CN103756386A - 一种化妆用身体彩绘胶及其制备方法 - Google Patents
一种化妆用身体彩绘胶及其制备方法 Download PDFInfo
- Publication number
- CN103756386A CN103756386A CN201410025903.5A CN201410025903A CN103756386A CN 103756386 A CN103756386 A CN 103756386A CN 201410025903 A CN201410025903 A CN 201410025903A CN 103756386 A CN103756386 A CN 103756386A
- Authority
- CN
- China
- Prior art keywords
- colored drawing
- parts
- drawing glue
- acrylate
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种化妆用身体彩绘胶及其制备方法，该彩绘胶由以下重量份组分组成：乳液橡胶44-48份，水43-47份，增塑剂4-8份甲基丙烯酸1-3份，丙烯酸羟乙酯1-3份，卡松0.1-0.5份，增稠剂0.5-0.9份；其制备方法为按重量份称取乳液橡胶、水、增塑剂、甲基丙烯酸、丙烯酸羟乙酯、卡松，然后加入到搅拌釜中搅拌均匀；检测搅拌均匀的混合料，并用增稠剂调节粘度，检测合格即可。本发明的配方制备简单合理、使用安全、环保，给身体彩绘效果良好，适合于防水与无刺激性皮肤使用者使用。
Description
【技术领域】
本发明涉及一种化妆用身体彩绘胶及其制备方法。
【背景技术】
随着人们物质生活水平的大大提高，出门化化妆，打扮得漂漂亮亮已成为人们尤其是女性朋友必不可少的环节，当夏天来临时不少女性朋友会穿得比较清凉，会漏出身体的不少部位，如何让裸露在外的部位也变得漂亮成了目前许多时尚女性所追求的潮流，因此纹身彩绘胶的需求量非常的大，并且具有广阔的市场空间而目前市面上的纹身胶都不具备防水作用，天热一流汗，身体上的彩绘金粉会被弄得全身，变成晕妆，影响美观，于是本申请人对纹身彩绘胶提出了一种适合夏天并且防水的新型纹身彩绘胶。
【发明内容】
本发明的目的在于针对目前市场需求，提供了一种安全、环保、耐水及防水效果好，稳定性好的化妆用身体彩绘胶。
本发明的另一目的是为了提供一种该彩绘胶的制备方法。
本发明为了实现上述目的，采用以下技术方案：
一种化妆用身体彩绘胶，其特征在于由以下重量份组分组成：
本发明中的乳液橡胶选自丙烯酸丁酯，丙烯酸，丙烯酸酯，丙烯酸树脂，丙稀酸酯压敏胶，苯乙烯、丙烯酸、丙烯酸丁酯、甲基丙烯酸甲酯、乙烯、丁二烯，溶液型苯乙烯丁二烯橡胶，一般顺丁橡胶，乙烯丙烯酸正丁酯聚合物，由异戊二烯制得的高顺式合成橡胶，合成天然橡胶，聚氨酯橡胶，氯醇橡胶，丙烯酸酯橡胶中的一种；优选为丙烯酸丁酯。
本发明中的增塑剂选自丙烯酸异辛酯，丙烯酸-2-乙基己酯，2-丙烯酸-2-乙基己基酯，丙烯酸乙酯，醋酸乙酯，棕榈酸异辛酯，油酸异辛酯，硬脂酸异辛酯，水杨酸异辛酯，癸二酸二异辛酯，阿魏酸异辛酯，异辛酯，异丁酸异丁酯，异丁酸酯，异丁酸丁酯中的一种；优选为丙烯酸异辛酯。
本发明中的增稠剂选自膨润土，高岭土，硅藻土，有机增稠剂，纤维素类增稠剂，聚丙烯酸酯增稠剂和缔合型聚氨酯增稠剂中的一种；可以是琼脂，明胶，羧甲基纤维素钠，海藻酸钠，海藻酸钾，果胶，卡拉胶，阿拉伯胶，黄原胶，海藻酸丙二醇酯，罗望子多糖胶，羧甲基淀粉钠，淀粉磷酸酯钠，羟丙基淀粉，乙酰化二淀粉磷酸酯，羟丙基二淀粉磷酸酯，磷酸化二淀粉磷酸酯，甲壳素，黄蜀葵胶，亚麻子胶，田青胶，聚葡萄糖，槐豆胶，β-环状糊精，瓜尔胶，结冷胶，羟丙基甲基纤维素，皂荚糖胶，氧化淀粉，乙酰化己二酸双淀粉，酸处理淀粉，氧化羟丙基淀粉，磷酸酯双淀粉，葫芦巴胶，聚丙烯酸钠，沙蒿胶，辛烯基琥珀酸铝淀粉中的一种或几种。
本发明中甲基丙烯酸，用作提高粘接强度及稳定性。
本发明中丙烯酸羟乙酯为硬单体交联剂。
本发明中用卡松对水性胶进行防腐及抗菌。
本发明中增稠剂与水用于对整个体系的粘度进行调节，本发明产品粘度优选为8500-12000CPS。
本发明各组分协调使产品具有防水与持久的优点。
一种制备上述化妆用身体彩绘胶的方法，其特征在于包括以下步骤：
a、按重量份称取乳液橡胶、水、增塑剂、甲基丙烯酸、丙烯酸羟乙酯、卡松，然后加入到搅拌釜中搅拌均匀；
b、检测搅拌均匀的混合料，并用增稠剂调节粘度，检测合格即可。
步骤a中搅拌釜的转速优选为45～60转/分钟，搅拌时间优选为1～1.5小时。
检测合格的混合料（即身体彩绘胶）的粘度为8500-12000CPS。
本发明相对于现有技术，有以下优点：
本发明的配方合理，制备简单，使用安全、环保，给身体彩绘效果良好，适合于防水与无刺激性皮肤使用者使用。
【具体实施方式】
一种化妆用身体彩绘胶，其由以下重量份组分组成：
乳液橡胶，水，增塑剂，甲基丙烯酸，丙烯酸羟乙酯，卡松，增稠剂；
上述身体彩绘胶的制备方法为：按重量份称取乳液橡胶、水、增塑剂、甲基丙烯酸、丙烯酸羟乙酯、卡松，然后加入到搅拌釜中以45～60转/分钟的转速搅拌1～1.5小时至混合均匀，然后检测搅拌均匀的混合料，并用增稠剂调节粘度至标准范围8500-12000cps，检测合格即可灌装密封保存。
上述检测合格的检测方法主要是检验水性纹身彩绘胶的耐水性能和黏度是否符合要求，其测试方法为：将按上述步骤搅拌生产出来的水性纹身彩绘胶成品取一小部分出来置于玻璃上，粘接彩绘金粉放置4小时后进行100小时耐水性能测试，置于玻璃上干燥观察固化速度。
下面结合具体实施例对本发明作进一步描述（以下配比均为重量份）：
实施例1：
称取丙烯酸丁酯44份，水45份，丙烯酸异辛酯4份，甲基丙烯酸1份，丙烯酸羟乙酯3份，卡松0.3份，然后将称取的原料加入到搅拌釜中以45转/分钟的转速搅拌1～1.5小时至混合均匀，然后检测搅拌均匀的混合料，并用增稠剂0.5～0.9份调节粘度至标准范围，检测合格即可灌装密封保存。
实施例2：
称取丙烯酸丁酯46份，水43份，丙烯酸异辛酯6份，甲基丙烯酸2份，丙烯酸羟乙酯2份，卡松0.1份，然后将称取的原料加入到搅拌釜中以50转/分钟的转速搅拌1～1.5小时至混合均匀，然后检测搅拌均匀的混合料，并用增稠剂0.5～0.9份调节粘度至标准范围，检测合格即可灌装密封保存。
实施例3：
称取丙烯酸丁酯48份，水47份，丙烯酸异辛酯8份，甲基丙烯酸3份，丙烯酸羟乙酯1份，卡松0.5份，然后将称取的原料加入到搅拌釜中以55转/分钟的转速搅拌1～1.5小时至混合均匀，然后检测搅拌均匀的混合料，并用增稠剂0.5～0.9份调节粘度至标准范围，检测合格即可灌装密封保存。
实施例4：
称取丙烯酸丁酯46份，水45份，丙烯酸异辛酯6份，甲基丙烯酸1份，丙烯酸羟乙酯1份，卡松0.3份，然后将称取的原料加入到搅拌釜中以60转/分钟的转速搅拌1～1.5小时至混合均匀，然后检测搅拌均匀的混合料，并用增稠剂0.5～0.9份调节粘度至标准范围，检测合格即可灌装密封保存。
实施例5：
称取丙烯酸树酯46份，水45份，丙烯酸乙酯6份，甲基丙烯酸2份，丙烯酸羟乙酯2份，卡松0.3份，然后将称取的原料加入到搅拌釜中以50转/分钟的转速搅拌1～1.5小时至混合均匀，然后检测搅拌均匀的混合料，并用增稠剂0.5～0.9份调节粘度至标准范围，检测合格即可灌装密封保存。
实施例6：
称取丙稀酸酯压敏胶46份，水45份，丙烯酸-2-乙基己酯6份，甲基丙烯酸2份，丙烯酸羟乙酯2份，卡松0.3份，然后将称取的原料加入到搅拌釜中以50转/分钟的转速搅拌1～1.5小时至混合均匀，然后检测搅拌均匀的混合料，并用增稠剂0.5～0.9份调节粘度至标准范围，检测合格即可灌装密封保存。
实施例1-6的检测结果如表1所示：
表1：
Claims (7)
1.一种化妆用身体彩绘胶，其特征在于由以下重量份组分组成：
2.根据权利要求1所述的一种化妆用身体彩绘胶，其特征在于所述的乳液橡胶选自丙烯酸丁酯，丙烯酸，丙烯酸酯，丙烯酸树脂，丙稀酸酯压敏胶，苯乙烯、丙烯酸、丙烯酸丁酯、甲基丙烯酸甲酯、乙烯、丁二烯，溶液型苯乙烯丁二烯橡胶，一般顺丁橡胶，乙烯丙烯酸正丁酯聚合物，由异戊二烯制得的高顺式合成橡胶，合成天然橡胶，聚氨酯橡胶，氯醇橡胶，丙烯酸酯橡胶中的一种。
3.根据权利要求1所述的一种化妆用身体彩绘胶，其特征在于所述的增塑剂选自丙烯酸异辛酯，丙烯酸-2-乙基己酯，2-丙烯酸-2-乙基己基酯，丙烯酸乙酯，醋酸乙酯，棕榈酸异辛酯，油酸异辛酯，硬脂酸异辛酯，水杨酸异辛酯，癸二酸二异辛酯，阿魏酸异辛酯，异辛酯，异丁酸异丁酯，异丁酸酯，异丁酸丁酯中的一种。
4.根据权利要求1所述的一种化妆用身体彩绘胶，其特征在于所述的增稠剂选自膨润土，高岭土，硅藻土，有机增稠剂，纤维素类增稠剂，聚丙烯酸酯增稠剂和缔合型聚氨酯增稠剂中的一种。
5.一种制备权利要求1所述化妆用身体彩绘胶的方法，其特征在于包括以下步骤：
a、按重量份称取乳液橡胶、水、增塑剂、甲基丙烯酸、丙烯酸羟乙酯、卡松，然后加入到搅拌釜中搅拌均匀；
b、检测搅拌均匀的混合料，并用增稠剂调节粘度，检测合格即可。
6.根据权利要求5所述的一种制备化妆用身体彩绘胶的方法，其特征在于所述步骤a中搅拌釜的转速为45～60转/分钟，搅拌时间为1～1.5小时。
7.根据权利要求5所述的一种制备化妆用身体彩绘胶的方法，其特征在于所述检测合格的混合料的粘度为8500～12000CPS。