CN103757881A - 一种防水耐磨的麻布的制备方法 - Google Patents

一种防水耐磨的麻布的制备方法 Download PDF

Info

Publication number
CN103757881A
CN103757881A CN201310749515.7A CN201310749515A CN103757881A CN 103757881 A CN103757881 A CN 103757881A CN 201310749515 A CN201310749515 A CN 201310749515A CN 103757881 A CN103757881 A CN 103757881A
Authority
CN
China
Prior art keywords
parts
burlap
preparation
resinous coat
linen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310749515.7A
Other languages
English (en)
Other versions
CN103757881B (zh
Inventor
张德轩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd
Original Assignee
SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd filed Critical SUZHOU XUANDE TEXTILE SCIENCE & TECHNOLOGY Co Ltd
Priority to CN201310749515.7A priority Critical patent/CN103757881B/zh
Publication of CN103757881A publication Critical patent/CN103757881A/zh
Application granted granted Critical
Publication of CN103757881B publication Critical patent/CN103757881B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种防水耐磨的麻布的制备方法，包括以下步骤：（1）取麻布，麻布由大麻和黄麻组成；（2）取碳化硅为12份～14份、二氧化锰为9份～12份、石英砂为11份～13份，将碳化硅、二氧化锰、石英砂用粉碎机粉碎至300目～450目后混合均匀；（3）取聚碳酸酯为4份～6份、聚芳砜为5份～7份、1-己烯为2份～3份，加热后将三种成分溶解均匀，为树脂涂层；（4）将步骤（2）中制备得到的粉末加入树脂涂层中，搅拌均匀；（5）将熔融的树脂涂层刮涂在麻布表面，树脂涂层厚度为0.2mm～0.4mm，通风晾干。

Description

一种防水耐磨的麻布的制备方法
技术领域
本发明涉及一种麻布的制备方法，特别是涉及一种具有防水和耐磨性能的麻布的制备方法。
背景技术
麻布由于其由麻纤维制备而成，麻纤维的强度较高，因此其耐磨性较好，但是其防水性能较差，在一些相应的用途当中，如麻布被用到帆布和车布中时，对麻布的防水性能有较高的要求。若麻布的防水性能较差，在多次和长时间雨淋的情况下，麻布会出现漏水的现象，影响正常的使用。此外，麻布还需要进一步提高它的耐磨的性能，如果耐磨性能不能满足需要的话，在多次的剐蹭和刻画之后可能麻布也会出现破损和透气的状况，这些都会极大的制约麻布的应用。
发明内容
要解决的技术问题：日常使用的普通的麻布的防水性能较差、麻布的耐磨性能还有待提高的问题。
技术方案：本发明公开了一种防水耐磨的麻布的制备方法，包括以下步骤：（1）取麻布，麻布由大麻和黄麻组成，大麻的质量分数为30wt%～45wt%，黄麻的质量分数为55wt%～70wt%；（2）取碳化硅为12份～14份、二氧化锰为9份～12份、石英砂为11份～13份，将碳化硅、二氧化锰、石英砂用粉碎机粉碎至300目～450目后混合均匀；（3）取聚碳酸酯为4份～6份、聚芳砜为5份～7份、1-己烯为2份～3份，加热后将三种成分溶解均匀，为树脂涂层；（4）将步骤（2）中制备得到的粉末加入树脂涂层中，搅拌均匀；（5）将熔融的树脂涂层刮涂在麻布表面，树脂涂层厚度为0.2mm～0.4mm，通风晾干。
制备过程中所述的黄麻的质量分数优选为70wt%。
制备过程中加入的碳化硅优选为14份。
制备过程中加入的1-己烯优选为3份。
所述的树脂涂层厚度优选为0.3mm～0.4mm。
有益效果：制备得到的麻布具有良好的防水性能和耐磨性能，麻布可室温下耐水喷淋30h至50h无漏水现象，在FZ/T01011-91的标准下，可耐磨的次数为762次至789次。 
具体实施方式
实施例1
（1）取麻布，麻布由大麻和黄麻组成，大麻的质量分数为45wt%，黄麻的质量分数为55wt%；（2）取碳化硅为12kg、二氧化锰为9kg、石英砂为13kg，将碳化硅、二氧化锰、石英砂用粉碎机粉碎至450目后混合均匀；（3）取聚碳酸酯为4kg、聚芳砜为7kg、1-己烯为3kg，加热后将三种成分溶解均匀，为树脂涂层；（4）将步骤（2）中制备得到的粉末加入树脂涂层中，搅拌均匀；（5）将熔融的树脂涂层刮涂在麻布表面，树脂涂层厚度为0.4mm，通风晾干。制备得到防水耐磨的麻布。
实施例2
（1）取麻布，麻布由大麻和黄麻组成，大麻的质量分数为35wt%，黄麻的质量分数为65wt%；（2）取碳化硅为14kg、二氧化锰为11kg、石英砂为12kg，将碳化硅、二氧化锰、石英砂用粉碎机粉碎至300目后混合均匀；（3）取聚碳酸酯为6kg、聚芳砜为5kg、1-己烯为2kg，加热后将三种成分溶解均匀，为树脂涂层；（4）将步骤（2）中制备得到的粉末加入树脂涂层中，搅拌均匀；（5）将熔融的树脂涂层刮涂在麻布表面，树脂涂层厚度为0.2mm，通风晾干。制备得到防水耐磨的麻布。
实施例3
（1）取麻布，麻布由大麻和黄麻组成，大麻的质量分数为30wt%，黄麻的质量分数为70wt%；（2）取碳化硅为13kg、二氧化锰为12kg、石英砂为11kg，将碳化硅、二氧化锰、石英砂用粉碎机粉碎至350目后混合均匀；（3）取聚碳酸酯为5kg、聚芳砜为6kg、1-己烯为3kg，加热后将三种成分溶解均匀，为树脂涂层；（4）将步骤（2）中制备得到的粉末加入树脂涂层中，搅拌均匀；（5）将熔融的树脂涂层刮涂在麻布表面，树脂涂层厚度为0.3mm，通风晾干。制备得到防水耐磨的麻布。
将实施例1、实施例2、实施例3制备得到的麻布展开，室温下向麻布上方喷淋水滴，喷淋时间分别为30h、40h、50h，喷淋后观察麻布是否有漏水现象。测定其耐磨次数，测试标准为FZ/T01011-91。结果如下。
  实施例1 实施例2 实施例3
防水性能 30h后未有漏水现象 40h后未有漏水现象 50h后未有漏水现象
耐磨次数 767 789 762
制备的麻布的防水性能和耐磨性能都较好，可以满足制备车布和帐篷等用具的需求，具有良好的市场前景。

Claims (5)

1.一种防水耐磨的麻布的制备方法，其特征在于包括以下步骤：（1）取麻布，麻布由大麻和黄麻组成，大麻的质量分数为30wt%～45wt%，黄麻的质量分数为55wt%～70wt%；（2）取碳化硅为12份～14份、二氧化锰为9份～12份、石英砂为11份～13份，将碳化硅、二氧化锰、石英砂用粉碎机粉碎至300目～450目后混合均匀；（3）取聚碳酸酯为4份～6份、聚芳砜为5份～7份、1-己烯为2份～3份，加热后将三种成分溶解均匀，为树脂涂层；（4）将步骤（2）中制备得到的粉末加入树脂涂层中，搅拌均匀；（5）将熔融的树脂涂层刮涂在麻布表面，树脂涂层厚度为0.2mm～0.4mm，通风晾干。
2.根据权利要求1所述的一种防水耐磨的麻布的制备方法，其特征在于所述的黄麻的质量分数为70wt%。
3.根据权利要求1所述的一种防水耐磨的麻布的制备方法，其特征在于制备过程中加入的碳化硅为14份。
4.根据权利要求1所述的一种防水耐磨的麻布的制备方法，其特征在于制备过程中加入的1-己烯为3份。
5.根据权利要求1所述的一种防水耐磨的麻布的制备方法，其特征在于所述的树脂涂层厚度为0.3mm～0.4mm。
CN201310749515.7A 2013-12-31 2013-12-31 一种防水耐磨的麻布的制备方法 Expired - Fee Related CN103757881B (zh)