CN103882450B - 一种水基除锈防锈液及其制备方法 - Google Patents

一种水基除锈防锈液及其制备方法 Download PDF

Info

Publication number
CN103882450B
CN103882450B CN201410063833.2A CN201410063833A CN103882450B CN 103882450 B CN103882450 B CN 103882450B CN 201410063833 A CN201410063833 A CN 201410063833A CN 103882450 B CN103882450 B CN 103882450B
Authority
CN
China
Prior art keywords
water
alpha
rust
preparation
auxiliary agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410063833.2A
Other languages
English (en)
Other versions
CN103882450A (zh
Inventor
宋玉春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuhai Zhibang Chemical Technology Co Ltd
Original Assignee
ANHUI TOPUSEN BATTERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TOPUSEN BATTERY Co Ltd filed Critical ANHUI TOPUSEN BATTERY Co Ltd
Priority to CN201410063833.2A priority Critical patent/CN103882450B/zh
Publication of CN103882450A publication Critical patent/CN103882450A/zh
Application granted granted Critical
Publication of CN103882450B publication Critical patent/CN103882450B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种水基除锈防锈液，由下列重量份的原料制成：辛基苯酚聚氧乙烯醚1-2、油酸聚氧乙烯酯2-3、乙醇20-23、柠檬酸1-2、磷酸锌2-3、十二烷基硫酸钠1.3-2.4、2，6-二叔丁基-α-二甲胺基对苯酚1.2-2.3、异丙醇1-2、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、EDTA二钠1-2、助剂4-5、水300。本发明防锈液具有除锈、去污、磷化、钝化、表调等多种功能,而且通过使用有机高分子聚合物单体以及螯合剂共同作用，能在金属表面形成薄膜，起到隔绝空气，防氧化的作用；生产工艺简单、清除容易，成本低、常温下反应,除锈时间短、防锈时间长,对金属无腐蚀性,不含有毒有害物,对环境无污染。

Description

一种水基除锈防锈液及其制备方法
技术领域
本发明涉及防锈技术领域，尤其涉及一种水基除锈防锈液及其制备方法。
背景技术
金属表面防锈是工业生产中的重要课题，传统的防锈液、防锈油有优点也有缺点。普通防锈水中含大量的亚硝酸钠，有致癌性，不利于环保和人身体健康，而采用保湿剂延长防锈水的寿命，又带来沾手、沾灰尘的弊病，且不能长期防锈；一般硬膜防锈油虽然适合长期防锈，成膜也透明美观，但是无色透明的树脂种类较少，不稳定也易氧化变色，还需要有机溶剂溶解，带来易燃易爆的危险也不利于环保和健康；一般的防锈油使用矿物油，难降解，而且用于短期防锈时也会带来除油难的问题。因此，研究综合性能更加优异，针对不同场合研究更加适合的防锈产品是新的方向和趋势。
发明内容
本发明的目的在于提供一种水基除锈防锈液及其制备方法，该防锈液具有除锈快、防锈效果好的特点。
本发明的技术方案如下：
一种水基除锈防锈液，其特征在于由下列重量份的原料制成：辛基苯酚聚氧乙烯醚1-2、油酸聚氧乙烯酯2-3、乙醇20-23、柠檬酸1-2、磷酸锌2-3、十二烷基硫酸钠1.3-2.4、2，6-二叔丁基-α-二甲胺基对苯酚1.2-2.3、异丙醇1-2、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、EDTA二钠1-2、助剂4-5、水300。所述的助剂由下列重量份的原料制成：聚氧乙烯山梨糖醇酐单油酸酯2-3、纳米二氧化钛0.1-0.2、三聚磷酸钠1-2、硅酸钠1-2、乌洛托品1-2、对苯二酚1-2、硼砂3-4、尿素2-3、过硫酸铵1-2、桃胶2-3、水20-24；所述助剂的制备方法是将过硫酸铵溶于水后，再加入其它剩余物料，搅拌10-15分钟，加热至70-80℃，搅拌反应1-2小时，即得。
所述水基除锈防锈液的制备方法，其特征在于包括以下步骤：将水加热至40-50℃，加入辛基苯酚聚氧乙烯醚、油酸聚氧乙烯酯、十二烷基硫酸钠；继续加热到85-90℃，加入乙醇、2，6-二叔丁基-α-二甲胺基对苯酚、异丙醇、乙氧基化三羟甲基丙烷三丙烯酸酯、EDTA二钠，搅拌10-15分钟；加入其他剩余成分，继续搅拌15-20分钟即得。
本发明的有益效果
本发明防锈液具有除锈、去污、磷化、钝化、表调等多种功能,而且通过使用有机高分子聚合物单体以及螯合剂共同作用，能在金属表面形成薄膜，起到隔绝空气，防氧化的作用；生产工艺简单、清除容易，成本低、常温下反应,除锈时间短、防锈时间长,对金属无腐蚀性,不含有毒有害物,对环境无污染。
具体实施方式
一种水基除锈防锈液，由下列重量份(公斤)成：辛基苯酚聚氧乙烯醚1-2、油酸聚氧乙烯酯2.5、乙醇22、柠檬酸1.5、磷酸锌2.5、十二烷基硫酸钠1.9、2，6-二叔丁基-α-二甲胺基对苯酚2、异丙醇1.5、乙氧基化三羟甲基丙烷三丙烯酸酯11、EDTA二钠1.5、助剂4.5、水300。所述的助剂由下列重量份(公斤)的原料制成：聚氧乙烯山梨糖醇酐单油酸酯3、纳米二氧化钛0.1、三聚磷酸钠1、硅酸钠2、乌洛托品2、对苯二酚1、硼砂3、尿素3、过硫酸铵1、桃胶2、水20；所述助剂的制备方法是将过硫酸铵溶于水后，再加入其它剩余物料，搅拌10-15分钟，加热至70-80℃，搅拌反应1-2小时，即得。
所述水基除锈防锈液的制备方法，包括以下步骤：将水加热至45℃，加入辛基苯酚聚氧乙烯醚、油酸聚氧乙烯酯、十二烷基硫酸钠；继续加热到87℃，加入乙醇、2，6-二叔丁基-α-二甲胺基对苯酚、异丙醇、乙氧基化三羟甲基丙烷三丙烯酸酯、EDTA二钠，搅拌13分钟；加入其他剩余成分，继续搅拌18分钟即得。
该实施例得到的水基除锈防锈液按国家标准检测，湿热试验*(1)合格；盐水浸渍试验*(1)：合格；腐蚀试验*(2)：合格；除膜性(次)＜6。将所制备的水基除锈防锈液刷涂在新加工成的、且没有油污的钢板基体表面，置于室内20天未见明显锈痕。

Claims (2)

1.一种水基除锈防锈液，其特征在于由下列重量份的原料制成：辛基苯酚聚氧乙烯醚1-2、油酸聚氧乙烯酯2-3、乙醇20-23、柠檬酸1-2、磷酸锌2-3、十二烷基硫酸钠1.3-2.4、2，6-二叔丁基-α-二甲胺基对苯酚1.2-2.3、异丙醇1-2、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、EDTA二钠1-2、助剂4-5、水300；所述的助剂由下列重量份的原料制成：聚氧乙烯山梨糖醇酐单油酸酯2-3、纳米二氧化钛0.1-0.2、三聚磷酸钠1-2、硅酸钠1-2、乌洛托品1-2、对苯二酚1-2、硼砂3-4、尿素2-3、过硫酸铵1-2、桃胶2-3、水20-24；所述助剂的制备方法是将过硫酸铵溶于水后，再加入其它剩余物料，搅拌10-15分钟，加热至70-80℃，搅拌反应1-2小时，即得。
2.根据权利要求1所述水基除锈防锈液的制备方法，其特征在于包括以下步骤：将水加热至40-50℃，加入辛基苯酚聚氧乙烯醚、油酸聚氧乙烯酯、十二烷基硫酸钠；继续加热到85-90℃，加入乙醇、2，6-二叔丁基-α-二甲胺基对苯酚、异丙醇、乙氧基化三羟甲基丙烷三丙烯酸酯、EDTA二钠，搅拌10-15分钟；加入其他剩余成分，继续搅拌15-20分钟即得。
CN201410063833.2A 2014-02-25 2014-02-25 一种水基除锈防锈液及其制备方法 Expired - Fee Related CN103882450B (zh)