CN103788677A - 一种新型玻璃钢复合涂层材料及其制备方法 - Google Patents
一种新型玻璃钢复合涂层材料及其制备方法 Download PDFInfo
- Publication number
- CN103788677A CN103788677A CN201410016850.0A CN201410016850A CN103788677A CN 103788677 A CN103788677 A CN 103788677A CN 201410016850 A CN201410016850 A CN 201410016850A CN 103788677 A CN103788677 A CN 103788677A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- reinforced plastic
- coating material
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型玻璃钢复合涂层材料，其特征在于，由下列重量份的原料制成：乙烯基树脂33-36、双酚A树脂10-12、氢氧化钙1-2、轻烧氧化镁2-3、氯化石蜡1-2、甲基丙烯酸酯20-25、硅烷偶联剂KH-5503-4、尿素2-3、山梨酸钾1-2、1，5-戊二醇4-6、过氧化苯甲酰4-6、玻璃纤维24-27、草木灰1-2、对羟基苯甲醚2-3、钛酸四正丁酯2-3、助剂1-2；本发明添加助剂，使材料具有良好的物理性能以及机械性能，起到补强的作用；本发明材料耐高温、抗冷冻、使用寿命长、无毒、体轻、耐火阻燃，制成的增强复合材料造价低、强度大、有韧性易于大批量生产，推广应用，适用于制作各种管道、罐体等。
Description
技术领域
本发明涉及一种复合材料及其制备方法，特别是一种新型玻璃钢复合涂层材料及其制备方法。
背景技术
玻璃钢材料是由玻璃纤维增强材料嵌入已固化的热固性树脂中或被其包裹形成复合结构的材料。目前市场上生产使用的玻璃钢材料多采用树脂浸润玻璃布材料来成型。该方法浸润效果好，所制备的玻璃纤维含量高。但由于受玻璃布体积和形状的限制，使其特别不适应用于诸如管接头、三通管件、弯头管件等不易均匀受压的产品。另外，该方法制备的玻璃钢材料其耐冲击性能差，且层合面容易发生分层。为了解决上述问题，有研究者将玻璃纤维切割成玻璃纤维粉，然后将玻璃纤维粉投入到由环氧树脂、增塑剂等组成的混合液中，再在球磨机中搅拌均匀加入填料、固化剂，由此制备成一种不含玻璃布铺层的玻璃钢材料。该方法所提供的玻璃钢材料虽然克服了玻璃布本身所导致的缺陷，但由于玻璃纤维被切割成粉状，因而其纤维本身所特有的物理特性亦被大大削弱。
发明内容
本发明的目的是提供一种新型玻璃钢复合涂层材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种新型玻璃钢复合涂层材料，由下列重量份的原料制成：乙烯基树脂33-36、双酚A 树脂10-12、氢氧化钙1-2、轻烧氧化镁2-3、氯化石蜡1-2、甲基丙烯酸酯20-25、硅烷偶联剂KH-550 3-4、尿素2-3、山梨酸钾1-2、1，5-戊二醇4-6、过氧化苯甲酰4-6、玻璃纤维24-27、草木灰1-2、对羟基苯甲醚2-3、钛酸四正丁酯2-3、助剂1-2；
所述助剂由下列重量份的原料制成：纳米氧化铝12-14、锆石4-6、云母粉3-4、氮化铝粉2-3、长石3-5、硼酸锌2-4、氧化锌5-7、碳酸氢铵3-4、氧化二丁基锡2-3、苯乙烯3-5、甲基丙烯酸正己酯3-4、丁香油2-3；制备方法是将纳米氧化铝、锆石、氮化铝粉、长石放入煅烧炉中，在550-570℃下煅烧4-5小时，取出，与云母粉、硼酸锌、氧化锌、碳酸氢铵混合，研磨得到300-400目粉末，然后，再加入苯乙烯、甲基丙烯酸正己酯、丁香油混合，继续研磨40-50分钟，至充分分散，再加入其它剩余成分，继续研磨30-45分钟后，在1400-1600转/分下搅拌15-30分钟，即得助剂。
本发明所述新型玻璃钢复合涂层材料，由以下具体步骤制成：
（1）将乙烯基树脂、双酚A 树脂、氯化石蜡、甲基丙烯酸酯、硅烷偶联剂KH-550 、、尿素、山梨酸钾、甲基丙烯酸酯放入反应釜中边搅拌边加热至熔融状态，得到A料；
（2）将玻璃纤维放入球磨机中磨碎，与氢氧化钙、轻烧氧化镁草木灰、对羟基苯甲醚、钛酸四正丁酯进行混合，搅拌15-20分钟，得到B料；
（3）将A料与B料混合，加入助剂以及其余剩余成分，在450-600转/分的速度下搅拌20-24分钟，浇注、固化即可。
本发明的优点为：本发明添加助剂，使材料具有良好的物理性能以及机械性能，起到补强的作用；本发明材料耐高温、抗冷冻、使用寿命长、无毒、体轻、耐火阻燃，制成的增强复合材料造价低、强度大、有韧性易于大批量生产，推广应用，适用于制作各种管道、罐体等，节约钢材。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种新型玻璃钢复合涂层材料，由下列重量份（公斤）的原料制成：乙烯基树脂33、双酚A 树脂10、氢氧化钙1、轻烧氧化镁2、氯化石蜡1、甲基丙烯酸酯20、硅烷偶联剂KH-550 3、尿素2、山梨酸钾1、1，5-戊二醇4、过氧化苯甲酰4、玻璃纤维24、草木灰1、对羟基苯甲醚2、钛酸四正丁酯2、助剂1；
所述助剂由下列重量份（公斤）的原料制成：纳米氧化铝12、锆石4、云母粉3、氮化铝粉2、长石3、硼酸锌2、氧化锌5、碳酸氢铵3、氧化二丁基锡2、苯乙烯3、甲基丙烯酸正己酯3、丁香油2；制备方法是将纳米氧化铝、锆石、氮化铝粉、长石放入煅烧炉中，在550-570℃下煅烧4-5小时，取出，与云母粉、硼酸锌、氧化锌、碳酸氢铵混合，研磨得到300-400目粉末，然后，再加入苯乙烯、甲基丙烯酸正己酯、丁香油混合，继续研磨40-50分钟，至充分分散，再加入其它剩余成分，继续研磨30-45分钟后，在1400-1600转/分下搅拌15-30分钟，即得助剂。
本发明所述新型玻璃钢复合涂层材料，由以下具体步骤制成：
（1）将乙烯基树脂、双酚A 树脂、氯化石蜡、甲基丙烯酸酯、硅烷偶联剂KH-550 、、尿素、山梨酸钾、甲基丙烯酸酯放入反应釜中边搅拌边加热至熔融状态，得到A料；
（2）将玻璃纤维放入球磨机中磨碎，与氢氧化钙、轻烧氧化镁草木灰、对羟基苯甲醚、钛酸四正丁酯进行混合，搅拌15-20分钟，得到B料；
（3）将A料与B料混合，加入助剂以及其余剩余成分，在450-600转/分的速度下搅拌20-24分钟，浇注、固化即可。
本发明实施例的玻璃钢材料的拉伸强度为248 Mpa。
Claims (2)
1.一种新型玻璃钢复合涂层材料，其特征在于，由下列重量份的原料制成：乙烯基树脂33-36、双酚A 树脂10-12、氢氧化钙1-2、轻烧氧化镁2-3、氯化石蜡1-2、甲基丙烯酸酯20-25、硅烷偶联剂KH-550 3-4、尿素2-3、山梨酸钾1-2、1，5-戊二醇4-6、过氧化苯甲酰4-6、玻璃纤维24-27、草木灰1-2、对羟基苯甲醚2-3、钛酸四正丁酯2-3、助剂1-2；
所述助剂由下列重量份的原料制成：纳米氧化铝12-14、锆石4-6、云母粉3-4、氮化铝粉2-3、长石3-5、硼酸锌2-4、氧化锌5-7、碳酸氢铵3-4、氧化二丁基锡2-3、苯乙烯3-5、甲基丙烯酸正己酯3-4、丁香油2-3；制备方法是将纳米氧化铝、锆石、氮化铝粉、长石放入煅烧炉中，在550-570℃下煅烧4-5小时，取出，与云母粉、硼酸锌、氧化锌、碳酸氢铵混合，研磨得到300-400目粉末，然后，再加入苯乙烯、甲基丙烯酸正己酯、丁香油混合，继续研磨40-50分钟，至充分分散，再加入其它剩余成分，继续研磨30-45分钟后，在1400-1600转/分下搅拌15-30分钟，即得助剂。
2.根据权利要求1所述新型玻璃钢复合涂层材料，其特征在于，由以下具体步骤制成：
（1）将乙烯基树脂、双酚A 树脂、氯化石蜡、甲基丙烯酸酯、硅烷偶联剂KH-550 、尿素、山梨酸钾、甲基丙烯酸酯放入反应釜中边搅拌边加热至熔融状态，得到A料；
（2）将玻璃纤维放入球磨机中磨碎，与氢氧化钙、轻烧氧化镁草木灰、对羟基苯甲醚、钛酸四正丁酯进行混合，搅拌15-20分钟，得到B料；
（3）将A料与B料混合，加入助剂以及其余剩余成分，在450-600转/分的速度下搅拌20-24分钟，浇注、固化即可。