CN103980562A - Rubber glove with antimicrobial and skin care functions - Google Patents
Rubber glove with antimicrobial and skin care functions Download PDFInfo
- Publication number
- CN103980562A CN103980562A CN201410238189.8A CN201410238189A CN103980562A CN 103980562 A CN103980562 A CN 103980562A CN 201410238189 A CN201410238189 A CN 201410238189A CN 103980562 A CN103980562 A CN 103980562A
- Authority
- CN
- China
- Prior art keywords
- skin care
- antibacterial
- rubber
- antimicrobial
- extract
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rubber glove with antimicrobial and skin care functions, which comprises a rubber latex and an antimicrobial and skin care active component. The rubber glove is characterized in that the rubber latex is composed of the following components in parts by weight: 70-80 parts of natural rubber, 20-30 parts of nitrile-butadiene rubber, 5-8 parts of emulsified liquid paraffin, 0.6-1.2 parts of colloid sulfur, 0.4-1.0 part of zinc oxide, 0.2-0.4 part of accelerator ZDBC, 0.3-0.5 part of accelerator ZMBT and 0.7-1.5 parts of antimicrobial and skin care active component. The antimicrobial and skin care active component is composed of a cinnamon extract and a herba houttuyniae extract in a weight ratio of (1-3):(2-4). The antimicrobial and skin care active component is added into the matrix of the operating glove, so that the antimicrobial and skin care active component can resist microbes and enhance the safety performance of the operating glove when in use.
Description
Technical field
The present invention relates to surgical glove, be specifically related to a kind of antibacterial and rubber gloves skin-care effect that has.
Background technology
Gloves, owing to having barrier protection effect, can be good at protecting user's safety, have been widely used in people's productive life.According to the difference of its purposes, can be divided into medical gloves, industrial gloves and domestic purpose gloves; According to the difference of manufacturing material used, can be divided into natural rubber gloves, butyronitrile gloves, PVC gloves etc.
At present, natural emulsion gloves, butyronitrile rubber breast gloves are divided into conventionally has powder type and without powder type.There is powder type gloves lubricating for glove surface, conventionally adopt talcum powder or treated starch to make separant, but talcum powder easily causes that user is allergic, even cause the untoward reaction of human body skin, in treated starch, because containing more protein composition, after being absorbed by human body skin, can cause equally skin adverse reaction.On the other hand, dress for a long time after natural emulsion gloves or butyronitrile rubber breast gloves, hand volume of perspiration can obviously increase, and this is not only conducive to some bacterium, virus, fungi hyperplasia at watch face, infringement user's health, and can produce peculiar smell.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of antibacterial and rubber gloves skin-care effect that has, in the matrix of surgical glove, add antibacterial and skin care activity composition, even if long-time wearing is also not easy to cause wearer's hand surface skin allergy and bacterial proliferation, nor can produce peculiar smell.
Above-mentioned a kind of antibacterial and rubber gloves skin-care effect that has, comprises elastomer latex and antibacterial and skin care activity composition, it is characterized in that: described rubber latex consists of the following composition, by weight:
Described antibacterial and skin care activity composition is made up of Cortex Cinnamomi extract and Herba Houttuyniae extract, and its weight ratio is 1-3:2-4.
Above-mentioned a kind of antibacterial and rubber gloves skin-care effect that has, comprises elastomer latex and antibacterial and skin care activity composition, it is characterized in that: described rubber latex consists of the following composition, preferred, by weight:
Described antibacterial and skin care activity composition is made up of Cortex Cinnamomi extract and Herba Houttuyniae extract, and preferred, its weight ratio is 2:3.
Described colloid sulphur is made up of SULPHUR POWDER, barium stearate, polyethylene wax and water, by weight, SULPHUR POWDER: barium stearate: polyethylene wax: water is 3:2:2:4, when preparation, first by SULPHUR POWDER, barium stearate, polyethylene wax and water with 120R/min speed, stir 10 minutes, stir.SULPHUR POWDER particle is 180 orders preferably.
Described promotor ZDBC is thiofide ZDBC, and chemical name is zinc dibutyl dithiocarbamate, and molecular formula is C
28h
30n
2s
4zn, molecular weight is 474.1, purity is 98.0%; Described promotor ZMBT is thiofide ZMBT, and chemical name is that MBT zinc salt molecular formula is C
14h
8n
2s
4zn, molecular weight is 398.
The preparation method of above-mentioned Cortex Cinnamomi extract is: Chinese cassia tree added to the pure water of 8-10 times of weight part, at 80-100 DEG C, extracts 1-2h, filter, get filtrate concentrating, and dry, to obtain final product.
The preparation method of above-mentioned Herba Houttuyniae extract is: Herba Houttuyniae added to the pure water of 8-10 times of weight part, at 80-100 DEG C, extracts 1-2h, filter, get filtrate concentrating, and dry, to obtain final product.
A preparation method with the rubber gloves of antibacterial and skin-care effect, its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, paracril, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, antibacterial and skin care activity composition, fully mixes, and regulating solid content is 25%;
B, mould first flood peptizer after drying, peptizer be weight percentage nitrocalcite or the calcium chloride solution of 8-15%;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 DEG C, takes out, through the high temperature drying of 120-140 DEG C, 20-40 minute;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Compared to the prior art, tool of the present invention has the following advantages:
1, elastomer latex of the present invention has adopted the mixing of natural rubber and paracril, has both had the tensile property that natural rubber is good, has avoided again the bad drawback of paracril tensile property, has also avoided a large amount of allergic problems that bring that use of natural rubber.
2, the present invention is taking pure natural Chinese cassia tree and Herba Houttuyniae extract as antibacterial and skin care activity composition, safe and effective, without any untoward reaction, can effectively avoid the appearance of allergic symptom, has strengthened the safety performance of this product, has expanded the scope of application of product.
Embodiment
With embodiment, the invention will be further described below, but the present invention is not limited to these embodiment.
Embodiment 1:
Have antibacterial and rubber gloves skin-care effect, wherein, described rubber latex consists of the following composition, by weight:
Described antibacterial and skin care activity composition is made up of Cortex Cinnamomi extract and Herba Houttuyniae extract, and its weight ratio is 1:2.
Its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, antibacterial and skin care activity composition, fully mixes, and adjusting solid content is 25-32%;
B, mould first flood peptizer after drying, peptizer be weight percentage 15% nitrocalcite or calcium chloride solution;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 DEG C, takes out, through the high temperature drying of 140 DEG C, 20 minutes;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Embodiment 2:
Have antibacterial and rubber gloves skin-care effect, wherein, described rubber latex consists of the following composition, by weight:
Described antibacterial and skin care activity composition is made up of Cortex Cinnamomi extract and Herba Houttuyniae extract, and its weight ratio is 3:4.
Its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, antibacterial and skin care activity composition, fully mixes, and regulating solid content is 32%;
B, mould first flood peptizer after drying, peptizer be weight percentage 8% nitrocalcite or calcium chloride solution;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 DEG C, takes out, through the high temperature drying of 120 DEG C, 40 minutes;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Embodiment 3:
Have antibacterial and rubber gloves skin-care effect, wherein, described rubber latex consists of the following composition, preferred, by weight:
Described antibacterial and skin care activity composition is made up of Cortex Cinnamomi extract and Herba Houttuyniae extract, and its weight ratio is 2:3.
Its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, antibacterial and skin care activity composition, fully mixes, and regulating solid content is 28%;
B, mould first flood peptizer after drying, peptizer be weight percentage 10% nitrocalcite or calcium chloride solution;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 DEG C, takes out, through the high temperature drying of 130 DEG C, 30 minutes;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Claims (4)
1. there is antibacterial and rubber gloves skin-care effect, comprise elastomer latex and antibacterial and skin care activity composition, it is characterized in that: described rubber latex consists of the following composition, by weight:
Described antibacterial and skin care activity composition is made up of Cortex Cinnamomi extract and Herba Houttuyniae extract, and its weight ratio is 1-3:2-4.
2. a kind of antibacterial and rubber gloves skin-care effect that has according to claim 1, is characterized in that: described rubber latex consists of the following composition, by weight:
Described antibacterial and skin care activity composition is made up of Cortex Cinnamomi extract and Herba Houttuyniae extract, and its weight ratio is 2:3.
3. a kind of antibacterial and rubber gloves skin-care effect that has according to claim 1 and 2, is characterized in that: the preparation method of described Cortex Cinnamomi extract is: Chinese cassia tree is added to the pure water of 8-10 times of weight part, at 80-100 DEG C, extract 1-2h, filter, get filtrate concentrated, dry, to obtain final product.
4. a kind of antibacterial and rubber gloves skin-care effect that has according to claim 1 and 2, it is characterized in that: the preparation method of described Herba Houttuyniae extract is: the pure water that Herba Houttuyniae is added to 8-10 times of weight part, at 80-100 DEG C, extract 1-2h, filter, get filtrate concentrated, dry, to obtain final product.