CN103882603B - A kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof - Google Patents
A kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof Download PDFInfo
- Publication number
- CN103882603B CN103882603B CN201410144519.7A CN201410144519A CN103882603B CN 103882603 B CN103882603 B CN 103882603B CN 201410144519 A CN201410144519 A CN 201410144519A CN 103882603 B CN103882603 B CN 103882603B
- Authority
- CN
- China
- Prior art keywords
- fabric
- temperature
- control
- deodouring
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of antibacterial and deodouring moisture absorption crib one side material, adopt warp thread and weft yarn 1:2 twill weave to form, described warp thread is that high absorbent hollow PET fiber and bamboo pulp fiber are with 1:1 blending, described weft yarn is Lycra fiber, and production technology comprises step: weaving process, singeing, desizing, oxygen bleaching process, pre-treatment process, dyeing, to soap technique, mercerization, stentering forming technique, preshrinking process and inspection process.Disclosed antibacterial and deodouring moisture absorption crib one side material has water suction, quick-drying, ventilative, poisture-penetrability, uvioresistant, antibacterial and deodouring, acid and alkali-resistance, sweat proof, resistance to dry-cleaning and wear-resisting, improves service life.
Description
Technical field
The present invention relates to a kind of fabric and production technology, particularly relate to a kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof.
Background technology
On current market, home textile product is a lot, and man spun industry and occurred the growth of explosion type at home recent years, but the bed necessaries exploitation that domestic market is directed to infant is specially few.
Summary of the invention
Goal of the invention: the present invention mainly provides a kind of antibacterial and deodouring moisture absorption crib one side material and production technology thereof.
Technical scheme: a kind of antibacterial and deodouring moisture absorption crib one side material, adopts warp thread and weft yarn 1: 2 twill weave to form, described warp thread be high absorbent hollow PET fiber and bamboo pulp fiber with 1: 1 blending, described weft yarn is Lycra fiber.
Described bamboo pulp fiber is 40 ~ 60.
Described Lycra is 40 ~ 60.
A production technology for antibacterial and deodouring moisture absorption crib one side material, specifically comprises the following steps:
A, weaving process: using high absorbent hollow PET fiber and bamboo pulp fibre blending as warp thread, using Lycra fiber as weft yarn, and warp thread and weft yarn are with 1: 2 twill weave;
B, singeing: the cloth weaved in step a instead to be singed with two positive 1, control cloth speed 80 ~ 100m/min, fabric and reducing flame distance 1 ~ 1.2cm, fabric and copper coin distance 0.5 ~ 0.8cm, fabric and cylinder distance 5 ~ 7cm, and control is singed, rank is 4 ~ 5 grades;
C, desizing: the fabric of having singed in step b is entered into 1 ~ 2min in hot water, then take out maceration enzyme liquid again, fixedly roll enzyme temperature 60 C, then take out and carry out insulation and to bank up 2h, the temperature that controls fixedly to bank up is 55 DEG C, and PH is 7, NaCL5g/L, JFClg/L, bath raio is 1: 20;
D, oxygen bleaching process: fabric step c destarch completed carries out oxygen bleaching process, wherein uses alkali 20-30kg.t
-1, use oxygen 12-15kg.t
-1, and control oxygen pressure 1.0mpa, oxygen bleaching temperature 95 ~ 110 DEG C, oxygen bleaching time 40 ~ 60min;
E, pre-treatment process: due to bamboo pulp fiber to alkali and temperature more responsive, so need to carry out pre-treatment before to high absorbent hollow PET fiber and bamboo pulp fibre blending textile dyeing, and control to touch concentration of lye and temperature, in case bamboo fibre is impaired, concrete treatment process be fabric is put into bath raio be 1: 25 concentration be that 30% hydrogen peroxide 5-6Sg/L and silicic acid 2-15g/L mixed liquor carry out pre-treatment 40min, control mixed liquor PH=11 ~ 12, temperature is 90 ~ 95 DEG C;
F, dyeing: adopt high temperature one-bath one-step dyeing, concrete technology prescription/% (owf)
G, technique of soaping: adopt surfactant 2 ~ 3.5g/L to soap;
H, mercerization: modulation alkali lye, wherein 26 ~ 28 parts, caustic soda, mercerising oil 3g.L
-1, control alkali liquid temperature 15 ~ 18 DEG C, fabric put into alkali lye 45 ~ 60min and carry out mercerization finish, control three groove washing temperature 60 ~ 70 DEG C, the speed of a motor vehicle 11 ~ 15m/min, guarantee that pick-up rate is 140% simultaneously;
I, stentering forming technique: sent into by fabric in framing shaping machine and carry out stentering forming, control tentering temperature: 90-110 DEG C, and add softener according to feel during sizing;
J, preshrinking process: shrink after washing for preventing fabric, have to pass through preshrunk process, washing shrinkage controls within 3%.
K, inspection process: by inspector by meter Jin Hang visual examination with find and process defective products.
Beneficial effect: disclosed antibacterial and deodouring moisture absorption crib one side material, its warp thread adopts high absorbent hollow PET fiber and bamboo pulp fibre blending, and high absorbent hollow PET fiber has hollow section, and surface has inside and outside through hole, thus has good water suction, quick-drying, ventilative and poisture-penetrability, bamboo pulp fiber not only moisture absorption is breathed freely, can also uvioresistant, antibacterial and deodouring, weft yarn adopts Lycra fiber, thus has acid and alkali-resistance, sweat proof, resistance to dry-cleaning and wear-resisting, improves service life.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be described in detail.
Disclosed a kind of antibacterial and deodouring moisture absorption crib one side material, warp thread and weft yarn 1: 2 twill weave is adopted to form, described warp thread is that high absorbent hollow PET fiber and bamboo pulp fiber are with 1: 1 blending, described weft yarn is Lycra fiber, wherein said bamboo pulp fiber is 40 ~ 60, and described Lycra is 40 ~ 60.
The production technology of antibacterial and deodouring moisture absorption crib one side material in the present embodiment is described with concrete step below:
A, weaving process: using high absorbent hollow PET fiber and bamboo pulp fibre blending as warp thread, using Lycra fiber as weft yarn, and warp thread and weft yarn are with 1: 2 twill weave;
B, singeing: the cloth weaved in step a instead to be singed with two n-two, control cloth speed 80 ~ 100m/min, fabric and reducing flame distance 1 ~ 1.2cm, fabric and copper coin distance 0.5 ~ 0.8cm, fabric and cylinder distance 5 ~ 7cm, and control is singed, rank is 4 ~ 5 grades;
C, desizing: the fabric of having singed in step b is entered into 1 ~ 2min in hot water, then take out maceration enzyme liquid again, fixedly roll enzyme temperature 60 C, then take out and carry out insulation and to bank up 2h, the temperature that controls fixedly to bank up is 55 DEG C, and PH is 7, NaCL5g/L, JFClg/L, bath raio is 1: 20;
D, oxygen bleaching process: fabric step c destarch completed carries out oxygen bleaching process, wherein uses alkali 20-30kg.t
-1, use oxygen 12-15kg.t
-1, and control oxygen pressure 1.0mpa, oxygen bleaching temperature 95 ~ 110 DEG C, oxygen bleaching time 40 ~ 60min;
E, pre-treatment process: due to bamboo pulp fiber to alkali and temperature more responsive, so need to carry out pre-treatment before to high absorbent hollow PET fiber and bamboo pulp fibre blending textile dyeing, and control to touch concentration of lye and temperature, in case bamboo fibre is impaired, concrete treatment process be fabric is put into bath raio be 1: 25 concentration be that 30% hydrogen peroxide 5-6g/L and sodium metasilicate 2-15g/L mixed liquor carry out pre-treatment 40min, control mixed liquor PH=11 ~ 12, temperature is 90 ~ 95 DEG C;
F, dyeing: adopt high temperature one-bath one-step dyeing, concrete technology prescription/% (owf)
G, technique of soaping: adopt surfactant 2 ~ 3.5g/L to soap;
H, mercerization: modulation alkali lye, wherein 26 ~ 28 parts, caustic soda, mercerising oil 3g.L
-1, control alkali liquid temperature 15 ~ 18 DEG C, fabric put into alkali lye 45 ~ 60min and carry out mercerization finish, control three groove washing temperature 60 ~ 70 DEG C, the speed of a motor vehicle 11 ~ 15m/min, guarantee that pick-up rate is 140% simultaneously;
I, stentering forming technique: sent into by fabric in framing shaping machine and carry out stentering forming, control tentering temperature: 90-110 DEG C, and add softener according to feel during sizing;
J, preshrinking process: shrink after washing for preventing fabric, have to pass through preshrunk process, washing shrinkage controls within 3%.
K, inspection process: by inspector by meter Jin Hang visual examination with find and process defective products.
Technology contents of the present invention and technical characteristic have disclosed as above; but those of ordinary skill in the art still may do all replacement and the modification that do not deviate from spirit of the present invention based on enlightenment of the present invention and announcement; therefore; scope should be not limited to the content that embodiment discloses; and various do not deviate from replacement of the present invention and modification should be comprised, and contained by present patent application claim.
Claims (1)
1. a production technology for antibacterial and deodouring moisture absorption crib one side material, is characterized in that specifically comprising the following steps:
A, weaving process: using high absorbent hollow PET fiber and bamboo pulp fibre blending as warp thread, using Lycra fiber as weft yarn, and warp thread and weft yarn are with 1:2 twill weave;
B, singeing: the cloth weaved in step a instead to be singed with two positive 1, control cloth speed 80 ~ 100m/min, fabric and reducing flame distance 1 ~ 1.2cm, fabric and copper coin distance 0.5 ~ 0.8cm, fabric and cylinder distance 5 ~ 7cm, and control is singed, rank is 4 ~ 5 grades;
C, desizing: the fabric of having singed in step b is entered into 1 ~ 2min in hot water, then take out maceration enzyme liquid again, fixedly roll enzyme temperature 60 C, then take out and carry out insulation and to bank up 2h, the temperature that controls fixedly to bank up is 55 DEG C, and PH is 7, NaCL5g/L, JFC1g/L, bath raio is 1:20;
D, oxygen bleaching process: fabric step c destarch completed carries out oxygen bleaching process, wherein uses alkali 20-30kg.t
-1, use oxygen 12-15kg.t
-1, and control oxygen pressure 1.0mpa, oxygen bleaching temperature 95 ~ 110 DEG C, oxygen bleaching time 40 ~ 60min;
E, pre-treatment process: due to bamboo pulp fiber to alkali and temperature more responsive, so need to carry out pre-treatment before to high absorbent hollow PET fiber and bamboo pulp fibre blending textile dyeing, and control to touch concentration of lye and temperature, in case bamboo fibre is impaired, concrete treatment process is that fabric to be put into bath raio be the concentration of 1:25 is that 30% hydrogen peroxide 5-6g/L and sodium metasilicate 2-15g/L mixed liquor carry out pre-treatment 40min, control mixed liquor PH=11 ~ 12, temperature is 90 ~ 95 DEG C;
F, dyeing: adopt high temperature one-bath one-step dyeing, concrete technology prescription/% (owf)
G, technique of soaping: adopt surfactant 2 ~ 3.5g/L to soap;
H, mercerization: modulation alkali lye, wherein 26 ~ 28 parts, caustic soda, mercerising oil 3g.L
-1, control alkali liquid temperature 15 ~ 18 DEG C, fabric put into alkali lye 45 ~ 60min and carry out mercerization finish, control three groove washing temperature 60 ~ 70 DEG C, the speed of a motor vehicle 11 ~ 15m/min, guarantee that pick-up rate is 140% simultaneously;
I, stentering forming technique: sent into by fabric in framing shaping machine and carry out stentering forming, control tentering temperature: 90-110 DEG C, and add softener according to feel during sizing;
J, preshrinking process: shrink after washing for preventing fabric, have to pass through preshrunk process, washing shrinkage controls within 3%;
K, inspection process: by inspector by meter Jin Hang visual examination with find and process defective products.