CN103778985B - 防辐射吸波粉及其制备方法以及限幅削波装置 - Google Patents
防辐射吸波粉及其制备方法以及限幅削波装置 Download PDFInfo
- Publication number
- CN103778985B CN103778985B CN201210410005.2A CN201210410005A CN103778985B CN 103778985 B CN103778985 B CN 103778985B CN 201210410005 A CN201210410005 A CN 201210410005A CN 103778985 B CN103778985 B CN 103778985B
- Authority
- CN
- China
- Prior art keywords
- parts
- radiation
- zinc
- present
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及防辐射领域，尤其涉及防辐射吸波粉及其制备方法以及限幅削波装置。本发明采取如下技术方案：防辐射的吸波粉，其特征在于，其为镍铜锌软磁铁氧体材料。所述为镍铜锌软磁铁氧体材料中重量含量中含镍4‑15份，含铜1.5‑7份，含有锌4‑21份。采用如上技术方案的本发明，具有如下有益效果：本产品发明采用吸波材料制成吸波振子再组成无源、宽带、自谐吸波器件。贴装在手机、电脑适当部位，在不影响主机工作前提下对电磁辐射波、脉冲波和杂散波谐振吸收变成热能消耗。经过数据证明，本发明能够有效降低手机辐射，减少电磁辐射。
Description
技术领域
本发明涉及防辐射领域，尤其涉及防辐射吸波粉及其制备方法以及限幅削波装置。
背景技术
在电子科技飞速发展的今天，电磁辐射已成为世界第四大污染源。常时间使用手机、电脑等电子产品会使人感到疲劳、头痛、免疫力下降，严重者会得白血病。
手机作为现代人常用的产品，更是对人的身体健康造成了很多潜在的危害。
发明内容
发明的目的：为了提供一种防辐射效果好的防辐射吸波粉及其制备方法。
本发明的另一个目的是制造一种限幅削波装置，该装置可以对在不影响主机工作前提下对电磁辐射波、脉冲波和杂散波谐振吸收变成热能消耗。
为了达到如上目的，本发明采取如下技术方案：防辐射的吸波粉，其特征在于，其为镍铜锌软磁铁氧体材料。
本发明进一步技术方案在于，所述为镍铜锌软磁铁氧体材料中重量含量中含镍4-15份，含铜1.5-7份，含有锌4-21份。
本发明进一步技术方案在于，所述为镍铜锌软磁铁氧体材料中重量含量中含镍11份，含铜6份，含有锌15份。
本发明可以提供的另外一种技术方案如下：
制备如上任意所述的防辐射的吸波粉的制备方法，其特征在于，包含如下步骤，
配方选择、原材料试验、合格配料：含镍4-15份，含铜1.5-7份，含有锌4-21份；
一次球磨：干混，比例为球∶料＝5∶1；
予烧：在900C°进行予烧，初步完成固相反应；
二次球磨：水磨，比例为球∶料∶水＝3∶1∶2；
烘干：用烘箱在150C°进行两小时的烘干；
制粉：采用造粒机进行制粉，使其过120目筛。
本发明进一步技术方案在于，所述步骤配方选择中是指含镍11份，含铜6份，含有锌15份。
本发明实现的另一种技术方案是：
限幅削波装置，其特征在于，包含有机材料，所述有机材料内部装有镍铜锌软磁铁氧体材料。
本发明进一步技术方案在于，所述有机材料为透明材料。
本发明进一步技术方案在于，所述透明材料为亚克力。
本发明进一步技术方案在于，所述亚克力内部有两个封闭空腔，其内部分别装有镍铜锌软磁铁氧体材料。
本发明进一步技术方案在于，所述有机材料外面镀有银层。
如上所述的限幅削波装置的使用方法，其特征在于，采用胶将所述装置贴在手机上
采用如上技术方案的本发明，具有如下有益效果：本产品发明采用吸波材料制成吸波振子再组成无源、宽带、自谐吸波器件。贴装在手机、电脑适当部位，在不影响主机工作前提下对电磁辐射波、脉冲波和杂散波谐振吸收变成热能消耗。经过数据证明，本发明能够有效降低手机辐射，减少电磁辐射。
附图说明
图1为发明的结构示意图；
图2为发明的结构分层示意图；
图3为发明的减辐射的效果对比图；
其中：1.有机材料；2.防辐射材料；3.银层；4.胶。
具体实施方式
结合图1-图3；
关于吸波材料的制备方法：
材料测试：
1.吸波能力(吸波特性)900MHZ/1800MHZ＞95％
2.材质：ū、μ′、μ″、tgδM、TC°(居里温度)ρ(密度)tgδM与C°、f关系tgδM为总损耗与使用频率关系的曲线
关于本发明的装置；自制磁性材料吸波粉-----制造吸波振子-----按装有机玻璃壳体内-----贴装不干胶------产品检测------入库。自制吸波特性很强的磁性材料是关键。
我厂生产的材质优于国外材质属铁氧体镍铜锌系列。吸波振子尺寸根据使用频率决定。示例产品频率：
800MHz-900MHz-1000MHz-1200MHz-1800MHz-2000MHz-2200MHz-4500MHz
外壳：亚克力材料.它不仅美观而且有很好的介电常数。当然，材质不限于亚克力，也可以是有类似功能材质。
壳内：镀银层。主要是具有电容C，可以和吸波材料进行谐振。
磁性材料镍铜锌系列，其结果比进口同类磁粉性能高。
镍铜锌软磁铁氧体材料具有很好的介电常数同时也具备很好的磁导率。而ū＝μ′-jμ″。tgδM＝μ″/μ′是损耗部分。ū＝μ′-jμ″为复数导磁率＝实部-虚数单位。tgδM＝μ″/μ为损耗＝虚部/实部。
以下提供三种配方，作为实施的具体方式：
实施例1：
含镍4份，含铜7份，含有锌4份；
实施例2：
含镍15份，含铜1.5份，含有锌21份；
实施例3：
含镍11份，含铜6份，含有锌15份。
结合图3，可知本发明的吸波效果非常好。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本领域的技术人员应该了解本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的范围内。
Claims (1)
1.防辐射的吸波粉的制备方法，其特征在于，其中，防辐射的吸波粉为镍铜锌软磁铁氧体材料，包含如下步骤，
经过配方选择、原材料试验、合格配料后，得到镍铜锌软磁铁氧体材料的配方为：所述镍铜锌软磁铁氧体材料中重量含量中含镍4份，含铜7份，含有锌4份；或者，含镍15份，含铜1.5份，含有锌21份；或者，含镍11份，含铜6份，含有锌15份；
一次球磨：干混，比例为球∶料＝5∶1；
予烧：在900℃进行予烧，初步完成固相反应；
二次球磨：水磨，比例为球∶料∶水＝3∶1∶2；
烘干：用烘箱在150℃进行两小时的烘干；
制粉：采用造粒机进行制粉，使其过120目筛。