CN107141641A - A kind of formula of PVC - Google Patents
A kind of formula of PVC Download PDFInfo
- Publication number
- CN107141641A CN107141641A CN201710374888.9A CN201710374888A CN107141641A CN 107141641 A CN107141641 A CN 107141641A CN 201710374888 A CN201710374888 A CN 201710374888A CN 107141641 A CN107141641 A CN 107141641A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- formula
- agent
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of formula of PVC, it is made from the following raw materials in parts by weight：80 100 parts of polyvinyl chloride resin, 35 parts of calcium stearate, 46 parts of zinc oxide, 68 parts of HMPA, 16 20 parts of alcohol-soluble resin, 12 parts of anti-impact agent, 12 parts of toughener, 23 parts of chlorinated paraffin, 1.5 2.5 parts of auxiliary agent.The beneficial effects of the invention are as follows：The PVC manufactured using the formula can strengthen erosion-resisting characteristics and intensity, be adapted to popularization and application.
Description
Technical field
The present invention relates to plastic cement pipeline technical field, and in particular to a kind of formula of PVC.
Background technology
PVC is a kind of rather popular in the world today and wide variety of synthetic material.The main component of PVC is poly-
Vinyl chloride is mainly used in water supply and sewage work, it is necessary to it is possible to additionally incorporate other compositions to strengthen its heat resistance, toughness, ductility etc..
PVC has good acidproof, alkaline-resisting, corrosion resistance, and intensity is high, but erosion-resisting characteristics is poor.
The content of the invention
It is an object of the invention to provide a kind of formula of PVC, the PVC manufactured using the formula can be with
Strengthen erosion-resisting characteristics and intensity.
To reach above-mentioned purpose, the present invention is adopted the following technical scheme that：A kind of formula of PVC, by following parts by weight
Raw material be made：80-100 parts of polyvinyl chloride resin, 3-5 parts of calcium stearate, 4-6 parts of zinc oxide, 6-8 parts of HMPA, alcohol is molten
Property 16-20 parts of resin, 1-2 parts of anti-impact agent, 1-2 parts of toughener, 2-3 parts of chlorinated paraffin, 1.5-2.5 parts of auxiliary agent.
Further, it is made up of following optimal proportion raw material：90 parts of polyvinyl chloride resin, 4 parts of calcium stearate, 5 parts of zinc oxide, six
7 parts of methyl phosphoric triamide, 18 parts of alcohol-soluble resin, 1.4 parts of anti-impact agent, 1.4 parts of toughener, 2.6 parts of chlorinated paraffin, 2 parts of auxiliary agent.
Further, auxiliary agent is one or both of plasticizer, wetting agent, stabilizer and coalescents composition described above.
The beneficial effects of the invention are as follows：The PVC manufactured using the formula can strengthen erosion-resisting characteristics and intensity,
Because with the addition of HMPA, cost is reduced while the antioxygenic property of PVC is greatly improved, being adapted to promote
Using.
Embodiment
With reference to specific embodiment, the invention will be further described.
Embodiment 1：A kind of formula of PVC, is made from the following raw materials in parts by weight：80 parts of polyvinyl chloride resin, calcium stearate
3 parts, 4 parts of zinc oxide, 6 parts of HMPA, 16 parts of alcohol-soluble resin, 1 part of anti-impact agent, 1 part of toughener, chlorinated paraffin 2
Part, 1.5 parts of auxiliary agent.
Auxiliary agent is one or both of plasticizer, wetting agent, stabilizer and coalescents composition described above.
Embodiment 2：A kind of formula of PVC, is made from the following raw materials in parts by weight：100 parts of PVC resins, it is stearic
Sour 5 parts of calcium, 6 parts of zinc oxide, 8 parts of HMPA, 20 parts of alcohol-soluble resin, 2 parts of anti-impact agent, 2 parts of toughener, chlorination stone
3 parts of wax, 2.5 parts of auxiliary agent.
Auxiliary agent is one or both of plasticizer, wetting agent, stabilizer and coalescents composition described above.
Embodiment 3, is most highly preferred embodiment of the invention：A kind of formula of PVC, by the raw material system of following parts by weight
Into：90 parts of polyvinyl chloride resin, 4 parts of calcium stearate, 5 parts of zinc oxide, 7 parts of HMPA, 18 parts of alcohol-soluble resin, anti-impact agent
1.4 parts, 1.4 parts of toughener, 2.6 parts of chlorinated paraffin, 2 parts of auxiliary agent.
Auxiliary agent is one or both of plasticizer, wetting agent, stabilizer and coalescents composition described above.
Claims (3)
1. a kind of formula of PVC, it is characterised in that：It is made from the following raw materials in parts by weight：80-100 parts of polyvinyl chloride resin, firmly
3-5 parts of resin acid calcium, 4-6 parts of zinc oxide, 6-8 parts of HMPA, 16-20 parts of alcohol-soluble resin, 1-2 parts of anti-impact agent increases
Tough dose 1-2 parts, 2-3 parts of chlorinated paraffin, 1.5-2.5 parts of auxiliary agent.
2. a kind of formula of PVC according to claim 1, it is characterised in that：It is made up of following optimal proportion raw material：
90 parts of polyvinyl chloride resin, 4 parts of calcium stearate, 5 parts of zinc oxide, 7 parts of HMPA, 18 parts of alcohol-soluble resin, anti-impact agent 1.4
Part, 1.4 parts of toughener, 2.6 parts of chlorinated paraffin, 2 parts of auxiliary agent.
3. a kind of formula of PVC according to claim 1, it is characterised in that：The auxiliary agent is plasticizer, wetting
One or both of agent, stabilizer and coalescents composition described above.