CN103937195A - 增韧工程塑料及其制备方法 - Google Patents

增韧工程塑料及其制备方法 Download PDF

Info

Publication number
CN103937195A
CN103937195A CN201410199285.6A CN201410199285A CN103937195A CN 103937195 A CN103937195 A CN 103937195A CN 201410199285 A CN201410199285 A CN 201410199285A CN 103937195 A CN103937195 A CN 103937195A
Authority
CN
China
Prior art keywords
resin
engineering plastics
engineering plastic
parts
glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410199285.6A
Other languages
English (en)
Other versions
CN103937195B (zh
Inventor
袁峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xi'an Yawei Material Technology Co., Ltd.
Original Assignee
Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd filed Critical Ningbo High-Tech Zone Zhuoer Chemical Engineering Technology Co Ltd
Priority to CN201410199285.6A priority Critical patent/CN103937195B/zh
Publication of CN103937195A publication Critical patent/CN103937195A/zh
Application granted granted Critical
Publication of CN103937195B publication Critical patent/CN103937195B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种增韧工程塑料及其制备方法，所述增韧工程塑料组成原料的重量份为：PC树脂60-80份、SAN树脂20-25份、SEBS树脂3-10份。本发明的增韧工程塑料，具有良好韧性，并具有类似有色金属的强度，同时又兼备延展性，冲击强度高。本发明的增韧工程塑料可用于各种安全灯罩、信号灯，体育馆、体育场的透明防护板，采光玻璃，高层建筑玻璃，汽车反射镜、挡风玻璃板，飞机座舱玻璃，摩托车驾驶安全帽，计算机，办公设备，汽车和片材。

Description

增韧工程塑料及其制备方法
技术领域
本发明涉及一种工程塑料及其制备方法，尤其涉及一种增韧工程塑料及其制备方法。
背景技术
工程塑料英文名为：engineering-plastics，工程塑料[2]是指被用做工业零件或外壳材料的工业用塑料，是强度、耐冲击性、耐热性、硬度及抗老化性均优的塑料。日本业界将它定义为“可以做为构造用及机械零件用的高性能塑料，耐热性在100℃以上，主要运用在工业上”。
和通用塑料相比，工程塑料在机械性能、耐久性、耐腐蚀性、耐热性等方面能达到更高的要求，而且加工更方便并可替代金属材料。工程塑料被广泛应用于电子电气、汽车、建筑、办公设备、机械、航空航天等行业，以塑代钢、以塑代木已成为国际流行趋势。工程塑料已成为当今世界塑料工业中增长速度最快的领域，其发展不仅对国家支柱产业和现代高新技术产业起着支撑作用，同时也推动传统产业改造和产品结构的调整。
由于我国汽车、电子和建筑等行业发展迅速，当前，我国已成为全球工程塑料需求增长最快的国家。据中投分析，在今后，随着国内经济的不断发展，工程塑料的需求将会进一步得到增长，我国工程塑料行业发展前景十分广阔。以家电行业来说，今后仅以冰箱、冷柜、洗衣机、空调及各类小家电产品每年的工程塑料需求量将达60万吨左右。而用于通信基础设施建设以及铁路、公路建设等方面的工程塑料用量则更为惊人，预计今后数年内总需求量将达到450万吨以上。
据《2013-2017年中国工程塑料行业产销需求与投资预测分析报告》显示，2010年，我国工程塑料消费量达244.3万吨，同比增长11％，是全球需求增长最快的国家；2011年我国工程塑料消费量为272万吨，同比增长11.34％。预计到2015年达到417万吨。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题之一是提供一种增韧工程塑料。
本发明所要解决的技术问题之二是提供上述增韧工程塑料的制备方法。
本发明是通过如下技术方案实现的：
一种增韧工程塑料，其组成原料的重量份为：PC树脂60-80份、SAN树脂20-25份、SEBS树脂3-10份。
SAN是Styrene Acrylonitrile的缩写。苯乙烯丙烯腈是苯乙烯丙烯腈的共聚物，是一种无色透明，具有较高的机械强度的聚丙烯基工程塑料。
SEBS是以聚苯乙烯为末端段，以聚丁二烯加氢得到的乙烯-丁烯共聚物为中间弹性嵌段的线性三嵌共聚物。SEBS不含不饱和双键，因此具有良好的稳定性和耐老化性。
优选地，本发明提供了：
一种增韧工程塑料，其组成原料的重量份为：PC树脂60-80份、SAN树脂20-25份、SEBS树脂3-10份、抗菌剂0.2-0.6份。
所述抗菌剂为2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮和/或1,6-双(正-对氯苯双胍)己烷。
最优地，所述抗菌剂为2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮和1,6-双(正-对氯苯双胍)己烷的混合物，2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮和1,6-双(正-对氯苯双胍)己烷的重量比为3:1-1:3。
2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮，CAS号：499-44-5。可用于化妆品防腐，但并未见任何将该原料用于塑料抗菌的书面报道。
1,6-双(正-对氯苯双胍)己烷，CAS号：55-56-1。可用于食品厂、化妆品厂、制药厂等的表面消毒，但并未见任何将该原料用于塑料抗菌的书面报道。
本发明还提供了上述增韧工程塑料的制备方法：按配比称取各组分，混合，熔融混炼、挤出造粒。
本发明的增韧工程塑料，具有良好韧性，并具有类似有色金属的强度，同时又兼备延展性，冲击强度高。本发明的增韧工程塑料可用于各种安全灯罩、信号灯，体育馆、体育场的透明防护板，采光玻璃，高层建筑玻璃，汽车反射镜、挡风玻璃板，飞机座舱玻璃，摩托车驾驶安全帽，计算机，办公设备，汽车和片材。
具体实施方式
实施例中，原料的具体选择：
PC树脂，选用美国通用电气塑料公司牌号241R的通用级PC树脂。
SAN树脂，选用台湾奇美公司生产的牌号为PN-117C的SAN树脂。
SEBS树脂，选用美国科腾公司牌号为FG1901的SEBS树脂。
实施例1-3
按照表1中对应实施例1-3数据称取各组分；加入混合机，室温下控制转速在1500转/分钟，混合10分钟；取出后，加入螺杆挤出机中，挤出造粒，即获得本发明的增韧工程塑料。
表1：增韧工程塑料配方表  单位：公斤
实施例1 实施例2 实施例3
PC树脂 70 70 70
SAN树脂 22 22 22
SEBS树脂 8 8 8
2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮 0.2 0.4 /
1,6-双(正-对氯苯双胍)己烷 0.2 / 0.4
测试例
(1)抗菌测试：
采用常规方法将实施例1-3制得的增韧工程塑料，分别切割出50mm×50mm×4mm的样品，进行抗菌测试，测试数据见表2。
抗菌测试标准：
QB/T2591-2003抗菌塑料抗菌性能试验方法和抗菌效果。
检测用菌：
大肠埃希氏菌(Escherichia coli)ATCC25922；金黄色葡萄球菌(Staphylococcus aureus)ATCC6538。
表2：增韧工程塑料抗菌性能测试表
实施例1 实施例2 实施例3
大肠杆菌杀菌率，％ 97.6 95.2 95.5
金黄色葡萄球菌杀菌率，％ 98.1 96.9 96.4
实施例1的增韧工程塑料，拉伸强度56.8MPa，维卡软化点124.5℃，弯曲强度92.7MPa，Izod冲击强度(23℃)974.5KJ/m2。相对于纯PC塑料，韧度增强。
本发明的增韧工程塑料，具有良好韧性，并具有类似有色金属的强度，同时又兼备延展性，冲击强度高。特别在配方中添加特定的抗菌剂后，使用环境中本身对沾污在塑料上的细菌、霉菌、醇母菌、藻类甚至病毒等起抑制或杀灭作用，通过抑制微生物的繁殖来保持塑料自身清洁。

Claims (5)

1.一种增韧工程塑料，其特征在于，其组成原料的重量份为：PC树脂60-80份、SAN树脂20-25份、SEBS树脂3-10份。
2.一种增韧工程塑料，其特征在于，其组成原料的重量份为：PC树脂60-80份、SAN树脂20-25份、SEBS树脂3-10份、抗菌剂0.2-0.6份。
3.如权利要求2所述的增韧工程塑料，其特征在于：所述抗菌剂为2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮和/或1,6-双(正-对氯苯双胍)己烷。
4.如权利要求3所述的增韧工程塑料，其特征在于：所述抗菌剂为2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮和1,6-双(正-对氯苯双胍)己烷的混合物，2-羟基-4-异丙基-2,4,6-环庚三烯-1-酮和1,6-双(正-对氯苯双胍)己烷的重量比为3:1-1:3。
5.如权利要求1-4中任一项所述的增韧工程塑料的制备方法，其特征在于：按配比称取各组分，混合，进行捏合塑练。
CN201410199285.6A 2014-05-12 2014-05-12 增韧工程塑料及其制备方法 Active CN103937195B (zh)