CN103897637A - High-performance polyisobutene rubber adhesive - Google Patents
High-performance polyisobutene rubber adhesive Download PDFInfo
- Publication number
- CN103897637A CN103897637A CN201410146534.5A CN201410146534A CN103897637A CN 103897637 A CN103897637 A CN 103897637A CN 201410146534 A CN201410146534 A CN 201410146534A CN 103897637 A CN103897637 A CN 103897637A
- Authority
- CN
- China
- Prior art keywords
- accounts
- agent
- rubber
- tackiness agent
- aging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-performance polyisobutene rubber adhesive comprising polyisobutene rubber, a curing agent, an anti-aging agent, a coupling agent, a toughening agent and a thinner, wherein the curing agent is polyethylene polyamine, the anti-aging agent is 2,6-tert-butyl-4-methylphenol, the coupling agent is vinyl triethoxy silane, the toughening agent is polyvinyl butyral, and the thinner is glycerol epoxy resin. The product is prepared by adopting the polyisobutene rubber and five additives namely the curing agent, the anti-aging agent, the coupling agent, the toughening agent and the thinner; the prepared adhesive has the characteristics of high viscosity strength, good toughness, anti-aging property, convenience in processing, low production cost and long service life.
Description
Technical field
The present invention relates to Chemicals, be specifically related to a kind of high-performance poly isobutene rubber tackiness agent.
Background technology
At present, the adhesive tape using on market is different by glue paste kind, and use field is also different.The raw material types of the glue paste of existing use is various, and the function possessing is also different.Polyisobutylene rubber tackiness agent has use in a lot of fields, but existing polyisobutylene rubber tackiness agent exists very large deficiency, as adhesive strength, easily aging in carrying and storage process, the storage time is short, and work-ing life is short, complete processing is loaded down with trivial details, and production cost is high, and result of use is poor.
Summary of the invention
The object of the present invention is to provide that a kind of adhesive strength is high, good toughness, anti-aging, easy to process, production cost is low, the high-performance poly isobutene rubber tackiness agent of long service life.
Technical scheme of the present invention is, a kind of high-performance poly isobutene rubber tackiness agent, comprise polyisobutylene rubber, solidifying agent, anti-aging agent, coupling agent, toughner and thinner, described solidifying agent is polyethylene polyamine, described anti-aging agent is 2, tri-grades of butyl-4-methylphenols of 6-, described coupling agent is vinyltriethoxysilane, described toughner is polyvinyl butyral acetal, described thinner is glycerol epoxy resin, the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is respectively: described polyisobutylene rubber accounts for 68.6%-73.1%, described polyethylene polyamine accounts for 8.6%-9.5%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 2.3%-3.2%, described vinyltriethoxysilane accounts for 1.9%-2.8%, described polyvinyl butyral acetal accounts for 1.4%-2.3%, described glycerol epoxy resin accounts for 12.7%-13.6%.
In a preferred embodiment of the present invention, the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is specially: described polyisobutylene rubber accounts for 72.5%, described polyethylene polyamine accounts for 8.7%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 2.4%, described vinyltriethoxysilane accounts for 2.1%, and described polyvinyl butyral acetal accounts for 1.5%, and described glycerol epoxy resin accounts for 12.8%.
In a preferred embodiment of the present invention, the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is specially: described polyisobutylene rubber accounts for 69.1%, described polyethylene polyamine accounts for 9.4%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 3.1%, described vinyltriethoxysilane accounts for 2.7%, and described polyvinyl butyral acetal accounts for 2.2%, and described glycerol epoxy resin accounts for 13.5%.
Of the present invention is a kind of high-performance poly isobutene rubber tackiness agent, this product adopts polyisobutylene rubber and solidifying agent, anti-aging agent, coupling agent, toughner and five kinds of additives of thinner to make, and the glue paste making has that adhesive strength is high, good toughness, anti-aging, easy to process, production cost is low, the feature of long service life.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
Of the present invention is a kind of high-performance poly isobutene rubber tackiness agent, comprise polyisobutylene rubber, solidifying agent, anti-aging agent, coupling agent, toughner and thinner, described solidifying agent is polyethylene polyamine, described anti-aging agent is 2, tri-grades of butyl-4-methylphenols of 6-, described coupling agent is vinyltriethoxysilane, described toughner is polyvinyl butyral acetal, described thinner is glycerol epoxy resin, the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is respectively: described polyisobutylene rubber accounts for 68.6%-73.1%, described polyethylene polyamine accounts for 8.6%-9.5%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 2.3%-3.2%, described vinyltriethoxysilane accounts for 1.9%-2.8%, described polyvinyl butyral acetal accounts for 1.4%-2.3%, described glycerol epoxy resin accounts for 12.7%-13.6%.
Further, the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is specially: described polyisobutylene rubber accounts for 72.5%, described polyethylene polyamine accounts for 8.7%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 2.4%, described vinyltriethoxysilane accounts for 2.1%, and described polyvinyl butyral acetal accounts for 1.5%, and described glycerol epoxy resin accounts for 12.8%.
Further, the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is specially: described polyisobutylene rubber accounts for 69.1%, described polyethylene polyamine accounts for 9.4%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 3.1%, described vinyltriethoxysilane accounts for 2.7%, and described polyvinyl butyral acetal accounts for 2.2%, and described glycerol epoxy resin accounts for 13.5%.
Carry out proportioning by each composition Different Weight per-cent, the product performance height obtaining is differed.
Of the present invention is a kind of high-performance poly isobutene rubber tackiness agent, this product adopts polyisobutylene rubber and solidifying agent, anti-aging agent, coupling agent, toughner and five kinds of additives of thinner to make, and the glue paste making has that adhesive strength is high, good toughness, anti-aging, easy to process, production cost is low, the feature of long service life.
The foregoing is only the specific embodiment of the present invention; but protection scope of the present invention is not limited to this; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; the variation that can expect without creative work or replacement, within all should being encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (3)
1. a high-performance poly isobutene rubber tackiness agent, it is characterized in that: comprise polyisobutylene rubber, solidifying agent, anti-aging agent, coupling agent, toughner and thinner, described solidifying agent is polyethylene polyamine, described anti-aging agent is 2, tri-grades of butyl-4-methylphenols of 6-, described coupling agent is vinyltriethoxysilane, described toughner is polyvinyl butyral acetal, described thinner is glycerol epoxy resin, the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is respectively: described polyisobutylene rubber accounts for 68.6%-73.1%, described polyethylene polyamine accounts for 8.6%-9.5%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 2.3%-3.2%, described vinyltriethoxysilane accounts for 1.9%-2.8%, described polyvinyl butyral acetal accounts for 1.4%-2.3%, described glycerol epoxy resin accounts for 12.7%-13.6%.
2. high-performance poly isobutene rubber tackiness agent according to claim 1, it is characterized in that: the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is specially: described polyisobutylene rubber accounts for 72.5%, described polyethylene polyamine accounts for 8.7%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 2.4%, described vinyltriethoxysilane accounts for 2.1%, and described polyvinyl butyral acetal accounts for 1.5%, and described glycerol epoxy resin accounts for 12.8%.
3. high-performance poly isobutene rubber tackiness agent according to claim 1, it is characterized in that: the shared weight percent of the each composition of described high-performance poly isobutene rubber tackiness agent is specially: described polyisobutylene rubber accounts for 69.1%, described polyethylene polyamine accounts for 9.4%, described 2, tri-grades of butyl-4-methylphenols of 6-account for 3.1%, described vinyltriethoxysilane accounts for 2.7%, and described polyvinyl butyral acetal accounts for 2.2%, and described glycerol epoxy resin accounts for 13.5%.