CN106336187A - 混凝土房屋楼板防渗漏填缝剂 - Google Patents

混凝土房屋楼板防渗漏填缝剂 Download PDF

Info

Publication number
CN106336187A
CN106336187A CN201610742376.9A CN201610742376A CN106336187A CN 106336187 A CN106336187 A CN 106336187A CN 201610742376 A CN201610742376 A CN 201610742376A CN 106336187 A CN106336187 A CN 106336187A
Authority
CN
China
Prior art keywords
parts
gap filler
joint mixture
building floor
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610742376.9A
Other languages
English (en)
Inventor
杨晓文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610742376.9A priority Critical patent/CN106336187A/zh
Publication of CN106336187A publication Critical patent/CN106336187A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混凝土房屋楼板防渗漏填缝剂，包括以重量份数计的500标号水泥80～90份和熟石膏10～20份。本发明所述的混凝土房屋楼板防渗漏填缝剂采用500标号水泥和熟石膏制成，可以修补楼房因地基下沉、高温爆裂、水坭砂浆收缩发生细小裂缝，解决渗漏的问题，本发明采用成本低廉的原材料，使用时工程量小，耐用，防水效果好。

Description

混凝土房屋楼板防渗漏填缝剂
技术领域
本发明涉及混凝土建筑的防渗漏领域，尤其涉及一种混凝土房屋楼板防渗漏填缝剂。
背景技术
楼房楼板经一段时间使用后因地基或气候变化会产生细小裂缝造成渗漏，影响使用居住。混凝土楼板裂缝分布一般在次梁所围成的方框内，有些沿板筋分布，有些裂纹则呈不均匀分布。目前常用的砼墙、板裂缝的处理方法有以下五类：采用环氧树脂类或氰凝聚氨脂类等在楼板表面涂抹法；二是表面涂刷加玻璃丝布法；三是切割成“v”字型或梯型槽，清洗干净后分层抹压环氧砂浆、水泥砂浆、沥青油膏、高分子密封材料或各种成品堵漏剂等材料以密封裂缝填充法；四是灌浆法；五是重浇楼板砼技术。以上防渗漏修补技术只能解决短期内的问题，成本高，不耐用，工程量大。
发明内容
本发明设计开发了一种成本低、工程量小、耐用的混凝土房屋楼板防渗漏填缝剂。
本发明提供的技术方案为：
一种混凝土房屋楼板防渗漏填缝剂，包括以重量份数计的500标号水泥80～90份和熟石膏10～20份。
优选的是，所述的混凝土房屋楼板防渗漏填缝剂中，所述熟石膏的粒径为200～300μm。
优选的是，所述的混凝土房屋楼板防渗漏填缝剂中，还包括以重量份数计的氧化钙0.3～0.8份。
优选的是，所述的混凝土房屋楼板防渗漏填缝剂，还包括以重量份数计的粉煤灰0.5～1份。
优选的是，所述的混凝土房屋楼板防渗漏填缝剂中，由以重量份数计的以下组分组成：500标号水泥80份、熟石膏10份、氧化钙0.8份和粉煤灰1份。
本发明所述的混凝土房屋楼板防渗漏填缝剂采用500标号水泥和熟石膏制成，可以修补楼房因地基下沉、高温爆裂、水坭砂浆收缩发生细小裂缝，解决渗漏的问题，本发明采用成本低廉的原材料，使用时工程量小，耐用，防水效果好。
具体实施方式
下面对本发明做进一步的详细说明，以令本领域技术人员参照说明书文字能够据以实施。
本发明提供一种混凝土房屋楼板防渗漏填缝剂，包括以重量份数计的500标号水泥80～90份和熟石膏10～20份。本发明采用成本低廉的原材料，使用时工程量小，耐用，防水效果好。
制备时，将熟石膏粉碎成粉末状，将熟石膏和水泥混合均匀，之后置于阴凉干燥库房中保存待用。
使用时，将楼板裂缝切割成V字型或梯形槽，清洗干净。将填缝剂加入适量水搅拌成糊状直接涂抹于裂缝沟内，直至填满后抹平即可。
优选地，所述的混凝土房屋楼板防渗漏填缝剂中，所述熟石膏的粒径为200～300μm。当熟石膏的粒径在上述设定范围内时，熟石膏可以更好地与水泥混合，进而获得更好的防渗水效果。
优选地，所述的混凝土房屋楼板防渗漏填缝剂中，还包括以重量份数计的氧化钙0.3～0.8份。氧化钙可以增强填缝剂的耐候性，延长其使用寿命。
优选地，所述的混凝土房屋楼板防渗漏填缝剂，还包括以重量份数计的粉煤灰0.5～1份。粉煤灰颗粒为多孔结构，在加水搅拌填缝剂时，粉煤灰颗粒可以吸收水分。因此，当将填缝剂涂抹于裂缝沟内时，在粉煤灰的作用下，填缝剂的干燥速度会下降，可以避免填缝剂内部因过快干燥而产生微小的裂纹，从而使填缝剂内部结构更稳定，具有更好的耐候性，防水效果更好。
优选地，所述的混凝土房屋楼板防渗漏填缝剂中，由以重量份数计的以下组分组成：500标号水泥80份、熟石膏10份、氧化钙0.8份和粉煤灰1份。制备时，各组分混合均匀即可。使用时，将楼板裂缝切割成V字型或梯形槽，清洗干净。将填缝剂加入适量水搅拌成糊状直接涂抹于裂缝沟内，直至填满后抹平即可。
以下提供实施例，以进一步本发明的技术方案。
实施例一
填缝剂由以重量份数计的以下组分组成：500标号水泥80份和熟石膏10份。
填缝剂在30min后的吸水量为2g，而在240min后的吸水量为5g。涂抹于底材上后，暴露于户外1～2年的时间无开裂。
实施例二
填缝剂由以重量份数计的以下组分组成：500标号水泥90份和熟石膏20份。熟石膏的粒径为200～300μm。
填缝剂在30min后的吸水量为2g，而在240min后的吸水量为5g。涂抹于底材上后，暴露于户外1～2年的时间无开裂。
实施例三
填缝剂由以重量份数计的以下组分组成：500标号水泥80份、熟石膏10份、氧化钙0.8份和粉煤灰1份。熟石膏的粒径为200～300μm。
填缝剂在30min后的吸水量为1g，而在240min后的吸水量为4g。涂抹于底材上后，暴露于户外1～2年的时间无开裂。
实施例四
填缝剂由以重量份数计的以下组分组成：500标号水泥90份、熟石膏20份、氧化钙0.3份和粉煤灰0.5份。熟石膏的粒径为200～300μm。
填缝剂在30min后的吸水量为1.5g，而在240min后的吸水量为4.5g。涂抹于底材上后，暴露于户外1～2年的时间无开裂。
尽管本发明的实施方案已公开如上，但其并不仅仅限于说明书和实施方式中所列运用，它完全可以被适用于各种适合本发明的领域，对于熟悉本领域的人员而言，可容易地实现另外的修改，因此在不背离权利要求及等同范围所限定的一般概念下，本发明并不限于特定的细节。

Claims (5)

1.一种混凝土房屋楼板防渗漏填缝剂，其特征在于，包括以重量份数计的500标号水泥80～90份和熟石膏10～20份。
2.如权利要求1所述的混凝土房屋楼板防渗漏填缝剂，其特征在于，所述熟石膏的粒径为200～300μm。
3.如权利要求2所述的混凝土房屋楼板防渗漏填缝剂，其特征在于，还包括以重量份数计的氧化钙0.3～0.8份。
4.如权利要求3所述的混凝土房屋楼板防渗漏填缝剂，其特征在于，还包括以重量份数计的粉煤灰0.5～1份。
5.如权利要求4所述的混凝土房屋楼板防渗漏填缝剂，其特征在于，由以重量份数计的以下组分组成：500标号水泥80份、熟石膏10份、氧化钙0.8份和粉煤灰1份。
CN201610742376.9A 2016-08-26 2016-08-26 混凝土房屋楼板防渗漏填缝剂 Pending CN106336187A (zh)