CN103773240A - 一种环氧沥青改性材料 - Google Patents

一种环氧沥青改性材料 Download PDF

Info

Publication number
CN103773240A
CN103773240A CN201410023415.0A CN201410023415A CN103773240A CN 103773240 A CN103773240 A CN 103773240A CN 201410023415 A CN201410023415 A CN 201410023415A CN 103773240 A CN103773240 A CN 103773240A
Authority
CN
China
Prior art keywords
parts
product
epoxy
epoxy resin
coal tar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201410023415.0A
Other languages
English (en)
Inventor
陈磊磊
吴志仁
马群锋
赵张飞
何平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG SOUTHEAST HIGHWAY ENGINEERING Co Ltd
Original Assignee
NANTONG SOUTHEAST HIGHWAY ENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG SOUTHEAST HIGHWAY ENGINEERING Co Ltd filed Critical NANTONG SOUTHEAST HIGHWAY ENGINEERING Co Ltd
Priority to CN201410023415.0A priority Critical patent/CN103773240A/zh
Publication of CN103773240A publication Critical patent/CN103773240A/zh
Withdrawn legal-status Critical Current

Abstract

一种环氧沥青改性材料，其组成成份以质量份数表示法为：环氧树脂为18-28份；石油沥青22-30份；煤焦油10-12份;铁红12-15份；氧化铬绿20-25份；滑石粉10-20份；云母粉5-10份;聚硫橡胶为10-15份；铝粉浆为5-10份；甲苯1-3份；二甲苯2-5份；丁腈橡胶20-25份；乙二胺2-5份；产品表干2-3h，实干21-23h；粘度高，耐水性好、机械强度好，硬度高，固含量65-75%；使用寿命长，耐弯曲，耐冲击，冲击强度40-50kg/cm；产品不易挥发，柔韧性好，不易开裂，可以广泛生产并不断代替现有材料。

Description

一种环氧沥青改性材料
技术领域
本申请属于环氧沥青材料领域，尤其涉及一种环氧沥青改性材料。
背景技术
环氧沥青涂料为高分子环氧沥青涂料防腐防水材料，为环氧树脂型高分子防腐防水系列，使用寿命为永久性防腐防水材料。环氧沥青涂料是以10号优质石油沥青和引入进口环氧树脂改性胶乳加入国内氯丁橡胶为主料，辅以轻柴油、油酸、煤焦沥青、煤焦油、熟石粉、石棉粉、滑石粉、云母粉、矿粉、石英粉再加以各种添加剂，填充剂配制而成的高分子沥青胶泥防腐防水材料，使用寿命长，施工方便。
沥青是由不同分子量的碳氢化合物及其非金属衍生物组成的黑褐色复杂混合物，呈液态，是一种防水防潮和防腐的有机胶凝材料。用于涂料、塑料、橡胶等工业以及铺筑路面等，石油沥青是原油蒸馏后的残渣。根据提炼程度的不同，在常温下成液体、半固体或固体。石油沥青色黑而有光泽，具有较高的感温性。由于它在生产过程中曾经蒸馏至400℃以上，因而所含挥发成分甚少，但仍可能有高分子的碳氢化合物未经挥发出来，这些物质或多或少对人体健康是有害的，随着社会城市化、科技化、人性化的发展，设计一种干燥时间短，粘度高的环氧沥青改性材料以满足市场需求，是非常必要的。
发明内容
解决的技术问题：
本申请针对现有环氧沥青改性材料干燥时间长和粘度低等技术问题，提供一种环氧沥青改性材料。
技术方案：
一种环氧沥青改性材料，由下列原料组成，以质量份数表示法为：环氧树脂为18-28份；石油沥青22-30份；煤焦油10-12份;铁红12-15份；氧化铬绿20-25份；滑石粉10-20份；云母粉5-10份;聚硫橡胶为10-15份；铝粉浆为5-10份；甲苯1-3份；二甲苯2-5份；丁腈橡胶20-25份；乙二胺2-5份。
作为本发明的一种优选技术方案：所述环氧沥青改性材料，其组成成分，以质量份数表示法为：环氧树脂为23份；石油沥青26份；煤焦油11份;铁红13份；氧化铬绿22份；滑石粉15份；云母粉7份;聚硫橡胶为12份；铝粉浆为7份；甲苯2份；二甲苯3份；丁腈橡胶22份；乙二胺3份。
作为本发明的一种优选技术方案：所述环氧树脂型号为环氧树脂E-44。
有益效果：
本发明所述一种环氧沥青改性材料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品表干2-3h，实干21-23h；2、粘度高，耐水性好、机械强度好，硬度高，固含量65-75%；3、使用寿命长，耐弯曲，耐冲击，冲击强度40-50kg/cm；4、产品不易挥发，柔韧性好，不易开裂，可以广泛生产并不断代替现有材料。 
具体实施方式
实施例1:
 一种环氧沥青改性材料，其组成成份以质量份数表示法为：环氧树脂E-44为18份；石油沥青22份；煤焦油10份;铁红12份；氧化铬绿20份；滑石粉10份；云母粉5份;聚硫橡胶为10份；铝粉浆为5份；甲苯1份；二甲苯2份；丁腈橡胶20份；乙二胺2份。将所有原材料在反应釜中加热到200℃后，充分混合4h即得到成品。
产品表干3h，实干23h；固含量65%；冲击强度40kg/cm；柔韧性好。
 实施例2:
 一种环氧沥青改性材料，其组成成份以质量份数表示法为：环氧树脂E-44为28份；石油沥青30份；煤焦油12份;铁红15份；氧化铬绿25份；滑石粉20份；云母粉10份;聚硫橡胶为15份；铝粉浆为10份；甲苯3份；二甲苯5份；丁腈橡胶25份；乙二胺5份。将所有原材料在反应釜中加热到200℃后，充分混合4h即得到成品。
产品表干2.5h，实干22h；固含量70%；冲击强度45kg/cm；柔韧性好。
 实施例3:
一种环氧沥青改性材料，其组成成份以质量份数表示法为：环氧树脂E-44为23份；石油沥青26份；煤焦油11份;铁红13份；氧化铬绿22份；滑石粉15份；云母粉7份;聚硫橡胶为12份；铝粉浆为7份；甲苯2份；二甲苯3份；丁腈橡胶22份；乙二胺3份。将所有原材料在反应釜中加热到200℃后，充分混合4h即得到成品。
产品表干2h，实干21h；固含量75%；冲击强度50kg/cm；柔韧性好。
以上实施例中的所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。

Claims (3)

1.一种环氧沥青改性材料，其特征在于：其组成成份以质量份数表示法为：环氧树脂为18-28份；石油沥青22-30份；煤焦油10-12份;铁红12-15份；氧化铬绿20-25份；滑石粉10-20份；云母粉5-10份;聚硫橡胶为10-15份；铝粉浆为5-10份；甲苯1-3份；二甲苯2-5份；丁腈橡胶20-25份；乙二胺2-5份。
2.根据权利要求1所述的一种环氧沥青改性材料，其特征在于：其组成成份以质量份数表示法为：环氧树脂为23份；石油沥青26份；煤焦油11份;铁红13份；氧化铬绿22份；滑石粉15份；云母粉7份;聚硫橡胶为12份；铝粉浆为7份；甲苯2份；二甲苯3份；丁腈橡胶22份；乙二胺3份。
3.根据权利要求1所述的一种环氧沥青改性材料，其特征在于：所述环氧树脂型号为环氧树脂E-44。
CN201410023415.0A 2014-01-20 2014-01-20 一种环氧沥青改性材料 Withdrawn CN103773240A (zh)