CN103785225A - 多组分阻燃易去污过滤材料及非织造过滤材料的制备方法 - Google Patents
多组分阻燃易去污过滤材料及非织造过滤材料的制备方法 Download PDFInfo
- Publication number
- CN103785225A CN103785225A CN201210434170.1A CN201210434170A CN103785225A CN 103785225 A CN103785225 A CN 103785225A CN 201210434170 A CN201210434170 A CN 201210434170A CN 103785225 A CN103785225 A CN 103785225A
- Authority
- CN
- China
- Prior art keywords
- fibre
- filtering material
- preparation
- polyester staple
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
多组分阻燃易去污过滤材料及非织造过滤材料的制备方法，它涉及一种过滤材料的制备方法，它的多组分阻燃易去污过滤材料的制备方法为：将质量比为30%-40%的熔点涤纶短纤维、20%-30%的三维中20%-30%的阻燃涤纶短纤维，8%-15%的芳纶短纤维进行开包检验后混合均匀，然后开松梳理，梳理后进行铺网，铺网后的原料进入热熔成型区，此时滤材的低熔点涤纶短纤维在为190-215度的高温下首先进行熔化，与均匀铺网的高熔点涤纶短纤维，芳纶短纤维形成热熔粘合为一体，即为成品，它的制备方法简单，产品环保安全，喷涂整理后的滤材强度增加，手感硬挺，利于打褶，增加有效过滤面积，阻燃性能稳定持久，去污效果好。
Description
技术领域：
本发明涉及一种过滤材料的制备方法，具体涉及多组分阻燃易去污过滤材料及非织造过滤材料的制备方法。
背景技术：
随着科学技术和现代工业的不断发展，人们越来越重视室外环境的空气质量和室内空气品质，除尘净化技术的不断发展和提高以及应用范围的扩展，对空气过滤材料不论在数量还是品种及质量上都提出了新的要求。
非织造布的过滤材料的开发应用，具有很多的优势，因它具有一定的厚度，纤维错综复杂形成网状结构，孔隙多而路径曲折，增加了过滤面积，气流阻力小，过滤效率高。但目前应用的非织造空气过滤材料看，功能还比较少，阻燃性能不稳定，不耐水洗，尤其是夏季温度升高，空气过滤材料容尘量饱和，易污染，消耗大，严重的会造成过滤器堵塞停机，影响空调过滤系统正常运转。
发明内容：
本发明的目的是提供多组分阻燃易去污过滤材料及非织造过滤材料的制备方法，它制备方法简单，产品环保安全，喷涂整理后的滤材强度增加，手感硬挺，利于打褶，增加有效过滤面积，阻燃性能稳定持久，且它去污效果好，用途广。
为了解决背景技术所存在的问题，本发明采用以下技术方案：它的多组分阻燃易去污过滤材料的制备方法为：将质量比为30%-40%，纤维长度为45-64mm，纤维细度为10-15D的低熔点涤纶短纤维、质量比为20%-30%，纤维长度64-75mm，纤维细度25-30D的三维中空阻燃涤纶短纤维，质量比为20%-30%，纤维长度为51-64mm，纤维细度为15-25D的阻燃涤纶短纤维，质量比为8%-15%，纤维长度为40-54mm，纤维细度为10-15D的芳纶短纤维先进行开包检验后，进行混合均匀，然后开松梳理，梳理后进行铺网，铺网后的原料进入热熔成型区，热熔成型的温度为190-215度，车速5-10米/分钟，此时滤材的低熔点涤纶短纤维在为190-215度的高温下首先进行熔化，与均匀铺网的高熔点涤纶短纤维，芳纶短纤维形成热熔粘合为一体，即成为多组分阻燃易去污过滤材料。
它的多组分阻燃易去污非织造过滤材料的制备方法为：将质量比为30%-40%，纤维长度为45-64mm，纤维细度为10-15D的低熔点涤纶短纤维、质量比为20%-30%，纤维长度64-75mm，纤维细度25-30D的三维中空阻燃涤纶短纤维，质量比为20%-30%，纤维长度为51-64mm，纤维细度为15-25D的阻燃涤纶短纤维，质量比为8%-15%，纤维长度为40-54mm，纤维细度为10-15D的芳纶短纤维先进行开包检验后，进行混合均匀，然后开松梳理，梳理后进行铺网，铺网后的原料进入热熔成型区进行热熔成型，成型后喷涂阻燃易去污整理剂，喷涂好后进行预烘，预烘温度为140-160℃，车速为4-8米/分钟，然后再进行烘焙，烘焙的温度为180-220℃，车速为6-12米/分钟，然后切边卷取，即为成品。
所述的阻燃易去污整理剂的制备方法为：将质量比为15%-35%的耐久性涤纶阻燃剂置于不锈钢搅拌器中搅拌5-10分钟，转速为1500-2500转/分钟，然后将5%-15%的易去污整理剂加入其中，继续搅拌5-10分钟，最后加入0.1%-2%的偶联剂，0.1%-2%的分散剂，3%-10%的粘合剂，0.1%-0.3%的消泡剂及35%-77%的水进行搅拌，搅拌时间为10-30分钟，转速为2000-3000转/分钟，制成水溶性阻燃易去污整理剂。
所述的偶联剂为钛酸酯或硬脂酸中的一种或其混合物。
所述的分散剂为聚羧酸铵盐共聚物、聚羧酸钠盐共聚物中的一种或者混合物。
所述的粘合剂为聚酯聚合物，丙烯酸聚合物，乙烯或者氯乙烯聚合物中的一种或者其混合物。
本发明具有以下有益效果：它制备方法简单，产品环保安全，喷涂整理后的滤材强度增加，手感硬挺，利于打褶，增加有效过滤面积，阻燃性能稳定持久，且它去污效果好，用途广。
具体实施方式：
本具体实施方式采取以下技术方案：它的多组分阻燃易去污过滤材料的制备方法为：将质量比为30%-40%，纤维长度为45-64mm，纤维细度为10-15D的低熔点涤纶短纤维、质量比为20%-30%，纤维长度64-75mm，纤维细度25-30D的三维中空阻燃涤纶短纤维，质量比为20%-30%，纤维长度为51-64mm，纤维细度为15-25D的阻燃涤纶短纤维，质量比为8%-15%，纤维长度为40-54mm，纤维细度为10-15D的芳纶短纤维先进行开包检验后，进行混合均匀，然后开松梳理，梳理后进行铺网，铺网后的原料进入热熔成型区，热熔成型的温度为190-215度，车速5-10米/分钟，此时滤材的低熔点涤纶短纤维在为190-215度的高温下首先进行熔化，与均匀铺网的高熔点涤纶短纤维，芳纶短纤维形成热熔粘合为一体，即成为多组分阻燃易去污过滤材料。
它的多组分阻燃易去污非织造过滤材料的制备方法为：将质量比为30%-40%，纤维长度为45-64mm，纤维细度为10-15D的低熔点涤纶短纤维、质量比为20%-30%，纤维长度64-75mm，纤维细度25-30D的三维中空阻燃涤纶短纤维，质量比为20%-30%，纤维长度为51-64mm，纤维细度为15-25D的阻燃涤纶短纤维，质量比为8%-15%，纤维长度为40-54mm，纤维细度为10-15D的芳纶短纤维先进行开包检验后，进行混合均匀，然后开松梳理，梳理后进行铺网，铺网后的原料进入热熔成型区进行热熔成型，成型后喷涂阻燃易去污整理剂，喷涂好后进行预烘，预烘温度为140-160℃，车速为4-8米/分钟，然后再进行烘焙，烘焙的温度为180-220℃，车速为6-12米/分钟，然后切边卷取，即为成品，
所述的阻燃易去污整理剂的制备方法为：将质量比为15%-35%的耐久性涤纶阻燃剂置于不锈钢搅拌器中搅拌5-10分钟，转速为1500-2500转/分钟，然后将5%-15%的易去污整理剂加入其中，继续搅拌5-10分钟，最后加入0.1%-2%的偶联剂，0.1%-2%的分散剂，3%-10%的粘合剂，0.1%-0.3%的消泡剂及35%-77%的水进行搅拌，搅拌时间为10-30分钟，转速为2000-3000转/分钟，制成水溶性阻燃易去污整理剂。
所述的偶联剂为钛酸酯或硬脂酸中的一种或其混合物。
所述的分散剂为聚羧酸铵盐共聚物、聚羧酸钠盐共聚物中的一种或者混合物。
所述的粘合剂为聚酯聚合物，丙烯酸聚合物，乙烯或者氯乙烯聚合物中的一种或者其混合物。
本具体实施方式具有以下有益效果：它制备方法简单，产品环保安全，喷涂整理后的滤材强度增加，手感硬挺，利于打褶，增加有效过滤面积，阻燃性能稳定持久，且它去污效果好，用途广。
Claims (3)
1.多组分阻燃易去污过滤材料及非织造过滤材料的制备方法，其特征在于它的多组分阻燃易去污过滤材料的制备方法为：将质量比为30%-40%，纤维长度为45-64mm，纤维细度为10-15D的低熔点涤纶短纤维、质量比为20%-30%，纤维长度64-75mm，纤维细度25-30D的三维中空阻燃涤纶短纤维，质量比为20%-30%，纤维长度为51-64mm，纤维细度为15-25D的阻燃涤纶短纤维，质量比为8%-15%，纤维长度为40-54mm，纤维细度为10-15D的芳纶短纤维先进行开包检验后，进行混合均匀，然后开松梳理，梳理后进行铺网，铺网后的原料进入热熔成型区，热熔成型的温度为190-215度，车速5-10米/分钟，此时滤材的低熔点涤纶短纤维在为190-215度的高温下首先进行熔化，与均匀铺网的高熔点涤纶短纤维，芳纶短纤维形成热熔粘合为一体，即成为多组分阻燃易去污过滤材料。
2.根据权利要求1所述的多组分阻燃易去污过滤材料及非织造过滤材料的制备方法，其特征在于所述的它的多组分阻燃易去污非织造过滤材料的制备方法为：将质量比为30%-40%，纤维长度为45-64mm，纤维细度为10-15D的低熔点涤纶短纤维、质量比为20%-30%，纤维长度64-75mm，纤维细度25-30D的三维中空阻燃涤纶短纤维，质量比为20%-30%，纤维长度为51-64mm，纤维细度为15-25D的阻燃涤纶短纤维，质量比为8%-15%，纤维长度为40-54mm，纤维细度为10-15D的芳纶短纤维先进行开包检验后，进行混合均匀，然后开松梳理，梳理后进行铺网，铺网后的原料进入热熔成型区进行热熔成型，成型后喷涂阻燃易去污整理剂，喷涂好后进行预烘，预烘温度为140-160℃，车速为4-8米/分钟，然后再进行烘焙，烘焙的温度为180-220℃，车速为6-12米/分钟，然后切边卷取，即为成品。
3.根据权利要求1所述的多组分阻燃易去污过滤材料及非织造过滤材料的制备方法，其特征在于所述的阻燃易去污整理剂的制备方法为：将质量比为15%-35%的耐久性涤纶阻燃剂置于不锈钢搅拌器中搅拌5-10分钟，转速为1500-2500转/分钟，然后将5%-15%的易去污整理剂加入其中，继续搅拌5-10分钟，最后加入0.1%-2%的偶联剂，0.1%-2%的分散剂，3%-10%的粘合剂，0.1%-0.3%的消泡剂及35%-77%的水进行搅拌，搅拌时间为10-30分钟，转速为2000-3000转/分钟，制成水溶性阻燃易去污整理剂。