CN103846990B - A kind of production method of bamboo fiber of weaving - Google Patents

Abstract

To weave the production method of bamboo fiber, comprise the following steps: choose bamboo age at the bamboo wood of 0.8 ~ 2 year; Remove the bamboo tip, the bamboo elbow part of bamboo wood, intercept into the thick bamboo tube of 3 ~ 5 meters with a chainsaw; Use wafer separator burst; Bamboo chip is sent into breaker beater, from surf green part, carries out comb separate, comb is separated thing by blower fan blowout dust and impurity, obtain the bamboo chip after bamboo fiber and comb solution; The out-of-flatness surface of the bamboo chip after comb solution is cut smooth, then sends into the comb solution that breaker beater carries out lower one deck; Repeat comb separate and cut step 5 ~ 8 time, until the thickness of bamboo chip is 2 ~ 5mm.The present invention can ensure that bamboo wood is controlled in even, neat, clear, the long fineness of each layer comb solution bamboo fiber out.

Description

A kind of production method of bamboo fiber of weaving

Technical field

The present invention is specifically related to a kind of production method of bamboo fiber of weaving.

Background technology

Producing bamboo fibre with bamboo wood is the focus of current bamboo processing and the developing direction of following bamboo wood.The method of bamboo fiber produced by existing bamboo wood, owing to not considering the heterogeneity of bamboo wood self, cause the bamboo fiber geometric shape produced to differ greatly, fiber is different in size, thickness is uneven, and bamboo block, stalk shape thing are more, limit the commercial application of bamboo fiber.

Summary of the invention

Technical problem to be solved by this invention is the production method providing a kind of bamboo fiber of weaving, and even, neat, clear, the long fineness of obtained bamboo fiber is controlled.

The present invention solves the problems of the technologies described above by the following technical programs: a kind of production method of bamboo fiber of weaving, comprises the following steps:

(1) selection: choose contemporaneity growth and bamboo age at the bamboo wood of 0.8 ~ 2 year;

(2) cut off: by little for initial and end diameter difference, whole linearly bamboo wood, remove the bamboo tip, bamboo elbow part, intercept into the thick bamboo tube of 3 ~ 5 meters with a chainsaw;

(3) burst: each thick bamboo tube is divided into 4 ~ 8 bamboo chips with wafer separator;

(4) comb is separated: bamboo chip is sent into breaker beater, carries out comb and separate from surf green part, comb is separated thing by blower fan blowout dust and impurity, obtains the bamboo chip after bamboo fiber and comb solution;

(5) cut: the bamboo chip after comb solution is placed on basket weaver's lathe and utilizes planing tool to carry out machining, the out-of-flatness surface of bamboo chip is cut smooth, then sends into the comb solution that breaker beater carries out lower one deck;

(6) repeat step (4) to step (5) 5 ~ 8 times, until bamboo chip becomes the tabasheer thin slice of 2 ~ 5mm thickness, obtain the bamboo fiber of 5 ~ 8 kinds of different qualities simultaneously.

Beneficial effect of the present invention is: ensure that bamboo wood is controlled in even, neat, clear, the long fineness of each layer comb solution bamboo fiber out.

Accompanying drawing explanation

The invention will be further described in conjunction with the embodiments with reference to the accompanying drawings.

Fig. 1 is the flow chart of the production method of a kind of bamboo fiber of weaving of the present invention.

Detailed description of the invention

Refer to Fig. 1, a kind of production method of bamboo fiber of weaving, comprises the following steps:

(1) selection: choose contemporaneity growth and bamboo age at the bamboo wood of 0.8 ~ 2 year;

(2) cut off: by little for initial and end diameter difference, whole linearly bamboo wood, remove the bamboo tip, bamboo elbow part, intercept into the thick bamboo tube of 3 ~ 5 meters with a chainsaw;

(3) burst: each thick bamboo tube is divided into 4 ~ 8 bamboo chips with wafer separator;

(4) comb is separated: bamboo chip is sent into breaker beater, carries out comb and separate from surf green part, comb is separated thing by blower fan blowout dust and impurity, obtains the bamboo chip after clear, neat bamboo fiber and comb solution;

(5) cut: the bamboo chip after comb solution is carried out machining, the out-of-flatness surface of bamboo chip is cut smooth, then sends into the comb solution that breaker beater carries out lower one deck;

(6) repeat step (4) to step (5) 5 ~ 8 times, until bamboo chip becomes the tabasheer thin slice of 2 ~ 5mm thickness, obtain the bamboo fiber of 5 ~ 8 kinds of different qualities simultaneously.

The different quality obtained and bamboo fiber at different levels are carried out fine design respectively, the bamboo fibre that can weave can be obtained by a series of means such as boiling, sub-drifts.

Embodiment one

Choose bamboo age in the new fresh and tender bamboo (i.e. cizu) of 8 months, remove the bamboo tip and bamboo head part with a chainsaw, the thick bamboo tube of residue length 5m; With wafer separator, thick bamboo tube is divided into six bamboo chips; Bamboo chip orientation is sent into breaker beater, from surf green part, carries out ground floor comb separate, breaker beater is combed solution comb solution thing out and bamboo fiber blower fan blowout the inside dust and impurity simultaneously, obtain clear, neat bamboo fiber; The bamboo chip combed by ground floor after solution carries out machining, and the out-of-flatness surface of being combed by bamboo chip after solution cuts smooth, then enters the comb solution of lower one deck; So repeatedly successively comb solution 5 times, bamboo chip becomes the tabasheer thin slice of the 2mm thickness cannot combing solution again, obtains the bamboo fiber of 5 kinds of different qualities.

Embodiment two

Choose bamboo age in the fresh mao bamboon of 2 years, remove the bamboo tip and bamboo head part with a chainsaw, be cut into 2 sections of thick bamboo tubes, every section of 3m; With wafer separator, thick bamboo tube is divided into eight bamboo chips; Bamboo chip orientation is sent into breaker beater, from surf green part, carries out ground floor comb separate, breaker beater is combed solution comb solution thing out and bamboo fiber blower fan blowout the inside dust and impurity simultaneously, obtain clear, neat bamboo fiber; The bamboo chip combed by ground floor after solution carries out machining, and the out-of-flatness surface of being combed by bamboo chip after solution cuts smooth, then enters the comb solution of lower one deck; So repeatedly successively comb solution 8 times, bamboo chip becomes the tabasheer thin slice of the 5mm thickness cannot combing solution again, obtains the bamboo fiber of 8 kinds of different qualities.

Embodiment three

Choose bamboo age on the green bamboo of 1 year, remove the bamboo tip and bamboo head part with a chainsaw, be cut into 2 sections of thick bamboo tubes, every section of 4m; With wafer separator, thick bamboo tube is divided into eight bamboo chips; Bamboo chip orientation is sent into breaker beater, from surf green part, carries out ground floor comb separate, breaker beater is combed solution comb solution thing out and bamboo fiber blower fan blowout the inside dust and impurity simultaneously, obtain clear, neat bamboo fiber; The bamboo chip combed by ground floor after solution carries out machining, and the out-of-flatness surface of being combed by bamboo chip after solution cuts smooth, then enters the comb solution of lower one deck; So repeatedly successively comb solution 7 times, bamboo chip becomes the tabasheer thin slice of the 4mm thickness cannot combing solution again, obtains the bamboo fiber of 7 kinds of different qualities.

For prepared by the direct fibrillation of bamboo wood bamboo fiber exist Fiber Uniformity poor, impurity content is high, too slightly, too short, this present situation of spinning cannot be realized, the present invention proposes a kind of production method by bamboo wood direct processing submicron order spinnable bamboo fiber.In order to ensure bamboo fiber uniformity, the present invention adopts machinery successively to comb solution fiber opening method, effectively can eliminate the gradient characteristics that bamboo wood presents, and by cutter cutting process, the stratiform bamboo wood of disposable non-fibrillation is thoroughly removed, this part material is avoided to continue the comb stalk shape thing that brings of solution and block, thus the fiber definition that processing is obtained, neat, even, and long fineness is controlled.The long fineness uniformity of bamboo fiber good (length 3-8cm, bamboo fiber diameter 50-150 micron) that the present invention obtains, nothing slightly stalk, powder and other impurity, be convenient to carry out process of refinement, bamboo fiber can reach pure and spin and blending technology index request.

Claims (1)

1. to weave the production method of bamboo fiber, it is characterized in that: comprise the following steps:

(1) selection: choose contemporaneity growth and bamboo age at the bamboo wood of 0.8 ~ 2 year;

(2) cut off: by little for initial and end diameter difference, whole linearly bamboo wood, remove the bamboo tip, bamboo elbow part, intercept into the thick bamboo tube of 3 ~ 5 meters with a chainsaw;

(3) burst: each thick bamboo tube is divided into 4 ~ 8 bamboo chips with wafer separator;

(4) comb is separated: bamboo chip is sent into breaker beater, carries out comb and separate from surf green part, comb is separated thing by blower fan blowout dust and impurity, obtains the bamboo chip after bamboo fiber and comb solution;

(5) cut: the bamboo chip after comb solution is carried out machining, the out-of-flatness surface of bamboo chip is cut smooth, then sends into the comb solution that breaker beater carries out lower one deck;

(6) repeat step (4) to step (5) 5 ~ 8 times, until bamboo chip becomes the tabasheer thin slice of 2 ~ 5mm thickness, obtain the bamboo fiber of 5 ~ 8 kinds of different qualities simultaneously.