CN103952910A - 一种船篷面料用涂料 - Google Patents
一种船篷面料用涂料 Download PDFInfo
- Publication number
- CN103952910A CN103952910A CN201410113678.0A CN201410113678A CN103952910A CN 103952910 A CN103952910 A CN 103952910A CN 201410113678 A CN201410113678 A CN 201410113678A CN 103952910 A CN103952910 A CN 103952910A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- coating
- minute
- coating material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种船篷面料用涂料,它是由下述重量份的原料组成的:氯化聚乙烯74-80、聚异二烯2-3、环氧氯丙烷2-3、聚乙烯醇2-3、环氧硬脂酸辛酯6-10、2-丁氧基乙醇1-2、N,N’-间苯撑双马来酰亚胺1-2、四水八硼酸二钠1-2、己二酸丙二醇聚酯3-4、轻质碳酸钙6-8、硅酸镁3-5、复合填料10-17;本发明的涂料涂覆后的面料耐磨性很好,轻便,防水能力强。耐海水或河水腐蚀,特别适用于船篷面料,用于各种海上江上作业船只。
Description
技术领域
本发明主要涉及一种涂料,尤其涉及一种船篷面料用涂料。
背景技术
物件暴露在大气之中,受到氧气、水分等的侵蚀,造成金属锈蚀、木材腐朽、水泥风化等破坏现象。在物件表面涂以涂料,形成一层保护膜,能够阻止或延迟这些破坏现象的发生和发展,因此为了使得各种材料的使用寿命延长,节约生产资源,发明一种高效的涂料具有很深远的影响。
随着涂料行业的不断发展,以丙烯酸酯、PVC聚合物等为涂层的产品也很多,但有的涂层有轻微的腐蚀性、吸尘、耐热性、耐候性差,而PE的化学性能稳定、耐候性好,无毒、无污染、密度低,可以广泛用于各种材料的涂装,可以起到很好的保护效果。
发明内容
本发明目的就是提供一种船篷面料用涂料。
本发明是通过以下技术方案实现的:
一种船篷面料用涂料,它是由下述重量份的原料组成的:
氯化聚乙烯74-80、聚异二烯2-3、环氧氯丙烷2-3、聚乙烯醇2-3、环氧硬脂酸辛酯6-10、2-丁氧基乙醇1-2、N,N’-间苯撑双马来酰亚胺1-2、四水八硼酸二钠1-2、己二酸丙二醇聚酯3-4、轻质碳酸钙6-8、硅酸镁3-5、复合填料10-17;
所述的复合填料是由下述重量份的原料组成的:
叶腊石25-30、绒毛粉10-13、甲基异噻唑啉酮2-3、线性低密度聚乙烯15-25、羧甲基纤维素钠1-2、磷酸三(丁氧基乙基)酯1-2、松油醇1-2;
将上述叶腊石在600-700℃下煅烧1-2小时,出料冷却后加入甲基异噻唑啉酮、线性低密度聚乙烯,研磨成粉,将羧甲基纤维素钠加入到6-10倍水中,搅拌均匀后加入绒毛粉,在60-70℃下搅拌混合4-6分钟,与上述得到的粉料混合,加入剩余各原料,充分研磨,烘干,过60-80目筛,即得所述复合填料。
一种船篷面料用涂料的制备方法,包括以下步骤:
将上述聚异二烯、轻质碳酸钙混合,在60-80℃下保温搅拌3-5分钟,加入环氧硬脂酸辛酯,继续搅拌4-6分钟,降低温度为40-50℃,加入四水八硼酸二钠,100-200转/分搅拌分散3-5分钟,再加入剩余各原料,混合均匀,送入双螺杆挤出机,进行熔融、挤出,过60-100目筛,即得所述船篷面料用涂料。
使用方法:
将涂料加热熔融,然后将涂覆件进行浸润,可以用橡胶辊对涂层施加压力来控制胶层的厚度,然后经塑化、冷却,即可。
本发明的优点是:
本发明的涂料涂覆后的面料耐磨性很好,轻便,防水能力强,耐海水或河水腐蚀,特别适用于船篷面料,用于各种海上江上作业船只。
具体实施方式
实施例1
一种船篷面料用涂料,它是由下述重量份(公斤)的原料组成的:
氯化聚乙烯80、聚异二烯2、环氧氯丙烷3、聚乙烯醇2、环氧硬脂酸辛酯6、2-丁氧基乙醇1、N,N’-间苯撑双马来酰亚胺2、四水八硼酸二钠2、己二酸丙二醇聚酯3、轻质碳酸钙8、硅酸镁5、复合填料17;
所述的复合填料是由下述重量份的原料组成的:
叶腊石30、绒毛粉13、甲基异噻唑啉酮3、线性低密度聚乙烯25、羧甲基纤维素钠1、磷酸三(丁氧基乙基)酯2、松油醇1;
将上述叶腊石在700℃下煅烧2小时,出料冷却后加入甲基异噻唑啉酮、线性低密度聚乙烯,研磨成粉,将羧甲基纤维素钠加入到10倍水中,搅拌均匀后加入绒毛粉,在70℃下搅拌混合4分钟,与上述得到的粉料混合,加入剩余各原料,充分研磨,烘干,过80目筛,即得所述复合填料。
一种船篷面料用涂料的制备方法,包括以下步骤:
将上述聚异二烯、轻质碳酸钙混合,在80℃下保温搅拌5分钟,加入环氧硬脂酸辛酯,继续搅拌6分钟,降低温度为50℃,加入四水八硼酸二钠,200转/分搅拌分散3分钟,再加入剩余各原料,混合均匀,送入双螺杆挤出机,进行熔融、挤出,过100目筛,即得所述船篷面料用涂料。
性能测试:
抗冲击性:≥50kg/cm;
铅笔硬度测试:2H 无划伤。
Claims (2)
1.一种船篷面料用涂料,其特征在于它是由下述重量份的原料组成的:
氯化聚乙烯74-80、聚异二烯2-3、环氧氯丙烷2-3、聚乙烯醇2-3、环氧硬脂酸辛酯6-10、2-丁氧基乙醇1-2、N,N’-间苯撑双马来酰亚胺1-2、四水八硼酸二钠1-2、己二酸丙二醇聚酯3-4、轻质碳酸钙6-8、硅酸镁3-5、复合填料10-17;
所述的复合填料是由下述重量份的原料组成的:
叶腊石25-30、绒毛粉10-13、甲基异噻唑啉酮2-3、线性低密度聚乙烯15-25、羧甲基纤维素钠1-2、磷酸三(丁氧基乙基)酯1-2、松油醇1-2;
将上述叶腊石在600-700℃下煅烧1-2小时,出料冷却后加入甲基异噻唑啉酮、线性低密度聚乙烯,研磨成粉,将羧甲基纤维素钠加入到6-10倍水中,搅拌均匀后加入绒毛粉,在60-70℃下搅拌混合4-6分钟,与上述得到的粉料混合,加入剩余各原料,充分研磨,烘干,过60-80目筛,即得所述复合填料。
2.一种如权利要求1所述的船篷面料用涂料的制备方法,其特征在于包括以下步骤:
将上述聚异二烯、轻质碳酸钙混合,在60-80℃下保温搅拌3-5分钟,加入环氧硬脂酸辛酯,继续搅拌4-6分钟,降低温度为40-50℃,加入四水八硼酸二钠,100-200转/分搅拌分散3-5分钟,再加入剩余各原料,混合均匀,送入双螺杆挤出机,进行熔融、挤出,过60-100目筛,即得所述船篷面料用涂料。