 0.25%, and the water reducer is lignosulfonates, described wooden
The content of plain sulfonate is 0.15%, and the adhesive material strength of cement grade is 32.5, and the content of the cement is 45%.
The aqua material includes pure-acrylic emulsion and water, and the wherein content of pure-acrylic emulsion is 80%, and remaining contains for water
Amount.
By the powder material with aqua material according to 2.3:1 ratio is mechanical or manual well mixed, directly brushes
On original old ceramic tile, smearing thickness 1mm, by the direct paving of new ceramic tile, tentatively coagulated after standing 24 hours after paving
Admittedly can normal use, place 7 days after pry open ceramic tile, interfacial agents solidify substantially.Interfacial agents are fed at ceramic tile hollowing in addition
Gap, irrigate to gap overflow interfacial agents, can be repaired at ceramic tile hollowing by flattening.
Embodiment 2
The ceramic tile interface agent of the present invention includes powder material and aqua material, the powder material including aggregate, activity filler,
Adjuvant and adhesive material, the content of the aggregate are 37.5%, and wherein rubble sand is the rubble sand of the mesh of 25 mesh~40, institute
The rubble sand content for stating the mesh of 25 mesh~40 is 5%, and the thin river sand is the fine quartz sand of the mesh of 80 mesh~150,80 mesh~
The fine quartz sand content of 150 mesh is 32.1%, and the activity filler is flyash, and the content of the flyash is 10%, quality
Grade is I grade of national standard, and the content of the adjuvant is 2.9%, and wherein mica powder is 1000 mesh mica powders, the 1000 mesh mica
The content of powder is 2.5%, and the water-loss reducer is starch ether, and the content of the starch ether is 0.3%, and the water reducer is naphthalene sulfonate
Yuban, the content of the naphthalene nucleus hydrochlorate yuban is 0.1%, and the adhesive material strength of cement grade is 42.5,
The content of the cement is 50%.
The aqua material includes silicone acrylic emulsion, pure-acrylic emulsion, styrene-acrylic emulsion and water, and the content of wherein silicone acrylic emulsion is
20%, the content of pure-acrylic emulsion is 50%, and the content of styrene-acrylic emulsion is 10%, and remaining is the content of water.
By the powder material with aqua material according to 2.5:1 ratio is mechanical or manual well mixed, after stirring,
Directly brush on original old ceramic tile, smearing thickness 2mm, it is small by standing 24 in the direct paving of new ceramic tile, after paving
When after preliminary solidification can normal use, pry open ceramic tile after placing 7 days, interfacial agents substantially completely solidify.Interfacial agents are filled in addition
The gap injected at ceramic tile hollowing, irrigate to gap and overflow interfacial agents, can be repaired at ceramic tile hollowing by flattening.
Embodiment 3
The ceramic tile interface agent of the present invention includes powder material and aqua material, the powder material including aggregate, activity filler,
Adjuvant and adhesive material, the content of the aggregate are 30%, and its mild-crude river sand is the thick river sand of purpose of 25 mesh~40,25 mesh
The thick river sand content of~40 purposes is 5%, and the thin river sand is the thin river sand of purpose of 80 mesh~150, the thin river of purpose of 180 mesh~150
Husky content is 25%, and the activity filler is flyash, and the content of the flyash is 11.45%, and credit rating is national standard II
Level, the content of the adjuvant is 3.55%, and wherein mica powder is 1200 mesh mica powders, and the content of the 1200 mesh mica powder is
3%, the water-loss reducer is starch ether, and the content of the starch ether is 0.35%, and the water reducer is high-efficiency water-reducing agent of poly-carboxylic acid, institute
The content for stating high-efficiency water-reducing agent of poly-carboxylic acid is 0.2%, and the adhesive material strength of cement grade is 32.5, the content of the cement
For 55%.
The aqua material includes silicone acrylic emulsion, pure-acrylic emulsion, styrene-acrylic emulsion and water, and the content of wherein silicone acrylic emulsion is
20%, the content of pure-acrylic emulsion is 30%, and the content of styrene-acrylic emulsion is 25%, and remaining is the content of water.
By the powder material with aqua material according to 2.8:1 ratio is mechanical or manual well mixed, after stirring,
Directly brush on original old ceramic tile, smearing thickness 3mm, it is small by standing 24 in the direct paving of new ceramic tile, after paving
When after preliminary solidification can normal use, pry open ceramic tile after placing 7 days, interfacial agents solidify substantially.Interfacial agents are fed into addition
Gap at ceramic tile hollowing, irrigate to gap and overflow interfacial agents, can be repaired at ceramic tile hollowing by flattening.
The powder material and fluent material of the ceramic tile interface agent of the present invention can be with two-way penetrations, the viscous of cement matrix
Relay plays completely, can be injected by the gap for tilting angle or tiles edges of ceramic tile at ceramic tile hollowing, it is not necessary to destroy or prize
Hollowing could be repaired by playing ceramic tile, simple to operate.
Detailed description above is only the explanation of the preferred embodiments of the invention, non-therefore the limitation present invention the scope of the claims,
So all, with this creation description institute, equivalence techniques changes for it, is both contained in the scope of the claims of this creation.
Claims (10)
- A kind of 1. ceramic tile interface agent, it is characterised in that：The ceramic tile interface agent includes powder material and aqua material, the pulvis Material is mixed by aggregate, filler, adjuvant and adhesive material, and the aggregate is made up of coarse aggregate and fine aggregate, described to fill out Expect to be made up of mica powder, water-loss reducer and water reducer for activity filler, the adjuvant, the adhesive material is cement；It is described Aqua material is mixed by the one or more in silicone acrylic emulsion, pure-acrylic emulsion and styrene-acrylic emulsion and water, the styrene-acrylic emulsion For viscous force adjuvant；The powder material is with aqua material according to weight than 2.3:1~2.8:1 ratio is mixed.
- A kind of 2. ceramic tile interface agent according to claim 1, it is characterised in that：In the powder material each composition according to The formula accounting of percentage by weight is as follows：Aggregate is 30%~45%, and wherein coarse aggregate is 5%~15%, and fine aggregate is 25%~40%；Activity filler is 10%~15%；Adjuvant is 2.35%~3.55%, and wherein mica powder is 2%~3%, and water-loss reducer is 0.25%~0.35%, water reducer 0.1% ~0.2%；Adhesive material cement is 40%~55%；Each composition is as follows according to the formula accounting of percentage by weight in the aqua material：Silicone acrylic emulsion is 0%~80%；Pure-acrylic emulsion is 30%~80%；Styrene-acrylic emulsion is 0%~50%；Water is 20%~25%.
- A kind of 3. ceramic tile interface agent according to claim 2, it is characterised in that：In the powder material each composition according to The formula accounting of percentage by weight is as follows：Aggregate is 45%, and wherein coarse aggregate is 5%, fine aggregate 40%；Activity filler is 12.6%；Adjuvant is 2.4%, and wherein mica powder is 2%, water-loss reducer 0.25%, water reducer 0.15%；Adhesive material cement is 40%；Each composition is as follows according to the formula accounting of percentage by weight in the aqua material：Silicone acrylic emulsion is 0%；Pure-acrylic emulsion is 80%；Styrene-acrylic emulsion is 0%；Water is 20%；The powder material is with aqua material according to weight than 2.3:1 ratio is mixed.
- A kind of 4. ceramic tile interface agent according to claim 2, it is characterised in that：In the powder material each composition according to The formula accounting of percentage by weight is as follows：Aggregate is 37.1%, and wherein coarse aggregate is 5%, fine aggregate 32.1%；Activity filler is 10%；The adjuvant is 2.9%, and wherein mica powder is 2.5%, water-loss reducer 0.3%, water reducer 0.1%；The adhesive material cement is 50%；Each composition is as follows according to the formula accounting of percentage by weight in the aqua material：Silicone acrylic emulsion is 20%；Pure-acrylic emulsion is 50%；Styrene-acrylic emulsion is 10%；Water is 20%；The powder material is with aqua material according to weight than 2.5:1 ratio is mixed.
- A kind of 5. ceramic tile interface agent according to claim 2, it is characterised in that：In the powder material each composition according to The formula accounting of percentage by weight is as follows：Aggregate is 30%, and wherein coarse aggregate is 5%, fine aggregate 25%；Activity filler is 11.45%；Adjuvant is 3.55%, and wherein mica powder is 3%, water-loss reducer 0.35%, water reducer 0.2%；Adhesive material cement is 55%；Each composition is as follows according to the formula accounting of percentage by weight in aqua material：Silicone acrylic emulsion is 20%；Pure-acrylic emulsion is 30%；Styrene-acrylic emulsion is 25%；Water is 25%；The powder material is with aqua material according to weight than 2.8:1 ratio is mixed.
- A kind of 6. ceramic tile interface agent according to claim 1, it is characterised in that：The mica powder is the mesh of 800 mesh~1200 Mica powder.
- A kind of 7. ceramic tile interface agent according to claim 1, it is characterised in that：The activity filler is flyash, institute It is II grade of I grade of national standard or national standard to state flyash quality rank.
- A kind of 8. ceramic tile interface agent according to claim 1, it is characterised in that：The water-loss reducer is starch ether, water reducer For lignosulfonates, naphthalene sulphonate formaldehyde polymer or high-efficiency water-reducing agent of poly-carboxylic acid.
- A kind of 9. ceramic tile interface agent according to claim 1, it is characterised in that：The coarse aggregate is thick river sand or rubble English Sand, the fine aggregate are thin river sand or fine quartz sand, and the thick river sand is the thick river sand of purpose of 25 mesh~40, and rubble sand is 25 mesh The rubble sand of~40 mesh, the thin river sand are the thin river sand of purpose of 80 mesh~150, and fine quartz sand is the microlith of the mesh of 80 mesh~150 The river sand dirt content of sand, the thick river sand and thin river sand is below 0.3%.
- A kind of 10. ceramic tile interface agent according to claim 1, it is characterised in that：The strength of cement grade be 32.5 or 42.5。