CN103773107A - 一种用于硅胶表面喷涂的黑色油墨及其制备方法 - Google Patents
一种用于硅胶表面喷涂的黑色油墨及其制备方法 Download PDFInfo
- Publication number
- CN103773107A CN103773107A CN201410029099.8A CN201410029099A CN103773107A CN 103773107 A CN103773107 A CN 103773107A CN 201410029099 A CN201410029099 A CN 201410029099A CN 103773107 A CN103773107 A CN 103773107A
- Authority
- CN
- China
- Prior art keywords
- parts
- black ink
- silica surface
- surface spraying
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于硅胶表面喷涂的黑色油墨,该黑色油墨包括以下按各组分重量份数计量的原料:色粉25~30份、乙烯基硅油25~30份、慢干剂25~30份、分散剂10~15份、固化剂3~5份和催化剂1~2份。此外,所述用于硅胶表面喷涂的黑色油墨还包括重量份数为2~3份的蜡粉。本发明色粉由U碳和卡博特按重量比为4:1的比例组成,可提高黑色油墨的遮光效果,同时使用低粘度的乙烯基硅油作为基胶,保证了黑色油墨的针孔漏光程度及制品表面平整程度,赋予制品不易漏光及表面平整的特点。本发明黑色油墨具有遮光效果差、易针孔漏光、制件表面不平整、易吸灰尘及生产不稳定等特点。
Description
技术领域
本发明涉及油墨领域,具体涉及一种用于硅胶表面喷涂的黑色油墨,本发明还涉及一种用于硅胶表面喷涂的黑色油墨的制备方法。
背景技术
按油墨用途划分,油墨包括硅胶油墨,硅胶油墨是一种用在硅胶类素材上的涂装保护油墨。随着社会及科技技术的不断进步,人们对各种承印物提出的要求也越来越高,传统的硅胶油墨已经不能够满足人们的需求。
电子产品的外壳造型的设计已经成为消费者选择产品的重要考虑元素之一,为了更好的满足消费者要求,提高企业的经济效益,提高对硅胶油墨的研究是多数企业的重要研究课题。然而,目前市场上的硅胶油墨却存在遮光效果差、易针孔漏光、制件表面不平整、易吸灰尘及生产不稳定等缺点。
发明内容
本发明的目的在于提出一种用于硅胶表面喷涂的黑色油墨,该黑色油墨具有遮光效果差、易针孔漏光、制件表面不平整、易吸灰尘及生产不稳定等特点。
为了解决现有技术问题,本发明通过以下技术方案实现:
一种用于硅胶表面喷涂的黑色油墨,该黑色油墨包括以下按各组分重量份数计量的原料:色粉25~30份、乙烯基硅油25~30份、慢干剂25~30份、分散剂10~15份、固化剂3~5份和催化剂1~2份。
所述用于硅胶表面喷涂的黑色油墨还包括重量份数为2~3份的蜡粉。
所述色粉由U碳和卡博特按重量比为4:1的比例组成。
所述慢干剂为航空煤油,固化剂为含氢硅油,催化剂为铂金水。
所述分散剂为改性硅油、偶联剂和环氧树脂中的任一种或几种组合。
本发明的另一个目的在于提出一种用于硅胶表面喷涂的黑色油墨的制备方法,该制备方法包括以下步骤:
1)先将配方量的色粉及乙烯基硅油充分混合,然后采用液压滚研磨;
2)将经步骤1)之后的原料及其他原料进行混合,混合均匀后得到用于硅胶表面喷涂的黑色油墨。
本发明色粉由U碳和卡博特按重量比为4:1的比例组成,可提高黑色油墨的遮光效果,同时使用低粘度的乙烯基硅油作为基胶,保证了黑色油墨的针孔漏光程度及制品表面平整程度,赋予制品不易漏光及表面平整的特点。其次,本发明还添加了蜡粉,蜡粉的添加不会给油墨带来负面影响,同时还使所得产品不易吸灰尘及招灰尘,再次,采用本发明原料制备的黑色油墨用于硅胶表面喷涂时不易发生结合现象。
本发明采用液压研磨机进行研磨,可进一步提高油墨的细度,减少黑色油墨中的颗粒,从而改善制品的平整度。
具体实施方式
本发明揭示了一种用于硅胶表面喷涂的黑色油墨,该黑色油墨包括以下按各组分重量份数计量的原料:色粉25~30份、乙烯基硅油25~30份、慢干剂25~30份、分散剂10~15份、固化剂3~5份和催化剂1~2份。
所述用于硅胶表面喷涂的黑色油墨还包括重量份数为2~3份的蜡粉。
所述色粉由U碳和卡博特按重量比为4:1的比例组成,U碳为德固赛炭黑,优选为德固赛PRINTEX、德固赛SB4或德固赛SB4A,卡博特为1255黑色色粉,U碳及卡博特均可由市购得到,本领域技术人员通过现有技术得到。本发明按重量比为4:1的比例将U碳及卡博特进行复配,提高了黑色油墨的遮光效果,同时采用低粘度的乙烯基硅油作为基胶,保证了黑色油墨的针孔漏光程度及制品表面平整程度,赋予制品不易漏光及表面平整的特点。
所述慢干剂为航空煤油,航空煤油是石油产品之一。英文名称Jet fuel No.3,别名航空煤油,可由市购得到;固化剂为含氢硅油,含氢硅油可由市购得到,该含氢硅油在金属触媒作用下,可进行交联,在基材表面形成防水膜;催化剂为铂金水,柏金水可由市购得到,属于催化效率高的高性能催化剂,可抑制制备黑色油墨过程中伴随发生的副反应,避免黑色物质的生成。
本发明所用的分散剂为本领域常用的硅胶分散剂,并无特别限定,为了进一步提高黑色油墨的品质,所述分散剂优选改性硅油、偶联剂和环氧树脂中的任一种或几种组合。
本发明还揭示了一种用于硅胶表面喷涂的黑色油墨的制备方法,该制备方法包括以下步骤:
1)先将配方量的色粉及乙烯基硅油充分混合,然后采用液压滚研磨;
2)将经步骤1)之后的原料及其他原料进行混合,混合均匀后得到用于硅胶表面喷涂的黑色油墨。
为了本领域技术人员的理解,以下通过具体实施例对本发明做进一步详细的描述。
实施例1
一种用于硅胶表面喷涂的黑色油墨的制备方法,该制备方法包括以下步骤:
1)先将重量份数为25份的色粉及重量份数为30份的乙烯基硅油充分混合,然后采用液压滚研磨;
2)将航空煤油25份、含氢硅油3份、铂金水1份、蜡粉2份、改性硅油14份及全部的经步骤1)之后的原料进行混合,混合均匀后得到用于硅胶表面喷涂的黑色油墨。
实施例2
一种用于硅胶表面喷涂的黑色油墨的制备方法,该制备方法包括以下步骤:
1)先将重量份数为30份的色粉及重量份数为25份的乙烯基硅油充分混合,然后采用液压滚研磨;慢干剂为航空煤油,固化剂为含氢硅油,催化剂为铂金水
2)将航空煤油25份、含氢硅油5份、铂金水2份、蜡粉3份、改性硅油10份及全部的经步骤1)之后的原料进行混合,混合均匀后得到用于硅胶表面喷涂的黑色油墨。
实施例3
一种用于硅胶表面喷涂的黑色油墨的制备方法,该制备方法包括以下步骤:
1)先将重量份数为26份的色粉及重量份数为28份的乙烯基硅油充分混合,然后采用液压滚研磨;慢干剂为航空煤油,固化剂为含氢硅油,催化剂为铂金水
2)将航空煤油30份、含氢硅油3份、铂金水1份、蜡粉2份、改性硅油10份及全部的经步骤1)之后的原料进行混合,混合均匀后得到用于硅胶表面喷涂的黑色油墨。
实施例4
一种用于硅胶表面喷涂的黑色油墨的制备方法,该制备方法包括以下步骤:
1)先将重量份数为25份的色粉及重量份数为25份的乙烯基硅油充分混合,然后采用液压滚研磨;慢干剂为航空煤油,固化剂为含氢硅油,催化剂为铂金水
2)将航空煤油25份、含氢硅油5份、铂金水2份、蜡粉3份、改性硅油15份及全部的经步骤1)之后的原料进行混合,混合均匀后得到用于硅胶表面喷涂的黑色油墨。
上述实施例中提到的内容并非是对本发明的限定,在不脱离本发明的发明构思的前提下,任何显而易见的替换均在本发明的保护范围之内。
Claims (6)
1.一种用于硅胶表面喷涂的黑色油墨,该黑色油墨包括以下按各组分重量份数计量的原料:色粉25~30份、乙烯基硅油25~30份、慢干剂25~30份、分散剂10~15份、固化剂3~5份和催化剂1~2份。
2.根据权利要求1所述的用于硅胶表面喷涂的黑色油墨,其特征在于:所述用于硅胶表面喷涂的黑色油墨还包括重量份数为2~3份的蜡粉。
3.根据权利要求2所述的用于硅胶表面喷涂的黑色油墨,其特征在于:所述色粉由U碳和卡博特按重量比为4:1的比例组成。
4.根据权利要求2所述的用于硅胶表面喷涂的黑色油墨,其特征在于:所述慢干剂为航空煤油,固化剂为含氢硅油,催化剂为铂金水。
5.根据权利要求2所述的用于硅胶表面喷涂的黑色油墨,其特征在于:所述分散剂为改性硅油、偶联剂和环氧树脂中的任一种或几种组合。
6.一种根据权利要求1~5中任一项所述的用于硅胶表面喷涂的黑色油墨的制备方法,包括以下步骤:
1)先将配方量的色粉及乙烯基硅油充分混合,然后采用液压滚研磨;
2)将经步骤1)之后的原料及其他原料进行混合,混合均匀后得到用于硅胶表面喷涂的黑色油墨。