CN109778394A - A kind of preparation method of fluffy ultra-soft towel - Google Patents
A kind of preparation method of fluffy ultra-soft towel Download PDFInfo
- Publication number
- CN109778394A CN109778394A CN201910076213.5A CN201910076213A CN109778394A CN 109778394 A CN109778394 A CN 109778394A CN 201910076213 A CN201910076213 A CN 201910076213A CN 109778394 A CN109778394 A CN 109778394A
- Authority
- CN
- China
- Prior art keywords
- towel
- acrylic fibers
- polyvinyl
- fluffy
- ultra
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation methods of fluffy ultra-soft towel, and the one side of the towel is using acrylic fibers and polyvinyl folded yarn as wool warp；The another side of the towel is using hollow cotton as wool warp, comprising the following steps: (1) weaves: consolidating fluffing mode using four latitudes, weaves into double-loop towel；(2) remove polyvinyl silk: towel caused by knitting removes the polyvinyl silk in the acrylic fibers and polyvinyl folded yarn in the hot water that temperature is 45~60 DEG C；(3) post-process: bath raio is 1:8~10,60~80 DEG C of temperature, handles 35~45min of time；(4) plus soft: bath raio 1:8~10, handle 20~40min of time by 40~50 DEG C of temperature；(5) dry: the drying uses airflow drying, and drying temperature is 125~140 DEG C.Product made of preparation method of the present invention is soft, warming, healthy, comfortable, is particularly suitable for old man, children use.
Description
Technical field
The present invention relates to towel technical fields, and in particular to a kind of preparation method of fluffy ultra-soft towel.
Background technique
Acrylic fiber has the title of artificial wool, has soft, bulk, easy dye, bright in colour, fast light, antibacterial, is not afraid of and damages by worms
The advantages that, according to the requirement of different purposes can it is pure spinning or with it is natural fibre blended, textile be widely used in clothes, dress
The fields such as decorations, industry.
In recent years, from the product structure of household textiles, middle low-level production is superfluous, and high-tech, height are attached
Value added product specific gravity is relatively low, is not able to satisfy demand of the consumer in terms of home textile field after stepping into " well-to-do level " society, especially
The home textile product of soft comfortable type increasingly has been favored by people.
Summary of the invention
The technical problems to be solved by the present invention are: in view of the deficienciess of the prior art, providing a kind of fluffy super softness
The preparation method of towel, it is environmental friendly pollution-free, and the towel feel being prepared it is fluffy, it is super it is soft, comfort is good.
In order to solve the above technical problems, the technical scheme is that
A kind of preparation method of fluffy ultra-soft towel, the towel are double-loop towel, and the towel is adopted on one side
Use acrylic fibers and polyvinyl folded yarn as wool warp；The another side of the towel uses hollow cotton as wool warp, including with
Lower step:
(1) it weaves: being passed through using the acrylic fibers and polyvinyl folded yarn, hollow cotton as the hair of the two sides looped pile of towel
Yarn consolidates fluffing mode using four latitudes, weaves into double-loop towel；
(2) remove polyvinyl silk: for towel caused by knitting in the hot water that temperature is 45~60 DEG C, bath raio is 1:8~10, place
5~15min is managed, the polyvinyl silk in the acrylic fibers and polyvinyl folded yarn is removed；
(3) post-process: bath raio is 1:8~10,60~80 DEG C of temperature, handles 35~45min of time, contains desizing in bath foam
1~2g/L of enzyme, 0.65~0.75g/L of emulsifier；
(4) plus soft: bath raio 1:8~10, contain 2.5~3.5g/L of softening agent, add supple-settlement by 40~50 DEG C of temperature in bath foam
20~40min of time；
(5) dry: the drying uses airflow drying, and drying temperature is 125~140 DEG C, and drying rate is 8~12m/
min。
As a kind of improved technical solution, the acrylic fibers and polyvinyl folded yarn include following processing step:
(1) acrylic fibers refine: carrying out refining treatment to acrylic fibers cylinder yarn with the bobbin dyeing machine of the vertical letter in Hong Kong, bath raio is 1:6~8, temperature
80~85 DEG C of degree contains 4~6g/L of Tea Saponin, 8~12ml/L of hydrogen peroxide in bath foam；Handle 40~60min；
(2) acrylic fibers pickling: in bath foam be added 0.1~0.15g/L of citric acid, under the conditions of 40~50 DEG C handle 5~
15min；
(3) acrylic fibers deoxidation: deoxygenase is added in bath foam, deoxygenase content is 0.10~0.15ml/L, in 35~45 DEG C of items
15~25min is handled under part；
(4) combine: the acrylic fibers handled well and polyvinyl are combineeed to obtain the acrylic fibers and polyvinyl folded yarn.
As a kind of improved technical solution, the twist of acrylic fibers and polyvinyl is opposite when the plying.
As a kind of improved technical solution, in step (3), the deoxygenase is deoxygenase MK-27.The deoxygenase
MK-27 is through catalase made of nonpathogenic bacteria submerged fermentation；It is preferable to use health grace biology Co., Ltd produces.
As a kind of improved technical solution, the hollow cotton includes following processing step of soaping: being added in bath foam
Soaping agent, agent content of soaping are 0.1~0.3g/L；Bath raio 1:6~10,60~80 DEG C of 5~15min that soap, then heat is carried out respectively
Washing and cold water are washed.
As a kind of improved technical solution, the soaping agent is soaping agent ZL-SN.The soaping agent ZL-SN is methoxy
Base fatty acyl amido benzene sulfonic acid sodium salt.
As a kind of improved technical solution, the hollow cotton further includes staining procedure before soaping: bath raio 1:6~
10,60~80 DEG C of bath temperature；The reactive dye of the hollow cotton yarn weight are added: Hensel steps the reactive dye Nowe clone of production
Red S-B 0.15%, Nowe clone black G 0.18%, and after handling 5~15min, anhydrous sodium sulfate, anhydrous slufuric acid in bath foam is added
Sodium content is 13~17g/L, handles 5~15min, and soda ash is added, and bath foam contains 8~10g/L of soda ash, then heats to 60~80
DEG C, dye 20~40min.
As a kind of preferred technical solution, the hollow cotton is short fine as with spinning material using degradable polyvinyl
Expect blended, is obtained after then removing polyvinyl at 95~105 DEG C.
As a kind of preferred technical solution, the weft yarn and body warp of the towel are all made of purified cotton yarns.
As a kind of improved technical solution, in step (3), the desizing enzyme is desizing enzyme MK-ZH；The emulsifier is
Emulsifier DF-60R.The desizing enzyme MK-ZH is the warm alpha-amylase of width made of one kind is fermented as nonpathogenic bacteria, can be wider
α -1.4 glucoside bond in starch molecule is arbitrarily hydrolyzed in temperature range with random basis, starches down into short chain rapidly
Dextrin and oligosaccharide；It is preferable to use health grace biology Co., Ltd produces.The emulsifier DF-60R is special efficient interface
Activating agent compound.
As a kind of improved technical solution, in step (4), the softening agent is softening agent HP-3C.The softening agent
HP-3C is the emulsion of fatty acid condensates and organically-modified silicone oil.
The Tea Saponin also known as tea saponin are five cyclic terpene of one kind, three saponins taken out in the tea seed cake after rolling experienced tea oil
Substance, is a kind of nonionic surfactant of good performance, and sterling is fine white column crystal.
The citric acid is 2- hydroxy propane -1,2,3- tricarboxylic acids；
By adopting the above-described technical solution, the beneficial effects of the present invention are:
The preparation method of fluffy ultra-soft towel of the invention is distinguished using acrylic fibers and polyvinyl folded yarn, hollow cotton
The wool warp of two sides looped pile as towel consolidates fluffing mode using four latitudes, weaves at double-loop towel, by what is woven
The ultra-light knop cloth is made through final finishing in fabric；Product made of preparation method through the invention is soft, warming, strong
Health, comfortable, particularly suitable old man, children's use.
Specific embodiment
Below with reference to specific embodiment, the present invention is further explained.It should be understood that these embodiments are merely to illustrate this hair
It is bright rather than limit the scope of the invention.In addition, it should also be understood that, after reading the content taught by the present invention, art technology
Personnel can make various changes or modifications the present invention, and such equivalent forms equally fall within the application the appended claims and limited
Fixed range.
Embodiment 1
One, yarn pre-treatment:
(1) acrylic fibers refine: carrying out refining treatment, bath raio 1:7, temperature 82 to acrylic fibers cylinder yarn with the bobbin dyeing machine of the vertical letter in Hong Kong
DEG C, Tea Saponin 5g/L, hydrogen peroxide 10ml/L are contained in bath foam；Handle 50min；
(2) acrylic fibers pickling: citric acid 0.12g/L is added in bath foam, handles 10min under the conditions of 45 DEG C；
(3) acrylic fibers deoxidation: deoxygenase MK-27 is added in bath foam, deoxygenase MK-27 content is 0.12ml/L, in 40 DEG C of items
20min is handled under part；
(4) staining procedure: bath raio 1:8,70 DEG C of bath temperature；The reactive dye of the hollow cotton yarn weight are added: Hensel steps
The reactive dye Nowe of production clones red S-B 0.15%, and Nowe clones black G 0.18%, and after handling 10min, anhydrous sulphur is added
Sour sodium, anhydrous slufuric acid sodium content is 15g/L in bath foam, handles 10min, and soda ash is added, and bath foam contains soda ash 9g/L, then heats up
To 70 DEG C, 30min is dyed.
(5) it soaps processing step: soaping agent ZL-SN being added in bath foam, soaping agent ZL-SN content is 0.2g/L；Bath raio 1:
8,70 DEG C of 10min that soap, then progress hot water wash and cold water are washed respectively.
(6) combine: the acrylic fibers handled well and polyvinyl are combineeed to obtain the acrylic fibers and polyvinyl folded yarn, acrylic fibers and dimension
The twist of synthetic fibre is opposite.
Two, warping: Switzerland's Benniger warping machine is selected when warping, its high degree of automation can be according to the not people having the same aspiration and interest of yarn count
The tension for saving warping, the tension to warping is electronic control, easy to operate, is conducive to the winding of yarn, can effectively reduce whole
Through fault, it can effectively cooperate the operating of high speed import loom.
Three, towel is weaved:
More Neil rapier looms or saliva field coltfoal, Bi Jianuo loom can be used when weaving；By the acrylic fibers and polyvinyl folded yarn,
Hollow cotton consolidates fluffing mode using four latitudes, weaves into two-sided terry respectively as the wool warp of the two sides looped pile of towel
Towel；
Four, final finishing: using the vertical letter high temperature and pressure overflow dyeing machine in Hong Kong, the equipment operation is steady, and nozzle is bigger, energy
Enough contact fabric adequately with treatment fluid.
(2) remove polyvinyl silk: towel caused by knitting is in the hot water that temperature is 50 DEG C, bath raio 1:9, handles 10min,
Remove the polyvinyl silk in the acrylic fibers and polyvinyl folded yarn；
(3) post-process: bath raio 1:9, temperature 70 C handle time 40min, contain desizing enzyme MK-ZH in bath foam
1.5g/L, emulsifier DF-60R0.70g/L；
(4) plus soft: bath raio 1:9, temperature 45 C contain softening agent HP-3C3.0g/L in bath foam, add the supple-settlement time
30min；
(5) dry: the drying uses airflow drying, and drying temperature is 130 DEG C, drying rate 10m/min.Subtract as far as possible
Few acrylic fibers product further felting due to mechanical external force during dressing, making acrylic fibers product both has fine and smooth flannelette,
There is the feel of fluffy softness again.
Finally sewing is examined to obtain finished product.
Embodiment 2
One, yarn pre-treatment:
(1) acrylic fibers refine: carrying out refining treatment, bath raio 1:6, temperature 84 to acrylic fibers cylinder yarn with the bobbin dyeing machine of the vertical letter in Hong Kong
DEG C, Tea Saponin 5.5g/L, hydrogen peroxide 10ml/L are contained in bath foam；Handle 55min；
(2) acrylic fibers pickling: citric acid 0.13g/L is added in bath foam, handles 12min under the conditions of 48 DEG C；
(3) acrylic fibers deoxidation: deoxygenase MK-27 is added in bath foam, deoxygenase MK-27 content is 0.14ml/L, in 42 DEG C of items
22min is handled under part；
(4) staining procedure: bath raio 1:7,68 DEG C of bath temperature；The reactive dye of the hollow cotton yarn weight are added: Hensel steps
The reactive dye Nowe of production clones red S-B 0.15%, and Nowe clones black G 0.18%, and after handling 12min, anhydrous sulphur is added
Sour sodium, anhydrous slufuric acid sodium content is 15.5g/L in bath foam, handles 12min, and soda ash is added, and bath foam contains soda ash 9g/L, then rises
Temperature dyes 32min to 72 DEG C.
(5) it soaps processing step: soaping agent ZL-SN being added in bath foam, soaping agent ZL-SN content is 0.25g/L；Bath raio 1:
8,72 DEG C of 12min that soap, then progress hot water wash and cold water are washed respectively.
(6) combine: the acrylic fibers handled well and polyvinyl are combineeed to obtain the acrylic fibers and polyvinyl folded yarn, acrylic fibers and dimension
The twist of synthetic fibre is opposite.
Two, warping: Switzerland's Benniger warping machine is selected when warping, its high degree of automation can be according to the not people having the same aspiration and interest of yarn count
The tension for saving warping, the tension to warping is electronic control, easy to operate, is conducive to the winding of yarn, can effectively reduce whole
Through fault, it can effectively cooperate the operating of high speed import loom.
Three, towel is weaved:
More Neil rapier looms or saliva field coltfoal, Bi Jianuo loom can be used when weaving；By the acrylic fibers and polyvinyl folded yarn,
Hollow cotton consolidates fluffing mode using four latitudes, weaves into two-sided terry respectively as the wool warp of the two sides looped pile of towel
Towel；
Four, final finishing: using the vertical letter high temperature and pressure overflow dyeing machine in Hong Kong, the equipment operation is steady, and nozzle is bigger, energy
Enough contact fabric adequately with treatment fluid.
(2) remove polyvinyl silk: towel caused by knitting is in the hot water that temperature is 52 DEG C, bath raio 1:9, handles 12min,
Remove the polyvinyl silk in the acrylic fibers and polyvinyl folded yarn；
(3) post-process: bath raio 1:9, handles time 42min, contains desizing enzyme MK-ZH1.6g/ in bath foam by 72 DEG C of temperature
L, emulsifier DF-60R0.68g/L；
(4) plus soft: bath raio 1:8, contains softening agent HP-3C3.2g/L, adds the supple-settlement time by 44 DEG C of temperature in bath foam
28min；
(5) dry: the drying uses airflow drying, and drying temperature is 132 DEG C, drying rate 11m/min.Subtract as far as possible
Few acrylic fibers product further felting due to mechanical external force during dressing, making acrylic fibers product both has fine and smooth flannelette,
There is the feel of fluffy softness again.
Finally sewing is examined to obtain finished product.
Claims (9)
1. a kind of preparation method of fluffy ultra-soft towel, the towel is double-loop towel, it is characterised in that: the towel
One side using acrylic fibers and polyvinyl folded yarn as wool warp；The another side of the towel is passed through using hollow cotton as hair
Yarn, comprising the following steps:
(1) it weaves: using the acrylic fibers and polyvinyl folded yarn, hollow cotton as the wool warp of the two sides looped pile of towel,
Fluffing mode is consolidated using four latitudes, is weaved into double-loop towel；
(2) remove polyvinyl silk: for towel caused by knitting in the hot water that temperature is 45~60 DEG C, bath raio is 1:8~10, processing 5
~15min removes the polyvinyl silk in the acrylic fibers and polyvinyl folded yarn；
(3) post-process: bath raio is 1:8~10,60~80 DEG C of temperature, handles 35~45min of time, contains desizing enzyme 1 in bath foam
~2g/L, 0.65~0.75g/L of emulsifier；
(4) plus soft: bath raio 1:8~10, contain 2.5~3.5g/L of softening agent, add the supple-settlement time by 40~50 DEG C of temperature in bath foam
20~40min；
(5) dry: the drying uses airflow drying, and drying temperature is 125~140 DEG C.
2. the preparation method of fluffy ultra-soft towel as described in claim 1, it is characterised in that the acrylic fibers and polyvinyl plying
Yarn includes following processing step:
(1) acrylic fibers refine: bath raio be 1:6~8,80~85 DEG C of temperature, in bath foam containing 4~6g/L of Tea Saponin, hydrogen peroxide 8~
12ml/L；Handle 40~60min；
(2) acrylic fibers pickling: being added 0.1~0.15g/L of citric acid in bath foam, 5~15min is handled under the conditions of 40~50 DEG C；
(3) acrylic fibers deoxidation: deoxygenase is added in bath foam, deoxygenase content is 0.10~0.15ml/L, under the conditions of 35~45 DEG C
Handle 15~25min；
(4) combine: the acrylic fibers handled well and polyvinyl are combineeed to obtain the acrylic fibers and polyvinyl folded yarn.
3. the preparation method of fluffy ultra-soft towel as claimed in claim 2, it is characterised in that: acrylic fibers and dimension when the plying
The twist of synthetic fibre is opposite.
4. the preparation method of fluffy ultra-soft towel as claimed in claim 2, it is characterised in that: in step (3), the deoxidation
Enzyme is deoxygenase MK-27.
5. the preparation method of fluffy ultra-soft towel as described in claim 1, it is characterised in that the hollow cotton includes
It soaps below processing step: soaping agent being added in bath foam, agent content of soaping is 0.1~0.3g/L；Bath raio 1:6~10,60~80
DEG C soap 5~15min, then carries out hot water wash respectively and cold water is washed.
6. the preparation method of fluffy ultra-soft towel as claimed in claim 5, it is characterised in that: the soaping agent is soaping agent
ZL-SN。
7. the preparation method of fluffy ultra-soft towel as claimed in claim 5, it is characterised in that the hollow cotton is in soap
Further include staining procedure before washing: bath raio 1:6~10,60~80 DEG C of bath temperature；The reactive dye of the hollow cotton yarn weight are added
0.2~0.5%；After handling 5~15min, anhydrous sodium sulfate is added, anhydrous slufuric acid sodium content is 13~17g/L, processing in bath foam
Soda ash is added in 5~15min, and bath foam contains 8~10g/L of soda ash, then heats to 60~80 DEG C, dyes 20~40min.
8. the preparation method of fluffy ultra-soft towel as described in claim 1, it is characterised in that: in step (3), the desizing
Enzyme is desizing enzyme MK-ZH；The emulsifier is emulsifier DF-60R.
9. the preparation method of fluffy ultra-soft towel as described in claim 1, it is characterised in that: in step (4), the softness
Agent is softening agent HP-3C.