CN103897278A - 一种改性水玻璃防火液 - Google Patents
一种改性水玻璃防火液 Download PDFInfo
- Publication number
- CN103897278A CN103897278A CN201410151340.4A CN201410151340A CN103897278A CN 103897278 A CN103897278 A CN 103897278A CN 201410151340 A CN201410151340 A CN 201410151340A CN 103897278 A CN103897278 A CN 103897278A
- Authority
- CN
- China
- Prior art keywords
- water glass
- percent
- fire
- modified water
- fireproof liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种改性水玻璃防火液,该防火液由硅溶胶5-50%,钠基水玻璃10-50%,氢氧化钾2-20%,氢氧化锂0.1-5%,氧化镧0.001-0.1%,水20-50%组成。本发明可用于提高聚苯板、挤塑板等有机保温材料的防火性能,提高材料强度,同时具有防水防潮的性能,也可用于锯末板、稻草板等木质板材的防火。
Description
技术领域
本发明属于一种防火添加剂,可用于建筑材料和保温材料的基体防火和表面防火。
技术背景
目前我国建筑市场上普遍采用聚苯乙烯泡沫(EPS、XPS)聚氨酯硬泡体(PU)等有机保温材料,这种材料具有轻质、保温效果好、施工方便等优点,但是这种材料防火性能较差,易燃、易老化,在发生建筑火灾时,这种材料往往不能阻止火焰的蔓延,并且本身会融化,产生有毒的烟雾,危害大,扑救难度大。
近年来,人们采用各种方法试图提高这类材料的防火性能,比如在材料表面涂覆无机防火材料,应用最多的就是聚苯板薄抹灰系统,但是这种涂覆的灰浆极易脱落,导致保温材料老化,同时起不到防火的作用。还有一种方法是向保温材料内部加入阻燃剂,在发生火灾时,一定程度上可以降低聚苯板等材料的易燃性,但是这种阻燃剂易挥发,使用寿命短,不能与建筑物的寿命保持同步,也就是说,只能在竣工的初期保有防火效果,几年之后就和普通的聚苯板没有区别。
发明内容
本发明所要解决的技术问题是各种有机保温材料在使用中出现的防火性能差、防水防潮性能差,使用寿命短,材料强度不高的问题。为达到上述目标,本发明采用下述技术方案实现:
一种改性水玻璃防火液,按照质量分数配制而成:硅溶胶5-50%,钠基水玻璃10-50%,氢氧化钾2-20%,氢氧化锂0.1-5%,氧化镧0.001-0.1%,水20-50%。按照以上配比,改性水玻璃防火液制备步骤为:
a.开动搅拌机,加入水玻璃,水;
b.搅拌均匀后,依次加入硅溶胶、氢氧化钾、氢氧化锂、氧化镧;
c.搅拌均匀后,制备完成。
本发明所能达到的有益效果为:聚苯板等有机保温材料在加入本发明所述的防火液后,防火性能达到A2级标准,提高材料的强度,同时具有防水防潮的性能,大大提高保温材料的使用寿命,与建筑物的使用年限保持同步。
具体实施方式
下面结合具体实施例对本发明进行进一步说明。
实施例1
开动搅拌器,将20份钠基水玻璃加入搅拌器中,然后加入30份的水,搅拌均匀后,依次加入10份硅溶胶,5份氢氧化钾,1份氢氧化锂,0.01份氧化镧,然后再加入适量水直到整个溶液达到100份质量。搅拌10分钟后,防火液制备完成。
将聚苯板或挤塑板放入方形器皿中,加入35%的硅溶胶,密封后抽气至真空度-0.07Mpa,5分钟后取出;将制备好的防火液与水按照1∶2的比例配制,加入另一个方形器皿中,将从硅溶胶中取出的聚苯板或挤塑板放入,密封后抽气至真空度-0.07Mpa,浸泡5分钟后取出,用80℃的热风烘干即可。成品达到A2级防火标准,750℃燃烧60分钟无滴落物,质量减少≤35%,容重>100Kg/m3,强度>200KPa。
实施例2
开动搅拌器,将25份钠基水玻璃加入搅拌器中,然后加入35份的水,搅拌均匀后,依次加入8份硅溶胶,5份氢氧化钾,0.5份氢氧化锂,0.01份氧化镧,再加入适量水直到整个溶液达到100份质量。搅拌10分钟后,防火液制备完成。
将制备好的防火液与水按照1∶2的比例配制,加入方形密闭器皿中,取锯末板或稻草板等板材放入器皿,密封后使用抽气机抽气,使得器皿中的真空度达到-0.07MPa,浸泡10分钟后取出,用80℃的热风烘干即可。
Claims (2)
1.一种改性水玻璃防火液,其特征在于该防火液由以下成分按照质量分数配制而成:硅溶胶5-50%,钠基水玻璃10-50%,氢氧化钾2-20%,氢氧化锂0.1-5%,氧化镧0.001-0.1%,水20-50%。
2.根据权利要求1所述的改性水玻璃防火液的制备方法,其特征在于制备步骤为:
a.开动搅拌机,加入水玻璃,水
b.搅拌均匀后,依次加入硅溶胶、氢氧化钾、氢氧化锂、氧化镧
c.搅拌均匀后,制备完成。