CN104003673A - 一种地下设施用刚柔复合型防水堵漏乳液 - Google Patents

一种地下设施用刚柔复合型防水堵漏乳液 Download PDF

Info

Publication number
CN104003673A
CN104003673A CN201410210945.6A CN201410210945A CN104003673A CN 104003673 A CN104003673 A CN 104003673A CN 201410210945 A CN201410210945 A CN 201410210945A CN 104003673 A CN104003673 A CN 104003673A
Authority
CN
China
Prior art keywords
emulsion
leakage
minutes
blend
mix
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410210945.6A
Other languages
English (en)
Other versions
CN104003673B (zh
Inventor
李军伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Tian Yuan Great Achievement Thermal-Insulating Waterproof Engineering Co Ltd
Original Assignee
Qingdao Tian Yuan Great Achievement Thermal-Insulating Waterproof Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Tian Yuan Great Achievement Thermal-Insulating Waterproof Engineering Co Ltd filed Critical Qingdao Tian Yuan Great Achievement Thermal-Insulating Waterproof Engineering Co Ltd
Priority to CN201410210945.6A priority Critical patent/CN104003673B/zh
Publication of CN104003673A publication Critical patent/CN104003673A/zh
Application granted granted Critical
Publication of CN104003673B publication Critical patent/CN104003673B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于防水堵漏施工技术领域，涉及一种地下设施用刚柔复合型防水堵漏乳液，包括重量比为1:1的复合粘接防水乳液与干粉复合砂料两种组分，所述复合粘接防水乳液组分：聚乙烯树脂液体40-60％，醋酸乙烯-乙烯共聚乳液20-40％，甲基纤维素液体2-4％，水溶性有机硅3-5％，聚乙烯醇胶粉液体11-14％，消泡剂0.01-0.03％；所述干粉复合砂料组分：硅酸盐水泥30-40％，石英砂35-40％，可分散胶粉4-6％，聚乙烯醇干胶粉3-5％，丙基纤维素0.5-2％，渗透结晶活性母料5-7％，粉煤灰4-6％，干石灰4-7％；其配方新颖科学，成分配比合理，制备工艺成熟，产品粘结度好，刚硬度强，防水性好，使用环境友好。

Description

一种地下设施用刚柔复合型防水堵漏乳液
技术领域：
本发明属于防水堵漏施工技术领域，涉及一种密实度高、强度大的刚柔复合型防水堵漏乳液，用于隧道、地下室、污水道、矿井和大坝等各类地下工程的修葺堵漏，以实现良好的防水密封堵漏。
背景技术：
防水堵漏简单来说就是对建筑物的户内外防水处理施工和户内外渗漏区域的补漏施工，具体来说是对房屋隧道堤坝漏水、管道容器内介质泄漏、井下井管破损泄漏等使用专业堵漏工具和材料进行修补填堵，以制止泄漏的行为，防水堵漏主要应用于隧道、地铁、地下车库、地下工程类、沟渠、池塘、变形缝、龟裂缝和震动不密实勾缝的防水处理、涂刷防水层、嵌缝、缝隙高压灌注等，存在的多种工艺包括高压灌浆工艺、高压灌脂工艺、嵌缝工艺、环氧施胶工艺和粉剂填堵工艺等等，其用到的堵漏材料大致有树脂类、粉末类和胶膏类三大类，目前市场上常见到的各类堵漏剂在使用时大都不区分地下工程与地上建筑，均是直接将堵漏剂广泛用于房屋、屋顶、隧道、地铁、沟渠、池塘、水下和流沙等的堵漏施工中，例如像中国专利2013107397722公开的一种用于封堵恶性漏失的静胶凝堵漏液，2013107484699公开的一种膨胀固结型堵漏剂，2013107277580公开的一种封堵浅层套管漏失的堵漏剂等，也有某些专门用于特殊场合施工的堵漏剂，例如中国专利2013107318025公开的一种煤层气井用复合堵漏剂，2012102257514公开的一种石油钻井用堵漏剂等。但是我们知道下水道、沟渠、隧道、地下室等各类地下工程与房屋、墙面、屋顶等地上工程有较大的区别，在发生渗水、漏水时进行填补堵漏的施工工艺和堵漏剂也应当有所区别，而现有技术中未见到有专门用于地下混凝土工程或地上工程的堵漏剂，因此寻求设计一种专门用于修复、填堵地下工程渗、漏水的复合堵漏防水乳液，具有良好的刚性、硬度和密实度，以实现良好的地下防水堵漏。
发明内容：
本发明的目的在于克服现有技术存在的缺点，设计一种专门用于地下工程的刚柔复合型防水堵漏乳液，其具有良好的刚硬性和柔和性，密封堵漏效果较佳。
为了实现上述目的，本发明涉及的防水堵漏乳液包括重量比为1:1的复合粘接防水乳液与干粉复合砂料两种组分，所述复合粘接防水乳液中各成分的重量百分比为：
所述干粉复合砂料中各成分的重量百分比为：
本发明涉及的复合粘接防水乳液配比过程为：将反应釜控温加热60-70℃后加入聚乙烯树脂液体和聚乙烯醇(PVA)胶粉液体，再升温至90-100℃待聚乙烯树脂和聚乙烯醇均彻底融化后，分别加入型号为EP707K的醋酸乙烯-乙烯共聚(VAE)乳液、甲基纤维素液体和水溶性有机硅，搅拌均匀后再加入消泡剂以起到消泡和稳定作用，最后密封包装备用；其使用环境温度应高于0℃以上。
本发明涉及的干粉复合砂料配比过程为：先取型号4.25的硅酸盐水泥进行搅拌2分钟，再加入80-100目石英砂混合搅拌3分钟；然后加入可分散胶粉混合搅拌5分钟；再加入聚乙烯醇(PVA)干胶粉后混合搅拌10分钟；再加入丙基纤维素[黏度(22℃，2％)5～200000mPa.s]混合搅拌10分钟；再加入渗透结晶活性母料混合搅拌10分钟；再加入粉煤灰混合搅拌10分钟；最后加入干石灰混合搅拌10分钟，制成干粉复合砂料密封包装备用。
本发明使用时将复合粘接防水乳液与干粉复合砂料按1:1的重量比在搅拌均匀状态下装入喷涂设备中用于地下场合的堵漏，应现场配比和密封使用，使用环境温度高于0℃，最好在5℃以上。
本发明与现有技术和产品相比，配方新颖科学，成分配比合理，制备工艺成熟，产品粘结度好，刚硬度强，防水性好，使用环境友好。
具体实施方式：
下面通过实施例对本发明作进一步详细描述。
实施例1：
本实施例涉及的防水堵漏乳液包括重量比为1:1的复合粘接防水乳液与干粉复合砂料两种组分，
(1)所述复合粘接防水乳液中各成分的重量百分比为：
(2)所述干粉复合砂浆中各成分的重量百分比为：
本实施例涉及的防水堵漏乳液的制备方法具体包括以下几个工艺步骤：
(1)配比复合粘接防水乳液：将反应釜控温加热60-70℃后加入聚乙烯树脂液体和聚乙烯醇(PVA)胶粉液体，再升温至90-100℃待聚乙烯树脂和聚乙烯醇均彻底融化后，分别加入型号为EP707K的醋酸乙烯-乙烯共聚(VAE)乳液、甲基纤维素液体和水溶性有机硅，搅拌均匀后再加入消泡剂以起到消泡和稳定作用，最后密封包装备用；上述配比及步骤细节需严格控制，其使用环境温度应高于0℃以上；
(2)配比干粉复合砂料：先取型号4.25的硅酸盐水泥进行搅拌2分钟，再加入80-100目石英砂混合搅拌3分钟；然后加入可分散胶粉混合搅拌5分钟；再加入聚乙烯醇(PVA)干胶粉后混合搅拌10分钟；再加入丙基纤维素[黏度(22℃，2％)5～200000mPa.s]混合搅拌10分钟；再加入渗透结晶活性母料混合搅拌10分钟；再加入粉煤灰混合搅拌10分钟；最后加入干石灰混合搅拌10分钟后密封包装备用；
(3)使用时在施工现场，将待堵缝口清理干净后进行配料，将步骤(1)中复合粘接防水乳液和步骤(2)中干粉复合砂料按重量比1:1混合，搅拌均匀后即可使用。
本实施例中制备的刚柔复合型防水堵漏乳液各项指标均达到发明目的要求，特别适宜下水道、地下室、防空洞、矿井、隧道等各类地下建筑工程的防水堵漏，具有良好的防水、密封和支撑效果。
实施例2：
本实施例涉及的防水堵漏乳液包括重量比为1:1的复合粘接防水乳液与干粉复合砂料两种组分，
(1)所述复合粘接防水乳液中各成分的重量百分比为：
(2)所述干粉复合砂料中各成分的重量百分比为：
本实施例的制备方法同实施例1，且各项指标均达到发明目的要求。

Claims (4)

1.一种地下设施用刚柔复合型防水堵漏乳液，其特征在于包括重量比为1:1的复合粘接防水乳液与干粉复合砂料两种组分，
所述复合粘接防水乳液中各成分的重量百分比为：
所述干粉复合砂料中各成分的重量百分比为：
2.根据权利要求1所述的地下设施用刚柔复合型防水堵漏乳液，其特征在于复合粘接防水乳液配比过程为：将反应釜控温加热60-70℃后加入聚乙烯树脂液体和聚乙烯醇胶粉液体，再升温至90-100℃待聚乙烯树脂和聚乙烯醇均彻底融化后，分别加入型号为EP707K的醋酸乙烯-乙烯共聚乳液、甲基纤维素液体和水溶性有机硅，搅拌均匀后再加入消泡剂以起到消泡和稳定作用，最后密封包装备用；其使用环境温度应高于0℃以上。
3.根据权利要求1所述的地下设施用刚柔复合型防水堵漏乳液，其特征在于干粉复合砂料配比过程为：先取型号4.25的硅酸盐水泥进行搅拌2分钟，再加入80-100目石英砂混合搅拌3分钟；然后加入可分散胶粉混合搅拌5分钟；再加入聚乙烯醇干胶粉后混合搅拌10分钟；再加入丙基纤维素[黏度(22℃，2％)5～200000mPa.s]混合搅拌10分钟；再加入渗透结晶活性母料混合搅拌10分钟；再加入粉煤灰混合搅拌10分钟；最后加入干石灰混合搅拌10分钟，制成干粉复合砂料密封包装备用。
4.根据权利要求1所述的地下设施用刚柔复合型防水堵漏乳液，其特征在于使用时将复合粘接防水乳液与干粉复合砂料按1:1的重量比进行搅拌混合，使用环境温度高于0℃。
CN201410210945.6A 2014-05-19 2014-05-19 一种地下设施用刚柔复合型防水堵漏乳液 Active CN104003673B (zh)