CN103910988A - Modified chlorinated polyether plastic - Google Patents
Modified chlorinated polyether plastic Download PDFInfo
- Publication number
- CN103910988A CN103910988A CN201410176379.1A CN201410176379A CN103910988A CN 103910988 A CN103910988 A CN 103910988A CN 201410176379 A CN201410176379 A CN 201410176379A CN 103910988 A CN103910988 A CN 103910988A
- Authority
- CN
- China
- Prior art keywords
- accounts
- plastics
- modified chlorinated
- agent
- penton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a modified chlorinated polyether which is prepared from chlorinated polyether plastic and additives, wherein the additives comprise an antioxidant, a corrosion inhibitor, a weather-resistant agent, a filler and a coupling agent; the antioxidant is butylated hydroxytoluene; the corrosion inhibitor is polyvinyl chloride plastic; the weather-resistant agent is pentaerythritol tetra[beta-(3,5-di-tert-butyl-4-hydroxyphenyl)]propionate; the filler is glass powder; and the coupling agent is aminopropyltriethoxysilane. The multiple additives are added into the chlorinated polyether plastic, so that the prepared modified chlorinated polyether plastic has the advantages of high quality, excellent oxidation resistance, excellent corrosion resistance, excellent weather resistance, excellent mechanical strength, excellent hardness and lower production cost.
Description
Technical field
The present invention relates to plastics, particularly relate to a kind of modified chlorinated polyethers plastics.
Background technology
Penton plastics are moulding compound and the goods thereof that make take oxetane resin as base-material.Penton is the good thermoplastics of processibility, and goods seldom have cracking phenomena.The method machine-shapings such as available injection moulding, extrusion molding, molding make sheet material, sheet material, tubing, bar and baroque thin wall parts and various metal inserts etc.Also can carry out secondary processing.Its goods are widely used in machinery, electronics, the aspects such as chemical industry, medicine equipment, household utensils, office accommodations.Along with scientific and technological development, existing penton plastics cannot meet the user demand of product at aspects such as quality, oxidation-resistance, erosion resistance, weathering resistance, physical strength, hardness, and production cost is also difficult to estimate.
Summary of the invention
The technical problem that the present invention mainly solves is to provide that a kind of quality is good, good in oxidation resistance, good corrosion resistance, good weatherability, physical strength is high, hardness is high, production cost is lower modified chlorinated polyethers plastics.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of modified chlorinated polyethers plastics are provided, made by penton plastics and additive, described additive comprises antioxidant, corrosion-resistant agent, weather resisting agent, weighting agent and coupling agent, described antioxidant is Yoshinox BHT, described corrosion-resistant agent is igelite, described weather resisting agent is four [β-(3, 5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester, described weighting agent is glass powder, described coupling agent is aminopropyl triethoxysilane, the shared weight percent of the each composition of described modified chlorinated polyethers plastics is respectively penton plastics and accounts for 81.5%-86.1%, Yoshinox BHT accounts for 1.3%-2.2%, igelite accounts for 2.1%-2.9%, four [β-(3, 5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester accounts for 1.5%-2.4%, glass powder accounts for 7.2%-8.3%, aminopropyl triethoxysilane accounts for 1.8%-2.7%.
In a preferred embodiment of the present invention, the described shared weight percent of the each composition of modified chlorinated polyethers plastics is specially penton plastics and accounts for 85.6%, Yoshinox BHT accounts for 1.4%, igelite accounts for 2.2%, four [β-(3,5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester accounts for 1.6%, and glass powder accounts for 7.3%, and aminopropyl triethoxysilane accounts for 1.9%.
In a preferred embodiment of the present invention, the described shared weight percent of the each composition of modified chlorinated polyethers plastics is specially penton plastics and accounts for 82.1%, Yoshinox BHT accounts for 2.1%, igelite accounts for 2.8%, four [β-(3,5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester accounts for 2.3%, and glass powder accounts for 8.1%, and aminopropyl triethoxysilane accounts for 2.6%.
The invention has the beneficial effects as follows: the modified chlorinated polyethers plastics of the present invention by adding multiple additives in penton plastics, make the modified chlorinated polyethers plastic quality that makes good, there is excellent oxidation-resistance, erosion resistance, weathering resistance, physical strength and hardness, and production cost is lower simultaneously.
Embodiment
To the technical scheme in the embodiment of the present invention be clearly and completely described below, obviously, described embodiment is only a part of embodiment of the present invention, rather than whole embodiment.Based on the embodiment in the present invention, those of ordinary skills, not making all other embodiment that obtain under creative work prerequisite, belong to the scope of protection of the invention.
A kind of modified chlorinated polyethers plastics, made by penton plastics and additive, described additive comprises antioxidant, corrosion-resistant agent, weather resisting agent, weighting agent and coupling agent, described antioxidant is Yoshinox BHT, described corrosion-resistant agent is igelite, described weather resisting agent is four [β-(3, 5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester, described weighting agent is glass powder, described coupling agent is aminopropyl triethoxysilane, the shared weight percent of the each composition of described modified chlorinated polyethers plastics is respectively penton plastics and accounts for 81.5%-86.1%, Yoshinox BHT accounts for 1.3%-2.2%, igelite accounts for 2.1%-2.9%, four [β-(3, 5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester accounts for 1.5%-2.4%, glass powder accounts for 7.2%-8.3%, aminopropyl triethoxysilane accounts for 1.8%-2.7%.
Further, the described shared weight percent of the each composition of modified chlorinated polyethers plastics is specially penton plastics and accounts for 85.6%, Yoshinox BHT accounts for 1.4%, igelite accounts for 2.2%, four [β-(3,5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester accounts for 1.6%, and glass powder accounts for 7.3%, and aminopropyl triethoxysilane accounts for 1.9%.
Further, the described shared weight percent of the each composition of modified chlorinated polyethers plastics is specially penton plastics and accounts for 82.1%, Yoshinox BHT accounts for 2.1%, igelite accounts for 2.8%, four [β-(3,5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester accounts for 2.3%, and glass powder accounts for 8.1%, and aminopropyl triethoxysilane accounts for 2.6%.
The beneficial effect of polyetherimide plastics of the present invention is: the modified chlorinated polyethers plastics of the present invention by adding multiple additives in penton plastics, make the modified chlorinated polyethers plastic quality that makes good, there is excellent oxidation-resistance, erosion resistance, weathering resistance, physical strength and hardness, and production cost is lower simultaneously.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. modified chlorinated polyethers plastics, made by penton plastics and additive, it is characterized in that: described additive comprises antioxidant, corrosion-resistant agent, weather resisting agent, weighting agent and coupling agent, described antioxidant is Yoshinox BHT, described corrosion-resistant agent is igelite, described weather resisting agent is four [β-(3, 5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester, described weighting agent is glass powder, described coupling agent is aminopropyl triethoxysilane, the shared weight percent of the each composition of described modified chlorinated polyethers plastics is respectively penton plastics and accounts for 81.5%-86.1%, Yoshinox BHT accounts for 1.3%-2.2%, igelite accounts for 2.1%-2.9%, four [β-(3, 5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester accounts for 1.5%-2.4%, glass powder accounts for 7.2%-8.3%, aminopropyl triethoxysilane accounts for 1.8%-2.7%.
2. modified chlorinated polyethers plastics according to claim 1, it is characterized in that, the described shared weight percent of the each composition of modified chlorinated polyethers plastics is specially penton plastics and accounts for 85.6%, Yoshinox BHT accounts for 1.4%, igelite accounts for 2.2%, four [β-(3,5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester and accounts for 1.6%, glass powder accounts for 7.3%, and aminopropyl triethoxysilane accounts for 1.9%.
3. modified chlorinated polyethers plastics according to claim 1, it is characterized in that, the described shared weight percent of the each composition of modified chlorinated polyethers plastics is specially penton plastics and accounts for 82.1%, Yoshinox BHT accounts for 2.1%, igelite accounts for 2.8%, four [β-(3,5-di-t-butyl-4 hydroxy phenyl) propionic acid] pentaerythritol ester and accounts for 2.3%, glass powder accounts for 8.1%, and aminopropyl triethoxysilane accounts for 2.6%.