CN103756469A - 环保黑板漆 - Google Patents
环保黑板漆 Download PDFInfo
- Publication number
- CN103756469A CN103756469A CN201110383930.6A CN201110383930A CN103756469A CN 103756469 A CN103756469 A CN 103756469A CN 201110383930 A CN201110383930 A CN 201110383930A CN 103756469 A CN103756469 A CN 103756469A
- Authority
- CN
- China
- Prior art keywords
- agent
- friendly blackboard
- blackboard paint
- ball milling
- environmentally
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环保黑板漆的制备方法。本环保黑板漆将德固赛树脂、溶剂、颜料、湿润分散剂、消泡剂、表面助剂等预混合后进行球磨,当球磨达到5-8μm细度时,加入消光剂、流平平滑剂进行分散制成主剂,施工时与专用固化剂、稀释剂按比例混合均匀后进行涂装。所制备的漆具有不反光、抗尘污、附着力好、耐擦洗、防腐性、抗老化性强,不龟裂的性能,适用于底材为水泥板、铁板及玻璃板的黑板的涂装。
Description
一、 技术领域
本发明涉及一种黑板漆的制备方法。
二、 背景技术
许多学校教学用的黑板永久了,在室外强光的照射下,会产生局部反光现象,不但影响学生看清楚老师的板书,而且有损师生眼睛的健康。因此制备环保黑板漆,解决上述问题,成为市场的需求。
三、 发明内容
本发明的目的是:提供一种不反光、抗尘污、漆膜丰满、滑爽、色泽鲜艳、柔韧性好、附着力强、耐擦洗、防腐蚀、抗老化、不龟裂的环保黑板漆。
本发明的目的是采用以下方法实现的:
将德固赛PQ611丙烯酸树脂、溶剂、颜料、湿润分散剂、消泡剂、表面助剂等预混和后进行球磨,其特征在于:球磨达到5-8微米细度时,加入消光剂,流平平滑剂进行分散制成主剂,施工时与专用固化剂、稀释剂按比例混合均匀后进行涂装。
上述主剂的重量配比表:
德固赛丙烯酸树脂60-80,溶剂24-29,颜料3-9,湿润分散剂1.6-6.4,消泡剂0.29-0.5,表面助剂0.19-3.46,流平平滑剂0.16-1.65,消光剂为总浆料的6.1%-11.9%.
四、 具体实施方式
1. 球磨时转速45-60转/分钟,细度达到5微米时,加入消光剂、流平平滑剂进行分散制成主剂。
2. 所述的溶剂由丙二醇、醋酸丁酯 与重芳烃S-100B配制而成。
3. 在添加消光剂、流平平滑剂时,分散速度为1800-3500转/分钟,时间8-28分钟。
4. 表面助剂由芳香族聚异氰酸酯树脂、醋酸丁酯、有机硅配制而成。配比1.8-2.1:1.2-0.9:0.006-0.01。
5. 实施举例:
主剂配(重量KG)德固塞丙烯酸树脂60、溶剂24(丙二醇、醋酸丁酯、重芳烃S-100B按1:3:4的比例配制),颜料8。将各料预混合后加入进行球磨,转速为45]转/分钟,当浆料的细度达到5微米时到出,基料色浆制成,按色浆总量加入11.9%消光剂,改性聚硅氧烷0.3kg进行分散,转速1800转/分钟,时间28分钟,黑板漆主剂制成。
将芳香聚异氰酸树脂、醋酸丁酯、甲基硅氧烷按2.1:0.9:0.008的比例配制成专用固化剂。
将主剂、专用固化剂、稀释剂按3.7:1:适量混合,先将主剂与固化剂混合搅拌15分钟,视粘稠度情况加入适量稀释剂,混合均匀进行涂装。
Claims (3)
1.一种环保黑板漆的制备方法,其特征在于将德固赛PQ611丙烯酸树脂、溶剂、颜料、湿润分散剂、消泡剂、表面助剂等预混和后进行球磨,球磨达到5-8微米细度时,加入消光剂,流平平滑剂进行分散制成主剂,施工时与专用固化剂、稀释剂按比例混合均匀后进行涂装。
2.根据权利要求1所述,环保黑板漆的特征在于,重量配比为:德固赛丙烯酸树脂60-80,溶剂24-29,颜料3-9,湿润分散剂1.6-6.4,消泡剂0.29-0.5,表面助剂0.19-3.46,流平平滑剂0.16-1.65,消光剂为总浆料的6.1%-11.9%。
3.根据权利要求1所述,环保黑板漆的特征在于,球磨时转速45-60转/分钟,细度达到5微米时,加入消光剂、流平平滑剂进行分散制成主剂;在添加消光剂、流平平滑剂时,分散速度为1800-3500转/分钟,时间8-28分钟。