CN104005291A - 一种强吸附降低烟气的水松纸及其制备方法 - Google Patents

一种强吸附降低烟气的水松纸及其制备方法 Download PDF

Info

Publication number
CN104005291A
CN104005291A CN201410237074.7A CN201410237074A CN104005291A CN 104005291 A CN104005291 A CN 104005291A CN 201410237074 A CN201410237074 A CN 201410237074A CN 104005291 A CN104005291 A CN 104005291A
Authority
CN
China
Prior art keywords
parts
tipping paper
water
add
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410237074.7A
Other languages
English (en)
Other versions
CN104005291B (zh
Inventor
杜威
侯国强
牛和建
郭杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou Cigarette Materials Factory
Original Assignee
Chuzhou Cigarette Materials Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chuzhou Cigarette Materials Factory filed Critical Chuzhou Cigarette Materials Factory
Priority to CN201410237074.7A priority Critical patent/CN104005291B/zh
Publication of CN104005291A publication Critical patent/CN104005291A/zh
Application granted granted Critical
Publication of CN104005291B publication Critical patent/CN104005291B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种强吸附降低烟气的水松纸，其特征在于，由下列重量份的原料制备制成：漂白亚麻浆43-46、漂白针叶木浆52-54、纳米二氧化硅2-3、碳酸钾3-4、柠檬酸1-1.5、灯芯草4-6、迷迭香叶片3-5、黄原胶2-3、四氧化三铁1-1.5、乙酰化二淀粉磷酸酯0.5-0.7、聚乙烯亚胺0.6-0.8、助剂1-2、水适量；本发明水松纸添加植物纤维，纤维分布均匀，色泽一致，施胶度适中，印刷性能好，添加纳米二氧化硅作为填充剂，具有良好的吸附作用，通过过滤嘴，再经过水松纸，吸附烟气效果强，添加助剂，不仅能够增加焦油吸附量，而且具有天然香味，减少口腔异味。

Description

一种强吸附降低烟气的水松纸及其制备方法
技术领域
本发明涉及香烟技术领域，特别是一种强吸附降低烟气的水松纸及其制备方法。
背景技术
现有过滤烟嘴由于过滤原理单一、过滤过程没有按烟气的具体情况考虑，无法达到充分理想的过滤效果。如一次性过滤烟嘴太过于简单化，使之大部分有害物质不能清除掉。又如专利号为ZL200920112618.1的"多节除焦油烟嘴"专利，虽具有滤烟道长，除焦油效果好，但忽视了一个重要环节，相同结构的除焦器，在滤烟烟道长时，会出现烟气堵塞，抽上几支烟后会更加堵塞，导致最终不能使用。现在就希望发明一种水松纸包裹在过滤嘴外层，能够起到过滤吸附作用，既不会堵塞，又能清楚掉有害物质。
发明内容
本发明的目的是提供一种强吸附降低烟气的水松纸及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种强吸附降低烟气的水松纸，由下列重量份的原料制备制成：漂白亚麻浆43-46、漂白针叶木浆52-54、纳米二氧化硅2-3、碳酸钾3-4、柠檬酸1-1.5、灯芯草4-6、迷迭香叶片3-5、黄原胶2-3、四氧化三铁1-1.5、乙酰化二淀粉磷酸酯0.5-0.7、聚乙烯亚胺0.6-0.8、助剂1-2、水适量；
所述助剂由以下重量份的原料制成：粉碎陈皮4-5、佛手柑冻干粉2-4、干燥茶叶渣2-4、珍珠粉1-2、硅藻土3-5、丁香精油1-2、西黄蓍胶0.8-1、水适量；制备方法是将柠檬冻干粉、小黄瓜冻干粉、粉碎柠檬草、粗孔硅胶、白土混合粉碎成60-80目的粉末，然后加入迷迭香精油、少量水进行研磨，研磨20-30分钟后加水稀释成固含量为10-15%的溶液，最后加入西黄蓍胶搅拌均匀，得到悬浊液即得。
本发明所述一种强吸附降低烟气的水松纸，由以下具体步骤制成：
（1）将灯芯草、迷迭香叶片加入2-3倍的水进行煎煮，过滤，滤液待用，取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时，加热至沸腾，小火蒸煮 2小时，然后水洗不溶物至无色，再用浓度为5％的盐酸和浓度为 4％的碳酸钠水溶液反复洗涤，直至不溶物的 pH 值为 7±0.2，然后干燥不溶物，即得植物纤维。
（2）将植物纤维、漂白亚麻浆、漂白针叶木浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在3.6-4.5％，叩解度在66～740SR，制得浆料；
（3）将纳米二氧化硅、碳酸钾混合均匀，研磨成40-60目的粉末，加入四氧化三铁，搅拌25-30分钟制成混合料，然后在50-60℃烘干1-1.5小时待用；
（4）将混合料加入浆料中，加入除助剂以外的其余剩余成分，搅拌均匀，加入步骤（1）中滤液以及适量的水调浆至固含量为2.4-3.5%，加热至65-72℃，将调好的浆料经网部及压榨部脱水成形，湿纸页进入前干阶段，在表面均匀涂刷助剂；
（5）在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水，然后电热鼓风干燥5-6min，最后在光机上进行压光，取出后即得水松纸原纸。
本发明的有益效果是：本发明水松纸添加植物纤维，纤维分布均匀，色泽一致，施胶度适中，印刷性能好，添加纳米二氧化硅作为填充剂，具有良好的吸附作用，通过过滤嘴，再经过水松纸，吸附烟气效果强，添加助剂，不仅能够增加焦油吸附量，而且具有天然香味，减少口腔异味。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种强吸附降低烟气的水松纸，由下列重量份（公斤）的原料制备制成：漂白亚麻浆43、漂白针叶木浆52、纳米二氧化硅2、碳酸钾3、柠檬酸1、灯芯草4、迷迭香叶片3、黄原胶2、四氧化三铁1、乙酰化二淀粉磷酸酯0.5、聚乙烯亚胺0.6、助剂1、水适量；
所述助剂由以下重量份（公斤）的原料制成：粉碎陈皮4、佛手柑冻干粉2、干燥茶叶渣2、珍珠粉1、硅藻土3、丁香精油1、西黄蓍胶0.8、水适量；制备方法是将柠檬冻干粉、小黄瓜冻干粉、粉碎柠檬草、粗孔硅胶、白土混合粉碎成60-80目的粉末，然后加入迷迭香精油、少量水进行研磨，研磨20-30分钟后加水稀释成固含量为10-15%的溶液，最后加入西黄蓍胶搅拌均匀，得到悬浊液即得。
本发明所述一种强吸附降低烟气的水松纸，由以下具体步骤制成：
（1）将灯芯草、迷迭香叶片加入2-3倍的水进行煎煮，过滤，滤液待用，取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时，加热至沸腾，小火蒸煮 2小时，然后水洗不溶物至无色，再用浓度为5％的盐酸和浓度为 4％的碳酸钠水溶液反复洗涤，直至不溶物的 pH 值为 7±0.2，然后干燥不溶物，即得植物纤维。
（2）将植物纤维、漂白亚麻浆、漂白针叶木浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在3.6-4.5％，叩解度在66～740SR，制得浆料；
（3）将纳米二氧化硅、碳酸钾混合均匀，研磨成40-60目的粉末，加入四氧化三铁，搅拌25-30分钟制成混合料，然后在50-60℃烘干1-1.5小时待用；
（4）将混合料加入浆料中，加入除助剂以外的其余剩余成分，搅拌均匀，加入步骤（1）中滤液以及适量的水调浆至固含量为2.4-3.5%，加热至65-72℃，将调好的浆料经网部及压榨部脱水成形，湿纸页进入前干阶段，在表面均匀涂刷助剂；
（5）在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水，然后电热鼓风干燥5-6min，最后在光机上进行压光，取出后即得水松纸原纸。
经检测，本发明制得的水松纸原纸的纵向抗张强度为1.68KN/m，透气度为70CU。

Claims (2)

1.一种强吸附降低烟气的水松纸，其特征在于，由下列重量份的原料制备制成：漂白亚麻浆43-46、漂白针叶木浆52-54、纳米二氧化硅2-3、碳酸钾3-4、柠檬酸1-1.5、灯芯草4-6、迷迭香叶片3-5、黄原胶2-3、四氧化三铁1-1.5、乙酰化二淀粉磷酸酯0.5-0.7、聚乙烯亚胺0.6-0.8、助剂1-2、水适量；
所述助剂由以下重量份的原料制成：粉碎陈皮4-5、佛手柑冻干粉2-4、干燥茶叶渣2-4、珍珠粉1-2、硅藻土3-5、丁香精油1-2、西黄蓍胶0.8-1、水适量；制备方法是将柠檬冻干粉、小黄瓜冻干粉、粉碎柠檬草、粗孔硅胶、白土混合粉碎成60-80目的粉末，然后加入迷迭香精油、少量水进行研磨，研磨20-30分钟后加水稀释成固含量为10-15%的溶液，最后加入西黄蓍胶搅拌均匀，得到悬浊液即得。
2.根据权利要求1所述一种强吸附降低烟气的水松纸，其特征在于，由以下具体步骤制成：
（1）将灯芯草、迷迭香叶片加入2-3倍的水进行煎煮，过滤，滤液待用，取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时，加热至沸腾，小火蒸煮 2小时，然后水洗不溶物至无色，再用浓度为5％的盐酸和浓度为 4％的碳酸钠水溶液反复洗涤，直至不溶物的 pH 值为 7±0.2，然后干燥不溶物，即得植物纤维；
（2）将植物纤维、漂白亚麻浆、漂白针叶木浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在3.6-4.5％，叩解度在66～740SR，制得浆料；
（3）将纳米二氧化硅、碳酸钾混合均匀，研磨成40-60目的粉末，加入四氧化三铁，搅拌25-30分钟制成混合料，然后在50-60℃烘干1-1.5小时待用；
（4）将混合料加入浆料中，加入除助剂以外的其余剩余成分，搅拌均匀，加入步骤（1）中滤液以及适量的水调浆至固含量为2.4-3.5%，加热至65-72℃，将调好的浆料经网部及压榨部脱水成形，湿纸页进入前干阶段，在表面均匀涂刷助剂；
（5）在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水，然后电热鼓风干燥5-6min，最后在光机上进行压光，取出后即得水松纸原纸。
CN201410237074.7A 2014-05-30 2014-05-30 一种强吸附降低烟气的水松纸及其制备方法 Active CN104005291B (zh)