CN103756536A - 铅锌合金表面耐冲击涂饰漆 - Google Patents

铅锌合金表面耐冲击涂饰漆 Download PDF

Info

Publication number
CN103756536A
CN103756536A CN201310742848.7A CN201310742848A CN103756536A CN 103756536 A CN103756536 A CN 103756536A CN 201310742848 A CN201310742848 A CN 201310742848A CN 103756536 A CN103756536 A CN 103756536A
Authority
CN
China
Prior art keywords
paint
parts
lead
coating paint
zinc alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310742848.7A
Other languages
English (en)
Inventor
陈汉刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU CITY BANGCHENG ELECTRICITY TECHNOLOGY CO LTD
Original Assignee
SUZHOU CITY BANGCHENG ELECTRICITY TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU CITY BANGCHENG ELECTRICITY TECHNOLOGY CO LTD filed Critical SUZHOU CITY BANGCHENG ELECTRICITY TECHNOLOGY CO LTD
Priority to CN201310742848.7A priority Critical patent/CN103756536A/zh
Publication of CN103756536A publication Critical patent/CN103756536A/zh
Pending legal-status Critical Current

Abstract

铅锌合金表面耐冲击涂饰漆，包括按照质量份数计的如下原料：直链十八碳脂肪酸醇酸树脂60-68份、颜料6-8份、三聚磷酸钠4-8份、聚醚改性硅氧烷0.1-0.5份、钛酸酯偶联剂0.2-0.4份、乙酸乙酯30-35份。本发明涂料对铅锌合金具有良好的附着力，漆膜的耐冲击强度较佳，可有效保护铅锌合金表面被氧化，可广泛应用于铅锌合金的涂饰。

Description

铅锌合金表面耐冲击涂饰漆
技术领域
本发明属于涂料领域，具体涉及一种铅锌合金表面耐冲击涂饰漆。
背景技术
近年来国内铅锌市场仍出现供不应求的局面，铅锌合金在工业生产中占据着重要地位。铅锌合金表面的涂饰漆既可有效防止铅被氧化，又可降低铅对施工人员的毒性影响，现有的铅锌表面涂饰漆仍存在附着力不佳耐冲击强度不佳的不足。
综上所述，如何克服现有技术的不足已成为涂料领域亟待解决的问题。
发明内容
本发明的目的是克服现有技术的不足而提出一种铅锌合金表面耐冲击涂饰漆，本发明涂料具有良好的附着力和耐冲击强度，可广泛应用于铅锌合金表面的涂饰。
本发明的技术方案如下：
铅锌合金表面耐冲击涂饰漆，包括按照质量份数计的如下原料：直链十八碳脂肪酸醇酸树脂60-68份、颜料6-8份、三聚磷酸钠4-8份、聚醚改性硅氧烷0.1-0.5份、钛酸酯偶联剂0.2-0.4份、乙酸乙酯30-35份。
所述的铅锌合金表面耐冲击涂饰漆，其中所述颜料为氧化铁红。
所述的铅锌合金表面耐冲击涂饰漆，其中所述钛酸酯偶联剂为钛酸四异丙酯或钛酸四丁酯中的一种
本发明的制备方法：按照质量配比，将各组分混合均匀，然后经砂磨机研磨至细度达20-25μm后出料，即得本发明成品。
有益效果：本发明涂料对铅锌合金具有良好的附着力，漆膜的耐冲击强度较佳，可有效保护铅锌合金表面被氧化，可广泛应用于铅锌合金的涂饰。
具体实施方式
本发明所述聚醚改性有机硅氧烷购自广州市怡申孚贸易有限公司，型号为NEK-1-11。
下面结合具体实施方式对本发明作进一步详细说明。
实施例1
铅锌合金表面耐冲击涂饰漆，包括按照质量份数计的如下原料：直链十八碳脂肪酸醇酸树脂60份、氧化铁红6份、三聚磷酸钠4份、聚醚改性硅氧烷0.1份、钛酸四异丙酯0.2份、乙酸乙酯30份。
将该成品进行性能检测，检测结果见表1。
实施例2
铅锌合金表面耐冲击涂饰漆，包括按照质量份数计的如下原料：直链十八碳脂肪酸醇酸树脂68份、钛白粉8份、三聚磷酸钠8份、聚醚改性硅氧烷0.5份、钛酸四丁酯0.4份、乙酸乙酯35份。
将该成品进行性能检测，检测结果见表1。
实施例3
铅锌合金表面耐冲击涂饰漆，包括按照质量份数计的如下原料：直链十八碳脂肪酸醇酸树脂66份、氧化铁红7份、三聚磷酸钠5份、聚醚改性硅氧烷0.3份、钛酸四异丙酯0.3份、乙酸乙酯32份。
将该成品进行性能检测，检测结果见表1。
将实施例1-3制备的成品进行性能测试，结果见表1：
表1 性能测试数据
性能 实施例1 实施例2 实施例3
耐冲击强度，J 20 25 25
附着力（划圈法），级 1 1 1
由上表可见，本发明涂料具有良好的附着力和耐冲击强度，实施例3所得产品效果较佳。
上述实施例仅是对本发明产品的说明，并非对本发明做出任何形式上的限制，在不脱离本发明的技术方案范围之内，任何利用上述揭示的技术内容作出简单变换的等同方案，均属本发明的保护范围。

Claims (3)

1.铅锌合金表面耐冲击涂饰漆，其特征在于，包括按照质量份数计的如下原料：直链十八碳脂肪酸醇酸树脂60-68份、颜料6-8份、三聚磷酸钠4-8份、聚醚改性硅氧烷0.1-0.5份、钛酸酯偶联剂0.2-0.4份、乙酸乙酯30-35份。
2.根据权利要求1所述的铅锌合金表面耐冲击涂饰漆，其特征在于，所述颜料为氧化铁红。
3.根据权利要求1所述的铅锌合金表面耐冲击涂饰漆，其特征在于，所述钛酸酯偶联剂为钛酸四异丙酯或钛酸四丁酯中的一种。
CN201310742848.7A 2013-12-30 2013-12-30 铅锌合金表面耐冲击涂饰漆 Pending CN103756536A (zh)