CN103882603A - Antibacterial, deodorant and moisture-absorbing child bed sheet shell fabric and production technology thereof - Google Patents

Antibacterial, deodorant and moisture-absorbing child bed sheet shell fabric and production technology thereof Download PDF

Info

Publication number
CN103882603A
CN103882603A CN201410144519.7A CN201410144519A CN103882603A CN 103882603 A CN103882603 A CN 103882603A CN 201410144519 A CN201410144519 A CN 201410144519A CN 103882603 A CN103882603 A CN 103882603A
Authority
CN
China
Prior art keywords
fabric
temperature
antibacterial
control
oxygen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410144519.7A
Other languages
Chinese (zh)
Other versions
CN103882603B (en
Inventor
陈晨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Shuzi Textile Technology Co ltd
Original Assignee
That Trade Co Ltd Of Nantong Derby
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by That Trade Co Ltd Of Nantong Derby filed Critical That Trade Co Ltd Of Nantong Derby
Priority to CN201410144519.7A priority Critical patent/CN103882603B/en
Priority to PCT/CN2014/076989 priority patent/WO2015154322A1/en
Publication of CN103882603A publication Critical patent/CN103882603A/en
Application granted granted Critical
Publication of CN103882603B publication Critical patent/CN103882603B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses antibacterial, deodorant and moisture-absorbing child bed sheet shell fabric. The shell fabric is formed by weaving weft yarn and warp yarn by the ratio of 1:2 in a twilled mode, wherein the warp yarn is formed by blending super-absorbent hollow polyester fibers and bamboo pulp fibers by the ratio of 1:1, and lycra fibers are adopted as the weft yarn. The production technology includes the steps of weaving, singeing, desizing, oxygen bleaching, pretreating, dyeing, soaping, mercerizing, tentering and shaping, preshrinking and detecting. The antibacterial, deodorant and moisture-absorbing child bed sheet shell fabric absorbs water, dries quickly and is breathable, moisture permeable, uvioresistant, antibacterial, deodorant and resistant to acid, alkaline, sweat, dry cleaning and abrasion, and service life is prolonged.

Description

A kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof
Technical field
The present invention relates to a kind of fabric and production technology, relate in particular to a kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof.
Background technology
On current market, home textile product is a lot, and recent years, the growth that explosion type has appearred in industry was at home spun by man, few but domestic market is directed to infant's bed necessaries exploitation specially.
 
Summary of the invention
Goal of the invention: the present invention mainly provides a kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof.
Technical scheme: a kind of antibacterial and deodouring moisture absorption crib one side material, adopt warp thread and weft yarn 1:2 twill weave to form, described warp thread be high absorbent hollow PET fiber and bamboo pulp fiber with 1:1 blending, described weft yarn is Lycra fiber.
Described bamboo pulp fiber is 40 ~ 60.
Described Lycra is 40 ~ 60.
A production technology for antibacterial and deodouring moisture absorption crib one side material, specifically comprises the following steps:
A, weaving process: using high absorbent hollow PET fiber and bamboo pulp fibre blending as warp thread, using Lycra fiber as weft yarn, and warp thread and weft yarn are with 1:2 twill weave;
B, singeing: by the cloth of having weaved in step a with two positive one or two counter singing, control cloth speed 80 ~ 100m/min, fabric and reducing flame distance 1 ~ 1.2cm, fabric and copper coin distance 0.5 ~ 0.8cm, fabric and cylinder distance 5 ~ 7cm, and to control the rank of singing be 4 ~ 5 grades;
C, desizing: the fabric of having singed in step b is entered into 1 ~ 2min in hot water, then take out maceration enzyme liquid again, fixedly roll enzyme temperature 60 C, then take out and be incubated the 2h that banks up, controlling the temperature of fixedly banking up is 55 ℃, and PH is 7, NaCL5g/L, JFC1g/L, bath raio is 1:20;
D, oxygen bleaching process: the fabric that step c destarch is completed carries out oxygen and floats processing, wherein uses alkali 20-30kg ℃ .t -1, use oxygen 12-15kg.t -1, and control oxygen and press 1.0mpa, oxygen floats 95 ~ 110 ℃ of temperature, and oxygen floats time 40 ~ 60min;
E, pre-treatment process: because bamboo pulp fiber is more responsive to alkali and temperature, so need to carry out pre-treatment before to high absorbent hollow PET fiber and bamboo pulp fibre blending textile dyeing, and control and touch concentration of lye and temperature, in case bamboo fibre is impaired, concrete treatment process is that fabric is put into bath raio is that the concentration of 1:25 is that 30% hydrogen peroxide 5-6 S/L and sodium metasilicate l5-2 t/L mixed liquor carry out pre-treatment 40min, control mixed liquor PH=11 ~ 12, temperature is 90 ~ 95 ℃;
F, dyeing: adopt high temperature one to bathe one-step method, concrete technology prescription/% (owf)
REACTIVE DYES X
DISPERSE DYES Y
Glauber salt 30 ~ 60/g.L -1
Sodium carbonate 0 ~ 12/gL -1
Bath raio 1:25
PH value 7 ~ 9.5;
G, the technique of soaping: adopt surfactant 2 ~ 3.5g/L to soap;
H, mercerization: modulation alkali lye, wherein 26 ~ 28 parts, caustic soda, mercerising oil 3 g.L-1, control 15 ~ 18 ℃ of alkali liquid temperatures, fabric is put into alkali lye 45 ~ 60min and carry out mercerization finish, control 60 ~ 70 ℃ of three-flute washing temperature, the speed of a motor vehicle 11 ~ 15m/min guarantees that pick-up rate is 140% simultaneously;
I, stentering forming technique: fabric is sent into and in framing shaping machine, is carried out stentering forming, control tentering temperature: 90-110 ℃, and when sizing according to the softener that adds of feel;
J, preshrinking process: for preventing shrinking after fabric washing, must be through preshrunk processing, washing shrinkage is controlled in 3%;
K, inspection process: by inspector by meter Jin Hang visual examination with find and process defective products.
Beneficial effect: disclosed antibacterial and deodouring moisture absorption crib one side material, its warp thread adopts high absorbent hollow PET fiber and bamboo pulp fibre blending, and high absorbent hollow PET fiber has hollow section, and surface has the inside and outside hole connecting, thereby has good water suction, quick-drying, ventilative and poisture-penetrability, bamboo pulp fiber not only moisture absorption is ventilative, can also uvioresistant, antibacterial and deodouring, weft yarn adopts Lycra fiber, thereby has acid and alkali-resistance, sweat proof, resistance to dry-cleaning and wear-resisting, has improved service life.
The specific embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail.
Disclosed a kind of antibacterial and deodouring moisture absorption crib one side material, adopt warp thread and weft yarn 1:2 twill weave to form, described warp thread is that high absorbent hollow PET fiber and bamboo pulp fiber are with 1:1 blending, described weft yarn is Lycra fiber, wherein said bamboo pulp fiber is 40 ~ 60, and described Lycra is 40 ~ 60.
The production technology of antibacterial and deodouring moisture absorption crib one side material in the present embodiment is described with concrete step below:
A, weaving process: using high absorbent hollow PET fiber and bamboo pulp fibre blending as warp thread, using Lycra fiber as weft yarn, and warp thread and weft yarn are with 1:2 twill weave;
B, singeing: by the cloth of having weaved in step a with two positive one or two counter singing, control cloth speed 80 ~ 100m/min, fabric and reducing flame distance 1 ~ 1.2cm, fabric and copper coin distance 0.5 ~ 0.8cm, fabric and cylinder distance 5 ~ 7cm, and to control the rank of singing be 4 ~ 5 grades;
C, desizing: the fabric of having singed in step b is entered into 1 ~ 2min in hot water, then take out maceration enzyme liquid again, fixedly roll enzyme temperature 60 C, then take out and be incubated the 2h that banks up, controlling the temperature of fixedly banking up is 55 ℃, and PH is 7, NaCL5g/L, JFC1g/L, bath raio is 1:20;
D, oxygen bleaching process: the fabric that step c destarch is completed carries out oxygen and floats processing, wherein uses alkali 20-30kg ℃ .t -1, use oxygen 12-15kg.t -1, and control oxygen and press 1.0mpa, oxygen floats 95 ~ 110 ℃ of temperature, and oxygen floats time 40 ~ 60min;
E, pre-treatment process: because bamboo pulp fiber is more responsive to alkali and temperature, so need to carry out pre-treatment before to high absorbent hollow PET fiber and bamboo pulp fibre blending textile dyeing, and control and touch concentration of lye and temperature, in case bamboo fibre is impaired, concrete treatment process is that fabric is put into bath raio is that the concentration of 1:25 is that 30% hydrogen peroxide 5-6 S/L and sodium metasilicate l5-2 t/L mixed liquor carry out pre-treatment 40min, control mixed liquor PH=11 ~ 12, temperature is 90 ~ 95 ℃;
F, dyeing: adopt high temperature one to bathe one-step method, concrete technology prescription/% (owf)
REACTIVE DYES X
DISPERSE DYES Y
Glauber salt 30 ~ 60/g.L -1
Sodium carbonate 0 ~ 12/gL -1
Bath raio 1:25
PH value 7 ~ 9.5;
G, the technique of soaping: adopt surfactant 2 ~ 3.5g/L to soap;
H, mercerization: modulation alkali lye, wherein 26 ~ 28 parts, caustic soda, mercerising oil 3 g.L-1, control 15 ~ 18 ℃ of alkali liquid temperatures, fabric is put into alkali lye 45 ~ 60min and carry out mercerization finish, control 60 ~ 70 ℃ of three-flute washing temperature, the speed of a motor vehicle 11 ~ 15m/min guarantees that pick-up rate is 140% simultaneously;
I, stentering forming technique: fabric is sent into and in framing shaping machine, is carried out stentering forming, control tentering temperature: 90-110 ℃, and when sizing according to the softener that adds of feel;
J, preshrinking process: for preventing shrinking after fabric washing, must be through preshrunk processing, washing shrinkage is controlled in 3%;
K, inspection process: by inspector by meter Jin Hang visual examination with find and process defective products.
Technology contents of the present invention and technical characterictic have disclosed as above; but those of ordinary skill in the art still may be based on enlightenment of the present invention and announcements and are done all replacement and modifications that does not deviate from spirit of the present invention; therefore; protection domain of the present invention should be not limited to the content that embodiment discloses; and should comprise various do not deviate from replacement of the present invention and modifications, and contained by present patent application claim.

Claims (4)

1. an antibacterial and deodouring moisture absorption crib one side material, adopts warp thread and weft yarn 1:2 twill weave to form, and it is characterized in that: described warp thread be high absorbent hollow PET fiber and bamboo pulp fiber with 1:1 blending, described weft yarn is Lycra fiber.
2. a kind of antibacterial and deodouring moisture absorption crib one side material according to claim 1, is characterized in that: described bamboo pulp fiber is 40 ~ 60.
3. a kind of antibacterial and deodouring moisture absorption crib one side material according to claim 1, is characterized in that: described Lycra is 40 ~ 60.
4. a production technology for antibacterial and deodouring moisture absorption crib one side material, is characterized in that specifically comprising the following steps:
A, weaving process: using high absorbent hollow PET fiber and bamboo pulp fibre blending as warp thread, using Lycra fiber as weft yarn, and warp thread and weft yarn are with 1:2 twill weave;
B, singeing: by the cloth of having weaved in step a with two positive one or two counter singing, control cloth speed 80 ~ 100m/min, fabric and reducing flame distance 1 ~ 1.2cm, fabric and copper coin distance 0.5 ~ 0.8cm, fabric and cylinder distance 5 ~ 7cm, and to control the rank of singing be 4 ~ 5 grades;
C, desizing: the fabric of having singed in step b is entered into 1 ~ 2min in hot water, then take out maceration enzyme liquid again, fixedly roll enzyme temperature 60 C, then take out and be incubated the 2h that banks up, controlling the temperature of fixedly banking up is 55 ℃, and PH is 7, NaCL5g/L, JFC1g/L, bath raio is 1:20;
D, oxygen bleaching process: the fabric that step c destarch is completed carries out oxygen and floats processing, wherein uses alkali 20-30kg ℃ .t -1, use oxygen 12-15kg.t -1, and control oxygen and press 1.0mpa, oxygen floats 95 ~ 110 ℃ of temperature, and oxygen floats time 40 ~ 60min;
E, pre-treatment process: because bamboo pulp fiber is more responsive to alkali and temperature, so need to carry out pre-treatment before to high absorbent hollow PET fiber and bamboo pulp fibre blending textile dyeing, and control and touch concentration of lye and temperature, in case bamboo fibre is impaired, concrete treatment process is that fabric is put into bath raio is that the concentration of 1:25 is that 30% hydrogen peroxide 5-6 S/L and sodium metasilicate l5-2 t/L mixed liquor carry out pre-treatment 40min, control mixed liquor PH=11 ~ 12, temperature is 90 ~ 95 ℃;
F, dyeing: adopt high temperature one to bathe one-step method, concrete technology prescription/% (owf)
REACTIVE DYES X
DISPERSE DYES Y
Glauber salt 30 ~ 60/g.L -1
Sodium carbonate 0 ~ 12/gL -1
Bath raio 1:25
PH value 7 ~ 9.5;
G, the technique of soaping: adopt surfactant 2 ~ 3.5g/L to soap;
H, mercerization: modulation alkali lye, wherein 26 ~ 28 parts, caustic soda, mercerising oil 3 g.L-1, control 15 ~ 18 ℃ of alkali liquid temperatures, fabric is put into alkali lye 45 ~ 60min and carry out mercerization finish, control 60 ~ 70 ℃ of three-flute washing temperature, the speed of a motor vehicle 11 ~ 15m/min guarantees that pick-up rate is 140% simultaneously;
I, stentering forming technique: fabric is sent into and in framing shaping machine, is carried out stentering forming, control tentering temperature: 90-110 ℃, and when sizing according to the softener that adds of feel;
J, preshrinking process: for preventing shrinking after fabric washing, must be through preshrunk processing, washing shrinkage is controlled in 3%;
K, inspection process: by inspector by meter Jin Hang visual examination with find and process defective products.
CN201410144519.7A 2014-04-11 2014-04-11 A kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof Expired - Fee Related CN103882603B (en)