CN103757913A - 一种阻燃的无纺布的制备方法 - Google Patents

一种阻燃的无纺布的制备方法 Download PDF

Info

Publication number
CN103757913A
CN103757913A CN201310751316.XA CN201310751316A CN103757913A CN 103757913 A CN103757913 A CN 103757913A CN 201310751316 A CN201310751316 A CN 201310751316A CN 103757913 A CN103757913 A CN 103757913A
Authority
CN
China
Prior art keywords
nonwoven fabric
parts
fire
preparation
woven fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310751316.XA
Other languages
English (en)
Inventor
张德轩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd
Original Assignee
SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd filed Critical SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd
Priority to CN201310751316.XA priority Critical patent/CN103757913A/zh
Publication of CN103757913A publication Critical patent/CN103757913A/zh
Pending legal-status Critical Current

Abstract

一种阻燃的无纺布的制备方法，包括以下步骤：（1）取聚丙烯材质的无纺布，将其室温下浸泡于水中1h～2h；（2）配制无纺布涂层，取硼酸锌粉末为6份～9份，膨润土为3～6份，聚磷酸铵为5～7份，硫酸铝为3～6份，ABS树脂为15份～18份；（3）加热后，将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀；（4）将加热后的涂层液涂布在无纺布的外表面，无纺布外涂层厚度为0.7mm～0.9mm，室温下晾干；（5）晾干后将无纺布保存，即为制备得到的阻燃的无纺布。

Description

一种阻燃的无纺布的制备方法
技术领域
本发明涉及一种无纺布的制备方法，特别是涉及一种具有阻燃性能的无纺布的制备方法。
背景技术
无纺布的材质多为聚丙烯，因为其纤维无固定结构，不是经过纺织制成的，因此被称为无纺布。无纺布的应用较多，如被制作为口罩、台布、幕墙材料等。这些材质在应用中，有时需要具备较好的阻燃性能，若无纺布的阻燃性能较弱，在遇到明火时，有可能会发生燃烧的现象，危害人们的人身安全。提高无纺布的阻燃性能，需要对无纺布进行特殊的加工和处理，如采用一些阻燃物质附着于无纺布上，增强无纺布的阻燃性能。但是如何大范围的提高无纺布的阻燃性能，仍然有待研究。
发明内容
要解决的技术问题：普通的无纺布材料多为聚丙烯制备而成，在遇到明火时易燃，阻燃性能较差的问题。
技术方案：本发明公开了一种阻燃的无纺布的制备方法，包括以下步骤：（1）取聚丙烯材质的无纺布，将其室温下浸泡于水中1h～2h；（2）配制无纺布涂层，取硼酸锌粉末为6份～9份，膨润土为3～6份，聚磷酸铵为5～7份，硫酸铝为3～6份，ABS树脂为15份～18份；（3）加热后，将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀；（4）将加热后的涂层液涂布在无纺布的外表面，无纺布外涂层厚度为0.7mm～0.9mm，室温下晾干；（5）晾干后将无纺布保存，即为制备得到的阻燃的无纺布。
其中，无纺布中聚丙烯的含量优选为75wt%～85wt%。所述的硼酸锌粉末优选为6份。无纺布外涂层厚度优选为0.8mm～0.9mm。所述涂层中，ABS树脂的含量为优选为18份。
有益效果：本方法制备得到的无纺布具有良好的阻燃效果，测试阻燃性能的方法为GB/T5455-1997，本发明的无纺布阻燃等级为B1和B2级。
具体实施方式
实施例1
（1）取聚丙烯材质的无纺布，将其室温下浸泡于水中2h；（2）配制无纺布涂层，取硼酸锌粉末为9kg，膨润土为6kg，聚磷酸铵为5kg，硫酸铝为3kg，ABS树脂为15kg；（3）加热后，将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀；（4）将加热后的涂层液涂布在无纺布的外表面，无纺布外涂层厚度为0.9mm，室温下晾干；（5）晾干后将无纺布保存，即为制备得到的阻燃的无纺布。
实施例2
（1）取聚丙烯材质的无纺布，将其室温下浸泡于水中1h；（2）配制无纺布涂层，取硼酸锌粉末为6kg，膨润土为3kg，聚磷酸铵为6kg，硫酸铝为4kg，ABS树脂为18kg；（3）加热后，将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀；（4）将加热后的涂层液涂布在无纺布的外表面，无纺布外涂层厚度为0.8mm，室温下晾干；（5）晾干后将无纺布保存，即为制备得到的阻燃的无纺布。
实施例3
（1）取聚丙烯材质的无纺布，将其室温下浸泡于水中2h；（2）配制无纺布涂层，取硼酸锌粉末为7kg，膨润土为5kg，聚磷酸铵为7kg，硫酸铝为6kg，ABS树脂为17kg；（3）加热后，将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀；（4）将加热后的涂层液涂布在无纺布的外表面，无纺布外涂层厚度为0.7mm，室温下晾干；（5）晾干后将无纺布保存，即为制备得到的阻燃的无纺布。
对本发明的无纺布的阻燃性能进行了试验，试验方法为GB/T5455-1997，实施例1、实施例2、实施例3的无纺布的阻燃等级如下。
  实施例1 实施例2 实施例3
阻燃等级 B1 B2 B1
如表中所述，本发明的实施例1、实施例2、实施例3的无纺布的阻燃等级都较高，具有良好的阻燃性能，具有不易燃烧的特点。

Claims (5)

1. 一种阻燃的无纺布的制备方法，其特征在于包括以下步骤：（1）取聚丙烯材质的无纺布，将其室温下浸泡于水中1h～2h；（2）配制无纺布涂层，取硼酸锌粉末为6份～9份，膨润土为3～6份，聚磷酸铵为5～7份，硫酸铝为3～6份，ABS树脂为15份～18份；（3）加热后，将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀；（4）将加热后的涂层液涂布在无纺布的外表面，无纺布外涂层厚度为0.7mm～0.9mm，室温下晾干；（5）晾干后将无纺布保存，即为制备得到的阻燃的无纺布。
2. 根据权利要求1所述的一种阻燃的无纺布的制备方法，其特征在于无纺布中聚丙烯的含量为75wt%～85wt%。
3. 根据权利要求1所述的一种阻燃的无纺布的制备方法，其特征在于所述的硼酸锌粉末为6份。
4. 根据权利要求1所述的一种阻燃的无纺布的制备方法，其特征在于无纺布外涂层厚度为0.8mm～0.9mm。
5. 根据权利要求1所述的一种阻燃的无纺布的制备方法，其特征在于所述的ABS树脂为18份。
CN201310751316.XA 2013-12-31 2013-12-31 一种阻燃的无纺布的制备方法 Pending CN103757913A (zh)