CN103788864A - 一种分子筛粉末紫外光固化涂料及其制备方法 - Google Patents

一种分子筛粉末紫外光固化涂料及其制备方法 Download PDF

Info

Publication number
CN103788864A
CN103788864A CN201410050049.8A CN201410050049A CN103788864A CN 103788864 A CN103788864 A CN 103788864A CN 201410050049 A CN201410050049 A CN 201410050049A CN 103788864 A CN103788864 A CN 103788864A
Authority
CN
China
Prior art keywords
parts
coating material
molecular sieve
acrylate
sieve powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410050049.8A
Other languages
English (en)
Inventor
张庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Baoyi Amusement Equipment Co Ltd
Original Assignee
Wuhu Baoyi Amusement Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Baoyi Amusement Equipment Co Ltd filed Critical Wuhu Baoyi Amusement Equipment Co Ltd
Priority to CN201410050049.8A priority Critical patent/CN103788864A/zh
Publication of CN103788864A publication Critical patent/CN103788864A/zh
Pending legal-status Critical Current

Abstract

一种分子筛粉末紫外光固化涂料,由下列重量份的原料制成：聚氨酯丙烯酸酯35-40、硬脂酸钙2-5、钛酸正丁酯4-6、丙氧化三羟甲基丙烷三甲基丙烯酸酯10-14、四甲基氢氧化铵1-2、分子筛粉末6-8、三氧化二锑3-5、醋酸丁酯8-12、丙烯酸异癸酯7-9、丙烯酸丁酯5-7、光引发剂1842-3、助剂4-5；本发明涂料具有优异的机械耐磨性、柔韧性，断裂伸长率高，耐化学性能和耐高低温性能好，涂膜对难以粘接的基材，如塑料，有较佳的附着力；还添加了分子筛粉末，具有吸附有害物质作用，有益于健康；通过添加三氧化二锑，阻燃效果好。本发明的助剂增加了涂料的分散性，流平性好，涂层平滑光亮。

Description

一种分子筛粉末紫外光固化涂料及其制备方法
技术领域
本发明属于涂料领域，尤其涉及一种分子筛粉末紫外光固化涂料及其制备方法。
背景技术
光固化涂料优点是固化时间短（几分之一秒到几分钟）、固化温度低、挥发分低，为省能源、省资源、无公害、高效率；但是还存在一些缺点，如自由基型光固化涂料固化过程受氧气阻抑，表面固化不良，还有黄变、易爆色、不耐低温、成本高、耐腐蚀性差等一系列问题，都需要针对不同的用途继续改良，降低生产成本，扩大用途。
发明内容
本发明的目的在于提供一种分子筛粉末紫外光固化涂料及其制备方法，该涂料具有优异的耐水性、耐热水性、耐药物性、粘结性、韧性和阻燃性能，而且容易涂装。
本发明的技术方案如下：
一种分子筛粉末紫外光固化涂料,其特征在于由下列重量份的原料制成：聚氨酯丙烯酸酯35-40、硬脂酸钙2-5、钛酸正丁酯4-6、丙氧化三羟甲基丙烷三甲基丙烯酸酯10-14、四甲基氢氧化铵1-2、分子筛粉末6-8、三氧化二锑3-5、醋酸丁酯8-12、丙烯酸异癸酯7-9、丙烯酸丁酯5-7、光引发剂184 2-3、助剂4-5；
所述助剂由以下重量份的原料制成: 活性白土2-3、纳米三氧化钨1-2、荷荷巴油1-2、衣康酸4-6、过氧化乙酰0.2-0.3、聚己二酸丙二醇酯0.2-0.3、2-甲基丙烯酸甲酯2-3、丙二醇6-9、聚二甲基硅氧烷5-7、二乙二醇二丁醚16-20；制备方法是将丙二醇、二乙二醇二丁醚、荷荷巴油混合，在10000-14000转/分搅拌下加入活性白土、纳米三氧化钨；再加入衣康酸、2-甲基丙烯酸甲酯、聚己二酸丙二醇酯、聚二甲基硅氧烷，加热至60-80℃，在1300-1500转/分下搅拌反应10-20分钟，加入过氧化乙酰，搅拌反应1-2小时，即得。
所述的分子筛粉末紫外光固化涂料的制备方法，其特征在于包括以下步骤：
（1）将硬脂酸钙、分子筛粉末混合，边搅拌边喷入雾状的钛酸正丁酯，混合均匀放置1-2小时；
（2）将聚氨酯丙烯酸酯、丙氧化三羟甲基丙烷三甲基丙烯酸酯、四甲基氢氧化铵、醋酸丁酯、丙烯酸异癸酯、丙烯酸丁酯混合，升温至60-80℃，在1200-1400/分下搅拌15-20分钟，加入和第（1）步得到的物料，降温到35℃以下再加入其他剩余成分，继续研磨搅拌10-20分钟，即得。
本发明的有益效果
本发明涂料具有优异的机械耐磨性、柔韧性，断裂伸长率高，耐化学性能和耐高低温性能好，涂膜对难以粘接的基材，如塑料，有较佳的附着力；还添加了分子筛粉末，具有吸附有害物质作用，有益于健康；通过添加三氧化二锑，阻燃效果好。本发明的助剂增加了涂料的分散性，流平性好，涂层平滑光亮。
具体实施方式
一种分子筛粉末紫外光固化涂料,由下列重量份（公斤）的原料制成：聚氨酯丙烯酸酯37、硬脂酸钙3、钛酸正丁酯5、丙氧化三羟甲基丙烷三甲基丙烯酸酯12、四甲基氢氧化铵1.5、分子筛粉末7、三氧化二锑4、醋酸丁酯10、丙烯酸异癸酯8、丙烯酸丁酯6、光引发剂184 2.5、助剂4.5；
所述助剂由以下重量份（公斤）的原料制成: 活性白土2.5、纳米三氧化钨1.5、荷荷巴油1.5、衣康酸5、过氧化乙酰0.2、聚己二酸丙二醇酯0.2、2-甲基丙烯酸甲酯2.5、丙二醇8、聚二甲基硅氧烷6、二乙二醇二丁醚18；制备方法是将丙二醇、二乙二醇二丁醚、荷荷巴油混合，在12000转/分搅拌下加入活性白土、纳米三氧化钨；再加入衣康酸、2-甲基丙烯酸甲酯、聚己二酸丙二醇酯、聚二甲基硅氧烷，加热至70℃，在1400转/分下搅拌反应15分钟，加入过氧化乙酰，搅拌反应1.5小时，即得。
所述的分子筛粉末紫外光固化涂料的制备方法，包括以下步骤：
（1）将硬脂酸钙、分子筛粉末混合，边搅拌边喷入雾状的钛酸正丁酯，混合均匀放置1.5小时；
（2）将聚氨酯丙烯酸酯、丙氧化三羟甲基丙烷三甲基丙烯酸酯、四甲基氢氧化铵、醋酸丁酯、丙烯酸异癸酯、丙烯酸丁酯混合，升温至70℃，在1300/分下搅拌17分钟，加入和第（1）步得到的物料，降温到30℃再加入其他剩余成分，继续研磨搅拌15分钟，即得。
该分子筛粉末紫外光固化涂料采用滚涂的方式涂覆于木板上。附着力≥二级，耐75％乙醇≥48 小时，耐5%NaOH≥48小时、耐5%H2SO4≥48小时,耐15％食盐水≥60 小时，硬度为3H，耐磨指数在3500转以上。

Claims (2)

1.一种分子筛粉末紫外光固化涂料,其特征在于由下列重量份的原料制成：聚氨酯丙烯酸酯35-40、硬脂酸钙2-5、钛酸正丁酯4-6、丙氧化三羟甲基丙烷三甲基丙烯酸酯10-14、四甲基氢氧化铵1-2、分子筛粉末6-8、三氧化二锑3-5、醋酸丁酯8-12、丙烯酸异癸酯7-9、丙烯酸丁酯5-7、光引发剂184 2-3、助剂4-5；
所述助剂由以下重量份的原料制成: 活性白土2-3、纳米三氧化钨1-2、荷荷巴油1-2、衣康酸4-6、过氧化乙酰0.2-0.3、聚己二酸丙二醇酯0.2-0.3、2-甲基丙烯酸甲酯2-3、丙二醇6-9、聚二甲基硅氧烷5-7、二乙二醇二丁醚16-20；制备方法是将丙二醇、二乙二醇二丁醚、荷荷巴油混合，在10000-14000转/分搅拌下加入活性白土、纳米三氧化钨；再加入衣康酸、2-甲基丙烯酸甲酯、聚己二酸丙二醇酯、聚二甲基硅氧烷，加热至60-80℃，在1300-1500转/分下搅拌反应10-20分钟，加入过氧化乙酰，搅拌反应1-2小时，即得。
2.根据权利要求1所述的分子筛粉末紫外光固化涂料的制备方法，其特征在于包括以下步骤：
（1）将硬脂酸钙、分子筛粉末混合，边搅拌边喷入雾状的钛酸正丁酯，混合均匀放置1-2小时；
（2）将聚氨酯丙烯酸酯、丙氧化三羟甲基丙烷三甲基丙烯酸酯、四甲基氢氧化铵、醋酸丁酯、丙烯酸异癸酯、丙烯酸丁酯混合，升温至60-80℃，在1200-1400/分下搅拌15-20分钟，加入和第（1）步得到的物料，降温到35℃以下再加入其他剩余成分，继续研磨搅拌10-20分钟，即得。
CN201410050049.8A 2014-02-13 2014-02-13 一种分子筛粉末紫外光固化涂料及其制备方法 Pending CN103788864A (zh)