CN103979860A - Waterproof lightweight partition plate and manufacturing method thereof - Google Patents
Waterproof lightweight partition plate and manufacturing method thereof Download PDFInfo
- Publication number
- CN103979860A CN103979860A CN201410135232.8A CN201410135232A CN103979860A CN 103979860 A CN103979860 A CN 103979860A CN 201410135232 A CN201410135232 A CN 201410135232A CN 103979860 A CN103979860 A CN 103979860A
- Authority
- CN
- China
- Prior art keywords
- parts
- partition plate
- powder
- oil
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a waterproof lightweight partition plate. The partition plate is characterized by being prepared from the following raw materials by weight: 20 to 25 parts of cement, 17 to 19 parts of metakaolin, 11 to 15 parts of steel wire type steel fiber, 6 to 8 parts of a naphthalene water reducer, 3 to 7 parts of a UEA-H type expanding agent, 7 to 9 parts of paraffin oil, 9 to 11 parts of nanometer zinc oxide, 13 to 17 parts of vermiculite, 15 to 18 parts of meerschaum, 16 to 19 parts of oil shale residue, 12 to 16 parts of shaddock peel, 3 to 6 parts of an auxiliary agent and a proper amount of water. According to the invention, since nanometer zinc oxide is added, the partition plate has ultraviolet resistance and sterilization and enzyme inhibition effects; as a small amount of shaddock peel particles having undergone high temperature carbonization are added, the partition plate can absorb harmful gas like formaldehyde in the air, and thus, the partition plate has a long-acting indoor air purifying effect and a waterproof effect.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of waterproof light partition plate and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, a kind of novel energy-conserving walling material forming through the maintenance of frequency conversion steam pressurized, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, when installation, only sheet material need be erected, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but the shortcomings such as the light cellular partition board ultimate compression strength using is in the market low, tensile strength weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of waterproof light partition plate and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of waterproof light partition plate, it is characterized in that, made by the raw material of following weight part: cement 20-25, metakaolin 17-19, type of wire form steel fiber 11-15, naphthalene water reducer 6-8, UEA-H type swelling agent 3-7, paraffin oil 7-9, Nano-class zinc oxide 9-11, vermiculite 13-17, sepiolite 15-18, oil shale waste 16-19, pomelo peel 12-16, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain in 3:2 ratio, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
The preparation method of described a kind of waterproof light partition plate, is characterized in that comprising the following steps:
(1) pomelo peel, metakaolin are sent in charring furnace, calcination processing 3-4 hour at 510-615 DEG C, takes out, and is ground into powder, makes it seethe spray form paraffin oil under condition to the powder of gained in air blast, makes it to mix;
(2) vermiculite, sepiolite, oil shale waste are calcined at 610-860 DEG C after 3-6 hour and taken out, pulverize, extremely even with spraying gun sprinkling 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions, dipping 10-12 hour;
(3) step (1), (2) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the present invention adds Nano-class zinc oxide, can uvioresistant and sterilization, enzyme inhibitor, and admixture a small amount of pomelo peel particle after high temperature carbonization, in can absorbed air, the obnoxious flavour such as formaldehyde, makes the present invention have the long-acting effect purifying the air of a room and waterproof effect.
Embodiment
Described a kind of waterproof light partition plate, it is characterized in that, made by the raw material of following weight part: cement 20-25, metakaolin 17-19, type of wire form steel fiber 11-15, naphthalene water reducer 6-8, UEA-H type swelling agent 3-7, paraffin oil 7-9, Nano-class zinc oxide 9-11, vermiculite 13-17, sepiolite 15-18, oil shale waste 16-19, pomelo peel 12-16, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain in 3:2 ratio, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Making method comprises the following steps:
(1) pomelo peel, metakaolin are sent in charring furnace, calcination processing 3-4 hour at 510-615 DEG C, takes out, and is ground into powder, makes it seethe spray form paraffin oil under condition to the powder of gained in air blast, makes it to mix;
(2) vermiculite, sepiolite, oil shale waste are calcined at 610-860 DEG C after 3-6 hour and taken out, pulverize, extremely even with spraying gun sprinkling 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions, dipping 10-12 hour;
(3) step (1), (2) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The technical indicator of processing the light cellular partition board obtaining by above-described embodiment is as follows:
(1) thermal conductivity (25 ± 2 DEG C of medial temperatures): 0.075W/ (mk);
(2) ultimate compression strength: 4.7MPa;
(3) high temperature resistant, flat appearance is smooth.
Claims (2)
1. a waterproof light partition plate, it is characterized in that, made by the raw material of following weight part: cement 20-25, metakaolin 17-19, type of wire form steel fiber 11-15, naphthalene water reducer 6-8, UEA-H type swelling agent 3-7, paraffin oil 7-9, Nano-class zinc oxide 9-11, vermiculite 13-17, sepiolite 15-18, oil shale waste 16-19, pomelo peel 12-16, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain in 3:2 ratio, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the making method of a kind of waterproof light partition plate according to claim 1, is characterized in that comprising the following steps:
(1) pomelo peel, metakaolin are sent in charring furnace, calcination processing 3-4 hour at 510-615 DEG C, takes out, and is ground into powder, makes it seethe spray form paraffin oil under condition to the powder of gained in air blast, makes it to mix;
(2) vermiculite, sepiolite, oil shale waste are calcined at 610-860 DEG C after 3-6 hour and taken out, pulverize, extremely even with spraying gun sprinkling 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions, dipping 10-12 hour;
(3) step (1), (2) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.