CN103289546A - 一种纳米复合汽车面漆 - Google Patents
一种纳米复合汽车面漆 Download PDFInfo
- Publication number
- CN103289546A CN103289546A CN2013101905675A CN201310190567A CN103289546A CN 103289546 A CN103289546 A CN 103289546A CN 2013101905675 A CN2013101905675 A CN 2013101905675A CN 201310190567 A CN201310190567 A CN 201310190567A CN 103289546 A CN103289546 A CN 103289546A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- dimethylbenzene
- automotive topcoat
- titanate coupling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开一种纳米复合汽车面漆，其特征在于是由以下原料按重量份数比制成的：醇酸树脂10-20份、聚酯树脂5-8份、环氧树脂0-10份、纳米二氧化硅3-10份、分散剂0.5-4份、二甲苯1-5份、钛白粉30-40份、轻质碳酸钙10-30份、钛酸酯偶联剂0-2份。本发明在汽车面漆中添加纳米二氧化硅，以提高汽车面漆的抗老化性能和力学性能。
Description
技术领域
本发明涉及一种汽车涂料组合物，具体是一种纳米复合汽车面漆，属于汽车表面的防护技术领域。
背景技术
汽车进入千家万户，汽车涂料的用量近几年得到不断增长，有机挥发物带来的环境问题也日益严重。汽车面漆是汽车外观的最终体现，汽车表面的平滑性、光泽赋予汽车高级、稳重、透明度等，都与油漆的性质有直接关系。汽车长期暴露在空气中，因此，汽车面漆必须具备优良的老化性能，才能够经受长时间太阳光的照射和风吹雨打等自然变化带来的破坏，具备优良的力学性能，防止出现的摩擦或碰撞所带来的损坏。
发明内容
本发明的目的在于提供一种耐气候变化、硬度高、耐摩擦、光泽好、附着力强的纳米复合汽车面漆。
本发明的目的可以通过以下技术方案实现：
一种纳米复合汽车面漆，其特征在于是由以下原料按重量份数比制成的：醇酸树脂10-20份、聚酯树脂5-8份、环氧树脂0-10份、纳米二氧化硅3-10份、分散剂0.5-4份、二甲苯1-5份、钛白粉30-40份、轻质碳酸钙10-30份、钛酸酯偶联剂0-2份。
本发明是由以下原料按重量份数比制成的：醇酸树脂15份、聚酯树脂6份、环氧树脂6份、纳米二氧化硅7份、分散剂2份、二甲苯1份、钛白粉35份、轻质碳酸钙25份、钛酸酯偶联剂1份。
本发明的制备方法：将醇酸树脂、聚酯树脂、环氧树脂放入混合釜中进行搅拌，搅拌下依次加入纳米二氧化硅、二甲苯、钛白粉、轻质碳酸钙，搅拌2小时，最后加入分散剂和钛酸酯偶联剂混合均匀，将混合液用超声分散仪分散90分钟，抽滤除去溶剂，得到本发明的纳米复合汽车面漆。
本发明的有益效果：本发明在汽车面漆中添加纳米二氧化硅，以提高汽车面漆的抗老化性能和力学性能。
具体实施方式
下面结合具体实施例对本发明作进一步描述。
实施例1
取重量份的醇酸树脂15份、聚酯树脂6份、环氧树脂6份、纳米二氧化硅7份、分散剂2份、二甲苯1份、钛白粉35份、轻质碳酸钙25份、钛酸酯偶联剂1份。
制备方法，取上述重量份的各组分，将醇酸树脂、聚酯树脂、环氧树脂放入混合釜中进行搅拌，搅拌下依次加入纳米二氧化硅、二甲苯、钛白粉、轻质碳酸钙，搅拌2小时，最后加入分散剂和钛酸酯偶联剂混合均匀，将混合液用超声分散仪分散90分钟，抽滤除去溶剂，得到本发明的纳米复合汽车面漆。
实施例2
取重量份的醇酸树脂20份、聚酯树脂8份、环氧树脂10份、纳米二氧化硅10份、分散剂0.5份、二甲苯5份、钛白粉30份、轻质碳酸钙10份、钛酸酯偶联剂2份。
制备方法，取上述重量份的各组分，将醇酸树脂、聚酯树脂、环氧树脂放入混合釜中进行搅拌，搅拌下依次加入纳米二氧化硅、二甲苯、钛白粉、轻质碳酸钙，搅拌2小时，最后加入分散剂和钛酸酯偶联剂混合均匀，将混合液用超声分散仪分散90分钟，抽滤除去溶剂，得到本发明的纳米复合汽车面漆。
Claims (2)
1.一种纳米复合汽车面漆，其特征在于是由以下原料按重量份数比制成的：醇酸树脂10-20份、聚酯树脂5-8份、环氧树脂0-10份、纳米二氧化硅3-10份、分散剂0.5-4份、二甲苯1-5份、钛白粉30-40份、轻质碳酸钙10-30份、钛酸酯偶联剂0-2份。
2.根据权利要求1所述的纳米复合汽车面漆，其特征在于是由以下原料按重量份数比制成的：醇酸树脂15份、聚酯树脂6份、环氧树脂6份、纳米二氧化硅7份、分散剂2份、二甲苯1份、钛白粉35份、轻质碳酸钙25份、钛酸酯偶联剂1份。