CN107189335A - 一种计算机用鼠标外壳材料及其制备方法 - Google Patents
一种计算机用鼠标外壳材料及其制备方法 Download PDFInfo
- Publication number
- CN107189335A CN107189335A CN201710563409.8A CN201710563409A CN107189335A CN 107189335 A CN107189335 A CN 107189335A CN 201710563409 A CN201710563409 A CN 201710563409A CN 107189335 A CN107189335 A CN 107189335A
- Authority
- CN
- China
- Prior art keywords
- parts
- essence
- computer mouse
- mouse case
- case according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种计算机用鼠标外壳材料,属于鼠标材料技术领域,包括以下重量份的原料:聚碳酸脂25‑30份、氟硅橡胶15‑18份、丙烯腈‑丁二烯‑苯乙烯共聚物40‑50份、玻璃纤维12‑14份、硅藻土4‑8份、铸石粉18‑20份、氮化硅6‑8份、硅油3‑5份、石蜡5‑7份、亚磷酸酯10‑14份、氧化锌8‑10份、香精2‑4份、增塑剂16‑18份、稳定剂1‑3份、抗静电剂1‑3份;本发明还公开了一种计算机用鼠标外壳材料的制备方法;本发明环保污染小,耐磨性、耐高温能力较佳,还散发香味。
Description
技术领域
本发明涉及鼠标材料技术领域,具体的说,涉及了一种计算机用鼠标外壳材料及其制备方法。
背景技术
鼠标是计算机的一种输入设备,也是计算机显示系统纵横坐标定位的指示器,因形似老鼠而得名“鼠标”。
鼠标外壳材料一般由塑料制成,但目前用的鼠标外壳塑料的耐磨性不足,强度较差,耐火能力差,使用时间较短,而且鼠标会散发塑料的异味,影响使用者的状态。
在公开号为CN106046645A的专利文件中,公开了一种计算机鼠标专用防滑复合材料及其制备方法,所述计算机鼠标专用防滑复合材料,按照重量份的主要原料包括:改性树脂26-32份、聚苯硫醚10-15份、二烯丙基二甲基氯化铵10-18份、3-羟基丁酸酯0.1-0.5份、改性二氧化硅粉末0.1-0.5份、过氧化二碳酸二异丙酯0.1-0.5份、炭黑0.1-0.5份、玻璃纤维2-6份。该发明中计算机鼠标专用防滑复合材料综合性能优异,具有成型加工性好、粗糙度高、成本低廉等优点。
在公开号为CN106009370A的专利文件中,公开了一种计算机用鼠标抗压抗拉材料及其制备方法,所述计算机用鼠标抗压抗拉材料,由基体和增强体组成,所述基体包括陶瓷粉末、钨钢粉末和玻璃纤维,所述增强体包括氯乙烯、丙烯酸酯、氧化镁粉末、氯化钙粉末、镀锡铜丝、亚氨基二琥珀酸、纳米二氧化钛粉末,以重量份来计,陶瓷粉末25-45份,钨钢粉末15-30份,玻璃纤维15-20份,氯乙烯5-10份,丙烯酸酯5-10份,氧化镁粉末2-8份,氯化钙粉末2-8份,镀锡铜丝2-8份,亚氨基二琥珀酸0.1-0.5份,纳米二氧化钛粉末0.1-0.3份。该发明通过对计算机用鼠标的抗压抗拉材料进行优化,显著地提高了计算机用鼠标的抗压抗拉性能。该发明的方法制备得到的计算机用鼠标抗压抗拉材料抗压强度20MPa以上,抗拉伸强度15MPa以上,弯曲强度6MPa以上。
上述鼠标材料中,环保性不足,而且耐磨能力较差,耐火能力差,所以需要一种计算机用鼠标外壳材料来解决上述问题。
发明内容
本发明的目的在于克服上述现有技术的不足,提供了一种计算机用鼠标外壳材料及其制备方法,制备简单,环保污染小,耐磨性、耐高温能力较佳,还散发香味。
本发明提供的一种计算机用鼠标外壳材料,包括以下重量份的原料:
聚碳酸脂25-30份、氟硅橡胶15-18份、丙烯腈-丁二烯-苯乙烯共聚物40-50份、玻璃纤维12-14份、硅藻土4-8份、铸石粉18-20份、氮化硅6-8份、硅油3-5份、石蜡5-7份、亚磷酸酯10-14份、氧化锌8-10份、香精2-4份、增塑剂16-18份、稳定剂1-3份、抗静电剂1-3份。
作为优选,玻璃纤维的长度为0.5-1mm,直径为0.1-0.5mm;铸石粉和氧化锌的目数为500目。
作为优选,香精为薄荷香精、茉莉香精、天竺葵香精、含羞草香精、依兰香精的一种或二种以上的混合物。
作为优选,增塑剂为柠檬酸三乙酯、柠檬酸三丁酯、乙酰柠檬酸三丁酯、柠檬酸三辛酯、乙酰柠檬酸三辛酯、柠檬酸三正己酯、乙酰柠檬酸三正己酯的一种或二种以上的混合物。
作为优选,稳定剂为硬脂酸钙、蓖麻油酸钙、硬脂酸锌、蓖麻油酸锌、环氧大豆油和紫外线吸收剂的混合物。
作为优选,抗静电剂为聚氧化乙烯烷基胺、甘油脂肪酸酯、山梨糖醇酐脂肪酸酯、聚氧化乙烯脂肪乙醚、聚氧化乙烯烷基苯醚、聚乙二醇酯脂肪酸酯的一种或二种以上的混合物。
本发明还提供了一种计算机用鼠标外壳材料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将聚碳酸脂、氟硅橡胶、丙烯腈-丁二烯-苯乙烯共聚物、玻璃纤维、硅藻土、铸石粉、氮化硅、亚磷酸酯、氧化锌、增塑剂、稳定剂、抗静电剂加入到搅拌机内搅拌5-10min,然后放入烘箱内干燥6h,得到混合物;
(3)、将步骤(2)中的混合物、石蜡、香精、硅油、加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、粒料干燥后加入注塑机注塑成型,即可。
其中,
步骤(2)中搅拌机的搅拌速度为200-300r/min。
步骤(3)中的双螺杆挤出机设有7个挤出工作温区,各个温区的挤出温度分别为190-195℃、195-205℃、205-210℃、210-215℃、215-218℃、218-220℃、220-225℃。
本发明的一种计算机用鼠标外壳材料及其制备方法,制备简单,环保污染小,耐磨性、耐高温能力较佳,还散发香味,具体的有益效果如下:
(1)、聚碳酸脂耐热、抗冲击、耐冲击性能好,折射率高,加工性能好,丙烯腈-丁二烯-苯乙烯共聚物具有较佳地耐热性、耐酸碱盐、硬度、加工的流动性及产品表面的光洁度,两者之间的配合能提高鼠标外壳材料的性能;氟硅橡胶能提高鼠标外壳材料的耐热性、耐寒性、耐高电压性、耐气候老化、耐油和耐酸碱性等性能;
(2)、玻璃纤维绝缘性好、耐热性强、抗腐蚀性好,机械强度高,能提高鼠标外壳材料的耐腐蚀耐热能力,提高强度;亚磷酸酯和氧化锌能增加鼠标外壳材料的阻燃性能,氧化锌还可以提供广谱的紫外保护,同时还有抗菌的作用;铸石粉和氮化硅能有效地提高鼠标外壳材料的耐磨性和耐酸碱能力;
(3)、香精能去除异味,使鼠标外壳材料散发香味,天竺葵香精和薄荷香精还具有驱除蚊虫的作用;增塑剂、稳定剂和抗静电剂均能有效地改善鼠标外壳材料的各项性能;
(4)、本发明各种原料对应比例的混合,能有效地保证鼠标外壳材料的耐磨性、耐高温耐腐蚀能力、耐候和耐油能力,增加鼠标外壳材料的使用寿命;本发明采用无毒增塑剂和阻燃物质,十分环保,而且制备方法能有效地将各原料之间充分混合。
具体实施方式
以下结合具体实施例对发明作进一步详细的描述。
实施例1
本实施例的一种计算机用鼠标外壳材料,包括以下重量份的原料:
聚碳酸脂25份、氟硅橡胶15份、丙烯腈-丁二烯-苯乙烯共聚物40份、玻璃纤维12份、硅藻土4份、铸石粉18份、氮化硅6份、硅油3份、石蜡5份、亚磷酸酯10份、氧化锌8份、香精2份、增塑剂16份、稳定剂1份、抗静电剂1份。
本实施例中,玻璃纤维的长度为0.5mm,直径为0.1mm;铸石粉和氧化锌的目数为500目。
本实施例中,香精为薄荷香精、茉莉香精、天竺葵香精、含羞草香精、依兰香精的混合物。
本实施例中,增塑剂为柠檬酸三乙酯、柠檬酸三丁酯、乙酰柠檬酸三丁酯、柠檬酸三辛酯、乙酰柠檬酸三辛酯、柠檬酸三正己酯、乙酰柠檬酸三正己酯的混合物。
本实施例中,稳定剂为硬脂酸钙、蓖麻油酸钙、硬脂酸锌、蓖麻油酸锌、环氧大豆油和紫外线吸收剂的混合物。
本实施例中,抗静电剂为聚氧化乙烯烷基胺、甘油脂肪酸酯、山梨糖醇酐脂肪酸酯、聚氧化乙烯脂肪乙醚、聚氧化乙烯烷基苯醚、聚乙二醇酯脂肪酸酯的混合物。
本实施例还提供了一种计算机用鼠标外壳材料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将聚碳酸脂、氟硅橡胶、丙烯腈-丁二烯-苯乙烯共聚物、玻璃纤维、硅藻土、铸石粉、氮化硅、亚磷酸酯、氧化锌、增塑剂、稳定剂、抗静电剂加入到搅拌机内搅拌5min,然后放入烘箱内干燥6h,得到混合物;
(3)、将步骤(2)中的混合物、石蜡、香精、硅油、加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、粒料干燥后加入注塑机注塑成型,即可。
其中,
步骤(2)中搅拌机的搅拌速度为200r/min。
步骤(3)中的双螺杆挤出机设有7个挤出工作温区,各个温区的挤出温度分别为190℃、195℃、205℃、210℃、215℃、218℃、220℃。
实施例2
本实施例的一种计算机用鼠标外壳材料,包括以下重量份的原料:
聚碳酸脂28份、氟硅橡胶17份、丙烯腈-丁二烯-苯乙烯共聚物45份、玻璃纤维13份、硅藻土6份、铸石粉19份、氮化硅7份、硅油4份、石蜡6份、亚磷酸酯12份、氧化锌9份、香精3份、增塑剂17份、稳定剂2份、抗静电剂2份。
本实施例中,玻璃纤维的长度为0.8mm,直径为0.3mm;铸石粉和氧化锌的目数为500目。
本实施例中,香精为薄荷香精、茉莉香精、天竺葵香精、含羞草香精、依兰香精的混合物。
本实施例中,增塑剂为柠檬酸三乙酯、柠檬酸三丁酯、乙酰柠檬酸三丁酯、柠檬酸三辛酯、乙酰柠檬酸三辛酯、柠檬酸三正己酯、乙酰柠檬酸三正己酯的混合物。
本实施例中,稳定剂为硬脂酸钙、蓖麻油酸钙、硬脂酸锌、蓖麻油酸锌、环氧大豆油和紫外线吸收剂的混合物。
本实施例中,抗静电剂为聚氧化乙烯烷基胺、甘油脂肪酸酯、山梨糖醇酐脂肪酸酯、聚氧化乙烯脂肪乙醚、聚氧化乙烯烷基苯醚、聚乙二醇酯脂肪酸酯的混合物。
本实施例还提供了一种计算机用鼠标外壳材料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将聚碳酸脂、氟硅橡胶、丙烯腈-丁二烯-苯乙烯共聚物、玻璃纤维、硅藻土、铸石粉、氮化硅、亚磷酸酯、氧化锌、增塑剂、稳定剂、抗静电剂加入到搅拌机内搅拌8min,然后放入烘箱内干燥6h,得到混合物;
(3)、将步骤(2)中的混合物、石蜡、香精、硅油、加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、粒料干燥后加入注塑机注塑成型,即可。
其中,
步骤(2)中搅拌机的搅拌速度为250r/min。
步骤(3)中的双螺杆挤出机设有7个挤出工作温区,各个温区的挤出温度分别为193℃、200℃、208℃、213℃、217℃、219℃、223℃。
实施例3
本实施例的一种计算机用鼠标外壳材料,包括以下重量份的原料:
聚碳酸脂30份、氟硅橡胶18份、丙烯腈-丁二烯-苯乙烯共聚物50份、玻璃纤维14份、硅藻土8份、铸石粉20份、氮化硅8份、硅油5份、石蜡7份、亚磷酸酯14份、氧化锌10份、香精4份、增塑剂18份、稳定剂3份、抗静电剂3份。
本实施例中,玻璃纤维的长度为1mm,直径为0.5mm;铸石粉和氧化锌的目数为500目。
本实施例中,香精为薄荷香精、茉莉香精、天竺葵香精、含羞草香精、依兰香精的混合物。
本实施例中,增塑剂为柠檬酸三乙酯、柠檬酸三丁酯、乙酰柠檬酸三丁酯、柠檬酸三辛酯、乙酰柠檬酸三辛酯、柠檬酸三正己酯、乙酰柠檬酸三正己酯的混合物。
本实施例中,稳定剂为硬脂酸钙、蓖麻油酸钙、硬脂酸锌、蓖麻油酸锌、环氧大豆油和紫外线吸收剂的混合物。
本实施例中,抗静电剂为聚氧化乙烯烷基胺、甘油脂肪酸酯、山梨糖醇酐脂肪酸酯、聚氧化乙烯脂肪乙醚、聚氧化乙烯烷基苯醚、聚乙二醇酯脂肪酸酯的混合物。
本实施例还提供了一种计算机用鼠标外壳材料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将聚碳酸脂、氟硅橡胶、丙烯腈-丁二烯-苯乙烯共聚物、玻璃纤维、硅藻土、铸石粉、氮化硅、亚磷酸酯、氧化锌、增塑剂、稳定剂、抗静电剂加入到搅拌机内搅拌10min,然后放入烘箱内干燥6h,得到混合物;
(3)、将步骤(2)中的混合物、石蜡、香精、硅油、加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、粒料干燥后加入注塑机注塑成型,即可。
其中,
步骤(2)中搅拌机的搅拌速度为300r/min。
步骤(3)中的双螺杆挤出机设有7个挤出工作温区,各个温区的挤出温度分别为195℃、205℃、210℃、215℃、218℃、220℃、225℃。
经检测,实施例1-3的抗压强度均大于25MPa,抗拉伸轻度均大于20MPa,弯曲强度均大于10MPa,具有较佳地的力学性能。
以上所述仅是本发明的优选实施方式,本发明的保护范围并不仅局限于上述实施例,凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理前提下的若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (9)
1.一种计算机用鼠标外壳材料,其特征在于:包括以下重量份的原料:
聚碳酸脂25-30份、氟硅橡胶15-18份、丙烯腈-丁二烯-苯乙烯共聚物40-50份、玻璃纤维12-14份、硅藻土4-8份、铸石粉18-20份、氮化硅6-8份、硅油3-5份、石蜡5-7份、亚磷酸酯10-14份、氧化锌8-10份、香精2-4份、增塑剂16-18份、稳定剂1-3份、抗静电剂1-3份。
2.根据权利要求1所述的计算机用鼠标外壳材料,其特征在于:玻璃纤维的长度为0.5-1mm,直径为0.1-0.5mm;铸石粉和氧化锌的目数为500目。
3.根据权利要求1所述的计算机用鼠标外壳材料,其特征在于:香精为薄荷香精、茉莉香精、天竺葵香精、含羞草香精、依兰香精的一种或二种以上的混合物。
4.根据权利要求1所述的计算机用鼠标外壳材料,其特征在于:增塑剂为柠檬酸三乙酯、柠檬酸三丁酯、乙酰柠檬酸三丁酯、柠檬酸三辛酯、乙酰柠檬酸三辛酯、柠檬酸三正己酯、乙酰柠檬酸三正己酯的一种或二种以上的混合物。
5.根据权利要求1所述的计算机用鼠标外壳材料,其特征在于:稳定剂为硬脂酸钙、蓖麻油酸钙、硬脂酸锌、蓖麻油酸锌、环氧大豆油和紫外线吸收剂的混合物。
6.根据权利要求1所述的计算机用鼠标外壳材料,其特征在于:抗静电剂为聚氧化乙烯烷基胺、甘油脂肪酸酯、山梨糖醇酐脂肪酸酯、聚氧化乙烯脂肪乙醚、聚氧化乙烯烷基苯醚、聚乙二醇酯脂肪酸酯的一种或二种以上的混合物。
7.根据权利要求1-6任意一项所述的一种计算机用鼠标外壳材料的制备方法,其特征在于:包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将聚碳酸脂、氟硅橡胶、丙烯腈-丁二烯-苯乙烯共聚物、玻璃纤维、硅藻土、铸石粉、氮化硅、亚磷酸酯、氧化锌、增塑剂、稳定剂、抗静电剂加入到搅拌机内搅拌5-10min,然后放入烘箱内干燥6h,得到混合物;
(3)、将步骤(2)中的混合物、石蜡、香精、硅油、加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、粒料干燥后加入注塑机注塑成型,即可。
8.根据权利要求7所述的计算机用鼠标外壳材料的制备方法,其特征在于:步骤(2)中搅拌机的搅拌速度为200-300r/min。
9.根据权利要求7所述的计算机用鼠标外壳材料的制备方法,其特征在于:步骤(3)中的双螺杆挤出机设有7个挤出工作温区,各个温区的挤出温度分别为190-195℃、195-205℃、205-210℃、210-215℃、215-218℃、218-220℃、220-225℃。