CN103642287B - 一种水溶性防锈液及其制备方法 - Google Patents
一种水溶性防锈液及其制备方法 Download PDFInfo
- Publication number
- CN103642287B CN103642287B CN201310612405.6A CN201310612405A CN103642287B CN 103642287 B CN103642287 B CN 103642287B CN 201310612405 A CN201310612405 A CN 201310612405A CN 103642287 B CN103642287 B CN 103642287B
- Authority
- CN
- China
- Prior art keywords
- water
- sodium
- urea
- soluble
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种水溶性防锈液，由下列重量份的原料制成：苯甲酸钠1-2、尿素3-4、乙酰柠檬酸三(2-乙基已)酯3-5、丙烯酸3-5、甲基丙烯酸羟乙酯10-15、3－甲基－1－丁醇3-4、氟硅酸钠4-5、三聚氰胺甲醛树脂12-14、十二烷基苯磺酸钠1-2、EDTA二钠1-2、助剂4-5、水300。本发明使用多种有机高分子聚合物单体以及增塑剂、螯合剂共同作用，能在金属表面形成薄膜，起到隔绝空气，防氧化的作用，薄膜易清除，水洗即掉；本发明有害物质少，成本低，适用于金属制品、机械零件的长短期防锈都可以，用于长期防锈只需放入防水袋中保存即可。
Description
技术领域
本发明涉及防锈技术领域，尤其涉及一种水溶性防锈液及其制备方法。
背景技术
金属表面防锈是工业生产中的重要课题，传统的防锈液、防锈油有优点也有缺点。普通防锈水中含大量的亚硝酸钠，有致癌性，不利于环保和人身体健康，而采用保湿剂延长防锈水的寿命，又带来沾手、沾灰尘的弊病，且不能长期防锈；一般硬膜防锈油虽然适合长期防锈，成膜也透明美观，但是无色透明的树脂种类较少，不稳定也易氧化变色，还需要有机溶剂溶解，带来易燃易爆的危险也不利于环保和健康；一般的防锈油使用矿物油，难降解，而且用于短期防锈时也会带来除油难的问题。因此，研究综合性能更加优异，针对不同场合研究更加适合的防锈产品是新的方向和趋势。
发明内容
本发明的目的在于提供一种水溶性防锈液及其制备方法，该防锈液具有防锈时间长、操作简便、易清洗的特点。
本发明的技术方案如下：
一种水溶性防锈液，其特征在于由下列重量份的原料制成：苯甲酸钠1-2、尿素3-4、乙酰柠檬酸三(2-乙基己)酯3-5、丙烯酸3-5、甲基丙烯酸羟乙酯10-15、3－甲基－1－丁醇3-4、氟硅酸钠4-5、三聚氰胺甲醛树脂12-14、十二烷基苯磺酸钠1-2、EDTA二钠1-2、助剂4-5、水300。所述的助剂由下列重量份的原料制成：烷基酚聚氧乙烯醚4-5、纳米二氧化钛0.1-0.2、儿茶酚1-2、吗啉2-3、阿拉伯胶2-3、硅酸钠1-2、尿素3-4、过硫酸铵1-2、水20-24；制备方法是将过硫酸铵溶于水后，再加入其它剩余物料，搅拌10-15分钟，加热至70-80℃，搅拌反应1-2小时，即得。
所述水溶性防锈液的制备方法，其特征在于包括以下步骤：将水加热至40-50℃，加入十二烷基苯磺酸钠、EDTA二钠；继续加热到85-90℃，加入苯甲酸钠、尿素、乙酰柠檬酸三(2-乙基己)酯、丙烯酸、甲基丙烯酸羟乙酯、3－甲基－1－丁醇、氟硅酸钠、三聚氰胺甲醛树脂，搅拌10-15分钟；加入其他剩余成分，继续搅拌10-15分钟，即得。
本发明的有益效果
本发明使用多种有机高分子聚合物单体以及增塑剂、螯合剂共同作用，能在金属表面形成薄膜，起到隔绝空气，防氧化的作用，薄膜易清除，水洗即掉；本发明有害物质少，成本低，适用于金属制品、机械零件的长短期防锈都可以，用于长期防锈只需放入防水袋中保存即可。
具体实施方式
一种水溶性防锈液，由下列重量份（公斤）的原料制成：苯甲酸钠1.5、尿素3.5、乙酰柠檬酸三(2-乙基己)酯4、丙烯酸4、甲基丙烯酸羟乙酯13、3－甲基－1－丁醇3.5、氟硅酸钠4.5、三聚氰胺甲醛树脂13、十二烷基苯磺酸钠1.5、EDTA二钠1.5、助剂4.5、水300。所述的助剂由下列重量份（公斤）的原料制成：烷基酚聚氧乙烯醚5、纳米二氧化钛0.1、儿茶酚1、吗啉2、阿拉伯胶2、硅酸钠1、尿素3、过硫酸铵1、水20；制备方法是将过硫酸铵溶于水后，再加入其它剩余物料，搅拌10-15分钟，加热至70-80℃，搅拌反应1-2小时，即得。
所述水溶性防锈液的制备方法，包括以下步骤：将水加热至45，加入十二烷基苯磺酸钠、EDTA二钠；继续加热到88℃，加入苯甲酸钠、尿素、乙酰柠檬酸三(2-乙基己)酯、丙烯酸、甲基丙烯酸羟乙酯、3－甲基－1－丁醇、氟硅酸钠、三聚氰胺甲醛树脂，搅拌13分钟；加入其他剩余成分，继续搅拌13分钟，即得。
该实施例得到的水溶性防锈液按国家标准检测，湿热试验*(1)合格；盐水浸渍试验*(1)：合格；腐蚀试验*(2)：合格；除膜性（次）＜6。将所制备的水溶性防锈液刷涂在新加工成的、且没有油污的钢板基体表面，置于室内20天未见明显锈痕。
Claims (2)
1.一种水溶性防锈液，其特征在于由下列重量份的原料制成：苯甲酸钠1-2、尿素3-4、乙酰柠檬酸三(2-乙基己)酯3-5、丙烯酸3-5、甲基丙烯酸羟乙酯10-15、3-甲基-1-丁醇3-4、氟硅酸钠4-5、三聚氰胺甲醛树脂12-14、十二烷基苯磺酸钠1-2、EDTA二钠1-2、助剂4-5、水300；所述的助剂由下列重量份的原料制成：烷基酚聚氧乙烯醚4-5、纳米二氧化钛0.1-0.2、儿茶酚1-2、吗啉2-3、阿拉伯胶2-3、硅酸钠1-2、尿素3-4、过硫酸铵1-2、水20-24；所述的助剂的制备方法是将过硫酸铵溶于水后，再加入其它剩余物料，搅拌10-15分钟，加热至70-80℃，搅拌反应1-2小时，即得。
2.根据权利要求1所述水溶性防锈液的制备方法，其特征在于包括以下步骤：将水加热至40-50℃，加入十二烷基苯磺酸钠、EDTA二钠；继续加热到85-90℃，加入苯甲酸钠、尿素、乙酰柠檬酸三(2-乙基己)酯、丙烯酸、甲基丙烯酸羟乙酯、3-甲基-1-丁醇、氟硅酸钠、三聚氰胺甲醛树脂，搅拌10-15分钟；加入其他剩余成分，继续搅拌10-15分钟，即得。