CN103771830A - Domestic ceramic product containing nanometer aluminium oxide - Google Patents
Domestic ceramic product containing nanometer aluminium oxide Download PDFInfo
- Publication number
- CN103771830A CN103771830A CN201410002650.XA CN201410002650A CN103771830A CN 103771830 A CN103771830 A CN 103771830A CN 201410002650 A CN201410002650 A CN 201410002650A CN 103771830 A CN103771830 A CN 103771830A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic product
- aluminium oxide
- nanometer
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a domestic ceramic product, and particularly relates to a domestic ceramic product containing nanometer aluminium oxide and a production technology thereof. The ceramic product is produced by adopting the following raw materials in parts by weight: 50-55 parts of natural clay, 12-14 parts of nanometer aluminium oxide, 2-3 parts of chromic oxide, 20-23 parts of sepiolite, 10-12 parts of aluminium silicate powder, 5-8 parts of titanium dioxide, 20-23 parts of nanometer fluorite powder, 15-20 parts of barium sulfate, 4-5 parts of polyvinyl alcohol and 5-6 parts of an additive. The strength and the toughness of the ceramic product are improved by using the unique characteristics of the nanometer raw materials such as the nanometer aluminium oxide and the nanometer fluorite powder; the nanometer materials are matched with the other raw materials, so that the prepared ceramic product has good whiteness and is uniform in color and luster and compact in glaze, the sintering temperature is effectively reduced, and the production energy consumption is controlled. Compared with a common ceramic product, the ceramic product produced by the technology has excellent performances and is high in application value; the production technology is relatively simple.
Description
Technical field
The present invention relates to ceramic ware for daily use, be specifically related to a kind of ceramic ware for daily use that contains nano-aluminium oxide and manufacture craft thereof.
Background technology
Pottery has long use history in China, nowadays in worldwide, be widely used, domestic ceramics has just like become a part indispensable in people's daily life, panoramic tableware, tea set, all kinds of sanitary equipment etc. are seen everywhere, these potteries are not only elegant in appearance, various shapes, also there is easy cleaning simultaneously, heatproof, the advantages such as wear resistant corrosion resistant, be well received by consumers, but ceramic product universal existence is crisp, not shock-resistant, poor toughness, glaze colours inequality easily comes off, the shortcomings such as production energy consumption is large, cause its breakage in production and transport and application process more serious, thereby increase production cost, therefore in the urgent need to its performance is improved, promote domestic ceramics industry to low cost, environmental protection future development.
Summary of the invention
The object of the invention is to, a kind of ceramic ware for daily use that contains nano-aluminium oxide is provided, to improve the performance of traditional ceramics goods, improve intensity and the toughness of material, reduce sintering temperature, to achieve these goals, the technical solution used in the present invention is as follows:
A kind of ceramic ware for daily use that contains nano-aluminium oxide, it is characterized in that, material of the present invention is made up of the raw material of following weight part: natural clay 50-55, nano-aluminium oxide 12-14, chromium sesquioxide 2-3, sepiolite 20-23, aluminium silicate powder 10-12, titanium dioxide 5-8, nanometer Fluorspar Powder 20-23, barium sulfate 15-20, polyvinyl alcohol 4-5, auxiliary agent 5-6.
Described auxiliary agent is made up of the raw material of following weight part: brown alundum powder 2-3, tripoly phosphate sodium STPP 5-6, jade powder 4-5, silane resin acceptor kh-550 1-2, carborundum powder 4-5, aluminium hydroxide 8-10; Its preparation method is that grinding distribution is even by each mixing of materials, to obtain final product.
Described a kind of ceramic ware for daily use that contains nano-aluminium oxide, its manufacture craft comprises following steps:
(1) first sepiolite is pulverized, crossed 100-200 mesh sieve;
(2) mixing of materials other remaining component except auxiliary agent and step (1) being obtained, adds grinding in ball grinder, crosses 400-600 mesh sieve;
(3) auxiliary agent is added in the material that step (2) obtains, after stirring, add water and make stock, stock is moulding after deironing, thick experienceds, old, refining processing must idiosome;
(4), after idiosome drying, cleaning, glazing, sintering 14-16 hour at 1245-1290 ℃ of temperature, gets product.
The invention has the advantages that: the special performance that utilizes the nano raw material such as nano-aluminium oxide, nanometer Fluorspar Powder, intensity and the toughness of material are improved, coordinate other raw material again, make pottery prepared by the present invention have good whiteness, color and luster is even, the densification of glaze layer, also effectively reduce sintering temperature, saved and produced power consumption, ceramic prepared by the present invention is more excellent compared with conventional ceramic performance, production technique is more simple, has wide using value.
Embodiment
Embodiment
The present embodiment ceramic is made up of following weight part raw material: natural clay 55, nano-aluminium oxide 14, chromium sesquioxide 3, sepiolite 22, aluminium silicate powder 12, titanium dioxide 6, nanometer Fluorspar Powder 23, barium sulfate 18, polyvinyl alcohol 5, auxiliary agent 6.
Described auxiliary agent is made up of the raw material of following weight part: brown alundum powder 3, tripoly phosphate sodium STPP 5, jade powder 4, silane resin acceptor kh-550 2, carborundum powder 4, aluminium hydroxide 8; Its preparation method is that grinding distribution is even by each mixing of materials, to obtain final product.
Described a kind of ceramic ware for daily use that contains nano-aluminium oxide, its manufacture craft comprises following steps:
(1) first sepiolite is pulverized, crossed 200 mesh sieves;
(2) mixing of materials other remaining component except auxiliary agent and step (1) being obtained, adds grinding in ball grinder, crosses 600 mesh sieves;
(3) auxiliary agent is added in the material that step (2) obtains, after stirring, add water and make stock, stock is moulding after deironing, thick experienceds, old, refining processing must idiosome;
(4), after idiosome drying, cleaning, glazing, at 1260 ℃ of temperature, sintering 16 hours, gets product.
The sintering temperature of the ceramic ware for daily use that the present embodiment makes reduces nearly 150-180 ℃ compared with like product sintering temperature, goods glaze color and luster is even, the fine and close free of pinholes of light, water-intake rate≤0.5%, glossiness >=85%, Lead and cadmium amount≤0.1mg/L, thermotolerance: three flawlesses of 220 ℃-20 ℃ exchanges occur.
Claims (2)
1. a ceramic ware for daily use that contains nano-aluminium oxide, it is characterized in that, this pottery is made up of the raw material of following weight part: natural clay 50-55, nano-aluminium oxide 12-14, chromium sesquioxide 2-3, sepiolite 20-23, aluminium silicate powder 10-12, titanium dioxide 5-8, nanometer Fluorspar Powder 20-23, barium sulfate 15-20, polyvinyl alcohol 4-5, auxiliary agent 5-6;
Described auxiliary agent is made up of the raw material of following weight part: brown alundum powder 2-3, tripoly phosphate sodium STPP 5-6, jade powder 4-5, silane resin acceptor kh-550 1-2, carborundum powder 4-5, aluminium hydroxide 8-10; Its preparation method is that grinding distribution is even by each mixing of materials, to obtain final product.
2. a kind of ceramic ware for daily use that contains nano-aluminium oxide as claimed in claim 1, its manufacture craft comprises following steps:
(1) first sepiolite is pulverized, crossed 100-200 mesh sieve;
(2) mixing of materials other remaining component except auxiliary agent and step (1) being obtained, adds grinding in ball grinder, crosses 400-600 mesh sieve;
(3) auxiliary agent is added in the material that step (2) obtains, after stirring, add water and make stock, stock is moulding after deironing, thick experienceds, old, refining processing must idiosome;
(4), after idiosome drying, cleaning, glazing, sintering 14-16 hour at 1245-1290 ℃ of temperature, gets product.