CN103965607A - 一种汽车塑料件用防水改性聚苯醚材料 - Google Patents

一种汽车塑料件用防水改性聚苯醚材料 Download PDF

Info

Publication number
CN103965607A
CN103965607A CN201410165037.XA CN201410165037A CN103965607A CN 103965607 A CN103965607 A CN 103965607A CN 201410165037 A CN201410165037 A CN 201410165037A CN 103965607 A CN103965607 A CN 103965607A
Authority
CN
China
Prior art keywords
parts
zinc
polyphenylene oxide
polyphenyl ether
stir
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410165037.XA
Other languages
English (en)
Inventor
章云
张娃妮
柯模松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yi Caini Fibrous Material Science And Technology Ltd
Original Assignee
Anhui Yi Caini Fibrous Material Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yi Caini Fibrous Material Science And Technology Ltd filed Critical Anhui Yi Caini Fibrous Material Science And Technology Ltd
Priority to CN201410165037.XA priority Critical patent/CN103965607A/zh
Publication of CN103965607A publication Critical patent/CN103965607A/zh
Pending legal-status Critical Current

Abstract

本发明属于高分子材料领域，具体涉及一种汽车塑料件用防水改性聚苯醚材料，该材料由下列重量份的原料制成：聚苯醚100、硅烷偶联剂KH-5501-2、间苯二酚双(二苯基磷酸酯)4-6、磷酸三(2一氯丙基)酯4-6、磷酸二氢锌5-7、硼酸锌3-4、焦磷酸锌12-15、硬脂酸3-4、乌洛托品1-2、助剂12-15；本发明在原料中添加了磷酸二氢锌、硼酸锌、焦磷酸锌等成分，改进了传统聚苯醚材料的性能，使其具有良好的加工性能和机械性能，制备的材料坚固柔韧，防水阻潮，耐热老化，耐化学品腐蚀，结实耐用，能够广泛的用于制作各类汽车用塑料件。

Description

一种汽车塑料件用防水改性聚苯醚材料
技术领域
本发明属于高分子材料领域，具体涉及一种汽车塑料件用防水改性聚苯醚材料及其制备方法。
背景技术
聚苯醚(PPO) 是五大工程塑料之一，具有优异的物理机械性能、耐热性和电器绝缘性，其吸湿性低、耐蠕变性能优异。被广泛应用于汽车零部件等领域。PPO 是非晶性高分子材料，其熔体粘度非常大，流动性很差，不改性的话由于加工不了基本上没法用。
为了提高聚苯醚(PPO)材料的性能，拓宽材料使用范围，需要改进聚苯醚(PPO)材料配方，对材料进行改性处理，使其能广泛的应用于汽车各个部位。
发明内容
本发明的目的在于，提供一种汽车塑料件用防水改性聚苯醚材料，提升了传统聚苯醚材料的性能，使其具备优良的机械性能，能够适应特定的使用环境，为了实现上述目的，本发明采用的技术方案如下：
一种汽车塑料件用防水改性聚苯醚材料，其特征在于，本发明材料由以下重量份的原料制成：聚苯醚 100、硅烷偶联剂KH-550 1-2、间苯二酚双(二苯基磷酸酯)4-6、磷酸三(2一氯丙基)酯4-6、磷酸二氢锌5-7、硼酸锌3-4、焦磷酸锌12-15、硬脂酸3-4、乌洛托品1-2、助剂12-15。
所述的助剂由下列重量份的原料制成：粘土300-320、丙烯酸二甲基氨基乙酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、SnO21-2、B2O3 5-7、亚硒酸钠4-5、抗氧剂1035 1-2、二甲基硅油1-2、丁香油1-2、促进剂TMTD 1-2、氢氧化铝8-10、交联剂 TAC1-2；制备方法是将粘土放入煅烧炉中在710-740℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
所述的一种汽车塑料件用防水改性聚苯醚材料，其制备方法为：将聚苯醚、磷酸三(2一氯丙基)酯、硼酸锌混合，加热到250-280℃，至聚苯醚熔融，搅拌5-8分钟，再加入焦磷酸锌、间苯二酚双(二苯基磷酸酯)，搅拌4-5分钟，最后加入其它剩余成分，搅拌5-8分钟后，送入双螺杆挤出机中挤出造粒，即得。
本发明原料中添加了磷酸二氢锌、硼酸锌、焦磷酸锌等成分，改进了传统聚苯醚材料的性能，使其具有良好的加工性能和机械性能，制备的材料坚固柔韧，防水阻潮，耐热老化，耐化学品腐蚀，结实耐用，能够满足特定的使用环境条件，市场应用前景广阔。
具体实施方式
实施例
本实施例材料由下列重量份的原料制成：聚苯醚 100、硅烷偶联剂KH-550 1、间苯二酚双(二苯基磷酸酯)6、磷酸三(2一氯丙基)酯6、磷酸二氢锌6、硼酸锌4、焦磷酸锌15、硬脂酸4、乌洛托品2、助剂15。所述聚苯醚选用粘度在0.35~0.65Pa·s 范围内的聚苯醚树脂。
所述的助剂由下列重量份的原料制成：粘土300、丙烯酸二甲基氨基乙酯3、纳米二氧化钛4、纳米二氧化硅1、SnO21、B2O3 5、亚硒酸钠5、抗氧剂1035 1、二甲基硅油1、丁香油1、促进剂TMTD 2、氢氧化铝8、交联剂 TAC1；制备方法是将粘土放入煅烧炉中在710-740℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
所述的一种汽车塑料件用防水改性聚苯醚材料，其制备方法为：将聚苯醚、磷酸三(2一氯丙基)酯、硼酸锌混合，加热到260℃，至聚苯醚熔融，搅拌8分钟，再加入焦磷酸锌、间苯二酚双(二苯基磷酸酯)，搅拌5分钟，最后加入其它剩余成分，搅拌8分钟后，送入双螺杆挤出机中挤出造粒，即得。
本发明材料的性能：熔体流动指数在280℃下15 -19.3g/10min，缺口冲击强度为10.1-13.2kJ/m2，拉伸强度为72.1-79.3MPa，弯曲强度138.0-147.9MPa，弯曲模量为2665.3-2851.7MPa，热变形温度为122.2-127.6℃。

Claims (2)

1.一种汽车塑料件用防水改性聚苯醚材料，其特征在于，该材料由以下重量份的原料制成：聚苯醚 100、硅烷偶联剂KH-550 1-2、间苯二酚双(二苯基磷酸酯)4-6、磷酸三(2一氯丙基)酯4-6、磷酸二氢锌5-7、硼酸锌3-4、焦磷酸锌12-15、硬脂酸3-4、乌洛托品1-2、助剂12-15；
所述的助剂由下列重量份的原料制成：粘土300-320、丙烯酸二甲基氨基乙酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、SnO2 1-2、B2O3 5-7、亚硒酸钠4-5、抗氧剂1035 1-2、二甲基硅油1-2、丁香油1-2、促进剂TMTD 1-2、氢氧化铝8-10、交联剂TAC 1-2；制备方法是将粘土放入煅烧炉中在710-740℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
2.如权利要求1所述的一种汽车塑料件用防水改性聚苯醚材料，其制作工艺为：将聚苯醚、磷酸三(2一氯丙基)酯、硼酸锌混合，加热到250-280℃，至聚苯醚熔融，搅拌5-8分钟，再加入焦磷酸锌、间苯二酚双(二苯基磷酸酯)，搅拌4-5分钟，最后加入其它剩余成分，搅拌5-8分钟后，送入双螺杆挤出机中挤出造粒，即得。
CN201410165037.XA 2014-04-23 2014-04-23 一种汽车塑料件用防水改性聚苯醚材料 Pending CN103965607A (zh)