CN103790018A - 织物耐久拒水整理剂的制备方法 - Google Patents
织物耐久拒水整理剂的制备方法 Download PDFInfo
- Publication number
- CN103790018A CN103790018A CN201310621937.6A CN201310621937A CN103790018A CN 103790018 A CN103790018 A CN 103790018A CN 201310621937 A CN201310621937 A CN 201310621937A CN 103790018 A CN103790018 A CN 103790018A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- weight parts
- water repellent
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种织物耐久拒水整理剂的制备方法,包括如下步骤:1)取100-150质量份去离子水、5-8质量份聚乙烯醇、30-35质量份环氧树脂、10-15质量份丙酮混合,在90-95℃反应40-45分钟;2)然后同时加入1-2质量份聚丙烯酸、5-6质量份邻苯二甲酸二甲酯、80-90质量份去离子水,5-10分钟内投料完毕,搅拌混合均匀,在80-85℃反应1-2小时;3)冷却至室温,依次加入1-2质量份三乙醇胺、1-2质量份尿素、1-2质量份氢氧化钠、7-8质量份羟丙基甲基纤维素、4-5质量份十二烷基三甲基氯化铵、6-7质量份醋酸铵、5-7质量份氯化钠、1-2质量份甲基含氢硅油乳液,搅拌混合均匀,即得织物耐久拒水整理剂。本发明制备的织物耐久拒水整理剂的拒水效果好,耐水洗、干洗。
Description
技术领域
本发明涉及织物耐久拒水整理剂的制备方法。
背景技术
目前市面上的织物拒水整理剂拒水效果一般,不耐水洗、干洗。
发明内容
本发明的目的在于提供一种织物耐久拒水整理剂的制备方法,其制备的织物耐久拒水整理剂的拒水效果好,耐水洗、干洗。
为实现上述目的,本发明的技术方案是设计一种织物耐久拒水整理剂的制备方法,包括如下步骤:
1)取100-150质量份去离子水、5-8质量份聚乙烯醇、30-35质量份环氧树脂、10-15质量份丙酮混合,在90-95℃反应40-45分钟;
2)然后同时加入1-2质量份聚丙烯酸、5-6质量份邻苯二甲酸二甲酯、80-90质量份去离子水,5-10分钟内投料完毕,搅拌混合均匀,在80-85℃反应1-2小时;
3)冷却至室温,依次加入1-2质量份三乙醇胺、1-2质量份尿素、1-2质量份氢氧化钠、7-8质量份羟丙基甲基纤维素、4-5质量份十二烷基三甲基氯化铵、6-7质量份醋酸铵、5-7质量份氯化钠、1-2质量份甲基含氢硅油乳液,搅拌混合均匀,即得织物耐久拒水整理剂。
本发明的优点和有益效果在于:提供一种织物耐久拒水整理剂的制备方法,其制备的织物耐久拒水整理剂的拒水效果好,耐水洗、干洗。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种织物耐久拒水整理剂的制备方法,包括如下步骤:
1)取150质量份去离子水、8质量份聚乙烯醇、35质量份环氧树脂、15质量份丙酮混合,在95℃反应45分钟;
2)然后同时加入2质量份聚丙烯酸、6质量份邻苯二甲酸二甲酯、90质量份去离子水,10分钟内投料完毕,搅拌混合均匀,在85℃反应2小时;
3)冷却至室温,依次加入2质量份三乙醇胺、2质量份尿素、2质量份氢氧化钠、8质量份羟丙基甲基纤维素、5质量份十二烷基三甲基氯化铵、7质量份醋酸铵、7质量份氯化钠、2质量份甲基含氢硅油乳液,搅拌混合均匀,即得织物耐久拒水整理剂。
实施例2
一种织物耐久拒水整理剂的制备方法,包括如下步骤:
1)取100质量份去离子水、5质量份聚乙烯醇、30质量份环氧树脂、10质量份丙酮混合,在90℃反应40分钟;
2)然后同时加入1质量份聚丙烯酸、5质量份邻苯二甲酸二甲酯、80质量份去离子水,5分钟内投料完毕,搅拌混合均匀,在80℃反应1小时;
3)冷却至室温,依次加入1质量份三乙醇胺、1质量份尿素、1质量份氢氧化钠、7质量份羟丙基甲基纤维素、4质量份十二烷基三甲基氯化铵、6质量份醋酸铵、5质量份氯化钠、1质量份甲基含氢硅油乳液,搅拌混合均匀,即得织物耐久拒水整理剂。
实施例3
一种织物耐久拒水整理剂的制备方法,包括如下步骤:
1)取130质量份去离子水、5.8质量份聚乙烯醇、34质量份环氧树脂、12质量份丙酮混合,在93℃反应43分钟;
2)然后同时加入1.2质量份聚丙烯酸、5.6质量份邻苯二甲酸二甲酯、85质量份去离子水,7分钟内投料完毕,搅拌混合均匀,在83℃反应1.5小时;
3)冷却至室温,依次加入1.2质量份三乙醇胺、1.2质量份尿素、1.2质量份氢氧化钠、7.8质量份羟丙基甲基纤维素、4.5质量份十二烷基三甲基氯化铵、6.7质量份醋酸铵、5.7质量份氯化钠、1.2质量份甲基含氢硅油乳液,搅拌混合均匀,即得织物耐久拒水整理剂。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.织物耐久拒水整理剂的制备方法,其特征在于,包括如下步骤:
1)取100-150质量份去离子水、5-8质量份聚乙烯醇、30-35质量份环氧树脂、10-15质量份丙酮混合,在90-95℃反应40-45分钟;
2)然后同时加入1-2质量份聚丙烯酸、5-6质量份邻苯二甲酸二甲酯、80-90质量份去离子水,5-10分钟内投料完毕,搅拌混合均匀,在80-85℃反应1-2小时;
3)冷却至室温,依次加入1-2质量份三乙醇胺、1-2质量份尿素、1-2质量份氢氧化钠、7-8质量份羟丙基甲基纤维素、4-5质量份十二烷基三甲基氯化铵、6-7质量份醋酸铵、5-7质量份氯化钠、1-2质量份甲基含氢硅油乳液,搅拌混合均匀,即得织物耐久拒水整理剂。