CN104230226B - A kind of light cellular partition board containing lignin - Google Patents
A kind of light cellular partition board containing lignin Download PDFInfo
- Publication number
- CN104230226B CN104230226B CN201410418855.6A CN201410418855A CN104230226B CN 104230226 B CN104230226 B CN 104230226B CN 201410418855 A CN201410418855 A CN 201410418855A CN 104230226 B CN104230226 B CN 104230226B
- Authority
- CN
- China
- Prior art keywords
- raw material
- partition board
- light cellular
- board containing
- containing lignin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of light cellular partition board containing lignin, gained partition plate materials of the present invention are reasonable, do under construction internal partition wall can alleviate building deadweight, saving steel cement, containing raw materials such as lignins, can increase partition plate intensity, improve Antiseismic building grade.
Description
Technical field
The present invention relates to building material field, be exactly a kind of light cellular partition board containing lignin.
Background technology
Light cellular partition board is a kind of novel energy-conserving walling material, constructs simple and convenient, reduces labor intensity, accelerate to construct into
Degree, saves project total cost, meets different client's requirement to modern architecture indoor and outdoor surroundings.Light cellular partition board is divided into interior wall
And exterior wall, the partition plate of interior wall can sufficiently expand the space in house.But common magnesia partition plate exist surface damp suction surface halide accumulation,
The shortcomings such as moisture content is high.
Summary of the invention
It is an object of the invention to provide a kind of light cellular partition board containing lignin.
Above-mentioned purpose is realized by below scheme:
A kind of light cellular partition board containing lignin, it is characterised in that it is to be prepared by the raw material of following weight parts:
Lignin 0.1-0.2, bentonite 2-4, cement 5-8, sodium bicarbonate 1-2, swelling perlite powder 30-42, white glue with vinyl
1-2, pulverized limestone 4-7, haydite 5-15, triethanolamine 0.2-0.4, sugar calcium 1-2, sulfamic acid 0.1-0.2, carbamide 4.2-4.8, first
Base acrylic acid methyl ester. 0.2-0.4, sodium pyrophosphate 1-2, Borax 1-2, citric acid 0.1-0.2, composite modified fiber grain 9-16；
Composite modified fiber grain is prepared by the raw material of following weight parts:
Attapulgite 10-20, flyash 3-4, aluminum vanadine 2-5, styrene-acrylic emulsion 1-3, perlite 1-2, calcium formate 1-2, carbon
Nanotube 2-4, Kaolin 0.2-0.5, antioxidant T501 0.5-0.7, asbestos fibre 2-3, Oxytarch 3-5, aluminium oxide 1-2；
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminum vanadine, perlite are ground, crosses 100-120 mesh sieve, be then 4-with concentration
The saline mixing of 8%, stirs, stands, filters and after drying, after remaining raw material blending, under 500-700 rev/min, and 35-45 DEG C
After stirring 15-25 minute, adding amount of water, pelletize, grain diameter is at 6-8mm, then dries, and to obtain final product；
A kind of light cellular partition board containing lignin stated, it is characterised in that:
Its preparation method is: takes cement plus water and stirs, and adds the uniform slurry that obtains of remaining raw material stirring, slurry entrance
Wall slab squeezing former molding, cutting, natural curing, to obtain final product.
The invention have the benefit that gained partition plate materials of the present invention are reasonable, do internal partition wall under construction and can alleviate and build
Build thing deadweight, saving steel cement, containing raw materials such as lignins, can increase partition plate intensity, improve Antiseismic building grade.
Detailed description of the invention
A kind of light cellular partition board containing lignin, it is to be prepared by the raw material of following weight (kg):
Lignin 0.1, bentonite 2.5, cement 8, sodium bicarbonate 2, swelling perlite powder 35, white glue with vinyl 2, pulverized limestone 7, pottery
Grain 15, triethanolamine 0.4, sugar calcium 1, sulfamic acid 0.2, carbamide 4.5, methyl methacrylate .4, sodium pyrophosphate 2, Borax 2,
Citric acid 0.2, composite modified fiber grain 16；
Composite modified fiber grain is prepared by the raw material of following weight (kg):
Attapulgite 13, flyash 4, aluminum vanadine 5, styrene-acrylic emulsion 2, perlite 2, calcium formate 2, CNT 2, Kaolin
0.5, antioxidant T501 0.7, asbestos fibre 3, Oxytarch 5, aluminium oxide 1；
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminum vanadine, perlite are ground, crosses 100 mesh sieves, be then the salt of 8% with concentration
Water mixes, and stirs, stands, filters and after drying, after remaining raw material blending, under 500 revs/min, after 45 DEG C of stirrings 15 minutes,
Adding amount of water, pelletize, grain diameter is at 6-8mm, then dries, and to obtain final product；
A kind of light cellular partition board containing lignin stated,
Its preparation method is: takes cement plus water and stirs, and adds the uniform slurry that obtains of remaining raw material stirring, slurry entrance
Wall slab squeezing former molding, cutting, natural curing, to obtain final product.
The unit weight of the present embodiment is 580Kg/m3 , comprcssive strength is 6.45MPa.
Claims (1)
1. the light cellular partition board containing lignin, it is characterised in that it is to be prepared by the raw material of following weight parts: wooden
Element 0.1-0.2, bentonite 2-4, cement 5-8, sodium bicarbonate 1-2, swelling perlite powder 30-42, white glue with vinyl 1-2, pulverized limestone 4-
7, haydite 5-15, triethanolamine 0.2-0.4, sugar calcium 1-2, sulfamic acid 0.1-0.2, carbamide 4.2-4.8, methyl methacrylate
0.2-0.4, sodium pyrophosphate 1-2, Borax 1-2, citric acid 0.1-0.2, composite modified fiber grain 9-16；Described composite modified fibre
Dimension granule prepared by the raw material of following weight parts: attapulgite 10-20, flyash 3-4, aluminum vanadine 2-5, styrene-acrylic emulsion 1-3,
Perlite 1-2, calcium formate 1-2, CNT 2-4, Kaolin 0.2-0.5, antioxidant T501 0.5-0.7, asbestos fibre 2-3,
Oxytarch 3-5, aluminium oxide 1-2；The preparation method of described composite modified fiber grain is: by attapulgite, flyash, aluminum
Vanadine, perlite grind, cross 100-120 mesh sieve, then mix with the saline that concentration is 4-8%, stir, stand, filter and
After drying, after remaining raw material blending, under 500-700 rev/min, after 35-45 DEG C is stirred 15-25 minute, add amount of water, make
Grain, grain diameter is at 6-8mm, then dries, and to obtain final product；
Described a kind of light cellular partition board containing lignin, its preparation method is: takes cement plus water and stirs, adds it
Remaining raw material stirring is uniform obtains slurry, and slurry enters wall slab squeezing former molding, cutting, natural curing, to obtain final product.