CN103937173A - 一种标签膜用聚酯钛白粉母粒及其制备方法 - Google Patents
一种标签膜用聚酯钛白粉母粒及其制备方法 Download PDFInfo
- Publication number
- CN103937173A CN103937173A CN201410141357.1A CN201410141357A CN103937173A CN 103937173 A CN103937173 A CN 103937173A CN 201410141357 A CN201410141357 A CN 201410141357A CN 103937173 A CN103937173 A CN 103937173A
- Authority
- CN
- China
- Prior art keywords
- titanium dioxide
- polyester
- master batch
- label
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种标签膜用聚酯钛白粉母粒,其是由以下质量份的原料组成:40-80份的PET、20-60份的钛白粉、0.05-0.5份的荧光增白剂、0.1-1份的分散剂、0.2-1份的抗氧剂。本发明也公开了标签膜用聚酯钛白粉母粒的制备方法,包括以下步骤:将各原料混合均匀,熔融挤出、造粒即可。本发明一方面解决了钛白粉颜料在制备聚酯标签薄膜中的分散性问题,另一方面会使得聚酯标签薄膜的白度和亮度得到很好的提高。
Description
技术领域
本发明涉及一种标签膜用聚酯钛白粉母粒及其制备方法。
背景技术
聚对苯二甲酸乙二醇酯(聚酯切片,PET)由于具备很好的力学性能和加工性能,其应用范围相当广泛,其中经过双向拉伸制备聚酯薄膜可应用在包装印刷、医疗器械、电子电器等多个领域。钛白粉作为目前世界上性能最好的一种白色颜料,广泛应用在涂料、塑料和橡胶、造纸、纺织和化学纤维、化妆品等多个行业中。其中,在制备聚酯标签薄膜过程中加入钛白粉白色颜料,可以使得制备的聚酯标签薄膜具备很好的白度和亮度。但是,如果在制备聚酯标签薄膜中直接添加钛白粉,由于钛白粉含量较高,其很难在聚酯标签薄膜中得到很好的均匀分散,容易导致聚酯标签薄膜外观白度不均匀等一系列问题。本发明先将PET和钛白粉制备成标签膜用聚酯钛白粉母粒,然后再按照一定比例添加在PET中制备聚酯标签薄膜,可以很好地解决钛白粉颜料在聚酯标签薄膜中的分散问题。而且,在制备标签膜用聚酯钛白粉母粒中添加了荧光增白剂,可以更好地提高聚酯标签薄膜的白度和亮度。
目前,国内已有钛白粉在塑料中应用的相关报道,如在CN 102627836 A中公开了一种太阳能背材基膜用母粒的制备方法,其应用于太阳能背材基膜领域,主要改善了基膜的断裂强度和水汽透过率等性能;在CN 103059520 A中公开了一种阻燃型PET白色母粒的制备方法,其主要改善了阻燃性能和力学性能。本发明制备的标签膜用聚酯钛白粉母粒可以很好解决在制备聚酯标签薄膜中直接添加钛白粉颜料而导致的分散不均匀问题,主要改善了聚酯标签薄膜的白度和亮度。
发明内容
本发明的目的是提供一种标签膜用聚酯钛白粉母粒及其制备方法。
本发明所采取的技术方案是:
一种标签膜用聚酯钛白粉母粒,其是由以下质量份的原料组成:40-80份的PET、20-60份的钛白粉、0.05-0.5份的荧光增白剂、0.1-1份的分散剂、0.2-1份的抗氧剂。
所述的PET的特性黏度范围为0.65~0.87dL/g。
所述的分散剂为乙撑双硬脂酰胺、季戊四醇硬脂酸酯、芥酸酰胺、油酸酰胺中的至少一种。
所述的抗氧剂包括受阻酚类抗氧剂与亚磷酸酯类抗氧剂。
所述的抗氧剂由主抗氧剂与辅助抗氧剂组成,所述的主抗氧剂为1010、所述的辅助抗氧剂为168。
一种标签膜用聚酯钛白粉母粒的制备方法,包括以下步骤:将各原料混合均匀,熔融挤出、造粒即可。
本发明的有益效果是:本发明一方面解决了钛白粉颜料在制备聚酯标签薄膜中的分散性问题,另一方面会使得聚酯标签薄膜的白度和亮度得到很好的提高。
具体实施方式
一种标签膜用聚酯钛白粉母粒,其是由以下质量份的原料组成:40-80份的PET、20-60份的钛白粉、0.05-0.5份的荧光增白剂、0.1-1份的分散剂、0.2-1份的抗氧剂。
所述的PET的特性黏度范围为0.65~0.87dL/g。
所述的分散剂为乙撑双硬脂酰胺、季戊四醇硬脂酸酯、芥酸酰胺、油酸酰胺中的至少一种。
所述的抗氧剂包括受阻酚类抗氧剂与亚磷酸酯类抗氧剂。
所述的抗氧剂由主抗氧剂与辅助抗氧剂组成,所述的主抗氧剂为1010、所述的辅助抗氧剂为168。
一种标签膜用聚酯钛白粉母粒的制备方法,包括以下步骤:将各原料混合均匀,熔融挤出、造粒即可。
下面结合具体实施例对本发明的配方做进一步的说明:
实施例1:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表1:
实施例2:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表2:
实施例3:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表3:
实施例4:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表4:
实施例5:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表5:
实施例6:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表6:
实施例7:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表7:
实施例8:
一种标签膜用聚酯钛白粉母粒,其配方组成如下表:
表8:
对比实施例:
对比例的配方组成如下:
表9:
实施例1~8和对比实施例按照各自的配方制得标签膜用聚酯钛白粉母粒,其测试按照GB/T标准进行测试:产品特性黏度按照GB/T 14190-2008进行测试;产品白度按照GB/T 17644-2008进行测试,测得产品的色值(L值、b值和a值),可根据此来判断产品的白度和亮度(外观色相)。其测试结果见表1。
表10 标签膜用聚酯钛白粉母粒的技术指标
表10为标签膜用聚酯钛白粉母粒的技术指标,其中从色值可以判断母粒的外观色相,L值越大母粒外观越显白相;b值越负,母粒外观越显蓝相;a值越大,母粒外观越显红相。从表10中可以看出,由于钛白粉作为白色颜料其遮盖力强,随着钛白粉含量的增加,色值L值随着增大,b值会变小,产品外观显得越白同时偏蓝相。而且在聚酯制备薄膜过程中,聚酯切片本身显黄相,根据黄蓝相互补原则,一般都会选择L值稍大和b值稍负的母粒,如此制备的聚酯标签薄膜其白度和亮度会越好。因此,本发明实施例8中,在制备标签膜用聚酯钛白粉母粒中同时加入荧光增白剂OB、荧光增白剂OB-1、荧光增白剂KSN会使得母粒的外观色相达到要求。本发明一方面解决了钛白粉颜料在制备聚酯标签薄膜中的分散性问题,另一方面会使得聚酯标签薄膜的白度和亮度得到很好的提高。
Claims (6)
1.一种标签膜用聚酯钛白粉母粒,其特征在于:其是由以下质量份的原料组成:40-80份的PET、20-60份的钛白粉、0.05-0.5份的荧光增白剂、0.1-1份的分散剂、0.2-1份的抗氧剂。
2.根据权利要求1所述的一种标签膜用聚酯钛白粉母粒,其特征在于:所述的PET的特性黏度范围为0.65~0.87dL/g。
3.根据权利要求1所述的一种标签膜用聚酯钛白粉母粒,其特征在于:所述的分散剂为乙撑双硬脂酰胺、季戊四醇硬脂酸酯、芥酸酰胺、油酸酰胺中的至少一种。
4.根据权利要求1所述的一种标签膜用聚酯钛白粉母粒,其特征在于:所述的抗氧剂包括受阻酚类抗氧剂与亚磷酸酯类抗氧剂。
5.根据权利要求1所述的一种标签膜用聚酯钛白粉母粒,其特征在于:所述的抗氧剂由主抗氧剂与辅助抗氧剂组成,所述的主抗氧剂为1010、所述的辅助抗氧剂为168。
6.权利要求1所述的一种标签膜用聚酯钛白粉母粒的制备方法,其特征在于:包括以下步骤:将各原料混合均匀,熔融挤出、造粒即可。