CN103849264A - Environmental protection coating capable of emitting far infrared, and preparation method thereof - Google Patents
Environmental protection coating capable of emitting far infrared, and preparation method thereof Download PDFInfo
- Publication number
- CN103849264A CN103849264A CN201210500522.9A CN201210500522A CN103849264A CN 103849264 A CN103849264 A CN 103849264A CN 201210500522 A CN201210500522 A CN 201210500522A CN 103849264 A CN103849264 A CN 103849264A
- Authority
- CN
- China
- Prior art keywords
- water
- environmental protection
- far infrared
- protection coating
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environmental protection coating capable of emitting far infrared, and a preparation method thereof. The environmental protection coating comprises, by weight, 20 to 40 parts of sienna stone or medical stone, 30 to 60 parts of water-based acrylic resin, 0.2 to 1 part of an antifoaming agent, 1 to 5 parts of a film forming auxiliary agent, 0.2 to 5 parts of a thickening agent, 0.1 to 5 parts of an emulsifier, 0.1 to 3 parts of a levelling agent, and 5 to 50 parts of water. The main base material of the environmental protection coating is water-based acrylic resin; the solvent is water; no harmful volatile organic solvent, such as benzene and methylbenzene, is released in spraying and drying processes. Natural materials capable of emitting far infrared are added into the environmental protection coating, so that when furniture is coated with the environmental protection coating, continuous emitting of far infrared is realized, human body metabolism is promoted, human body health is improved, indoor living environment is improved, and natural and environmental protection living space is provided.
Description
Technical field
The present invention relates to a kind of coating, relate in particular to a kind of environmentally safe, releasing far infrared furniture paint application and preparation method thereof.
Background technology
Along with the raising of people's living standard, more and more higher to the demand of living environment, require comfortable time, more to focus on the healthy impact of environment on human body.
In furniture, the coating material that is absolutely necessary.Conventional coating in the market, contains hazardous property volatile matter mostly, as benzene, dimethylbenzene, formaldehyde etc., and constantly volatilization in the use of furniture, serious environment pollution and people's health.
Far infrared rays is can deep enough skin and hypodermic a kind of ray in all sunlights.Far infrared rays impels subcutaneous deep temperature rise, and makes Marjoram Extract, accelerates blood circulation, be conducive to remove blood vessel and hoard objectionable impurities in thing and body, the vigor that can increase cell is adjusted neurohumor body, adds excitometabolic, has aging, the strengthening immune system effect that prevents.Far infrared rays has been widely used in treating in the therapeutic equipment and anti-ageing healthcare beauty apparatus of the various diseases that blood circulation and microcirculation disturbance causes, but the application of far infrared rays aspect coating also rarely has report.
Summary of the invention
The object of this invention is to provide one does not have volatile harmful material, and has the environment-friendly type coating of releasing far infrared function.
Adopt following technical scheme in order to realize object of the present invention.
Environment-friendly type coating of the present invention, comprises following component by weight: loess stone or medical stone 20-40, water-borne acrylic resin 30-60, defoamer 0.2-1, film coalescence aid 1-5, thickening material 0.2-5, emulsifying agent 0.1-5, flow agent 0.1-3, water 5-50.
Defoamer described in technique scheme, film coalescence aid, thickening material, emulsifying agent, flow agent can be selected from reagent conventional in the preparation of water-miscible paint, without any particular requirement, all can buy in market.
The material that produces far infrared rays has a lot, as loess stone, medical stone, charcoal, tourmalinite etc.
Loess stone is natural crystal, has radiation and the function of reflection to the useful far infrared rays of human body, and its far infrared rays reflectivity reaches 93%, and for greenhouse, the occasions such as decorative and health-care product can have health protection and therapeutic action.The far infrared rays of loess stone radiation is more easily penetrated into human body, cause the resonance of atom and the molecule of human body cell, impel subcutaneous deep temperature rise, and make Marjoram Extract, accelerate blood circulation, be conducive to remove blood vessel and hoard objectionable impurities in thing and body, there is aging, the strengthening immune system effect that prevents.
Medical stone is also a kind of natural medicine ore, contains the necessary trace element of human body, and can discharge far infrared rays.
A kind of releasing far infrared environmental protection coating material of the present invention, its preparation method is as follows:
1. the loess stone of solid state or medical stone powder being broken into granularity is 2500-3000 object ultrafine powder;
2. the water that adds 2-5 doubly to measure in powder, stirs, and room temperature is placed 24 hours, removes upper strata liquid, obtains throw out;
3. by throw out at 30-50 ℃ of complete drying powdered;
4. under 400-800rpm/min stirs, add water to stir water-borne acrylic resin, obtain acrylic resin soln;
5. the powder that slowly adds step 3. to make under 400-800rpm/min stirs acrylic resin soln stirs, and obtains mixed solution I;
6. defoamer, film coalescence aid, thickening material, emulsifying agent and flow agent are mixed, make mixed solution II;
7. the mixed solution I of 5. step being made adds mixed solution II to stir under 800-1200rpm/min stirs.
Loess stone and medical stone all have its intrinsic color, affect the color of coating after being prepared into coating, and have intersecting of color with the follow-up coating adding, and affect the allotment of the color of coating.The present invention adopts loess stone and medical stone powder to be broken into after ultrafine powder, be soaked in water 24 hours, the intrinsic color of stripping loess stone and medical stone by water-soluble go out, remove supernatant liquor, be conducive to remove loess stone or the intrinsic color of medical stone.
Loess stone or medical stone powder are broken into ultrafine powder by the present invention, is prepared into after coating and is easy to spraying, prevents the phenomenon because of the blocked up check surface of rete after spraying.On the other hand, be ground into after ultrafine powder, the surface-area of loess stone or medical stone increases, and effectively improves the far infrared rays amount discharging.
In coating of the present invention, add and discharge ultrared natural materials, paint spay-coating, after furniture, can penetrate far infrared rays by type discharge, strengthens human body metabolism, promotes health, and improves indoor living environment, and the living space of nature environmental protection is provided.
On the other hand, the main base-material of coating of the present invention is water-soluble water-borne acrylic resin, and solvent is water, in spraying and drying process, all can not discharge the volatile organic solvent that benzene, toluene etc. are harmful to health, and is a kind of environment-friendly type aqueous coating.
Embodiment
Following non-limiting example can make the present invention of those of ordinary skill in the art's comprehend, but does not limit the present invention in any way.
Embodiment 1
A releasing far infrared environmental protection coating material, comprises following component:
Loess stone 300g,
Water-borne acrylic resin 400g,
Defoamer 5g,
Film coalescence aid 20g,
Thickening material 30g,
Dispersion agent 20g,
Flow agent 15g,
Water 400g.
Loess stone is purchased from Jinan Mao Caishi industry company limited; Water-borne acrylic resin is purchased from Tai Xin plastic raw materials company limited; Defoamer is the FoamasterNXZ of German Ke Ning chemical company; Film coalescence aid is the FilmerC40 of Union Carbide Corp of the U.S.; Described thickening material is the RM-2020 of Rhom and Hass of the U.S.; Described dispersion agent is the SN-5040 of German Ke Ning chemical company; Described flow agent is the TEGO Glide450 of German Di Gao chemical company.
Preparation method is as follows:
1. the loess stone flour of solid state being broken into granularity is 2500-3000 object ultrafine powder;
2. the water that adds 5 times of amounts in powder, stirs, and room temperature is placed 24 hours, removes upper strata liquid, obtains throw out;
3. by throw out at 30-50 ℃ of complete drying powdered;
4. under 600rpm/min stirs, add water to stir water-borne acrylic resin, obtain acrylic resin soln;
5. the powder that slowly adds step 3. to make under 600rpm/min stirs acrylic resin soln stirs, and obtains mixed solution I;
6. defoamer, film coalescence aid, thickening material, emulsifying agent and flow agent are mixed, make mixed solution II;
7. the mixed solution I of 5. step being made adds mixed solution II to stir under 1000rpm/min stirs.
Claims (2)
1. a releasing far infrared environmental protection coating material, is characterized in that comprising by weight following component: loess stone or medical stone 20-40, water-borne acrylic resin 30-60, defoamer 0.2-1, film coalescence aid 1-5, thickening material 0.2-5, emulsifying agent 0.1-5, flow agent 0.1-3, water 5-50.
2. a kind of releasing far infrared environmental protection coating material according to claim 1, is characterized in that its preparation method is as follows:
1. the loess stone of solid state or medical stone powder being broken into granularity is 2500-3000 object ultrafine powder;
2. the water that adds 2-5 doubly to measure in powder, stirs, and room temperature is placed 24 hours, removes upper strata liquid, obtains throw out;
3. by throw out at 30-50 ℃ of complete drying powdered;
4. under 400-800rpm/min stirs, add water to stir water-borne acrylic resin, obtain acrylic resin soln;
5. the powder that slowly adds step 3. to make under 400-800rpm/min stirs acrylic resin soln stirs, and obtains mixed solution I;
6. defoamer, film coalescence aid, thickening material, emulsifying agent and flow agent are mixed, make mixed solution II;
7. the mixed solution I of 5. step being made adds mixed solution II to stir under 800-1200rpm/min stirs.