CN103980566A - Rubber glove with antimicrobial function - Google Patents
Rubber glove with antimicrobial function Download PDFInfo
- Publication number
- CN103980566A CN103980566A CN201410238367.7A CN201410238367A CN103980566A CN 103980566 A CN103980566 A CN 103980566A CN 201410238367 A CN201410238367 A CN 201410238367A CN 103980566 A CN103980566 A CN 103980566A
- Authority
- CN
- China
- Prior art keywords
- rubber
- antibacterial
- extract
- parts
- gloves
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rubber glove with antimicrobial function, which comprises a rubber latex and an antibacterial active component. The rubber glove is characterized in that the rubber latex is composed of the following components in parts by weight: 70-80 parts of natural rubber, 20-30 parts of nitrile-butadiene rubber, 5-8 parts of emulsified liquid paraffin, 0.6-1.2 parts of colloid sulfur, 0.4-1.0 part of zinc oxide, 0.2-0.4 part of accelerator ZDBC, 0.3-0.5 part of accelerator ZMBT and 0.7-1.5 parts of antimicrobial active component. The antibacterial active component is composed of a fructus momordicae extract and a centella extract in a weight ratio of (1-3):(2-4). The antimicrobial active component is added into the matrix of the operating glove, so that the antimicrobial active component can resist microbes and enhance the safety performance of the operating glove when in use.
Description
Technical field
The present invention relates to surgical glove, be specifically related to a kind of rubber gloves with antibacterial.
Background technology
Gloves, owing to having barrier protection effect, can be good at protecting user's safety, have been widely used in people's productive life.According to the difference of its purposes, can be divided into medical gloves, industrial gloves and domestic purpose gloves; Difference according to manufacturing material used, can be divided into natural rubber gloves, butyronitrile gloves, PVC gloves etc.
But in the disposable surgical gloves that use at Hospitals at Present, the overwhelming majority remains natural rubber gloves.Its major cause has two aspects: 1, the tensile property of acrylonitrile butadiene glove, elasticity are all poor than natural rubber latex; In the disposable use antiseptic rubber of standard GB/T 7543-2006 < < surgical glove > >, also stipulated the tensile property requirement of gloves, wherein to classification 1 gloves, the namely requirement of natural rubber gloves is: the minimum 12.5N of breaking tenacity, elongation 700%; To classification 2 gloves, the requirement that comprises acrylonitrile butadiene glove is the minimum 9.ON of breaking tenacity, elongation 600%; 2, the fatigue performance of acrylonitrile butadiene glove is weaker than natural rubber gloves, and lasting duration of service is longer, and acrylonitrile butadiene glove glued membrane easily chaps, destroys.These are all the weak points of current existing butyronitrile gloves.
But; the various gloves that use at present; substantially be only to there is provide protection; there is no the effect of skin care, and, the material of a part of gloves; as fourth eyeball, PVC; larger with human body skin environmental difference, this class material of Long Term Contact, can cause slight allergic, the phenomenon such as inflammation even.Meanwhile, when hand skin has wound or wound, be not suitable for directly wearing these gloves, these gloves do not have maintenance and promote the effect of wound healing, and they also can make wound not contact with air, hinder the healing rate of wound.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of rubber gloves with antibacterial, in the matrix of surgical glove, adds Antibacterial Constituents, there will not be in use allergic symptom, increases the safety performance of surgical glove.
Above-mentioned a kind of rubber gloves with antibacterial, comprises elastomer latex and Antibacterial Constituents, it is characterized in that: described rubber latex consists of the following composition, by weight:
Described Antibacterial Constituents is comprised of Fructus Monordicae extract and Herba Centellae extract, and its weight ratio is 1-3:2-4.
Above-mentioned a kind of rubber gloves with antibacterial, comprises elastomer latex and Antibacterial Constituents, it is characterized in that: described rubber latex consists of the following composition, preferred, by weight:
Described Antibacterial Constituents is comprised of Fructus Monordicae extract and Herba Centellae extract, and preferred, its weight ratio is 2:3.
Described colloid sulphur is comprised of SULPHUR POWDER, barium stearate, polyethylene wax and water, by weight, SULPHUR POWDER: barium stearate: polyethylene wax: water is 3:2:2:4, during preparation, first by SULPHUR POWDER, barium stearate, polyethylene wax and water with 120R/min speed, stir 10 minutes, stir.SULPHUR POWDER particle is 180 orders preferably.
Described promotor ZDBC is thiofide ZDBC, and chemical name is zinc dibutyl dithiocarbamate, and molecular formula is C
28h
30n
2s
4zn, molecular weight is 474.1, purity is 98.0%; Described promotor ZMBT is thiofide ZMBT, and chemical name is that MBT zinc salt molecular formula is C
14h
8n
2s
4zn, molecular weight is 398.
The preparation method of above-mentioned Fructus Monordicae extract is: Grosvenor Momordica added to the pure water of 8-10 times of weight part, at 80-100 ℃, extracts 1-2h, filter, get filtrate concentrating, and dry, obtain.
The preparation method of above-mentioned Herba Centellae extract is: Herba Centellae added to the pure water of 8-10 times of weight part, at 80-100 ℃, extracts 1-2h, filter, get filtrate concentrating, and dry, obtain.
A preparation method with the rubber gloves of antibacterial, its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, paracril, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, Antibacterial Constituents, fully mixes, and regulating solid content is 25%;
B, mould first flood peptizer after drying, peptizer be weight percentage nitrocalcite or the calcium chloride solution of 8-15%;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 ℃, takes out, through the high temperature drying of 120-140 ℃, 20-40 minute;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Compared to the prior art, tool of the present invention has the following advantages:
1, elastomer latex of the present invention has adopted the mixing of natural rubber and paracril, has both had the tensile property that natural rubber is good, has avoided again the bad drawback of paracril tensile property, has also avoided a large amount of allergic problems that bring that use of natural rubber.
2, the present invention be take pure natural Grosvenor Momordica and Herba Centellae extract and is Antibacterial Constituents, safe and effective, without any untoward reaction, can effectively avoid the appearance of allergic symptom, has strengthened the safety performance of this product, has expanded the scope of application of product.
Embodiment
With embodiment, the invention will be further described below, but the present invention is not limited to these embodiment.
Embodiment 1:
A rubber gloves with antibacterial, wherein, described rubber latex consists of the following composition, by weight:
Described Antibacterial Constituents is comprised of Fructus Monordicae extract and Herba Centellae extract, and its weight ratio is 1:2.
Its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, Antibacterial Constituents, fully mixes, and adjusting solid content is 25-32%;
B, mould first flood peptizer after drying, peptizer be weight percentage 15% nitrocalcite or calcium chloride solution;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 ℃, takes out, through the high temperature drying of 140 ℃, 20 minutes;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Embodiment 2:
A rubber gloves with antibacterial, wherein, described rubber latex consists of the following composition, by weight:
Described Antibacterial Constituents is comprised of Fructus Monordicae extract and Herba Centellae extract, and its weight ratio is 3:4.
Its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, Antibacterial Constituents, fully mixes, and regulating solid content is 32%;
B, mould first flood peptizer after drying, peptizer be weight percentage 8% nitrocalcite or calcium chloride solution;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 ℃, takes out, through the high temperature drying of 120 ℃, 40 minutes;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Embodiment 3:
A rubber gloves with antibacterial, wherein, described rubber latex consists of the following composition, preferred, by weight:
Described Antibacterial Constituents is comprised of Fructus Monordicae extract and Herba Centellae extract, and its weight ratio is 2:3.
Its preparation method is as follows:
The rubber latex of A, preparation dipping use, by natural rubber, emulsifying aq paraffin, colloid sulphur, zinc oxide, promotor ZDBC, promotor ZMBT, Antibacterial Constituents, fully mixes, and regulating solid content is 28%;
B, mould first flood peptizer after drying, peptizer be weight percentage 10% nitrocalcite or calcium chloride solution;
C, dry mould, the then above-mentioned rubber latex preparing of mould dipping, crimping subsequently, then immerses the warm water 2 minutes of 45 ℃, takes out, through the high temperature drying of 130 ℃, 30 minutes;
D, cooling, handle sleeve is taken off from mould, obtains finished product.
Prepared a kind of anti-microbial property (inhibiting rate) data with the rubber gloves of antibacterial of embodiment are as following table:
Claims (4)
1. a rubber gloves with antibacterial, comprises elastomer latex and Antibacterial Constituents, it is characterized in that: described rubber latex consists of the following composition, by weight:
Described Antibacterial Constituents is comprised of Fructus Monordicae extract and Herba Centellae extract, and its weight ratio is 1-3:2-4.
2. a kind of rubber gloves with antibacterial according to claim 1, is characterized in that: described rubber latex consists of the following composition, by weight:
Described Antibacterial Constituents is comprised of Fructus Monordicae extract and Herba Centellae extract, and its weight ratio is 2:3.
3. a kind of rubber gloves with antibacterial according to claim 1 and 2, is characterized in that: the preparation method of described Fructus Monordicae extract is: Grosvenor Momordica is added to the pure water of 8-10 times of weight part, at 80-100 ℃, extract 1-2h, filter, get filtrate concentrated, dry, obtain.
4. a kind of rubber gloves with antibacterial according to claim 1 and 2, is characterized in that: the preparation method of described Herba Centellae extract is: Herba Centellae is added to the pure water of 8-10 times of weight part, at 80-100 ℃, extract 1-2h, filter, get filtrate concentrated, dry, obtain.