CN104005292A - 一种新型透气防火水松纸原纸及其制备方法 - Google Patents

一种新型透气防火水松纸原纸及其制备方法 Download PDF

Info

Publication number
CN104005292A
CN104005292A CN201410237075.1A CN201410237075A CN104005292A CN 104005292 A CN104005292 A CN 104005292A CN 201410237075 A CN201410237075 A CN 201410237075A CN 104005292 A CN104005292 A CN 104005292A
Authority
CN
China
Prior art keywords
parts
water
powder
base paper
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410237075.1A
Other languages
English (en)
Inventor
杜威
杨文涛
牛和建
郭杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou Cigarette Materials Factory
Original Assignee
Chuzhou Cigarette Materials Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chuzhou Cigarette Materials Factory filed Critical Chuzhou Cigarette Materials Factory
Priority to CN201410237075.1A priority Critical patent/CN104005292A/zh
Publication of CN104005292A publication Critical patent/CN104005292A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型透气防火水松纸原纸，其特征在于，由下列重量份的原料制备制成：纳米结晶纤维素1-2、辣木油0.4-0.7、氢氧化铝1-2、氢氧化镁1-1.5、白茅根3-5、水性聚氨酯胶粘剂2-2.6、棉浆43-46、漂白麦草浆52-54、蛭石粉2-3、白云母粉2-2.5、玉米秸秆4-6、食用明胶2-3、助剂1-2、水适量；本发明水松纸原纸施胶度适中，湿强度良好，添加植物纤维，使得纸张纤维分布均匀，透气性好，而且添加氢氧化铝、氢氧化镁等阻燃成分能够自动熄灭，防止火宅发生，添加助剂，不仅能够增加焦油吸附量，而且具有天然香味，清新宜人，减少口腔异味。

Description

一种新型透气防火水松纸原纸及其制备方法
技术领域
本发明涉及香烟技术领域，特别是一种新型透气防火水松纸原纸及其制备方法。
背景技术
随着国家对火灾安全问题的重视，人们自身安全意识的提高，对于卷烟行业需要加强卷烟产品自身的安全性，降低卷烟产品的火灾安全隐患，同时利用水松纸的透气性能稀释烟气是降低卷烟烟气中有害物质的一种重要手段，它包括采用打孔水松纸和自然透气水松纸两种办法。打孔水松纸是指利用静电或激光等手段在本身不透气的水松纸上打上许多小孔从而使其具有透气性能的一项技术，因其方法简单在国外被普遍使用。但由于其肉眼可见的小孔影响了卷烟外观，许多中国消费者对打孔稀释卷烟的接受程度不高，因此在国内只有少量使用。
发明内容
本发明的目的是提供一种新型透气防火水松纸原纸及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种新型透气防火水松纸原纸，由下列重量份的原料制备制成：纳米结晶纤维素1-2、辣木油0.4-0.7、氢氧化铝1-2、氢氧化镁1-1.5、白茅根3-5、水性聚氨酯胶粘剂2-2.6、棉浆43-46、漂白麦草浆52-54、蛭石粉2-3、白云母粉2-2.5、玉米秸秆4-6、食用明胶2-3、助剂1-2、水适量；
所述助剂由以下重量份的原料制成：粉碎陈皮4-5、佛手柑冻干粉2-4、干燥茶叶渣2-4、珍珠粉1-2、硅藻土3-5、丁香精油1-2、西黄蓍胶0.8-1、水适量；制备方法是将柠檬冻干粉、小黄瓜冻干粉、粉碎柠檬草、粗孔硅胶、白土混合粉碎成60-80目的粉末，然后加入迷迭香精油、少量水进行研磨，研磨20-30分钟后加水稀释成固含量为10-15%的溶液，最后加入西黄蓍胶搅拌均匀，得到悬浊液即得。
本发明所述一种新型透气防火水松纸原纸，由以下具体步骤制成：
（1）将白茅根、玉米秸秆加入2-3倍的水进行煎煮，过滤，滤液待用，取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时，加热至沸腾，小火蒸煮 2小时，然后水洗不溶物至无色，再用浓度为5％的盐酸和浓度为 4％的碳酸钠水溶液反复洗涤，直至不溶物的 pH 值为 7±0.2，然后干燥不溶物，即得植物纤维。
（2）将植物纤维、棉浆、漂白麦草浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在3.5-4.5％，叩解度在66～740SR，制得浆料；
（3）将氢氧化铝、氢氧化镁、蛭石粉、白云母粉混合均匀，研磨成40-60目的粉末，加入纳米结晶纤维素，搅拌25-30分钟制成混合料，然后在50-60℃烘干1-1.5小时待用；
（4）将混合料加入浆料中，加入除助剂以外的其余剩余成分，搅拌均匀，加入步骤（1）中滤液以及适量的水调浆至固含量为2.4-3.5%，加热至65-72℃，将调好的浆料经网部及压榨部脱水成形，湿纸页进入前干阶段，在表面均匀涂刷助剂；
（5）在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水，然后电热鼓风干燥5-6min，最后在光机上进行压光，取出后即得水松纸原纸。
本发明的有益效果是：本发明水松纸原纸施胶度适中，湿强度良好，添加植物纤维，使得纸张纤维分布均匀，透气性好，而且添加氢氧化铝、氢氧化镁等阻燃成分能够自动熄灭，防止火宅发生，添加助剂，不仅能够增加焦油吸附量，而且具有天然香味，清新宜人，减少口腔异味。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种新型透气防火水松纸原纸，由下列重量份（公斤）的原料制备制成：纳米结晶纤维素1、辣木油0.4、氢氧化铝1、氢氧化镁1、白茅根3、水性聚氨酯胶粘剂2、棉浆43、漂白麦草浆52、蛭石粉2、白云母粉2、玉米秸秆4、食用明胶2、助剂1、水适量；
所述助剂由以下重量份（公斤）的原料制成：粉碎陈皮4、佛手柑冻干粉2、干燥茶叶渣2、珍珠粉1、硅藻土3、丁香精油1、西黄蓍胶0.8、水适量；制备方法是将柠檬冻干粉、小黄瓜冻干粉、粉碎柠檬草、粗孔硅胶、白土混合粉碎成60-80目的粉末，然后加入迷迭香精油、少量水进行研磨，研磨20-30分钟后加水稀释成固含量为10-15%的溶液，最后加入西黄蓍胶搅拌均匀，得到悬浊液即得。
本发明所述一种新型透气防火水松纸原纸，由以下具体步骤制成：
（1）将白茅根、玉米秸秆加入2-3倍的水进行煎煮，过滤，滤液待用，取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时，加热至沸腾，小火蒸煮 2小时，然后水洗不溶物至无色，再用浓度为5％的盐酸和浓度为 4％的碳酸钠水溶液反复洗涤，直至不溶物的 pH 值为 7±0.2，然后干燥不溶物，即得植物纤维。
（2）将植物纤维、棉浆、漂白麦草浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在3.5-4.5％，叩解度在66～740SR，制得浆料；
（3）将氢氧化铝、氢氧化镁、蛭石粉、白云母粉混合均匀，研磨成40-60目的粉末，加入纳米结晶纤维素，搅拌25-30分钟制成混合料，然后在50-60℃烘干1-1.5小时待用；
（4）将混合料加入浆料中，加入除助剂以外的其余剩余成分，搅拌均匀，加入步骤（1）中滤液以及适量的水调浆至固含量为2.4-3.5%，加热至65-72℃，将调好的浆料经网部及压榨部脱水成形，湿纸页进入前干阶段，在表面均匀涂刷助剂；
（5）在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水，然后电热鼓风干燥5-6min，最后在光机上进行压光，取出后即得水松纸原纸。
经检测，本发明制得的水松纸原纸的纵向抗张强度为1.74KN/m，透气度为68CU。

Claims (2)

1.一种新型透气防火水松纸原纸，其特征在于，由下列重量份的原料制备制成：纳米结晶纤维素1-2、辣木油0.4-0.7、氢氧化铝1-2、氢氧化镁1-1.5、白茅根3-5、水性聚氨酯胶粘剂2-2.6、棉浆43-46、漂白麦草浆52-54、蛭石粉2-3、白云母粉2-2.5、玉米秸秆4-6、食用明胶2-3、助剂1-2、水适量；
所述助剂由以下重量份的原料制成：粉碎陈皮4-5、佛手柑冻干粉2-4、干燥茶叶渣2-4、珍珠粉1-2、硅藻土3-5、丁香精油1-2、西黄蓍胶0.8-1、水适量；制备方法是将柠檬冻干粉、小黄瓜冻干粉、粉碎柠檬草、粗孔硅胶、白土混合粉碎成60-80目的粉末，然后加入迷迭香精油、少量水进行研磨，研磨20-30分钟后加水稀释成固含量为10-15%的溶液，最后加入西黄蓍胶搅拌均匀，得到悬浊液即得。
2.根据权利要求1所述一种新型透气防火水松纸原纸，其特征在于，由以下具体步骤制成：
（1）将白茅根、玉米秸秆加入2-3倍的水进行煎煮，过滤，滤液待用，取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时，加热至沸腾，小火蒸煮 2小时，然后水洗不溶物至无色，再用浓度为5％的盐酸和浓度为 4％的碳酸钠水溶液反复洗涤，直至不溶物的 pH 值为 7±0.2，然后干燥不溶物，即得植物纤维；
（2）将植物纤维、棉浆、漂白麦草浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在3.5-4.5％，叩解度在66～740SR，制得浆料；
（3）将氢氧化铝、氢氧化镁、蛭石粉、白云母粉混合均匀，研磨成40-60目的粉末，加入纳米结晶纤维素，搅拌25-30分钟制成混合料，然后在50-60℃烘干1-1.5小时待用；
（4）将混合料加入浆料中，加入除助剂以外的其余剩余成分，搅拌均匀，加入步骤（1）中滤液以及适量的水调浆至固含量为2.4-3.5%，加热至65-72℃，将调好的浆料经网部及压榨部脱水成形，湿纸页进入前干阶段，在表面均匀涂刷助剂；
（5）在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水，然后电热鼓风干燥5-6min，最后在光机上进行压光，取出后即得水松纸原纸。
CN201410237075.1A 2014-05-30 2014-05-30 一种新型透气防火水松纸原纸及其制备方法 Pending CN104005292A (zh)