CN103859868B - Antibiotic bed mattress and preparation method thereof - Google Patents

Abstract

The invention discloses a kind of antibiotic bed mattress and preparation method thereof. Described antibiotic bed mattress, is made up of the raw material of following weight parts: vinylon fibre 85-95 part, pupa albumen fiber 5-15 part, complex antimicrobials 0.5-1.5 part. Antibiotic bed mattress of the present invention, bacteriostasis rate is high, safety and Health.

Description

Antibiotic bed mattress and preparation method thereof

Technical field

The present invention relates to a kind of mattress and preparation method thereof, relate in particular to a kind of antibiotic bed mattress andPreparation method.

Background technology

Acupuncture cotton is a kind of without weaving, directly fiber is become to the product of flocculus with acupuncture. WithNatural cotton, cashmere, wool, camel hair, flaxen fiber, bamboo fibre, zein fiber, soybean fibreThe acupuncture cotton of the making such as dimension does filler or base material, product softness, fluffy, breathe freely,Can be used as mattress.

Mattress is in order to ensure that consumer secures good health and comfortable sleep and the one that uses is situated betweenArticle between human body and bed.

Conventional acupuncture cotton preparation method is: evenly mix fiber (1), and feeding opener entersRow shredding; (2) through carding machine combing; (3) carry out lapping by lapping machine; (4) through acupunctureMachine, lower thorn and upper thorn; (5) toast through baking oven; (6) through pressure roller cooling and shaping, finally outputFinished product acupuncture cotton. This acupuncture cotton can use as mattress.

There is the poor shortcoming of anti-microbial property in existing mattress.

Summary of the invention

A kind of antibiotic bed mattress, is made up of the raw material of following weight parts: vinylon fibre 85-95 part, silkwormPupa protein fiber 5-15 part.

A kind of antibiotic bed mattress, is made up of the raw material of following weight parts: vinylon fibre 85-95 part, silkwormPupa protein fiber 5-15 part, complex antimicrobials 0.5-1.5 part.

Preferably,

Described complex antimicrobials is made up of following compositions in weight percentage: poly hexamethylene biguanideHydrochloride 85-95% and coupling agent 5-15%.

Described coupling agent is 2-[(2-amino-ethyl) amino] ethanol zirconium complex and/or silane coupledAgent SI-40.

Described coupling agent is made up of following compositions in weight percentage: 40-60%2-[(2-amino-ethyl)Amino] ethanol zirconium complex and 40-60% silane coupler SI-40.

Concrete,

Described hexamethylene, No. CAS: 32289-58-0.

Described 2-[(2-amino-ethyl) amino] ethanol zirconium complex, No. CAS: 103373-95-1.

Described silane coupler SI-40, No. CAS: 11099-06-2.

The preparation method of antibiotic bed mattress of the present invention is:

(1) take in proportion each fiber, mix, add complex antimicrobials, mix, feeding is openedPine machine carries out shredding;

(2) through carding machine combing;

(3) by lapping machine lapping;

(4) through needing machine, lower thorn and upper thorn;

(5) toast through baking oven;

(6) through pressure roller cooling and shaping. Final output finished product antibiotic bed mattress.

Antibiotic bed mattress of the present invention, bacteriostasis rate is high, safety and Health.

Detailed description of the invention

Embodiment 1-4

(1) take each fiber by the corresponding embodiment 1-4 of table 1, each fiber is mixed; AgainComplex antimicrobials is added in composite fibre, guarantee to mix, then take the side of multilayer tilingFormula feeding opener carries out shredding;

(2) fiber after shredding, is sucked in the hopper being connected with carding machine and is stored by induced-draught fan,By carrying out combing on hopper feeding carding machine;

(3) fiber after combing is by a lapping of lapping machine;

(4) enter needing machine, carry out lower thorn and upper thorn;

(5) enter baking oven and toast, control baking temperature at 160 DEG C, baking time is 25Second;

(6), through pressure roller cooling and shaping, finally export the antibiotic bed mattress of the present invention of finished product.

Embodiment 5

By table 1, corresponding embodiment 5 takes each fiber, adopts and the essentially identical side of embodiment 1-4Method is prepared, and unique difference is: step is not added any antiseptic and coupling agent in (1).

Table 1: antibiotic bed mattress formula table unit: kilogram

Test case 1

Adopt standard GB/T/T20944.3-2008 " the 3rd of evaluation of antibacterial textile performancePoint: succusion " carry out antibiotic property quantitative test, adopt color fastness to washing testing machine washing methods,The bacteriostasis rate of the antibiotic bed mattress after 5 times is washed in test, and test result is in table 2.

Table 2: bacteriostasis rate test chart after washing 5 times

	Bacteriostasis rate (Escherichia coli), %
		Embodiment 1	65.8
Embodiment 2	62.4
		Embodiment 3	60.7
Embodiment 4	45.5
		Embodiment 5	24.2

Claims (2)

1. an antibiotic bed mattress, is characterized in that, is made up: polyvinyl of the raw material of following weight partsFiber 85-95 part, pupa albumen fiber 5-15 part, complex antimicrobials 0.5-1.5 part;

Described complex antimicrobials is made up of following compositions in weight percentage: poly hexamethylene biguanideHydrochloride 85-95% and coupling agent 5-15%;

Described coupling agent is made up of following compositions in weight percentage: 40-60%2-[(2-amino-ethyl)Amino] ethanol zirconium complex and 40-60% silane coupler SI-40.

2. the preparation method of antibiotic bed mattress as claimed in claim 1, is characterized in that, by followingStep composition:

(1) take in proportion each fiber, mix, add complex antimicrobials, mix, feeding is openedPine machine carries out shredding;

(2) through carding machine combing;

(3) by lapping machine lapping;

(4) through needing machine, lower thorn and upper thorn;

(5) toast through baking oven;

(6) through pressure roller cooling and shaping.