CN103983569A - 一种镀层板镀层剥落检测方法 - Google Patents

一种镀层板镀层剥落检测方法 Download PDF

Info

Publication number
CN103983569A
CN103983569A CN201410204206.6A CN201410204206A CN103983569A CN 103983569 A CN103983569 A CN 103983569A CN 201410204206 A CN201410204206 A CN 201410204206A CN 103983569 A CN103983569 A CN 103983569A
Authority
CN
China
Prior art keywords
coating
sample
force
blank holder
plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410204206.6A
Other languages
English (en)
Inventor
李晓刚
滕华湘
刘李斌
章军
朱国森
李本海
刘立现
赵宁
郑天然
陈庆
徐晓宁
郑学斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shougang Corp
Original Assignee
Shougang Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shougang Corp filed Critical Shougang Corp
Priority to CN201410204206.6A priority Critical patent/CN103983569A/zh
Publication of CN103983569A publication Critical patent/CN103983569A/zh
Pending legal-status Critical Current

Abstract

一种镀层板镀层剥落检测方法，属于镀层板镀层检测技术领域。包括，工艺步骤为，将镀层板剪切成圆片试样，对模具与试验装置进行检查清洗，进行预试验确定合理的压边力，将圆片试样压置到凹模与压边圈之间，施加压边力后，启动凸模对其进行拉深成形，通过试样的拉延变形以及试样与模具摩擦力的作用，镀层在剪切力作用下发生剥落，然后评价所述镀层板的镀层剥落程度。优点在于，能快速准确地检测汽车板、家电板、建筑用板等镀层板镀层剥落程度，适合工业广泛应用。

Description

一种镀层板镀层剥落检测方法
技术领域
本发明属于镀层板镀层检测技术领域，特别提供了一种一种镀层板镀层剥落检测方法，适用于热镀纯锌镀层板、合金化热镀锌板等镀层板镀层剥落检测，能快速检测汽车板、家电板、建筑用板等各种镀层板在变形中是否会出现镀层剥落等缺陷。
背景技术
镀层剥落是指镀层板在冲压成形过程中，在冲压模具和工件间产生的摩擦力作用下，镀层成片状或粉状脱落现象。镀层剥落不仅影响成形后零件的外观质量，而且因剥落的锌粉粘附于模具，并在模具中积聚，会加剧工件与模具间的摩擦，影响模具的使用寿命，增加用户对模具的清理工作量。对于热镀纯锌镀层板(GI)，由于镀层比较软，镀层剥落时成片状。对于合金化热镀锌板(GA)，镀层比较硬脆，剥落后成粉化状，国内外学者对其成因、影响因素及预防措施已作了大量的研究。其他类型镀层板镀层剥落形式类似。目前检查镀层板镀层剥落的检测方法主要有折弯法、双杯突法等，但该类方法不能准确模拟镀层板在使用时，材料流动情况以及镀层如何剥落，没有把材料使用中最易出现镀层剥落的状态模拟出来。鉴于此，需寻求一种新的镀层板镀层剥落粉化检测方法来解决上述问题。
镀层剥落现象的本质是镀层在剪切应力作用下遭到破坏的结果，而在材料使用中发生剪切应力有两种情况：一是材料变形处于压应力状态下，而材料只有在拉延应力状态下板面内才能发生压应力；二是镀层在冲压成形过程中板材与模具间摩擦力作用下发生剪切应力。以上两种剪切力同时出现时，镀层剥落情况最严重。因此，只有同时两种剪切力都存在的实验方法才是最高效最准确的检测方法。
发明内容
本发明的目的在于提供一种镀层板镀层剥落检测方法，快速检测汽车板、家电板、建筑用板等镀层板镀层剥落粉化，提高检测效率和精准度。
本发明的工艺步骤为，将镀层板剪切成圆片试样，对模具与试验装置进行检查清洗，进行预试验确定合理的压边力，将圆片试样压置到凹模与压边圈之间，施加压边力后，启动凸模对其进行拉深成形，通过试样的拉延变形以及试样与模具摩擦力的作用，镀层在剪切力作用下发生剥落，然后评价所述镀层板的镀层剥落程度。
本发明所述镀层板试样为圆形片状。
所述压边力应保证试样能够在凸模的拉深力作用下发生流动和拉深变形，允许压边圈下面的试样材料起皱。
本发明利用镀层板在使用中产生镀层剥落的主要变形因素：压应变和摩擦阻力，能快速准确地检测汽车板、家电板、建筑用板等镀层板镀层剥落程度，适合工业广泛应用。
附图说明
图1为本发明实施提供的一种拉深试验原理图。其中，压边圈1、凸模2、凹模3、试样4
具体实施方式
下面结合具体实施方式对本发明进行进一步的详细描述，给出的实施例仅为了阐明本发明，而不是为了限制本发明的范围。
将被测量的镀层板加工成直径为100mm圆形片状试样，厚度以薄板的厚度为准，用无水丙酮把试样表面清洗干净并干燥。试验前将模具的工作面检查清理，模具和试样均用拉延油作适度润滑，以满足试验的要求。进行预试验确定压边力10KN，把试样用压边圈与凹模夹紧放置好以后，控制凸模对试样施加设定载荷，将试样以1mm/s的速度进行拉深试验，当拉深深度为25mm时停止试验，卸去压边力和凸模压力并取出试样。然后检查试样表面镀层剥落情况，接着进行镀层剥落程度评价。

Claims (1)

1.一种镀层板镀层剥落的检测方法，其特征在于，工艺步骤为，将镀层板剪切成圆片试样，对模具与试验装置进行检查清洗，进行预试验确定合理的压边力，将圆片试样压置到凹模与压边圈之间，施加压边力后，启动凸模对其进行拉深成形，通过试样的拉延变形以及试样与模具摩擦力的作用，镀层在剪切力作用下发生剥落，然后评价所述镀层板的镀层剥落程度；
所述压边力应保证试样能够在凸模的拉深力作用下发生流动和拉深变形，允许压边圈下面的试样材料起皱。
CN201410204206.6A 2014-05-14 2014-05-14 一种镀层板镀层剥落检测方法 Pending CN103983569A (zh)