CN103923364A - 一种高阻燃高强度护套材料 - Google Patents

一种高阻燃高强度护套材料 Download PDF

Info

Publication number
CN103923364A
CN103923364A CN201410191764.3A CN201410191764A CN103923364A CN 103923364 A CN103923364 A CN 103923364A CN 201410191764 A CN201410191764 A CN 201410191764A CN 103923364 A CN103923364 A CN 103923364A
Authority
CN
China
Prior art keywords
parts
high strength
sheathing material
pvc
flame retardancy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410191764.3A
Other languages
English (en)
Other versions
CN103923364B (zh
Inventor
钱章兴
王兵兵
田敏
周春杰
季飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Lanhao Electric Co.,Ltd.
Original Assignee
SHANGHAI LANHAO ELECTRIC JIANGSU Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI LANHAO ELECTRIC JIANGSU Co Ltd filed Critical SHANGHAI LANHAO ELECTRIC JIANGSU Co Ltd
Priority to CN201410191764.3A priority Critical patent/CN103923364B/zh
Publication of CN103923364A publication Critical patent/CN103923364A/zh
Application granted granted Critical
Publication of CN103923364B publication Critical patent/CN103923364B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明所揭示的一种高阻燃高强度护套材料，其制成有效成分所涉及的原料及配重比为：CR/PVC100份；氧化锌3.5～5份；氧化镁4～6份；NA-22 0.5～1.5份；TMTD 0.5～1.5份；DM 0.5～1.5份；硬脂酸1～3份；防老剂2～4份；滑石粉10～30份；陶土30～50份；炭黑10～15份；白炭黑10～15份；偶联剂0.5～1份；石蜡3～6份；阻燃剂8～15份。本发明所揭示的一种高阻燃高强度护套材料，采用的CR/PVC共沉胶，其采用乳液共聚的方法，使CR与PVC在分子水平有很好的相互作用，其优势远超过普通的物理共混方式，并且加工工艺性能优异，所得产品强度高，阻燃性能更佳。

Description

一种高阻燃高强度护套材料
技术领域
本发明涉及一种护套材料，尤其涉及一种高强度、高阻燃性能的护套材料。 
背景技术
目前应用于电缆护套的胶种主要有氯化聚乙烯以及氯丁橡胶两种，氯化聚乙烯价格便宜，老化性能、阻燃性能、耐油性及加工性能均较好，但弹性、撕裂性能较差，长期应用过程中弹性恢复慢，并且护套极易出现撕裂破损而失去对电缆的保护作用。 
氯丁橡胶综合性能比较优异，但也存在焦烧时间短，混炼过程中粘辊严重等缺点，在混炼过程中不仅要十分注意温度的控制，同时劳动强度高，危险系数大，生产效率低下，部分厂家采用CR与CM机械共混的方式改进加工性能，但由此得到的产品机械性能会明显降低。 
发明内容
本发明的目的就是克服上述背景技术中存在的一些缺点，提供一高阻燃高强度护套材料，利用氯丁橡胶特有的综合性能，同时改善氯丁橡胶在加工中存在的严重粘辊及极易焦烧等现状，采用CR/PVC替代CR橡胶作为电缆护套的主体材料，在成本降低的同时明显改善了加工工艺性能，单位时间产出得到提高，并且所得成品胶具有强度高，定伸应力大，阻燃性能更加优异等特点。 
为达到上述目的，本发明所揭示的一种高阻燃高强度护套材料，其制成有效成分所涉及的原料及配重比为： 
CR/PVC                 100份；
氧化锌                  3.5~5份；
氧化镁                  4~6份；
NA-22                  0.5~1.5份；
TMTD                  0.5~1.5份；
DM                     0.5~1.5份；
硬脂酸                  1~3份；
防老剂                  2~4份；
滑石粉                  10~30份；
陶土                    30~50份；
炭黑                    10~15份；
白炭黑                  10~15份；
偶联剂                  0.5~1份；
石蜡                    3~6份；
阻燃剂                  8~15份。
作为优选，用ODA作为防老剂。 
作为优选，用KH-550作为偶联剂。 
作为优选，用三氧化二锑与十溴联苯醚协同作为阻燃剂。 
与现有技术相比，本发明所揭示的一种高阻燃高强度护套材料，具有如下优点： 
与现有氯丁橡胶加工工艺性能相比，所采用CR/PVC材料易于加工，在更强的剪切力、更快的牵引速度下也不会出现粘辊现象，加快生产效率的同时降低了操作危险性。
与现有氯丁橡胶成品胶性能相比，所采用CR/PVC材料定伸应力明显增大，提升了对电缆的保护性能，延长电缆的使用寿命。 
与现有氯丁橡胶成品相比，所采用CR/PVC材料阻燃性能更加优异，这对有阻燃性能要求的电缆护套至关重要。 
与现有氯丁橡胶成品相比，所采用CR/PVC材料所得电缆表面光滑度得到有效改善，提高电缆外观认可度。 
本发明所采用的CR/PVC共沉胶，其采用乳液共聚的方法，使CR与PVC在分子水平有很好的相互作用，其优势远超过普通的机械共混方式，并且加工工艺性能优异，所得产品强度高，阻燃性能更佳。 
具体实施例
下面将对本发明的技术方案进行清楚、完整的描述。 
具体实施例1 
本发明所揭示的一种高阻燃高强度护套材料，选用CR/PVC100份，氧化镁4份，TMTD 0.5份，DM 1.5份，硬脂酸1份，ODA 2份，滑石粉10份，陶土50份，炭黑10份，白炭黑15份，KH-550 1份，石蜡3份，阻燃剂8份。
将上述材料投入密炼机中混炼5~7min，提起上顶栓进行扫料，重复两次，然后继续混炼直至温度显示105℃将混炼胶排放至开炼机翻包混炼，然后不开条出片，冷却后重新投入密炼机加氧化锌3.5份及NA-22 1.5份，混炼时间1min，在三辊碾页机进行开条出片，成品放置16小时之后投入连硫车间使用，在电缆挤出过程中，挤出机温度设定为65~45℃，硫化蒸汽压力1MPa，牵引速度3.5m/min得到成品。 
具体实施例2 
本发明所揭示的一种高阻燃高强度护套材料，选用CR/PVC100份，氧化镁5份，TMTD 1份，DM0.8份，硬脂酸2份，ODA 3份，滑石粉20份，陶土40份，炭黑13份，白炭黑12份，KH-550 0.8份，石蜡4份，阻燃剂10份。
将上述材料投入密炼机中混炼5~7min，提起上顶栓进行扫料，重复两次，然后继续混炼直至温度显示105℃将混炼胶排放至开炼机翻包混炼，然后不开条出片，冷却后重新投入密炼机加氧化锌4份及NA-22 1份，混炼时间1min，在三辊碾页机进行开条出片，成品放置16小时之后投入连硫车间使用，在电缆挤出过程中，挤出机温度设定为65~45℃，硫化蒸汽压力1.1MPa，牵引速度4m/min得到成品。 
具体实施例3 
本发明所揭示的一种高阻燃高强度护套材料，选用CR/PVC100份，氧化镁6份，TMTD 1.5份，DM 0.5份，硬脂酸3份，ODA 4份，滑石粉30份，陶土30份，炭黑15份，白炭黑10份，KH-550 0.5份，石蜡6份，阻燃剂15份。
将上述材料投入密炼机中混炼5~7min，提起上顶栓进行扫料，重复两次，然后继续混炼直至温度显示105℃将混炼胶排放至开炼机翻包混炼，然后不开条出片，冷却后重新投入密炼机加氧化锌5份及NA-22 0.5份，混炼时间1min，在三辊碾页机进行开条出片，成品放置16小时之后投入连硫车间使用，在电缆挤出过程中，挤出机温度设定为65~45℃，硫化蒸汽压力1.2MPa，牵引速度4.5m/min得到成品。 
上述三个实施例中配比完成的成品各项性能与国标及现有技术对比如表1所示： 
表1

Claims (4)

1. 一种高阻燃高强度护套材料，其特征在于：其制成有效成分所涉及的原料及配重比为：
CR/PVC                 100份；
氧化锌                  3.5~5份；
氧化镁                  4~6份；
NA-22                  0.5~1.5份；
TMTD                  0.5~1.5份；
DM                     0.5~1.5份；
硬脂酸                  1~3份；
防老剂                  2~4份；
滑石粉                  10~30份；
陶土                    30~50份；
炭黑                    10~15份；
白炭黑                  10~15份；
偶联剂                  0.5~1份；
石蜡                    3~6份；
阻燃剂                  8~15份。
2. 根据权利要求1所述的一种高阻燃高强度护套材料，其特征在于：所述防老剂为ODA。
3. 根据权利要求1所述的一种高阻燃高强度护套材料，其特征在于：所述偶联剂为KH-550。
4. 根据权利要求1所述的一种高阻燃高强度护套材料，其特征在于：所述阻燃剂为三氧化二锑和十溴联苯醚。
CN201410191764.3A 2014-05-08 2014-05-08 一种高阻燃高强度护套材料 Active CN103923364B (zh)